• Macromolecular Research
• /
• 제12권4호
• /
• pp.336-341
• /
• 2004

A new type of cross-linked methylaluminoxane (MAO)-supported cocatalyst has been prepared by the reaction of a soluble MAO and a cross-liking agent such as an aromatic diamine compound. The cross-linked MAO-supported cocatalyst was used for the polymerization of ethylene in the presence of bis(n-butylcyclopentadienyl) zirconium dichloride, (n-BuCp)$_2$ZrCl$_2$. The catalyst activity of (n-BuCp)$_2$ZrCl$_2$ cocatalyzed with the new supported cocatalyst was higher than that of the commercial silica-supported MAO (SMAO) cocatalyst. The molecular weight and the bulk density of the polyethylene produced by using the new supported cocatalyst were slightly higher than those of polyethylene synthesized using commercial SMAO. The resulting polyethylene particles possess spherical morphologies with very few fine particles.

• 공업화학
• /
• 제32권6호
• /
• pp.627-631
• /
• 2021

휘발성유기화합물을 제거하기 위한 기존 촉매 시스템의 문제를 해결하고자 유도가열 촉매 시스템에 대한 연구를 수행하였다. 본 연구에서는 3종류의 Ni계 상용촉매를 적용하였으며, 촉매 부피, 조성, 열처리 분위기, 코일 내 위치를 포함한 유도가열 반응 특성을 조사하였다. 촉매의 조성 및 부피는 유도가열 시스템에 의한 발열 및 톨루엔 산화 성능에 영향을 미쳤다. 특히 철이 첨가된 촉매는 99% 이상의 Ni로 구성된 촉매에 비해 높은 발열을 나타내었으나 낮은 톨루엔 산화 성능을 나타내었다. 또한 Ni계 촉매의 열처리에 있어 공기 분위기는 촉매의 성능을 급격히 저하시킨다. 유도가열 시스템에서 촉매는 코일 내 중심에 위치하는 것이 최적 조건으로 나타났다. 연구를 통해 도출한 최적의 조건에서 촉매를 7회 반복 실험하였으며, 유사한 성능을 확인하였다.

• 한국전산유체공학회:학술대회논문집
• /
• 한국전산유체공학회 2010년 춘계학술대회논문집
• /
• pp.228-232
• /
• 2010

In this paper, various operating parameters of stream reforming process from methane in preconverter for MCFC is studied by numerical method. Commercial code is used to simulated the porous catalyst with user subroutine to model three dominant chemical reactions which are Stream Reforming(SR), Water-Gas Shift(WGS), and Direct Stram Reforming(DSR). The hydrogen production is tested with different wall temperature, Gas Hourly Space Velocity(GHSV), and different reactor shapes.

• 공업화학
• /
• 제19권5호
• /
• pp.466-470
• /
• 2008

본 연구에서는 가연성 폐기물에서 발생되는 합성가스 내 $CH_4$를 나노기공성 촉매를 사용하여 $H_2$로 전환하고자 하였다. 이때 사용된 나노기공성 촉매는 $Ni/Al_2O_3$ 촉매를 one-pot 방법으로 제조하여 사용하였다. 촉매의 분석 결과, 삼차원으로 연결된 스폰지 모양을 갖는 입자가 형성되었으며, 구형의 상용 촉매보다 넓은 표면적과 작은 입자크기, 균일한 기공 크기의 특성을 지닌 나노기공성 촉매가 제조된 것을 확인할 수 있었다. $CH_4$ 개질반응에 사용된 $Ni/Al_2O_3$ 촉매의 Ni 최적 담지량은 16 wt%였으며 $750^{\circ}C$에서 $CH_4$ 전환율 91%, $CO_2$ 전환율 92%로 가장 높은 전환율을 나타냈다. 또한, 상용 알루미나를 사용하여 제조한 촉매와의 성능 비교 결과 자체 제조한 촉매가 약 20% 향상된 전환율을 나타냈다.

• 공업화학
• /
• 제32권1호
• /
• pp.35-41
• /
• 2021

NH3-SCR에서 상용촉매로 사용되고 있는 VWTi (VOx/WO3-TiO2)는 300~400 ℃에서 우수한 탈질성능을 나타내지만 300℃ 이하 저온에서는 효율이 저하되는 문제가 있다. 저온 탈질효율을 높이기 위하여 promoter를 첨가한 촉매 연구는 꾸준히 진행되고 있으나 촉매의 저온 탈질효율 증진원인과 촉매특성에 관한 연구는 미비한 실정이다. 본 연구에서는 VWTi에 Sb(antimony)를 첨가함으로써 300 ℃ 이하의 NH3-SCR 반응에서 탈질 성능이 10% 이상 증진되는 것을 확인하였고, 이 때 외부확산/내부확산에 의한 영향을 배제하고자 공간속도와 촉매입자 크기를 제어하였다. 또한 Sb의 첨가 유·무에 따른 촉매특성을 BET, TEM/EDS, O2-TPD, H2-TPR, DRIFTs 분석을 수행하여 고찰하였다. Sb의 첨가는 촉매의 표면 흡착 산소 종을 증가시켰으며, 이에 따라 저온에서 촉매의 산화·환원(redox) 특성이 증진되어 우수한 탈질성능을 나타내는 것으로 판단되었다.

• Bulletin of the Korean Chemical Society
• /
• 제28권7호
• /
• pp.1119-1126
• /
• 2007

Hydrogen gas and carbon nanotubes along with nanocarbon were produced from commercial natural gas using fixed bed catalyst reactor system. The maximum amount of carbon (491 g/g of catalyst) formation was achieved on 25% Ni, 3% Cu supported catalyst without formation of CO/CO2. Pure carbon nanotubes with length of 308 nm having balloon and horn type shapes were also formed at 673 K. Three sets of catalysts were prepared by varying the concentration of Ni in the first set, Cu concentration in the second set and doping with K in the third set to investigate the effect on stabilization of the catalyst and production of carbon nanotubes and hydrogen by copper and potassium doping. Particle size analysis revealed that most of the catalyst particles are in the range of 20-35 nm. All the catalysts were characterized using powder XRD, SEM/EDX, TPR, CHN, BET and CO-chemisorption. These studies indicate that surface geometry is modified electronically with the formation of different Ni, Cu and K phases, consequently, increasing the surface reactivity of the catalyst and in turn the Carbon nanotubes/H2 production. The addition of Cu and K enhances the catalyst dispersion with the increase in Ni loadings and maximum dispersion is achieved on 25% Ni: 3% Cu/Al catalyst. Clearly, the effect of particle size coupled with specific surface geometry on the production of hydrogen gas and carbon nanotubes prevails. Addition of K increases the catalyst stability with decrease in carbon formation, due to its interaction with Cu and Ni, masking Ni and Ni:Cu active sites.

• 한국수소및신에너지학회논문집
• /
• 제15권4호
• /
• pp.274-282
• /
• 2004

This study focused on the development of high performance catalyst for autothermal reforming (ATR) of gasoline to produce hydrogen. The ATR was carried out over MgO/Al2O3 supported metal catalysts prepared under various experimental conditions. The catalysts before and after reaction were characterized by N2-physisorption, CO-chemisorption, SEM and XRD. The performance of supported multi-metal catalysts were better than that of supported mono-metal catalysts. Especially, it was observed that the conversion of iso-octane over prepared Ni/Fe/MgO/Al2O3 catalyst was 99.9 % comparable with commercial catalyst (ICI) and the selectivity of hydrogen over the prepared catalyst was 65% higher than ICI catalyst. Furthermore, it was identified that the sulfur tolerance of prepared catalyst was much better than ICI catalyst based on the ATR reaction of iso-octane containing sulfur of 100 ppm. Therefore, Ni/Fe/MgO/Al2O3 catalyst can be applied for a fuel reformer, hydrogen station and on-board reformer in furl cell powered vehicles.

• 한국추진공학회지
• /
• 제13권1호
• /
• pp.19-26
• /
• 2009

과산화수소 단일추진제 추력기의 응답성에 대한 실험적 연구를 수행하였다. 촉매베드의 특성을 배제하고 추력기 설계 인자에 따른 응답특성을 살펴보기 위해 $MnO_2$/$Al_2O_3$를 주 촉매로 고정하였다. 세 가지 50 N 급 추력기를 이용하여 인젝터 방식, ullage volume, 촉매 펠렛 크기, 반응기 부피에 따른 응답 속도를 측정하였다. 측정 결과 16-20 mesh 크기 촉매, shower head 인젝터를 사용한 경우 점화지연, 압력 상승 및 하강시간은 각각 14, 108, 94 ms로 상용 하이드라진 추력기 응답성에 근접한 특성을 보였다.

• Carbon letters
• /
• 제4권3호
• /
• pp.121-125
• /
• 2003

The Pt-Ru/Carbon as an anode catalyst supported on the commercial activated carbon (AC) having high surface area and micropore was characterized for application of Direct Methanol Fuel Cell (DMFC). The Pt-Ru/AC anode catalyst used in this experiment showed the performance of $600\;mA/cm^2$ current density at 0.3 V. The borohydride reduction process using $NaBH_4$, denoted as a process A, showed much higher current and power densities than process B prepared by changing the reduction and washing process of process A. The particle sizes are strongly affected by the reduction process than the specific surface area of raw active carbon and the sizes are almost constant when the specific surface area of carbon are over than the $1200\;m^2/g$. Smaller particle size of catalyst and more narrow intercrystalite distance increased the performance of DMFC.

• 공업화학
• /
• 제25권4호
• /
• pp.425-429
• /
• 2014

호기성 벤질 알코올 산화반응용 상용촉매 개발을 위하여 팔라듐이 담지된 차콜 입자를 제조하였다. 특히 촉매의 팔라듐 분산도를 높이기 위해서 상온 이온성액체 중 하나인 [Hmim][$PF_6$]을 기능성 용매로 사용하여 입자를 합성하였다. 다양한 농도의 팔라듐을 함침하여 제조된 입자의 반응성을 측정한 결과 7.5 wt%의 촉매가 가장 우수한 반응 활성과 안정성을 나타내었다. 또한 조촉매로서 다양한 농도의 은입자를 합침하여 촉매를 제조하였다. 동일한 반응조건에서 팔라듐과 은의 질량 비율이 9 : 1인 촉매가 높은 금속 분산도로 인하여 가장 반응성이 우수하였다.