• 한국세라믹학회지
• /
• 제33권2호
• /
• pp.177-182
• /
• 1996

strontium titanate (SrTiO3) thin films deposited on Pt/MgO were prepared by Plasma Enhanced Metal Orgainc Chemical vapor Deposition (Pe-MOCVD). The crystallinity of SrTiO3 thin films increased with increasing depo-sition temperature and SrF2 second phase disappeared at 55$0^{\circ}C$ The films showed a dielectric constant of 177 and a dissipation factor of 0.0195 at 100 kHz. The variation of capacitance of the films with applied voltage was small showing paraelectric properties. The charge storage density and leakage current density were 40fC/${\mu}{\textrm}{m}$2 and 3.49$\times$10-7 A/cm2 at 0.25 MV/cm, respectively.

• Bulletin of the Korean Chemical Society
• /
• 제29권4호
• /
• pp.777-781
• /
• 2008

In this work, silver nanoparticles-containing polyacrylonitrile (PAN) solutions in N,N-dimethylformamide (DMF) were electrospun to be webs consisting of nanofibers. The inputted voltage and PAN content in the solution were fixed at 15 kV and 10 wt.% in DMF with 10 cm of tip-to-collector distance (TCD). The PAN/Ag nanofiber webs were stabilized by oxidation at 250 ${^{\circ}C}$ for 2 h in air and carbonized at 1000 ${^{\circ}C}$ for 2 h in $N_2$. The resultant diameter distribution and morphologies of the nanofibers were evaluated by scanning electron microscope analysis. The electrochemical behaviors of the nanofiber webs were also observed by cyclic voltammetry tests. It was found that the presence of silver nanoparticles in carbon nanofiber webs led to the increase of specific capacitance and the decrease of fiber diameters.

• 대한화학회지
• /
• 제39권9호
• /
• pp.722-727
• /
• 1995

순환 전압-전류법으로 합성한 폴리아닐린 막의 전기화학적 임피던스 측정을 0.1M 황산용액에서 수행하였다. 전기 전도성을 갖는 퍼텐셜 영역에서 전하-이동 정항은 낮은 값을 나타냈으며, 따라서 교환 전류밀도는 큰 값으로 측정되었다. 고분자의 축전 용량은 이중층 축전 용량보다 크게 나타났으며 이값은 전극 퍼텐셜에 따라 변하였다. 측정된 임피던스 데이터로부터 전극의 등가 회로를 추정하였으며, 이 등가 회로를 토대로 하여 폴리아닐린 막대에서 혼입된 이온의 물질 이동 파라미터를 산출하였다.

• 대한화학회지
• /
• 제20권2호
• /
• pp.129-135
• /
• 1976

4-전극 측정 용기와 정전위 전자회로를 써서 직독식 전기전도도 측정장치를 고안하여 KCl, HCl등 전해질 용액의 전기전도도를 측정하였다. 이 장치는 상용되고 있는 브릿지회로와 2-전극 용기를 쓰는 방법에서 당면하는 어려운 문제들, 특히 전극에서의 전기 이중층의 존재와 파라디임피던스 등으로 나타나는 전기화학적으로 복잡한 성질들로 인한 문제들을 피하여 정밀하고 간편한 측정에 쓰이도록 만들었다.

• Bulletin of the Korean Chemical Society
• /
• 제13권1호
• /
• pp.30-32
• /
• 1992

The apparent depth of space charge region on the ZnO $(10{\bar{1}}0)$ surface in chemisorption of oxygen has been estimated from the capacitance of two contacting faces. When the sample (donor concentration: $2.4{\times}10^{22}\;m^{-3}$) was evacuated at 773 K for 1 hr the depth reached to 40-100 ${\AA}$ depending on sample assembly. Admission of oxygen to the sample resulted in an increase of the depth to 3600 ${\AA}$ where the increment was greater at higher oxygen pressure between 6.6-1600 $N/m^2$. Admission of CO to the sample previously exposed to oxygen yields a decrease in the depth. The results of the measurement support that oxygen is adsorbed as an acceptor on ZnO $(10{\bar{1}}0)$.

• Bulletin of the Korean Chemical Society
• /
• 제20권9호
• /
• pp.1049-1055
• /
• 1999

Electrochemical oxidation of silicon (p-type Si(100)) at room temperature in ethylene glycol and in aqueous solutions has been performed by applying constant low current densities for the preparation of thin SiO2 layers. In-situ ac impedance spectroscopic methods have been employed to characterize the interfaces of electrolyte/oxide/semiconductor and to estimate the thickness of the oxide layer. The thicknesses of SiO2 layers calculated from the capacitive impedance were in the range of 25-100Å depending on the experimental conditions. The anodic polarization resistance parallel with the oxide layer capacitance increased continuously to a very large value in ethylene glycol solution. However, it decreased above 4 V in aqueous solutions, where oxygen evolved through the oxidation of water. Interstitially dissolved oxygen molecules in SiO2 layer at above the oxygen evolution potential were expected to facilitate the formation of SiO2 at the interfaces. Thin SiO2 films grew efficiently at a controlled rate during the application of low anodization currents in aqueous solutions.

• Bulletin of the Korean Chemical Society
• /
• 제18권11호
• /
• pp.1175-1179
• /
• 1997

The adsorption of oxygen on ZnO was monitored by measuring the capacitance of two contacting crystals which have depletion layers originated from the interaction between oxygen and ZnO at 298 K-473 K. An admission of oxygen to the sample induced an irreversible increase in the depth and the amount of adsorbed oxygen was less than 0.001 monolayer in the experimental condition. The relation between pressure of oxygen and variation of the depth was tested from the view point of Langmuir or Freundlich isotherm. Using Hall effect measurement and kinetic experiment, a model equation on the adsorption process was proposed. From the results, it was suggested that oxygen adsorption depended on the rate of electron transfer from ZnO to oxygen while the amount of adsorbed oxygen was kinetically restricted by the height of surface potential barrier.

• Journal of Industrial and Engineering Chemistry
• /
• 제67권
• /
• pp.478-485
• /
• 2018

The effect of reduced graphene oxide (RGO) addition on the dielectric and piezoelectric behavior of the polyvinylidene fluoride (PVDF) films was studied. Dielectric constant increased by four times and piezoelectric coefficient also increased twice by the addition of RGO in the PVDF films. Based on capacitance-voltage and ellipsometry measurements and the Kramers-Kronig transformation, it is concluded that the enhanced dielectric and piezoelectric properties of the PVDF/RGO films resulted from the increased orientational polarization due to a phase transition from nonpolar crystalline ${\alpha}$ phase to polar crystalline ${\beta}$ phase in the PVDF structure.

• 전기화학회지
• /
• 제4권3호
• /
• pp.113-117
• /
• 2001

탄소계 전극을 사용하는 EDLC(Electric Double Layer Capacitor)용의 축전용량과 충방전속도는 전해질의 종류, 충방전 조건 그리고 탄소계 물질의 물리화학적 성질에 따라 크게 달라질 수 있다. 이에 본 연구에서는 dip coating method에 의해 제조된 EDLC용 활성탄소 전극에서 유기 전해질의 종류를 달리하여 충방전 실험과 전기화학적인 실험을 시행하였다. 또한 충전전류밀도와 방전전류밀도의 변화에 따른 비축전 용량의 변화를 조사하였고, 최적 유기전해질의 조건에서 leakage current 특성, 자가방전 특성 그리고 시간전압곡선을 기존의 $1M-Et_4NBF_4/PC$와 비교하였다 활성탄, 소전극으로 비표면적이 $2000m^2/g$인 MSP-20을 사용하고 유기전해질로는 $1M-LiPF_6/PC-DEC(1:1)$를 사용한 EDLC에서 130 F/g 정도의 우수한 비축전 용량을 나타내었고 저항면에서도 가장 낮은 수치를 나타내었다 $1M-LiPF_6/PCDEC(1:1)$를 사용한 EDLC는 15분동안 0.0004A의 낮은 leakage current와 100시간 경과 후 0.8V의 우수한 자가 방전 특성 그리고 IR-drop이 적은 선형의 시간-전압곡선을 보여주었다.

• 공업화학
• /
• 제19권2호
• /
• pp.185-190
• /
• 2008

전기흡착용 전극의 비표면적을 증가시키기 위하여 상전이법을 이용한 다공성 탄소전극을 제조하였다. 활성탄소분말, polyvinylidene fluoride (PVdF)를 유기용매인 N-methyl-2-pyrrolidone (NMP)과 혼합한 전극슬러리를 전도성 흑연박막 위에 캐스팅한 후 비용매인 증류수에 침지시켜 상전이를 통해 다공성 탄소전극을 제조하였다. 제조된 전극에 대하여 SEM, porosimetry, cyclic voltammetry 분석을 통해 전극의 물리적, 전기화학적 특성을 분석하였다. SEM 측정 결과 다양한 크기의 미세한 기공이 전극 표면에 균일하게 형성된 것을 확인할 수 있었다. NMP 함량을 변화시켜 제조한 전극들의 평균 기공크기를 측정한 결과 64.2~82.4 nm 범위의 기공을 갖는 것으로 나타났으며 NMP 함량이 증가할수록 기공의 크기도 증가하는 것을 알 수 있었다. 또한 탄소전극에 대한 cyclic voltammogram을 측정한 결과 전형적인 전기이중층에서의 흡착 및 탈착 특성을 보였다. 전극의 축전용량은 NMP의 함량에 따라 $3.88{\sim}5.87F/cm^2$ 범위의 값을 나타냈으며 NMP의 함량이 감소할수록 축전용량이 증가하는 것으로 나타났다. 이상의 연구결과로부터 상전이 방법으로 다공성 탄소전극을 제조할 때 유기용매의 함량은 전극의 기공 크기를 제어할 수 있는 중요한 인자이며 이를 통해 전극의 비표면적을 향상시킬 수 있음을 확인할 수 있었다.