• Journal of the korean academy of Pediatric Dentistry
• /
• v.27 no.3
• /
• pp.410-418
• /
• 2000

An in vitro study was performed to evaluate the effect of four variables on the temperature rise produced by polishing of restorations. The four variables were : restorative material, base, thickness of remaining dentin, continuous polishing or intermittent polishing. Class V cavities were cut on extracted molar and restored with composite resin, resin-modified glass ionomer cement, compomer, amalgam on the various bases (glass ionomer cement, zinc oxide eugenol cement, zinc phosphate cement) Dentin thickness under the restoration was 0.5mm, 1.5mm. Polishing was done with an aluminum oxide-coated disc. Polishing time was continuous or intermittent for up to 1 minute. Intra-pulpal temperature increased almost linearly in all cases. Amalgam produced highest temperature rises at the pulp, while the composite resin, resin-modified glass ionomer cement and compomer were not different for each other. The rate and extent of temperature rising of amalgam restoration was reduced by presence of a cement base. Zinc oxide eugenol cement bases showed the highest temperature rise, while glass ionomer cement, zinc phosphate cement were not different to the untreated tooth Thickness of remaining dentin was only significant for the amalgam restoration. Continuous polishing produced higher temperature rise than intermittent polishing.

• Restorative Dentistry and Endodontics
• /
• v.25 no.1
• /
• pp.17-40
• /
• 2000

Resin cements are used for cementing indirect esthetic restorations such as resin or porcelain inlays. Because of its limitations in curing of purely light cured resin cements due to attenuation of the curing light by intervening materials, dual cured resin cements are recommended for cementing restorations. The physical properties of resin cements are greatly influenced by the extent to which a resin cures and the degree of cure is an important factor in the success of the inlay. The purpose of this study was to evaluate the influence of porcelain thickness and exposure time on the polymerization of resin cements by measuring the microhardness and the degree of conversion, to investigate the nature of the correlation between two methods mentioned above, and to determine the exposure time needed to harden resin cements through various thickness of porcelain. The degree of resin cure was evaluated by the measurements of microhardness [Vickers Hardness Number(VHN)] and degree of conversion(DC), as determined by Fourier Transform Infrared Spectroscopy(FTIR) on one light cured composite resin [Z-100(Z)] and three dual cured resin cements [Duo cement(D), 3M Resin cement(R), and Dual cement(DA)] which were cured under porcelain discs thickness of 0mm, 1mm, 2mm, 3mm with light exposure time of 40sec, 80sec, 120sec, and regression analysis was performed to determine the correlation between VHN and DC. In addition, to determine the exposure time needed to harden resin cements under various thickness of porcelain discs, the changes of the intensity of light attenuated by 1mm, 2mm, and 3mm thickness of porcelain discs were measured using the curing radiometer. The results were obtained as follows ; 1. The values of microhardness and the degree of conversion of resin cements without intervening porcelain discs were 31~109VHN and 51~63%, respectively. In the microhardness Z was the highest, followed by R, D, DA. In the degree of conversion, D and DA was significantly greater than Z and R(p<0.05). 2. The microhardness and the degree of conversion of the resin cements decreased with increasing thickness of porcelain discs, and increased with increasing exposure time, D and R showed great variation with inlay thickness and exposure time, whereas, DA showed a little variation. 3. The intensity of light through 1mm, 2mm, and 3mm porcelain inlays decreased by 0.43, 0.25, and 0.14 times compared to direct illumination, and the respective needed exposure times are 53 sec, 70 sec, and 93 sec. In D and R, 40 sec of light irradiation through 2mm porcelain disc and 80 sec of light irradiation through 3mm porcelain disc were not enough to complete curing. 4. The microhardness and the degree of conversion of the resin cements showed a positive correlationship(R=0.791~0.965) in the order of R, D, Z, DA. As the thickness of porcelain discs increased, the decreasing pattern of microhardness was different from that of the degree of conversion, however.

• Journal of Wind Energy
• /
• v.10 no.4
• /
• pp.20-27
• /
• 2019

High-speed shaft coupling in a wind power system transmits power and absorbs variations in length and spindle dislocation between the gearbox and generator. Furthermore, the coupling has an insulation function that prevents electrical corrosion caused by the flow of the generator's current into the gearbox and prevents overload resulting from sudden power failure from being transferred to the gearbox. Its design, functions, and part verification are described in the IEC61400 and GL Guidelines, which specify that the part must have a durability life of 20 years or longer under distance variation and axial misalignment between the gearbox and the generator. This study presents the design of a high-speed coupling through composite stiffness calculation, structural analysis, and comparative analysis of test and theory to identify the characteristics of high-speed coupling for a large-capacity 6 MW wind power generator. A prototype was fabricated by optimizing the manufacturing process for each part based on the design, and the reliability of the fabricated prototype was verified by evaluating the performance of the target quantitative evaluation items.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.2
• /
• pp.133-141
• /
• 2004

Statement of problem : Porcelain restorations are widely used in restorative dentistry with a high degree of general success. However, porcelain is brittle and may fracture intraorally. Sometimes a repair may be attempted using composite resin and bonding system available. Color stability of porcelain repair resins affects esthetics and prognosis of prosthesis, so that provides important criteria for the choice of porcelain repair resins. Purpose : The purpose of this study was to investigate the color stability of composite resins used widely as porcelain repair system. Materials and method : Composite resins used for this study were Carisma(Kulzer, Germany), Tetric ceram(Ivoclar, Liechtenstein), Filtek Z250(3M, USA), and Arabesk Top(VOCO, Germany). Thirty disc-shaped specimens($10{\times}2mm$) were fabricated from each composite resin. Color changes of specimens after treatment using thermocycling system(KD-TCS30, Kwang-duk F.A. Korea) and after immersion in methylene blue(0.05% by Wt) were measured with colorimeter(Model Tc-6Fx, Tokyo Denshoku Co.) and obtained data were analyzed. Results and Conclusion: The results obtained from this study were as fo11ows. 1. The color change of Filtek Z250 was lesser than those of Tetric ceram and Arabesk Top after thermocycling (12000 times). 2. All of the composite resins in this study showed increase of color change according to increase of thermocycling frequency. 3. After treatment with methylene blue, the color change of Arabesk Top was greater than those of Carisma and Tetric ceram, and Tetric ceram was more stable than others.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.5
• /
• pp.322-328
• /
• 2020

PURPOSE. This study evaluated the shear bond strength between 3D printed provisional resin and conventional provisional resin depending on type of conventional provisional resin and different surface treatments of 3D printed resin. MATERIALS AND METHODS. Ninety-six disc-shaped specimens (Ø14 mm × 20 mm thickness) were printed with resin for 3D printing (Nextdent C&B, Vertex-Dental B. V., Soesterberg, Netherlands). After post-processing, the specimens were randomly divided into 8 groups (n=12) according to two types of conventional repair resin (methylmethacrylate and bis-acryl composite) and four different surface treatments: no additional treatment, air abrasion, soaking in methylmethacrylate (MMA) monomer, and soaking in MMA monomer after air abrasion. After surface treatment, each repair resin was bonded in cylindrical shape using a silicone mold. Specimens were stored in 37℃ distilled water for 24 hours. The shear bond strength was measured using a universal testing machine at a crosshead speed of 0.5 mm/min. Failure modes were analyzed by scanning electron microscope. Statistical analysis was done using one-way ANOVA test and Kruskal-Wallis test (α=.05). RESULTS. The group repaired with bis-acryl composite without additional surface treatment showed the highest mean shear bond strength. It was significantly higher than all four groups repaired with methylmethacrylate (P<.05). Additional surface treatments, neither mechanical nor chemical, increased the shear bond strength within methylmethacrylate groups and bis-acryl composite groups (P>.05). Failure mode analysis showed that cohesive failure was most frequent in both methylmethacrylate and bis-acryl composite groups. CONCLUSION. Our results suggest that when repairing 3D printed provisional restoration with conventional provisional resin, repair with bis-acryl composite without additional surface treatment is recommended.

• Restorative Dentistry and Endodontics
• /
• v.25 no.4
• /
• pp.599-605
• /
• 2000

Among the effects of tooth bleaching on composite resins, degree of color change and dye deposition onto composite resins after office bleaching were investigated in vitro. Seventy two disc-shaped resin samples were fabricated with hybrid type composite resin, Z-100 under 3 different environments(24 samples for each environment) characterized by 3 kinds of light-curing intensity and duration($250mW/cm^2$-20sec., $250mW/cm^2$-40sec., $550mW/cm^2$-20sec.). As control, one-third samples of each group were not treated with bleaching agent. The remaining two-thirds samples of each group were treated with bleaching agent(bleaching group). Then, before thermocycling procedure in coffee bath, the half of the samples treated with bleaching agent were polished(polishing group) with polishing system. SofLex, but the other half(not-polishing group) and control group were not polished. Another 72 samples were also made with microfilled type composite resin. Sillux Plus and treated according to the experimental procedures mentioned above. The color of each resin sample was measured before bleaching, after bleaching, and after thermocycling preceded by bleaching. And color difference was evaluated. It was concluded as follows: 1. The amount of color change of resin samples after office bleaching was not statistically significant(p>0.05). But the samples which were treated with bleaching agent showed more color change than that of control group. 2. After thermocycling in coffee bath, the amount of color change of resin samples between control and bleaching group was not statistically significant(p>0.05). 3. After thermocycling in coffee bath, the polishing procedure of resin samples showed no statistically significant difference(p>0.05) between polishing and not-polishing group in the aspect of color change.

• Restorative Dentistry and Endodontics
• /
• v.40 no.3
• /
• pp.188-194
• /
• 2015

Objectives: This study evaluated the effect of lactic acid and acetic acid on the microhardness of a silorane-based composite compared to two methacrylate-based composite resins. Materials and Methods: Thirty disc-shaped specimens each were fabricated of Filtek P90, Filtek Z250 and Filtek Z350XT. After measuring of Vickers microhardness, they were randomly divided into 3 subgroups (n = 10) and immersed in lactic acid, acetic acid or distilled water. Microhardness was measured after 48 hr and 7 day of immersion. Data were analyzed using repeated measures ANOVA (p < 0.05). The surfaces of two additional specimens were evaluated using a scanning electron microscope (SEM) before and after immersion. Results: All groups showed a reduction in microhardness after 7 day of immersion (p < 0.001). At baseline and 7 day, the microhardness of Z250 was the greatest, followed by Z350 and P90 (p < 0.001). At 48 hr, the microhardness values of Z250 and Z350 were greater than P90 (p < 0.001 for both), but those of Z250 and Z350 were not significantly different (p = 0.095). Also, the effect of storage media on microhardness was not significant at baseline, but significant at 48 hr and after 7 day (p = 0.001 and p < 0.001, respectively). Lactic acid had the greatest effect. Conclusions: The microhardness of composites decreased after 7 day of immersion. The microhardness of P90 was lower than that of other composites. Lactic acid caused a greater reduction in microhardness compared to other solutions.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.6
• /
• pp.54-63
• /
• 2022

This paper is a study on the friction damper, which is one of the seismic reinforcement devices for structures. This study developed a damper by replacing the internal friction material with ultra high molecular weight polyethylene (UHMWPE), a type of composite material. In addition, this study applied a multi-friction method in which the internal structure where frictional force is generated is laminated in several layers. To verify the performance of the developed multi-friction damper, this study performed a characteristic analysis test for the basic physical properties, wear characteristics, and disc springs of the material. As a result of the wear test, the mass reduction rate of UHMWPE was 0.003%, which showed the best performance among the friction materials based on composite materials. Regarding the disc spring, this study secured the design basic data from the finite element analysis and experimental test results. Moreover, to confirm the quality stability of the developed multi-friction damper, this study performed an seismic load test on the damping device and the friction force change according to the torque value. The quality performance test result showed a linear frictional force change according to the torque value adjustment. As a result of the seismic load test, the allowable error of the friction damper was less than 15%, which is the standard required by the design standards, so it satisfies the requirements for seismic reinforcement devices.

• Structural Engineering and Mechanics
• /
• v.64 no.6
• /
• pp.819-826
• /
• 2017

The effects of thermocycling procedure and material shade on the mechanical properties and wear resistance of resin-based dental restorative materials are investigated. The modulus of elasticity, hardness, plasticity index and wear resistance are determined for the conventional composite, the nanohybrid composite and the nanofilled dental composites. Disc-shape samples are prepared from each material to investigate the effects of thermocycling procedure on the mechanical properties and wear resistance of different types of dental restorative materials. In this respect, a group of samples is thermocycled and the other group is stored in ambient conditions. Then nano-indentation and nano-scratch tests are performed on the samples to measure their mechanical properties and wear resistance. Results show that the A1E shade of the dental nanocomposite possesses higher modulus of elasticity and hardness values compared to the two other shades. According to the experimental results, the mean values for the modulus of elasticity and hardness of the A1E shade of the nanocomposite are 13.71 GPa and 1.08 GPa, respectively. The modulus of elasticity and hardness of the conventional dental composite increase around 30 percent in the oral environment due to the moisture and temperature changes. The wear resistance of the dental composites is also significantly affected by moisture and temperature changes in the oral conditions. It is observed that thermocycling has no significant effect on the hardness, plasticity index and wear resistance of the nanohybrid composite and the nanocomposite dental materials.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.6
• /
• pp.682-697
• /
• 2001

This investigation evaluated the fracture toughness($K_{IC}$) of eight currently available core materials, and relate the fracture toughness value to fractography analysis and surface characteristics using a atomic force microscope (AFM). Single-edge notched (SEN) test specimens (n=10) and compact tension (CT) test specimens (n=10) were prepared conforming to the ASTM Standard E-399 for a high copper amalgam, three composite core materials (Core-Max II, Core Paste, Bisfil Core), two reinforced composite core materials (Ti-Core, Ti-Core Natural), a resin-modified glass ionomer core material (Vitremer), and a conventional glass ionomer core material (Ketac-Molar). The specimens were tested with an Instron Universal Testing Machine. The maximum loads were measured to calculate the fracture toughness ($K_{IC}$). Thereafter, fracture surfaces of SEN specimens of each material were investigated for fractography analysis using scanning electron microscope. And, disc-shaped specimens with 1mm thickness were fabricated for each material and were investigated under AFM for surface morphology analysis. The results were as follows: 1. Bisfil Core showed the highest mean fracture toughness regardless of test methods. 2. For the tooth-colored materials, Ti-Core Natural exhibited the highest fracture toughness. 3. Ketac Molar showed a significantly low fracture toughness when compared with the amalgam and the composite resin core materials(p<0.05). 4. The fracture toughness values obtained with the single-edge notched test, except Ketac Molar, were higher than those obtained in the compact tension test. 5. SEM revealed that the fracture surface of high fracture toughness material was rougher than that of low fracture toughness material. 6. AFM revealed that the surface particles of the composite resins were smaller in size, with a lower surface roughness than the glass ionomer core materials.