• The Journal of Korean Academy of Prosthodontics
• /
• v.52 no.2
• /
• pp.67-73
• /
• 2014

Purpose: The purpose of present study is to compare mechanical properties and microstructural characteristics of fractured surface for cast, 3-D printing laser sintered and CAD/CAM milled cobalt-chromium (Co-Cr) alloy specimens and to investigate whether laser sintered technique is adequate for dental applications. Materials and methods: Thirty six flat disc shape Co-Cr alloy specimens were fabricated for surface hardness test and divided into three groups according to the manufacturing methods; 12 specimens for casting (n=12), 12 specimens for laser sintered technology (n=12) and 12 specimens for milled technology (n=12). Twelve dumbbell shape specimens for each group were also fabricated for a tensile test. Statistical comparisons of the mechanical properties for the alloys were performed by Kruskal-Wallis test followed by Mann-Whitney and Bonferroni test. The microstructural characteristics of fractured surfaces were examined using SEM. Results: There were significant differences in the mean Vickers hardness values between all groups and the cast specimen showed the highest (455.88 Hv) while the CAD/CAM milled specimen showed the lowest (243.40 Hv). Significant differences were found among the three groups for ultimate tensile strength, 0.2% yield stress, elongation, and elastic modulus. The highest ultimate tensile strength value (1442.94 MPa) was shown in the milled group and the highest 0.2% yield strength (1136.15 MPa) was shown in the laser sintered group. Conclusion: Different manufacturing methods influence the mechanical properties and microstructure of the fractured surfaces in Co-Cr alloys. The cast Co-Cr alloy specimens showed the highest Vickers hardness, and the CAD/CAM milled specimens revealed the highest tensile strength value. All alloys represent adequate mechanical properties satisfying the ISO standards of dental alloy.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.107-107
• /
• 2008

• The Journal of the Korea Contents Association
• /
• v.10 no.11
• /
• pp.228-234
• /
• 2010

Ni-Cr and Co-Cr alloy uncontained Be element for using as dental porcelain alloy were analyzed the mechanical properties through bonding strength and fracture test after the bonding with porcelain. The bonding strengths between alloy and ceramic were measured through the shear bond strength test. Consequently, the T-3 group contained Be element that had shear strength of 41.13(${\pm}5.11$)MPa was showed the highest shear strength than the other groups. The second highest group was a verabond contained Be element that had shear strength of 40.72(${\pm}5.98$)MPa. The results of the other groups according to the shear strength were Wirobond(38.40(${\pm}9.66$)MPa) belonged to Co-Cr alloy, and Verabond 2V(32.77(${\pm}4.31$)MPa), Bellabond N(28.63(${\pm}6.39$)MPa), Bellabond plus(24.97(${\pm}6.13$)MPa), Argeloy N.P. Star(22.69(${\pm}3.41$)MPa) uncontained Be element, respectively. The morphological aspects of the fracture surface between alloys and ceramic were observed that all groups were caused mixed failure as conformation attached ceramic fragments to metallic surface by fracture process.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.1
• /
• pp.1-8
• /
• 2016

PURPOSE. The purpose of this study was to evaluate the efficacy of two different metal conditioners for non-precious metal alloys for the bonding of porcelain to a cobalt-chromium (Co-Cr) alloy. MATERIALS AND METHODS. Disk-shaped specimens ($2.5{\times}10.0mm$) were cast with Co-Cr alloy and used as adherend materials. The bonding surfaces were polished with a 600-grid silicon carbide paper and airborne-particle abraded using $110{\mu}m$ alumina particles. Bonding specimens were fabricated by applying and firing either of the metal conditioners on the airborne-particle abraded surface, followed by firing porcelain into 5 mm in diameter and 3 mm in height. Specimens without metal conditioner were also fabricated. Shear bond strength for each group (n=8) were measured and compared (${\alpha}=.05$). Sectional view of bonding interface was observed by SEM. EDS analysis was performed to determine the chemical elements of metal conditioners and to determine the failure modes after shear test. RESULTS. There were significant differences among three groups, and two metal conditioner-applied groups showed significantly higher values compared to the non-metal conditioner group. The SEM observation of the sectional view at bonding interface revealed loose contact at porcelain-alloy surface for non-metal conditioner group, however, close contact at both alloy-metal conditioner and metal conditioner-porcelain interfaces for both metal conditioner-applied groups. All the specimens showed mixed failures. EDS analysis showed that one metal conditioner was Si-based material, and another was Ti-based material. Si-based metal conditioner showed higher bond strengths compared to the Ti-based metal conditioner, but exhibited more porous failure surface failure. CONCLUSION. Based on the results of this study, it can be stated that the application of metal conditioner is recommended for the bonding of porcelain to cobalt-chromium alloys.

• Journal of Technologic Dentistry
• /
• v.33 no.4
• /
• pp.349-357
• /
• 2011

Purpose: In this study, for the reasons of observing the changes when using bonding agent with Ni-Cr alloy and Co-Cr alloy and using VM13 and Vintage MP ceramic which have the disparity in coefficient of thermal expansion, it is carried out to evaluate the characteristics of the bonding agent through the analysis of the interface between metal and ceramic and the analysis of bond strength by variable. Methods: The surface treatment was performed on the two kinds of alloy(Ni-Cr alloy and Co-Cr alloy) specimens, which were sandblasted and were treated with bonder application. The metal-ceramic interfaces were analyzed with EPMA in order to ionic diffusion, and the shear test was performed. Results: As a result of observation of metal-ceramic interfacial properties, it was observed that Cr atoms were spread from the alloy body to the ceramic floor in the specimen of Group B. It was also seen that Cr, W atoms were spread from the alloy body to the ceramic floor in the specimen of Group S. In consequence of observing Shear bond strength, it was calculated that the specimen of BSV was 27.75(${\pm}11.21$)MPa, BSM was 27.02(${\pm}5.23$)MPa, BCV was 30.20(${\pm}5.99$)MPa, BCM was 27.94(${\pm}10.76$)MPa, SSV was 20.83(${\pm}2.58$)MPa, SSM was 23.98(${\pm}3.94$)MPa, SCV was 32.32(${\pm}4.68$)MPa, and SCM was 34.54(${\pm}10.63$)MPa. Conclusion: In the metal-ceramic interface of Bellabond plus sample group, diffusion of Cr atoms was incurred and diffusion of C Cr atoms and W atoms in the sample group of $Starloy{(R)}\;C$ was observed. Using bonding agent showed the higher bond strength than using the sand blasting treatment. In the Bellabond plus alloys, the specimen group with the use of binding materials showed higher shear bond strength, but didn't show statistically significant differences (p>0.05). In the $Starloy{(R)}\;C$ alloys, the specimen group with the use of binding materials showed higher shear bond strength and statistically significant differences(p<0.05). In terms of VM13 ceramic, it was in the Bellabond plus alloys that the high shear bond strength was showed, but there's no statistically significant differences(p>0.05). In terms of Vintage MP ceramic, it was in the $Starloy{(R)}\;C$ alloys that the high shear bond strength was showed and statistically significant differences(p<0.05). Metal-ceramic to fracture of the shear strength measurements and an analysis of all aspects of military usage fracture of the composite, respectively.

• Journal of Technologic Dentistry
• /
• v.23 no.1
• /
• pp.21-30
• /
• 2001

For biomedical applications. Ti-X%Zr-Y%Pd(X: $10{\sim}20$, Y:0.2 or 0.4) based alloys not containing harmful Al and V were newly designed, and polarization curves for their alloys were measured at $37^{\circ}C$ in 5% HCl solution in order to understand effects of Zr on the corrosion. From the results of anodic polarization behavior, it was found that the corrosion resistance increased with increasing Zr content. The results show their potential to develope Ti-based alloys for biomedical materials. The Ti-20%Zr-0.2%Pd alloy shows excellent corrosion resistance and was superior to those of the Ti. Ti-6%Al-4%V ELI alloy, Co-30%Cr-6%Mo alloy and STS 316L stainless steel.

• Journal of Technologic Dentistry
• /
• v.42 no.2
• /
• pp.129-137
• /
• 2020

Purpose: The aim of this study is to observe the compressive fracture strength of the crown according to the direction of the occlusal force of the mandibular canine and carnassial of the small dog. Methods: The abutment models of mandibular canine and carnassial were prepared, specimens of zirconia, PMMA and Ni-Cr alloy were produced. The experimental jig was fabricated with Co-Cr alloy and buried in acrylic resin after make tilt to specified angle. The specimen was attached to a jig and loaded using a universal testing machine until the specimen fractured. Results: The compressive fracture strengths of CXZ and CXP specimens were found to be 999.21 ± 31.15 N on average and 731.42 ± 59.13 N on average. And CZZ and CZP specimens were 730.48 ± 70.14 N on average and 377.65 ± 11.87 N on average. CXN and CZN specimens were not fractured. In addition, MZZ and MZP specimens were 746.46 ± 50.75 N and 258.64 ± 31.86 N on average. The MZN specimens were not fractured. Conclusion: Zirconia has compressive fracture strength that can be applied to small dog's canine and Carnassial prosthetics, while PMMA has inadequate strength to small dog's carnassial prosthesis.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.95-101
• /
• 2019

Purpose: The aim of this study is to evaluate the effects of various primers on the microtensile bond strength (${\mu}TBS$) of resin cements to cobalt-chromium (Co-Cr) dental casting alloy. Materials and methods: Four adhesive primers (Universal primer, Metal primer II, Alloy primer, and Metal/Zirconia primer) and two resin cements (Panavia F2.0, G-CEM LinkAce) were tested. One hundred fifty Co-Cr beams were prepared from Co-Cr ingots via casting ($6mm\;ength{\times}1mm\;width{\times}1mm\;thick$). The metal beams were randomly divided into ten groups according to the adhesive primers and resin cements used; the no-primer groups served as the control (n = 15). After sandblasting with aluminum oxide ($125{\mu}m$ grain), the metal and resin cements were bonded together using a silicone mold. Prior to testing, all metal-resin beams were examined under stereomicroscope, and subjected to the ${\mu}TBS$ test. The mean value of each group was analyzed via one-way ANOVA with Tukey's test as post hoc (${\alpha}=.05$) using SPSS software. Results: The mean ${\mu}TBS$ of all groups was ranged from 20 to 28 MPa. There is no statistically significant difference between groups (P > .05). Mixed failure, which is the combination of adhesive and cohesive failures, is the most prevalent failure mode in both the Panavia F2.0 and G-Cem LinkAce groups. Conclusion: The ${\mu}TBS$ of all tested groups are relatively high; however, the primers used in this study result in no favorable effect in the ${\mu}TBS$ of Panavia F2.0 and G-Cem LinkAce resin cement to Co-Cr alloy.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.78-94
• /
• 1997

The purpose of this experiment was to determine the effects of various treatments on denture base resin to metal bond for cobalt-chromium alloy. The metal surface was treated as follows. Group 1 : Sandblasted with $50{\mu}m$ aluminum oxide. Group 2 : Sandblasted with $250{\mu}m$ aluminum oxide. Group 3 : Sandblasted with $250{\mu}m$ aluminum oxide and followed by silicoating. Group 4 : Electrochemically etched. Group 5 : treated with oxidizing solution. Group 6 : Beaded with $200{\mu}m$ retention structure and followed by silicoating. All specimens were applied with 4-META resin and were thermocycled 1000 times at temperature of $5^{\circ}C$ to $55^{\circ}C$. The effects of various surface treatments on the bond strength between 4-META resin and metal interface were measured by using the universal testing machine. All specimens were observed with SEM. The results were as follows 1. The bond strength of 4-META resin were significantly higher to Co-Cr alloy. 2. The bond strength decreased in the following orders : group 6, group 3, groups 1 and 2, group 4, group 5 and there was no statistically significant difference in bond strength among groups 1 and 2.(p>0.05) 3. The bond strength of cobalt-chromium alloy to 4-META resin were not significantly different.(p>0.05) 4. The treated surface of groups 1, 2 and 3 has more fine undercut than that of groups 4 and 5 with SEM. 5. Stable adhesion can be achieved when mechanically roughened metal surface by sandblasting than treating in an electrochemical etching and an oxidizing solution with potassium manganate.

• The Journal of the Korean dental association
• /
• v.53 no.11
• /
• pp.804-816
• /
• 2015

PURPOSE: The aim of this study was to evaluate the influence of the oxide layer removal process in the Co-Cr-Mo (CCM) abutment after casting procedure on the prosthesis settlement and screw stability. MATERIALS AND METHODS: CCM abutments of four different interface conditions (CCM-M; machined, CCM-O; oxide layer formed, CCM-B; blasted, CCM-P; polished after blasted) and gold abutment (Gold-C; Cast with type III Gold alloy) were used. The initial settling values of abutments were evaluated according to the difference of implant-abutment length when the tightening torques were applied at 5 Ncm and 30 Ncm, and the settling values of abutments caused by loading were evaluated according to the difference of implant-abutment length before and after loading with 250 N, 100000 cycle. The loss ratios of removal torque for abutment screws were evaluated according to the difference in value of removal torques under 30 Ncm tightening torque applied before and after cyclic loading. RESULTS: The CCM-P and CCM-B group showed a higher initial settling value compared with the Gold-C group (P<.05), while the Gold-C group showed the highest settling values caused by loading (P<.05) and no significant differences were observed for between CCM groups (P>.05). The loss ratio of removal torque values for the CCM-B, CCM-P groups did not differ significantly from that of the Gold-C group (P>.05). CONCLUSION: Even though the oxide layer was removed by different methods, CCM abutment with internal conical connection structure showed lower abutment settling and similar screw loosening after cyclic loading compared with gold abutment.