• KIEAE Journal
• /
• 제7권4호
• /
• pp.127-133
• /
• 2007

As a fundamental study on the corrosion resistance of reinforced concrete structures using Natural Inorganic Minerals exposed to carbonation environment, The test specimens were concrete(W/C=60%) with Natural Inorganic Minerals content of 0%, 10%. Accelerated carbonation and autoclave corrosion accelerated curing were then conducted with them. The corrosion resistance of steel in concrete with Natural Inorganic Minerals content of 0%, 10% was examined by corrosion form, half-cell potential, polarization resistance, corrosion area and weight loss after 24 hours of autoclave corrosion accelerated curing.The results of the study showed that as for steel in concrete with Natural Inorganic Minerals content of 10%, the corrosion resistance was more excellent than steel in concrete with Natural Inorganic Minerals content of 0%.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.537-542
• /
• 2001

Recently long-span bridges, such as Kwang-Ahn Grand bridge, Seo-Hae Grand Bridge, Young-Jong Grand Bridge, etc, have been designed and constructed near the shore. It needs to maintain the durability of marine concrete structures which are exposed to severe chloride environments. It is well known that corrosion of reinforcement steels in concrete structure is the most important cause for the durability of concrete structure which can be controlled by systematic preparatory corrosion protection works for economic and safe infrastructures. Various corrosion protection systems have been used for the corrosion protection of reinforcement steels from detrimental chemical components such as chloride, sulphate and etc. Since chloride can be penetrated into concrete in a variety way, an effective method has to be adopted by taking into full economical aspects and technical data of each protection system. The objective of this experimental study is to investigate the corrosion behavior of reinforcing steel in laboratory concrete specimens which are exposed to cyclic wet and dry saltwater, and then to develop pertinent corrosion protection system, such as corrosion inhibitors and cathodic protection for reinforced concrete bridges exposed to chloride environment. Resistance of various corrosion inhibitors and impressed current system have been experimentally evaluated under severe environmental conditions, and thus effective corrosion protection systems could have been Practically developed for future concrete construction.

• 콘크리트학회논문집
• /
• 제11권3호
• /
• pp.193-203
• /
• 1999

The corrosion of steel reinforcements in concrete is of great concern in recent years. This study is focused on the corrosion behavior of steel bars induced by internal chlorides in concrete at early ages. The main objective of this study is to determine the chloride thresholds causing depassivation and active corrosion of steel reinforcement in concrete. To examine the threshold concentration of chloride ion, the half-cell potential, chemical composition of expressed pore solutions of concrete and the rate of corosion area of the specimens were measured. Major variables include the added amount of chlorides in concrete, types of binders, and water-to-binder ration. From the present comprehensive experimental results, the factors influencing chloride-induced corrosion are investigated, and the chloride thresholds causing active corrosion of steel bars are proposed. The present study will enable to specify the realistic chloride limit in concrete which can be used in the future technical specification.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1996년도 가을 학술발표회 논문집
• /
• pp.207-212
• /
• 1996

Recently, massive concrete structures exposed to salt from ocean marine environments, or from winter deicing. The corrosion caused by chloride-penetration may affect severey the durability and service life of such a concretestructures. Thus, it is necessary to develop durable concrete to enhance the corrosion resistance. In this study, we investigate the usage of adequate corrosion-protection materials in order to reduce permability-coefficient of concrete and method of enhancing the durability of concrete structures using by penetrating corrosion-protection materials.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 봄 학술발표회 논문집
• /
• pp.345-350
• /
• 2001

Reinforced concrete is, in general, known as a high durability material due to a strong alkalinity of cement. Probable concrete cracks could incur steel corrosion of RC structures and then could easily deteriorate the concrete durability, which can be fully secured by a systematic quality control for the construction of concrete structures. For the corrosion protection of reinforcing steels in concrete, however, current design specifications of concrete cover depth do not in-depth consider the effect of the cracks as well as the chloride content of RC structures. Therefore, appropriate provisions for concrete cover depth should be coded by considering the influence of concrete cracks on the corrosion of reinforcing steels. The objective of this research is to investigate pertinent cover depth, which can prohibit rebar corrosion, on the basis of experimental corrosion measurements of reinforcing steels on crack characteristics such as the width, depth and frequency of concrete cracks.

• Structural Engineering and Mechanics
• /
• 제53권6호
• /
• pp.1183-1200
• /
• 2015

Reinforcement corrosion can cause serious safety deterioration to aging concrete structures exposed in aggressive environments. This paper presents an approach for reliability analyses of deteriorating reinforced concrete structures affected by reinforcement corrosion on the basis of the representative symptoms identified during the deterioration process. The concrete cracking growth and rebar bond strength evolution due to reinforcement corrosion are chosen as key symptoms for the performance deterioration of concrete structures. The crack width at concrete cover surface largely depends on the corrosion penetration of rebar due to the expansive rust layer at the bond interface generated by reinforcement corrosion. The bond strength of rebar in the concrete correlates well with concrete crack width and decays steadily with crack width growth. The estimates of cracking development and bond strength deterioration are examined by experimental data available from various sources, and then matched with symptom-based lifetime Weibull model. The symptom reliability and remaining useful life are predicted from the predictive lifetime Weibull model for deteriorating concrete structures. Finally, a numerical example is provided to demonstrate the applicability of the proposed approach for forecasting the performance of concrete structures subject to reinforcement corrosion. The results show that the corrosion rate has significant impact on the reliability associated with serviceability and load bearing capacity of reinforced concrete structures during their service life.

• International Journal of Concrete Structures and Materials
• /
• 제5권1호
• /
• pp.65-73
• /
• 2011

Corrosion of steel bars embedded in concrete admixed with 0%, 2% and 4% calcium nitrite (CN), having compressive strengths of 20 and 46 MPa was investigated. Reinforced concrete specimens were immersed in 3% NaCl solutions for 1, 7 and 15 days where 0.4A external current was applied to accelerate the chemical reactions. Corrosion rate was measured by retrieving electrochemical data via potentiodynamic polarization technique. Pull-out tests of reinforced concrete specimens were then conducted to assess the corroded steel-concrete bond characteristics. Experimental results showed that corrosion rate of steel bars and steel-concrete bond strength were dependent on concrete strength, amount of CN added and accelerated corrosion period. As concrete strength increased from 20 to 46 MPa, corrosion rate of embedded steel decreased. The addition of 2% CN to concrete of 20 MPa was not effective in retarding corrosion of steel at long time of exposure. However, the combination of higher strength concrete and 2% or 4% CN appear to be a desirable approach to reduce the effect of chloride-induced corrosion of steel reinforcement. After 1 day of corrosion acceleration, specimens without CN showed higher bond strength in both concrete mixes than those with CN. After 7 and 15 days of exposure, the higher concentration of CN, the higher bond strength in both concrete mixes achieved, except for the concrete specimen of 20 MPa compressive strength with 2% CN that recorded the highest deterioration in bond strength at 15 days of exposure.

• Steel and Composite Structures
• /
• 제14권3호
• /
• pp.229-242
• /
• 2013

Corrosion is important reason for the deterioration of the bond between reinforcing steel and the surrounding concrete. Corrosion of the steel mainly depends on its microstructure. Smooth S220, ribbed S420 and S500 grade reinforcing steels were used in the experiments. Samples were subjected to accelerated corrosion. Pullout tests were carried out to evaluate the effects of corrosion on bond strength of the specimens. S500 grade steel which has tempered martensite microstructure showed lower corrosion rate in concrete than S220 and S420 steels which have ferrite+perlite microstructure. S500 grade steel showed highest bond strength among the other steel grades in concrete. Bond strength between reinforcing steel and concrete increased with increase in the strength of steel and concrete. It also depends on whether reinforcing bar is ribbed or not.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 봄 학술발표회 논문집(I)
• /
• pp.129-134
• /
• 1999

Recent construction activities and maintenance of marine facilities have been accelerating to keep up with rapid economic growth in Korea. Marine concrete structures are to salts and chloride from ocean environments. The corrosion of reinforcement steel caused by chloride-penetration into concrete may severely affect the durability of concrete structures. the objective of this research is to develop a durable concrete by investigating the resistance of various corrosion protection systems utilizing different water/cement ratio, silica fumes, corrosion inhibitors, etc. A two-year verification test on various corrosion protection system has been doing in the laboratory. Corrosion investigations on reinforcement steel are now under progress for more than 63 concrete specimen. Corrosion-related measurements include microcell corrosion current.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회논문집(I)
• /
• pp.503-507
• /
• 2000

The corrosion protection methods of reinforcing steel in concrete are the various methods such as increasing thickness of cover concrete, using of reinforcing bars coated with epoxy, dosage of corrosion inhibitor as concrete admixture, cathodic protection method and etc. In this study, the performance of corrosion protection was investigated for the test specimens using corrosion inhibitors and cathodic protection, respectively. For this purpose, the accelerated corrosion tests for reinforcing steel were conducted according to the periodic cycles(140 days) of wetting($65^{\circ}C$, 90% R.H) and drying period($15^{\circ}C$, 65% R.H) for the test specimens. As a result, it can be concluded from the test that the effect of corrosion inhibitor was found to be variable with products, the cathodic protection method was found to be independent of salt concentration in concrete.