Various compressive specimens were fabricated using autoclave do-gassing moulding to find out the compressive characteristics of the carbon/epoxy plain weave fabric composites with respect to the bias and shear angles. The stacking angles of the bias specimens are $[0]_{10T,}\;[3]_{10T,}\;[6]_{10T,}\;[9]_{10T,}\;[12]_{10T,}\;[15]_{10T,}\;[30]_{10T,}\;[45]_{10T}$ and those of the sheared specimens are $[{\pm}37]_{10T,}\;[{\pm}32]_{10T,}\;[{\pm}28]_{10T,}\;[{\pm}22]_{10T,}$ respectively. In order to verify the effect of micro-tow structures on compressive strength and modulus of the composites, compressive test specimens of uni-directional carbon/epoxy composites with the same materials and the same stacking conditions were fabricated. The modulus and strength of both types of composite specimens were compared with the prediction results based on the CLPT and a proposed strength formula. The tow deformation and fracture modes were investigated by microscopic observation.

• 한국농공학회지
• /
• 제18권3호
• /
• pp.4163-4170
• /
• 1976

This study was conducted to investigate the effect of starch as a retarder on the maximum dry density and the unconfined compressive strength of soil cement mixtures for varied starch contents (0-3%), cement contents (3-12%), and delay times (0-6hrs) in four soils. The experimental results obtained from maximum dry density and unconfined compressive strength tests are as follows: 1. Maximum dry density and unconfined compressive strength were increased greatly in soil cement mixtues rwhen starch was added as retarder but their value schanged according to soil varieties. 2. Maximum dry density showed at about 0.5 percent to 1.0 percent of starch in KY soil and about 2.0 percent to 2.5 percent in SS soil when delay time was changed in 2.4, and 6 hours in compaction test. 3. The larger content of cement was, the bigger effects of maximum dry density and compressive strength were in soil cement. mixtures. 4. As delay time changed 2.4, and 6 hours in compaction test, 7-day unconfined compressive strength showed the biggest value at about 0.5 percent of starch in KY soil and 2.0 percent in SS soil, and the maximum value of 28-day unconfined compressive strength showed at about 0.5 percent in KY soil and 1.5 percent in SS soil.

• International Journal of Concrete Structures and Materials
• /
• 제10권2호
• /
• pp.221-236
• /
• 2016

The aim of this paper is to investigate the compressive behavior and characteristics of amorphous metallic fiber-reinforced concrete (AMFRC). Compressive tests were carried out for two primary parameters: fiber volume fractions ($V_f$) of 0, 0.3, 0.6 and 0.8 %; and design compressive strengths of 27, 35, and 50 MPa at the age of 28 days. Test results indicated that the addition of amorphous metallic fibers in concrete mixture enhances the toughness, strain corresponding to peak stress, and Poisson's ratio at high stress level, while the compressive strength at the 28-th day is less affected and the modulus of elasticity is reduced. Based on the experimental results, prediction equations were proposed for the modulus of elasticity and strain at peak stress as functions of fiber volume fraction and concrete compressive strength. In addition, an analytical model representing the entire stress-strain relationship of AMFRC in compression was proposed and validated with test results for each concrete mix. The comparison showed that the proposed modeling approach can properly simulate the entire stress-strain relationship of AMFRC as well as the primary mechanical properties in compression including the modulus of elasticity and strain at peak stress.

• 한국철도학회논문집
• /
• 제12권1호
• /
• pp.110-114
• /
• 2009

본 연구에서는 스카프 패취가 접착된 복합소재 샌드위치 적층판의 압축강도 회복특성을 평가하였다. 본 연구에서는 알루미늄 허니콤 심재와 CF1263 직조된 탄소/에폭시 면재를 갖는 틸팅열차차체에 적용된 샌드위치 시험편이 이용되었다. 샌드위치 시험편은 저속충격에 의해 손상을 가하고, 스카프 보수기법에 의해 보수되었다. 보수 후 CAI시험을 통해 충격 후 압축강도를 평가하여 강도회복정도를 정량적으로 규명하였다. 본 시험으로부터 단지 스카프 보수를 적용한 경우 약 72%정도의 강도를 회복하였고, 추가보수층 한층을 추가했을 경우 약 91%까지 강도를 회복시킬 수 있음을 확인하였다.

• Geomechanics and Engineering
• /
• 제14권2호
• /
• pp.203-209
• /
• 2018

Reliable estimation of compressive as well as tensile in-situ stresses is critical in the design and analysis of underground structures and openings in rocks. Kaiser effect technique, which uses acoustic emission from rock specimens under cyclic load, is well established for the estimation of in-situ compressive stresses. This paper investigates the Kaiser effect on marble specimens under cyclic uniaxial compressive as well as cyclic uniaxial tensile conditions. The tensile behavior was studied by means of Brazilian tests. Each specimen was tested by applying the load in four loading cycles having magnitudes of 40%, 60%, 80% and 100% of the peak stress. The experimental results confirm the presence of Kaiser effect in marble specimens under both compressive and tensile loading conditions. Kaiser effect was found to be more dominant in the first two loading cycles and started disappearing as the applied stress approached the peak stress, where felicity effect became dominant instead. This behavior was observed to be consistent under both compressive and tensile loading conditions and can be applied for the estimation of in-situ rock stresses as a function of peak rock stress. At a micromechanical level, Kaiser effect is evident when the pre-existing stress is smaller than the crack damage stress and ambiguous when pre-existing stress exceeds the crack damage stress. Upon reaching the crack damage stress, the cracks begin to propagate and coalesce in an unstable manner. Hence acoustic emission observations through Kaiser effect analysis can help to estimate the crack damage stresses reliably thereby improving the efficiency of design parameters.

• 한국지반공학회논문집
• /
• 제35권9호
• /
• pp.15-28
• /
• 2019

PHC말뚝을 생산하는 17개 중소산업체의 품질 성능 검사 자료, 17개 중소산업체 및 6개 대기업 산업체의 장기허용압축하중 제원 표를 분석하였다. 현 단계의 국내 설계에서는 PHC말뚝의 장기허용압축하중의 평균 약 70% 수준을 반영하고 있고 품질이 우수함에도 불구하고 PHC말뚝의 장기허용압축하중에는 안전율 4.0을 적용하고 있다. 대부분의 품질 검사 기준은 KS F 4306에 명시되어 있다. 그러나 원심력으로 다져진 콘크리트 압축강도시험 기준은 KS F 2454에 명시되어 있다. 각 제조사의 품질 시험 자료를 분석한 결과 모든 항목에서 기준값 보다 높은 성능을 보였다. 따라서 PHC말뚝 설계 시 PHC말뚝의 지지력을 PHC말뚝의 허용연직압축하중의 최대값까지 사용할 수 있을 것으로 판단되었다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제20권2호
• /
• pp.1-9
• /
• 2016

저자들은 비파괴시험에 의한 고강도콘크리트의 강도 예측식을 제안하기 위하여 실험적 연구를 수행하였다. 본 연구에서 사용된 콘크리트의 설계압축강도는 40~80 MPa 범위이며, 압축공시체를 제작하여 반발경도법과 초음파 속도법으로 실험한후 KS기준에 따라 압축강도 실험을 실시하였다. 실험결과는 기존의 연구자들에 의하여 제안된 다양한 실험예측식들과 비교분석하였다. 실험결과 고강도 콘크리트에서도 반발경도법과 초음파속도법의 경우 간편성과 신뢰성에 있어 콘크리트 강도를 측정하기에 충분한 유용성을 확보한 것을 확인할 수 있었다. 기존식들과의 비교를 통하여 고강도 콘크리트에 적합한 강도예측식을 제안하였으며, 실험결과에 대한 충분한 신뢰성을 확보한 것으로 판단되어, 향후 고강도 콘크리트 구조물에 적용할 수 있을 것으로 판단된다.

• 한국재난정보학회 논문집
• /
• 제14권1호
• /
• pp.79-88
• /
• 2018

본 연구에서는 긴급복구용 팽창재료의 온도에 따른 팽창량 및 강도의 변화를 컵발포 실험과 일축압축강도 실험을 통하여 물리적 특성을 확인하였고, 장기안전성을 확인하기 위하여 가속 압축 크리프 시험을 진행하였다. 크리프 성능을 평가하기 위하여 단기 크리프 시험과 가속 압축 크리프 실험을 실시하였으며, 단기크리프 실험은 팽창재료의 초기 크리프 변형률을 결정하고 시간-온도 중첩정리가 적용된 단계 등온법은 가속시험방법으로 장기 압축 크리프 성능을 평가하였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 추계 학술논문 발표대회
• /
• pp.77-79
• /
• 2012

This paper intends to review possible application in the high strength area through compressive strength estimation of the simulated high strength concrete member using Rock Test Hammer and suggest it as a reference data for the strength estimation technique of the ultra high strength concrete in the future. From the results of our test, in the low strength area less than 15MPa and normal strength area in 15~60MPa, as shown on the existing studies, it is indicated that P Type Schmidt Hammer in the low strength area and N Type Schmidt Hammer in the normal strength area have high correlation of rebound-compressive strength. As the Rock Test Hammer indicated more or less reduced accuracy in the low strength area and the normal strength area but high correlation on the high strength area (50~100MPa) defined on this test, it is determined that it would be possible to make the fastest and simplest compressive strength estimation on the site where the high strength concrete is applied.

• Composites Research
• /
• 제22권2호
• /
• pp.24-29
• /
• 2009

본 연구에서는 알루미늄 허니컴 코어와 카본 면재가 적용된 샌드위치 복합재 구조에 대해 준정적 압입 손상 이후의 잔류 강도 평가에 대한 연구를 수행하였다. 3점 굽힘 시험과 압축 시험을 통해 시편의 강도를 확인하고 시편에 손상을 모사하기 위하여 준정적 압입 손상을 가하였다. 손상된 시편을 손상 전 시편과 동일한 시험을 통해 손상 전의 강도와 비교하였다. 압입 손상 이후 압축 강도와 굽힘 강도는 압입 깊이의 증가에 따라 강도가 감소하였고 손상 단계에 따른 잔류 강도 정도를 확인하였다.