• Transactions of Materials Processing
• /
• v.18 no.5
• /
• pp.377-384
• /
• 2009

The shape of edge cracking in rolling process generally occurred "V" shape. This cracking is successively generated at width edge of strip. The edge cracking is developed to center of strip during rolling process. In the results, the strip is occurred fracture, and the productivity is gone down because of the extensive production time. Accordingly, we need to control crack propagation during rolling process. But, the control of cracking is very difficult in rolling process. Previously the studies of edge cracking were mainly performed on hot rolling process. In this paper, the shape of the edge cracking in rolling was estimated according to process conditions such as initial edge crack size, reduction ratio and tension using FE-simulation and the simplicity experiments on cold rolling process.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.405-408
• /
• 2009

Edge cracks in cold rolling always influence to the quality of productions, while the "V" shaped cracks were propagated by passing the roll gap. We set up the sizes and shapes of initial cracks in simulation according to the references from real productions. Different to in hot rolling, the cracks in cold rolling couldn't be reduced from propagation automatically after generated, even if these could be reduced by changing the process parameters. In this paper, we described the affections of process parameters on the propagation of edge cracks, such as reduction ratio and tension. We predicted that the dependence of the cracks propagations of changing of process conditions and expected to gain the smaller edge cracks. By raising the reduction ratio, the cracks were propagated increasingly in both transverse and rolling directions. And as tension raise, the cracks became propagated in both directions in which transverse direction was less effectively.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2003.11a
• /
• pp.158-163
• /
• 2003

Several simulation techniques have been developed which are not practical deformation processes but are designed to embody specific tribological aspects. Sliding rolling type friction test machine (Cold rolling tribosimulator) was developed to simulate the tribological phenomena at the roll bite in real mill by laboratory scale. A rolled material is fed at a low speed of Max. 1/20 to that of roll speed, so as to obtain simultaneous plastic deformation in the material during rotation of the rolls in simulator. New cold rolling tribe-simulator is effective for evaluation of the lubricity of lubricant in cold rolling process.

• 제어로봇시스템학회:학술대회논문집
• /
• 2000.10a
• /
• pp.183-183
• /
• 2000

In this paper, web-based remote monitoring for cold-rolling system is developed and the analysis of spatial control system is performed. The remote monitoring system is able to grasp the status of cold-rolling system regardless of time and locations. We analyzed spatial control algorithm of the system with the collected data. The usefulness of spatial control system is shown by simulation studies.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.2
• /
• pp.302-312
• /
• 1994

In this study, a fuzzy theory is introduced to control the cross-sectional strip shape in cold rolling. A fuzzy controller is developed based on the production data and the operational knowledge. The cold rolled products are characterized into several types based on their irregularities. For each type of irregular strip shape, fuzzy controller calculates the changes of bender forces of work and intermediate rolls using fuzzy control algorithm. To simulate the continuous shape control, fuzzy controller is linked with emulator which is developed using neural network. The developed fuzzy controller and emulator simulate the cold rolling process until the irregularities converge to the tolerable range to produce unifrom cross-sectional strip shape. The results from this simulation are reasonable for various irregular strip shapes.

• 제어로봇시스템학회:학술대회논문집
• /
• 2000.10a
• /
• pp.39-39
• /
• 2000

In this paper, a decoupler of tandem cold rolling mill is designed. Before designing the decoupler, this paper improved conventional linear model by considering friction and yield stress of rolling strip. In a stand, the decoupler let an output be controlled by an input. And even if states of other stands should be changed, current stand takes no interference from those changes. In addition, with the same method, a feedforward controller is designed for an input strip thickness error. Finally, performance of controllers above is shown with nonlinear simulation.

• Transactions of Materials Processing
• /
• v.12 no.2
• /
• pp.123-127
• /
• 2003

The cold rolling conditions for the ultra thin steel for tension mask are very important because the residual stress that affects the flatness of strip is generate during the cold rolling. The residual stress in the sheet causes etching curls when it suffers perforation process. The residual stress through the thickness. To estimate the residual stress and deformation due to etching curl. FEM analysis is performed. Numerical simulation employ a ANSY5 5.6 and an elastic-plastic constitutive equation. The simulation results indicate the distribution of residual stress in the rolled sheet can be controlled by selecting the rolling conditions properly.

• Korean Journal of Metals and Materials
• /
• v.48 no.7
• /
• pp.644-650
• /
• 2010

Interstitial free (IF) steel sheets were cold rolled by the cross-roll rolling mill in which the roll axes are tilted by ${\pm}7.5^{\circ}$ away from the transverse direction of the rolled sample. After cross-roll rolling of IF steel sheets, the cold rolling and the recrystallization textures were distinguished from those observed after rolling in a normal rolling mill. The three-dimensional finite element method (FEM) simulation revealed that the operation of a large shear strain ${\varepsilon}_{23}$ during cross-roll rolling leads to the formation of a distinct cold rolling texture. During recrystallization annealing, a pronounced change in texture components was not observed, which is attributed to the lack of either selective growth or oriented nucleation during the recrystallization process. Cold cross-roll rolling led to the formation of finer recrystallized grains in IF steel sheets.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.05a
• /
• pp.413-416
• /
• 2007

In general, by means of the electrodepositing technique, a copper foil sample was prepared with a high purity and a high density. But the mechanical properties of the electrodepositing copper foil was lower than it's the rolling copper foil. However, the production of copper foil with approximately 36 microns thick in rolling process was very difficult. This paper describes the outline of the high accuracy cold rolling in 6 high mill which was developed for the purpose of rolling very thin accurate gauge copper foil(36 micron thick), and give several rolling characteristic of 600 mm wide copper foil. a) Large strain can be accumulated pass by pass in industrial multi-pass rolling processing to overcome large critical strain for thickness accuracy through optimization of rolling schedule. b) Also, permissible tension for rolling 0.45 $\sim$ 0.036 mm thick copper strip stably in accordance with the each pass work had been established by FEM simulation results. c) During the plate rolling process, considerable values of the forces of material pressure on the tool occur. These pressures cause the elastic deformation of the roll, thus changing the shape of the deformation region. A numerical simulation of roll deflection during cold rolling is presented in the paper. d) The proposed pass schedule can roll very thin copper foil of 36 micron thickness to a tolerance of ${\pm}1$ microns. The validity of simulated results was verified into rolling experiments on the copper foil.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.1
• /
• pp.34-43
• /
• 1994

In order to improve thickness profile of cold rolled steel strip, a computer simulation and actual cold rolling experiments on a 4-high tandem cold mill were carried out. In this study, tapered barrel end at top work roll and incurved barrel body at bottom work roll were examined for reducing edge drop and threading of stripe. Also, the most effective stand of tandem cold mill and magnitude of optimal taper crown at several stand were investigated under a typical rolling condition. From actual rolling experiments, it was verified that thickness deviation over strip width could be improved up to 1.06% by applying tapered and incurved work roll only at the second and up to 0.89% by applying them at both the second and the third stand.