• 한국재료학회지
• /
• 제12권6호
• /
• pp.447-451
• /
• 2002

Pulsed DC-plasma nitriding has been applied to form nitride layer having only a diffusion layer. The discharge current with the variation of discharge gases is proportional to the intensity of $N_2^+$ peak in optical emission spectroscopy during the plasma nitriding. The discharge current, microhardness in surface of substrate and depth of nitride layer increased with the ratio of $N_2\;to\;H_2$ gas in discharge gases. When the ratio of $N_2\;to\;H_2$ is lower than 60% in the discharge gases, high microhardness value of 1100Hv nitride layer which contains no compound layer has been formed.

• 열처리공학회지
• /
• 제12권1호
• /
• pp.9-20
• /
• 1999

The effect of post oxidation, water-quenched after holding in air for 5~420 seconds or cooling or furnace cooling, on corrosion resistance and phase formation characteristics of the surface layer of SM20C and SM45C carbon steels after gas nirtrocarbursing in the $NH_3-5%CO_2-N_2$ gas atmosphere at $580^{\circ}C$ for 3hours is studied. The compound layers of two steels consist of ${\varepsilon}-Fe_{2-3}N$, ${\gamma}^{\prime}-Fe_4N$ and $Fe_3O_4$, phases, however, the quantity of ${\gamma}^{\prime}-Fe_4N$ phase increases for the furnace cooled specimen compared to that of air cooling specimen. With increasing $NH_3$ content in the gas mixture and also increasing the keeping time in the air after gas nitrocarburising, the ${\varepsilon}-Fe_{2-3}N$ phase of compound layer increases, while the decreased current density recognizing the improvement of corrosion resistance are shown. the passive current density of SM45C steel is lower than that of SM20C steel at the same nitrocarburising conditions.

• 한국광물학회지
• /
• 제17권1호
• /
• pp.75-83
• /
• 2004

석조문화재 표면에 형성된 흑화 부위는 미적인 면에서뿐만 아니라 문화재 자체에도 손상을 끼치기 때문에 많은 문제가 되고 있다. 이러한 흑화 부위는 종종 많은 량의 철화합물을 함유하고 있어서, 다른 요소들과 함께 철화합물도 암석 표면의 흑화 현상에 영향을 끼치는 것으로 추정되고 있다. 독일 베를린 시에 있는 석조문화재(Museumsinsel) 내의 표면에서 시료를 채취한 후 함유 철의 이온상태와 화학성분을 결정하기 위하여 뫼스바우어 분광분석법을 사용하였다. 사용된 암석의 원상태와 흑화 부위의 분말시료에 대한 광물학적 및 화학적 분석을 선회절법과 X-선형광법으로 각각 시행하였다. 형성된 철 성분의 기원은 흑화 부위의 제거 등 석조문화재의 보존처리에 중요한 단서를 제공하기 때문에, 철을 다량 함유하고 있는 적색 사암에서 형성된 흑화 부위와 매우 소량 함유하고 있는 백색사암의 표면에 형성된 흑화 부위를 비교하였다. 연구 결과 백색사암 흑화 부위에서는 주변 환경물질에서 기인한 철 성분이, 적색사암 흑색부위에서는 원암에서 보여지는 철 성분이 주성분으로 추정되었다. 적색사암에 있어서는 흑화부위를 제거한 이후에라도 흑화의 주원인인 철 성분이 계속해서 모암의 내부로부터 표면으로 이동될 수 있기 때문에, 제거 이외의 보존처리법이 더 연구되어야한다.

• 대한기계학회논문집
• /
• 제8권5호
• /
• pp.476-480
• /
• 1984

본 연구에서는 S15C 및 S45C의 이온 질화에 있어서 확산층 및 합성층의 생성 속도를 계산하였고 이를 기초로 질소의 활성화 에너지를 구하였다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.487-492
• /
• 2002

The growth kinetics of intermetallic compound layers formed between eutectic Sn-58Bi solder and (Cu, electroless Ni-P/Cu) substrate were investigated at temperature between 70 and 120 C for 1 to 60 days. The layer growth of intermetallic compound in the couple of the Sn-58Bi/Cu and Sn-58Bi/electroless Ni-P system satisfied the parabolic law at given temperature range. As a whole, because the values of time exponent (n) have approximately 0.5, the layer growth of the intermetallic compound was mainly controlled by volume diffusion over the temperature range studied. The apparent activation energies of Cu$_{6}$Sn$_{5}$ and Ni$_3$Sn$_4$ intermetallic compound in the couple of the Sn-58Bi/Cu and Sn-58Bi/electroless Ni-P were 127.9 and 81.6 kJ/mol, respectively.ely.

• 한국표면공학회지
• /
• 제55권6호
• /
• pp.408-416
• /
• 2022

In this study, the effect of Au-Sn alloy coating on reliability of electrical contacts was investigated via comparison with Au-Co alloy coating. The results show that Au-Sn alloy exhibited lower contact resistance and higher solder spreadability than those of Au-Co alloy after thermal aging. In the case of Au-Co alloy plating, the underlying Ni element diffused into Au-Co layer to form Ni oxides on surface during thermal aging, leading to increased contact resistance and decreased solder spreadability. Meanwhile, for Au-Sn alloy plating, Au-Ni-Sn metallic compound was formed at the interface between Au-Sn layer and underlying Ni layer. This compound acted as a diffusion barrier, thereby inhibiting the diffusion of Ni to Au-Sn layer during thermal aging. Consequently, Au-Sn alloy layer showed better contact reliability than that of Au-Co alloy layer.

• Mycobiology
• /
• 제37권1호
• /
• pp.31-36
• /
• 2009

A phytochemical study on the flower of Calotropis gigantea (Linn.) using silica gel column chromatography and preparative thin layer chromatography, led to the first time isolation of Di-(2-ethylhexyl) phthalate (compound 1) and anhydrosophoradiol-3-acetate (compound 2). The structures of these compounds were confirmed by spectroscopic analyses (IR, HRTOFMS and NMR). The antibacterial and antifungal activities of ethyl acetate extract, compound 1 and compound 2 were measured using the disc diffusion method. Ethyl acetate extract and compound 1 presented better results than compound 2. The minimum inhibitory concentrations (MICs) of the extract and compounds were found to be in the range of $16{\sim}128{\mu}g/ml$. The cytotoxicity ($LC_{50}$) against brine shrimp nauplii (Artemia salina) were also evaluated and found to be 14.61 ${\mu}g/ml$ for ethyl acetate, 9.19 ${\mu}g/ml$ for compound 1 and 15.55 ${\mu}g/ml$ for compound 2.

• 열처리공학회지
• /
• 제12권2호
• /
• pp.117-128
• /
• 1999

This study was carried out to investigate the surface characteristics of SCM440 steel nitrided with various nitrogen contents for 7 hours at $520^{\circ}C$ by using micro-pulse plasma nitriding apparatus of hot wall type. The effects of oxidation treatment was also investigated on plasma nitrided in 30% nitrogen and post oxidized SCM440 steel at $500^{\circ}C$ in $H_2O$ atmosphere. The ${\gamma}^{\prime}-Fe_4N$ and ${\varepsilon}-Fe_{2-3}N$ phases were detected in compound layer of the nitrided steel. As the content of nitrogen in plasma gas increased with 30, 50, 70% on the micro-pulse plasma nitriding for SCM440 steel, the thickness of compound, diffusion layer and the surface hardness were increased. From the wear test results, the best wear resistance was appeared in the condition of ductile ${\gamma}^{\prime}-Fe_4N$ phase formed specimen at 30% nitrogen, whereas that of the treated with 50% and 70% nitrogen decreased owing to the exfoliation of brittle ${\varepsilon}-Fe_{2-3}N$ phase in the compound layer. On the nitrided and subsequently oxidized SCM440 steel, the surface layer consisted of $Fe_3O_4$, ${\gamma}^{\prime}-Fe_4N$, and ${\varepsilon}-Fe_{2-3}N$ phases. In these treatments, the dissolution of nitrides affect hardness and hardening depth in compound and diffusion layers. For the nitrided in 30% nitrogen and post oxidized specimen at $500^{\circ}C$ for 1 hour, the wear resistance was lower than that of the only nitrided one in 30% nitrogen but higher than those of the nitrided ones in 50 and 70% nitrogen.

• 한국항공우주학회지
• /
• 제48권9호
• /
• pp.671-680
• /
• 2020

본 연구에서는 복합형 회전익 항공기 동체의 설계를 위해 확장된 보 해석을 기술한다. 개발된 보 접근 방법은 등가 보강재 층 방법을 사용하여 보강재로 구성된 동체의 해석이 가능하다. 통합 정식화 보 이론에 기반하여 외피의 두께 및 적층 고려 방법을 제시하였다. 보강재가 고려된 동체에 대해 등가 보강재 층 방법을 적용하여 해석을 수행하였고, 보강재의 제원에 관한 예비 연구 결과를 도출하였으며 상용 프로그램을 이용하여 검증 및 비교를 수행했다.

• 열처리공학회지
• /
• 제9권2호
• /
• pp.130-138
• /
• 1996

It has been investigated that the ion nitriding effects of a STD61 steel in various time conditions of 3 to 9 hours, and the microstructure of compound and diffusion layers of the ion nitrided specimen for 6 hours and subsequently reheated for 1 hour at various temperatures of $400{\sim}800^{\circ}C$ As the nitriding time increased, the thickness of compound and diffusion layers was increased, but the hardness of surface was not considerably increased (Max Hv=1045 at 9hrs). Some of the nitrogen was denitrided out of the surfac and diffused into the core, and also the oxides ($Fe_3O_4$, $Fe_2O_3$) were formed on the surface of the specimen during reheating. The compound layer was partially decomposed at about $600^{\circ}C$ but the diffusion layer was increased up to $800^{\circ}C$. With increasing reheated temperture, the hardness of the surface was decreased, whereas the hardness depth of diffusion layer (0.25mm) was increased up to $600^{\circ}C$ more than that of ion nitrided (0.18mm). The blend-heat treated STD61 steel by ion nitriding is therefore expected to hold on the characteristics of ion nitriding up to $600^{\circ}C$.