• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.388-388
• /
• 2010

In this study, Ferroelectric vinylidene fluoride-trifluoroethylene (VF2-TrFE) copolymer films were directly deposited on degenerated Si (n+, $0.002\;{\Omega}{\cdot}cm$) using by spin coating method. A 1~5 wt% diluted solution of purified vinylidene fluoride-trifluoroethylene (VF2:TrFE = 70:30) in a dimethylformamide (DMF) solvent were prepared and deposited on silicon wafers at a spin rate of 2000 ~ 4000 rpm for 2 ~ 30 seconds. After annealing in a vacuum ambient at 100 ~ $200^{\circ}C$ for 60 min, upper aluminum electrodes were deposited by vacuum evaporation for electrical measurement. X-ray diffraction results showed that the VF2-TrFE films on Si substrates had $\beta$-phase of copolymer structures. The capacitance on highly doped Si wafer showed hysteresis behavior like a butterfly shape and this result indicates clearly that the copolymer films have ferroelectric properties. The typical measured remnant polarization ($P_r$) and coercive filed ($E_c$) values were about $5.7\;{\mu}C/cm^2$ and 710 kV/em, respectively, in an applied electric field of ${\pm}$ 1.5 MV/em. The gate leakage current densities measured at room temperature was less than $7{\times}10^{-7}\; A/cm^2$ under a field of 1 MV/cm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.12
• /
• pp.1108-1114
• /
• 1998

$BaTiO_3$ thin films preferred c-axis orientation for the potential application of ferroelectric memory devices were deposited on silicon substrates(100) by RF sputtering and annealed at 800 and 900[$^{\circ}C$] in air. The BT(100)/BT(110) peak ratio of the sputtered sample was decreased with post-annealing in air. According to increasing with annealing temperature and time, the peak ratio of BT(100)/BT(110) was decreased and the surface density of thin film was high. Dielectric characteristics of $BaTiO_3$ thin film was measured as a function of annealing temperature and frequency. The dielectric constants were increased with annealing and decreased with frequency by space charge polarization and dipole polarization below 600[kHz]. The remanent polarization and coercive field in P-E hysteresis loop of $BaTiO_3$thin film were increased with the annealing temperature in air. The remanent polarization and coercive filed annealed at 800[$^{\circ}C$] for 1hr were 1.2[$\mu$C/$cm^2$] and 200[kV/cm]

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.12
• /
• pp.1283-1288
• /
• 2004

Metal-ferroelectric-insulator-semiconductor(WFIS) capacitors using rapid thermal annealed LiNbO$_3$/AlN/Si(100) structure were fabricated and demonstrated nonvolatile memory operations. The capacitors on highly doped Si wafer showed hysteresis behavior like a butterfly shape due to the ferroelectric nature of the LiNbO$_3$ films. The typical dielectric constant value of LiNbO$_3$ film in the MFIS device was about 27, The gate leakage current density of the MFIS capacitor was 10$^{-9}$ A/cm$^2$ order at the electric field of 500 kV/cm. The typical measured remnant polarization(2P$_{r}$) and coercive filed(Ec) values were about 1.2 $\mu$C/cm$^2$ and 120 kV/cm, respectively The ferroelectric capacitors showed no polarization degradation up to 10$^{11}$ switching cycles when subjected to symmetric bipolar voltage pulses of 1 MHz. The switching charges degraded only by 10 % of their initial values after 4 days at room temperature.e.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.9
• /
• pp.947-952
• /
• 2004

Tb-doped lead zirconate titanate(Pb(Zr$\_$0.6/,Ti$\_$0.4/)O$_3$; PZT) thin films on Pt(111)/Ti/SiO$_2$/Si(100) substrates were fabricated by the sol-gel method. The effect on the structural and electrical properties of films measured according to Tb content. The dielectric and ferroelectric properties of Tb-doped PZT thin films were altered significantly by Tb-doping. The PZT thin film with higher dielectric constant and improved leakage current characteristic was obtained by adding 0.3 mol% Tb. The relative dielectric constant and the dielectric loss of the 0.3 mol% Tb-doped PZT thin film were 1611 and 0.024, respectively. Typical value of the swichable remanent poaraization(2Pr) and the coercive filed of the PZT film capacitor for 0.3 mol% Tb-doped were 61.4 ${\mu}$C/cm$^2$ and 61.9 kV/cm, respectively. Tb-doped PZT thin films showed improved fatigue characteristics comparing to the undoped PZT thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.869-873
• /
• 2004

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient, piezoelectric, and a photo refractive properties. In this study, SBN60(x=0.6) thin film was manufactured by ion beam sputtering technique. Using the prepared SBN60 target in $Ar/O_2$ atmosphere as-deposited SBN60 thin film on Pt(100)/$TiO_2/SiO_2/Si$ substrate crystallization and orientation behavior as well as electric properties of SBN60 thin film were examined. SBN60 deposition up to $3000{\AA}$ in thickness, SBN60 thin film was heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation was shown primarily along (001) plane from XRD pattern where working pressure was $4.3{\times}10^{-4}$ torr. The deposited layer was uniform, preferred orientatin and crystallization behavior resulted in the change of $O_2$ ratio was observed. In electric propertie of Pt/SBN60/Pt thin film capacitor remnant polarization (2Pr) value was $10{\mu}C/cm^2$, the coercive filed (Ec) 50 kV/cm, and the dielectric constant 615, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.169-170
• /
• 2006

In this study, ultra thin films of ferroelectric vinylidene fluoride-trifluoroethylene (VF2-TrFE) copolymer were fabricated on degenerated Si (n+, $0.002\;{\Omega}{\cdot}cm$) using by spin coating method. A 1~5 wt% diluted solution of purified vinylidene fluoride-trifluoroethylene (VF2:TrFE=70:30) in a dimethylformamide (DMF) solvent were prepared and deposited on silicon wafers at a spin rate of 2000~5000rpm for 30 seconds. After annealing in a vacuum ambient at $200^{\circ}C$ for 60 min, upper gold electrodes were deposited by vacuum evaporation for electrical measurement. X-ray diffraction results showed that the VF2-TrFE films on Si substrates had $\beta$-phase of copolymer structures. The capacitance on $n^+$-Si(100) wafer showed hysteresis behavior like a butterfly shape and this result indicates clearly that the dielectric films have ferroelectric properties. The typical measured remnant polarization (2Pr) and coercive filed (EC) values measured using a computer controlled a RT-66A standardized ferroelectric test system (Radiant Technologies) were about $0.54\;C/cm^2$ and 172 kV/cm, respectively, in an applied electric field of ${\pm}0.75\;MV/cm$.