• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.2
• /
• pp.179-185
• /
• 2013

The behavior of surface film formation was greatly dependent on the speed of potential cycling. In $LiClO_4$ / EC + DEC, cyclic voltammetry results showed that the peaks originated from surface film formation on graphite electrode at the high charge-discharge rate was shifted to the lower potentials as the charge-discharge rate decrease. This indicates that surface films with different morphology and thickness were formed by different charge-discharge rate. Transmission electron microscopy (TEM) results indicated that the properties such as thickness and morphology of the surface film were greatly affected by the charge-discharge rate. Electrochemical impedance spectroscopy (EIS) showed that the resistance of surface film was affected by the speed of potential cycling. In addition, the charge transfer resistance was also dependent on the charge-discharge rate indicating that the charge transfer reaction was affected by the nature of surface film. TEM and EIS results suggested that the chemical property as well as the physical property of the surface film was affected by the charge-discharge rate.

• Korean Journal of Materials Research
• /
• v.26 no.12
• /
• pp.696-703
• /
• 2016

In this study, we intensively investigated the effect of conductive additive amount on electrochemical performance of organic supercapacitors. For this purpose, we assembled coin-type organic supercapacitor cells with a variation of conductive additive(carbon black) amount; carbon aerogel and polyvinylidene fluoride were employed as active material and binder, respectively. Carbon aerogel, which is a highly mesoporous and ultralight material, was prepared via pyrolysis of resorcinol-formaldehyde gels synthesized from polycondensation of two starting materials using sodium carbonate as the base catalyst. Successful formation of carbon aerogel was well confirmed by Fourier-transform infrared spectroscopy and $N_2$ adsorption-desorption analysis. Electrochemical performances of the assembled organic supercapacitor cells were evaluated by cyclic voltammetry, galvanostatic charge/discharge, and electrochemical impedance spectroscopy measurements. Amount of conductive additive was found to strongly affect the charge transfer resistance of the supercapacitor electrodes, leading to a different optimal amount of conductive additive in organic supercapacitor electrodes depending on the applied charge-discharge rate. A high-rate charge-discharge process required a relatively high amount of conductive additive. Through this work, we came to conclude that determining the optimal amount of conductive additive in developing an efficient organic supercapacitor should include a significant consideration of supercapacitor end use, especially the rate employed for the charge-discharge process.

• Journal of Electrical Engineering and Technology
• /
• v.10 no.3
• /
• pp.1102-1106
• /
• 2015

A hybrid supercapacitor (HS) is an energy storage device used to enhance the low weight energy density (Wh/kg) of a supercapacitor. On the other hand, a sudden decrease in capacity has been pointed out as a reliability problem after many charge/discharge cycles. The reliability problem of a HS affects the early aging process. In this study, the capacity performance of a HS was observed after charge/discharge. For detailed analysis of the initial charge/discharge cycles, the charge and discharge curve was measured at a low current density. In addition, a solid electrolyte interphase (SEI) layer was confirmed after the charge/discharge. A HC composed of a lithium titanate (LTO) anode and active carbon cathode was used. The charge/discharge efficiency of the first cycle was lower than the late cycles and the charge/discharge rate was also lower. This behavior was induced by SEI layer formation, which consumed Li ions in the LTO lattice. The formation of a SEI layer after the charge/discharge cycles was confirmed using a range of analysis techniques.

• Journal of the Korea Safety Management & Science
• /
• v.2 no.2
• /
• pp.187-200
• /
• 2000

The charge and discharge current in EPR(Ethylene Propylene Rubber), which were irradiated with the radiant capacity of 0~600 ［kgy/h］, have been measured in order to investigate the influence of the atmosphere (oxygen, air and vacuum) on electrical properties. It has been shown that the charge and discharge current increase as the amount of radiant capacity increases in air and vacuum atmosphere. This electrical property degradation can be speculated due to that the C＝O radicals or impurities, which comes from during shaping process, may act as dipoles. On the other hand, the charge and discharge current are shown to be higher in the amount of 1［kgy/h］ than these in 10［kgy/h］ in air atmosphere, because the charge and discharge current can be increased as the exposure time is extended with slower rate. Under the same amount of irradiation, the charge and discharge current in oxygen atmosphere are shown to be higher than those in vacuum. This is possibly due to that the main chain can be broken by oxidation when it is exposed to the $\gamma$ -rays.

• Journal of the Korean Electrochemical Society
• /
• v.7 no.1
• /
• pp.32-37
• /
• 2004

The charge/discharge capacity of natural graphite anode in lithium secondary batteries was examined as a function of charge/discharge rate. When the natural graphite anode was galvanostatically cycled in the range of 0.0-2.0V $(vs.\;Li/Li^+)$, the charging capacity decreased with an increase in the charging rate, which is caused by an earlier approach to the charging cut-off (0.0 V) before the complete charging that is in turn caused by an ever-increasing overpotential at higher rates. Even if the overpotential of discharging reaction also increased at higher discharge rates, the discharging reaction took place in the range of 0.0-0.3 V that is far below the discharge cut-off (2.0 V). As a result, the discharge capacity was not affected by the discharge rate because all the lithium ions once intercalated are fully discharged even at high current condition. As the overpotential of lithium deposition reaction also increased at high current condition, the charge capacity of natural graphite could be enlarged by lowering the charging cut-off voltage below 0.0 V, There is, however, a limitation for the lowering of cut-off voltage because the resistance for lithium deposition is smaller than that of lithium intercalation into graphite. When the charge cut-off voltage was lowered down to -0.04 V under IC condition, lithium ions were inserted into graphite without lithium deposition such that the discharge capacity could be raised up to $11\%$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.1
• /
• pp.34-39
• /
• 2015

In this study, the characteristics of partial discharge was measured for the four core silicone cable (0.6/1.0 kV, $1.0SQ{\times}4C$) with insulated part of 15 cm and conductor of 1cm. The following results have been confirmed as a result of this study. When the first line of cable is connected to the positive electrode and the second, third line of cable is connected to the negative electrode, it found that the inception voltage and extinction voltage decreased with increasing the line of negative electrode, and the partial discharge charge quantity(Q) increases, while the number of discharge occurrence has decreased. The inception voltage and extinction voltage of partial discharge has decreased with increasing the degradation rate in the 33%, 67%, 100%. Also, it confirmed that the partial discharge charge quantity(Q) and the number of discharge occurrence has decreased.

• Journal of Energy Engineering
• /
• v.20 no.4
• /
• pp.278-285
• /
• 2011

Computational modelling and simulation for the charge-discharge characteristics of Lithium-ion batteries have been carried out. The battery system consists of a simplified 2-dimensional single cell for the modelling, in which the thermal modelling on the charge-discharge characteristics was conducted in the temperature range from 288 K through 318 K by using FEMLAB as an engineering PDE solver. While material parameters adopted in the present modelling were dependent on the system temperature, their thermal modelling were applied on the simulations of the charge-discharge period and the rate of transferring charges systematically. The resulting simulation shows that the cycle of the charge-discharge shorten itself by reducing the system temperature, regardless of the charge-discharge rates. In addition, the mass-transport phenomena of Lithium ion have been discussed in connection with the charge-discharge characteristics in the battery.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.7
• /
• pp.636-643
• /
• 2006

Si-C materials were synthesized by the heating the mixture of silicon and polyvinylidene fluoride (PVDF). The electrochemical properties of the Si-C materials as the high capacitive anode materials of lithium secondary batteries were evaluated by the galvanostatic charge-discharge test through 2032 type $Si-C{\mid}Li$ coin cells. Charge-discharge tests were performed at C/10 hour rate(C = 372 mAh/g). Initial discharge and charge capacities of $Si-C{\mid}Li$ cell using a Si-C material derived from PVDF(20wt.%) were found to be 1,830 and 526 mAh/g respectively. The initial discharge-charge characteristics of the developed Si-C electrode were analyzed by the electrochemical galvanostatic test adopting the capacity limited charge cut-off condition(GISOC). The range of reversible specific capacity IIE(intercalation efficiency at initial discharge-charge) and IICs(surface irreversible specific capacity) were 216 mAh/g, 68 % and 31 mAh/g, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.9
• /
• pp.656-661
• /
• 2013

In this study, the moisture content, charge discharge current, electrostatic capacity and dielectric loss tangent are measured for the specimen of bisphenol type epoxy resin which is mixed with squared amorphous silica filler and dipped in hot water of $50^{\circ}C$ for 169 days. The results of this study are listed below. The longer of deposition day, the charge and discharge current was increased. It is considered that the reason is because there was water attack through the squared silica surface. The longer of deposition day, the absorption rate of all specimens was increased. It found that the absorption rate reached saturated state after 100 days. The higher frequency and the longer of deposition day, the $tan{\delta}$ was decreased. Also, It found that the $tan{\delta}$ and electrostatic capacity of the specimen which is mixed with squared filler are greater.

• Transactions of the Korean hydrogen and new energy society
• /
• v.5 no.2
• /
• pp.99-109
• /
• 1994

To develop high capacity hydrogen storage alloys for secondary Ni/MH batteries, electrochemical charge/discharge characteristics of $Zr_{1-x}Ti_xMn_{1-y}V_yNi_{1-z}M_z$ (M=Al,Co,Fe) alloys were investigated, in which $0.2{\leq}x{\leq}0.6$, $0.2{\leq}y{\leq}0.8$, $0.2{\leq}z{\leq}0.4$. With increasing Ti content(x) and/or decreasing V content(y), lattice constants and maximum theoretical capacities of the alloys were decreased and equilibrium pressure of hydrogen absorption were increased. Electrochemical discharge capacities were increased with increasing Ti content(x). Especially, the alloys of x= 0.4~0.6 showed better charge/discharge efficiencies than those of x<0.4. Discharge capacities of $Zr_{0.4}Ti_{0.6}Mn_{0.4}V_{0.6}Ni_{0.8}Fe_{0.2}$, $Zr_{0.4}Ti_{0.6}Mn_{0.4}V_{0.6}Ni_{0.8}Al_{0.2}$ and $Zr_{0.5}Ti_{0.5}Mn_{0.4}V_{0.6}Ni_{0.6}Co_{0.4}$ were 385, 328 and 333mAh/g, respectively. These alloys were fully activated within five charge/discharge cycles and had a good charge and discharge rate capabilities and temperature characteristics.