Hexagonal boron nitride (h-BN) is a two dimensional material which has high band-gap, flatness and inert properties. This properties are used various applications such as dielectric for electronic device, protective coating and ultra violet emitter so on. 1) In this report, we were growing h-BN sheet directly on sapphire 2"wafer. Ammonia borane (H3BNH3) and nickel were deposited on sapphire wafer by evaporate method. We used nickel film as a sub catalyst to make h-BN sheet growth. 2) During annealing process, ammonia borane moved to sapphire surface through the nickel grain boundary. 3) Synthesized h-BN sheet was confirmed by raman spectroscopy (FWHM: ~30cm-1) and layered structure was defined by cross TEM (~10 layer). Also we controlled number of layer by using of different nickel and ammonia borane thickness. This nickel film supported h-BN growth method may propose fully and directly growing on sapphire. And using deposited ammonia borane and nickel films is scalable and controllable the thickness for h-BN layer number controlling.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2001년도 추계학술발표회 초록집
• /
• pp.29-30
• /
• 2001

This paper presents some results of plasma nitriding on hard chromium deposit. The substrates were C45 steel and $30~50{\;}\mu\textrm{m}$ of chromium deposit by electroplating was formed. Plasma nitriding was carried out in a plasma nitriding system with $95NH_3{\;}+{\;}SCH_4$ atmosphere at the pressure about 600 Pa and different temperature from $450^{\circ}C{\;}to{\;}720^{\circ}C$ for various time. Optical microscopy and X-ray diffraction were used to evaluate the characteristics of surface nitride layer formed by nitrogen diffusion from plasma atmosphere inward iCr coating and interface carbide layer formed by carbon diffusion from substrate outward Cr coating. The microhardness was measured using microhareness tester at the load of 100 gf. Corrosion resistance was evaluated using the potentiodynamic measurement in 3.5% NaG solution. A saturated calomel electrode (SiCE) was used as the reference electrode. Fig.1 shows the typical microstructures of top surface and cross-section for nitrided and unnitrided samples. Aaer plasma nitriding a sandwich structure was formed consisting of surface nitride layer, center chromium layer and interface carbide layer. The thickness of nitride and carbide layers was increased with the increase of processing temperature and time. Hardness reached about 1000Hv after nitriding while 900Hv for unnitrided hard chromium deposit. X-ray diffraction indicated that surface nitrided layer was a mixture of $Cr_2N$ and CrN at low temperature and erN at high temperature (Fig.2). Anodic polarization curves showed that plasma nitriding can greatly improve the corrosion resistance of chromium e1ectrodeposit. After plasma nitriding, the corrosion potential moved to noble direction and passive current density was lower by 1 to 4 orders of magnitude compared with chromium deposit(Fig.3).

• 한국표면공학회지
• /
• 제49권2호
• /
• pp.211-217
• /
• 2016

Boride coating applied on steam turbine parts of power plants has provided good particle erosion resistance under temperature of $550^{\circ}C$, but it isn't able to protect the parts effectively any more in ultra super critical (USC) steam turbine which is being operated up to temperature of $650^{\circ}C$. To ensure stable durability for USC steam turbine parts, an alternative coating replacing boride coating should be developed. In this study, multi-component boride coatings containing elements such as chromium (Cr) and vanadium (V) were formed on base metal (B50A365B) using thermochemical treatment method called by pack cementation. The thermochemical treatments involve consecutive diffusion of boron(B) and Cr or/and V using pack powders containing diffusion element sources, activators and diluents. The top layer of Cr-boride coating is primarily consisted of $Cr_2B_3$ and $Cr_5B_3$, while that of V-boride coating is mostly consisted of $VB_2$ and $V_2B_3$. The (Cr,V)-boride coating is consisted of $Cr_2B_3$, $Cr_5B_3$ and $V_2B_3$ mostly. The top surfaces of 3 multi-component boride coatings show hardness of $3200-3400H_v$, which is much higher than that of boride, about $1600-2000H_v$. In 5 wt.% NaCl solution immersion tests, the multi-component boride coatings show much better corrosion resistance than boride coating.

• 한국전기전자재료학회논문지
• /
• 제15권2호
• /
• pp.147-152
• /
• 2002

Carbon nitride thin films were deposited by reactive sputtering for the hard coating materials on Si wafer and tool steels. When the nitrogen content of carbon nitride film on tool steel is 33.4%, the mean hardness and elastic modulus are 49.34 GPa and 307.2 GPa respectively. The nitrided or carburised surface acts as the diffusion barrier which shows better adhesion of carbon nitride thin film on the steel surface. To prevent nitrogen diffusion from the film, steel substrate can be saturated by nitrogen forming a Fe$_3$N layer. The desirable structure at the surface after carburising is martensite, but sometimes, due to high carbon content an proeutectoid Fe$_3$C structure may form at the grain boundaries, leaving the overall surface brittle and may cause defects.

• 대한설비공학회:학술대회논문집
• /
• 대한설비공학회 2009년도 하계학술발표대회 논문집
• /
• pp.645-649
• /
• 2009

Liquid desiccant cooling technology can supply cooling by using waste heat and solar heat which are hard to use effectively. For compact and efficient design of a dehumidifier, it is important to sustain sufficient heat and mass transfer surface area for water vapor diffusion from air to liquid desiccant on heat exchanger. In this study, the plate type heat exchanger is adopted which has extended surface, and hydrophilic coating and porous layer coating are adopted to enhance surface wettedness. PP(polypropylene) plate is coated by porous layer and PET(polyethylene terephthalate) non-woven fabric is coated by hydrophilic polymer. These coated surfaces have porous structure, so that falling liquid film spreads widely on the coated surface foaming thin liquid film by capillary force. The temperature of liquid desiccant increases during dehumidification process by latent heat absorption, which leads to loss of dehumidification capacity. Liquid desiccant is cooled by cooling water flowing in plate heat exchanger. On the plate side, the liquid desiccant can be cooled by internal cooling. However the liquid desiccant on extended surface should be moved and cooled at heat exchanger surface. Optimal mixing and distribution of liquid desiccant between extended surface and plate heat exchanger surface is essential design parameter. The experiment has been conducted to verify effective surface treatment and distribution characteristics by measuring wall side flow rate and visualization test. It is observed that hydrophilic and porous layer coating have excellent wettedness, and the distribution can be regulated by adopting holes on extended surface.

• 한국수소및신에너지학회논문집
• /
• 제20권2호
• /
• pp.116-124
• /
• 2009

We investigated the influences of cobalt coating deposited by DC electroplating on the ferritic stainless steel, STS 430, as a protective layer on a metallic interconnect for SOFC applications. Cobalt coated STS 430 revealed a uniform and denser-packing oxide surface and a reduced growth rate of $Cr_2O_3$ scales after oxidation at $800^{\circ}C$in air. Cobalt coating layer was oxidized to $CoCo_2O_4$ and Co containing mixed oxide spinels such as $Co_2CrO_4$, $CoCr_2O_4$, and $CoCrFeO_4$. The area specific resistance value of Co coated sample was $0.020\;{\Omega}cm^2$ lower than that of uncoated at $800^{\circ}C$ in air during 500 h. After 1000 h oxidation, cobalt oxide coating layer suppressed chromium outward diffusion.

• 연구논문집
• /
• 통권33호
• /
• pp.175-182
• /
• 2003

In this study, the wear resistance of the complex powder diffusion treated KS STD 61 has been investigatived. KS STD 61 tool steel was pretreated in quenching and tempering processes to obtain the tempered martensitic microstructure. The samples were packed with complex powder in steel pot($\Phi$90x60mm) and heated in a box furnace. the complex powder diffusion treatment are carried out at $540^{\circ}C$, $520^{\circ}C$, $500^{\circ}C$ for 40min, 1.5hr and 2.5hr. The microstructure, microhardness, wear resistance, and coating layer thickness of the complex powder diffusion treated samples were investigation. The weight loss of as heat treated sample was 0.4mg and that of the complex powder treated at $540^{\circ}C$ for 2.5hr was 0.17mg. These result means that the wear resistance of tool steels can be easily improved by the powder diffusion process at conventional tempering treatment temperature.

• 한국재료학회지
• /
• 제8권6호
• /
• pp.538-544
• /
• 1998

열차폐코팅층의 박리는 세라믹/금속접합층 계면에서 취성이 큰 스피텔의 생성, 금속과 세라믹의 열팽창계수의 차이, 세라믹층의 상변태, 코팅층의 잔류응력에 기인한다. 본 연구에서는 인코넬 713C에 전자빔 코팅 및 플라즈마 용사법으로 코팅된 안정화지르코니아/CoNiCrAIY 계면의 산화거동을 조사하기 위하여 $900^{\circ}C$에서 등온산화시험동안 생성되는 산화막층과 스피넬 생성 거동을 관찰, 분석하였다. 코팅 직후 코팅층에 고르게 분포하고 있는 Co,Ni,Cr,AI,Zr의 원소들이 산화시간에 따라 확산하여 산화반응을 하였다. 초기 20시간의 산화기시간에 안정화지르코니아/CoNiCrAIY 계면에 주요 성분이 $\alpha$-$AI_2O_3$인 산화막층이 생성되었고, CoNiCrAIY층에는 AI의 외부확산으로 인한 AI 결핍지역이 생성되었다. 산화시험동안 $\alpha$-AI2O층이 임계두께까지 성장한 후에 산화막층의 성장속도는 감소하였고, 안정화지르코니아/산화막층 계면에 스피넬, $Cr_2O_3$, $CO_2CrO_4$의 형성으로 인한 크랙이 관찰되었다.

• 한국환경보건학회지
• /
• 제36권3호
• /
• pp.236-246
• /
• 2010

In preparative anti-corrosive coating experiments, polyaniline was obtained by reacting an oxidizing agent with the monomer aniline. Further, the primer coating was prepared using a variety of widely-used materials such as urethane resin. For the top coating, epoxy resin and acrylic urethane resin were used. Characteristics of the coatings were assessed according to KS and ASTM specifications, and the structure of the polyaniline was characterized using FT-IR and TGA. For analysis of anti-corrosive properties in salt-spray experiments, measurements of the oxidation state of iron and surface atomic analysis were conducted using XPS and SEM-EDX. Unlike general anti-corrosive coatings which exhibit anti-corrosive effects only as a primer coating, the anti-corrosive coatings using polyaniline as the anti-corrosive pigment showed a marked synergistic effect with the top coatings. In other words, the top coatings not only produce a fine view effect, but also increase, through interaction with the primer coatings, the resistance to diffusion of corrosive factors from the external environment. It was also found that, unlike the heavy metal oxide-forming layer of the passive barrier alone, the polyaniline anti-corrosive pigment oxidized iron at the interface with the iron substrate to form a passive barrier in the oxidic layer, and itself formed a potential barrier layer with anti-corrosive factors from the external environment. Although the passive layer was damaged, the damaged area did not become completely oxidized iron; on the contrary, it showed a tendency to reduction. This can be interpreted such that a passive layer is formed again on the damaged area, and that at the same time there is a tendency to self-healing.

• 대한금속재료학회지
• /
• 제48권2호
• /
• pp.141-147
• /
• 2010

An Ni-Al intermetallic coating has been produced by induction heating on mild steel. The effect of the induction heating conditions on the microstructure of the coating has been investigated. The reaction synthesis of the intermetallic compounds was promoted while increasing the heating rate and the holding time at reaction temperature. Especially, an NiAl phase corresponding to the initial composition of mixed powder was predominantly formed. However, the synthesis at low reaction temperatures occurred by solid state diffusion during the holding time and an Fe-Al reaction layer was formed at the interface with the substrate, regardless of the heating rate. The combustion synthesis of the intermetallic compound occurred at a temperature higher than 1023 K and resulted in an almost single phase NiAl structure.