Abstract
In this study, the wear resistance of the complex powder diffusion treated KS STD 61 has been investigatived. KS STD 61 tool steel was pretreated in quenching and tempering processes to obtain the tempered martensitic microstructure. The samples were packed with complex powder in steel pot($\Phi$90x60mm) and heated in a box furnace. the complex powder diffusion treatment are carried out at $540^{\circ}C$, $520^{\circ}C$, $500^{\circ}C$ for 40min, 1.5hr and 2.5hr. The microstructure, microhardness, wear resistance, and coating layer thickness of the complex powder diffusion treated samples were investigation. The weight loss of as heat treated sample was 0.4mg and that of the complex powder treated at $540^{\circ}C$ for 2.5hr was 0.17mg. These result means that the wear resistance of tool steels can be easily improved by the powder diffusion process at conventional tempering treatment temperature.