• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.907-911
• /
• 2002

Using the two-dimensional Wulff plot, the equilibrium shape of a sapphire crystal was investigated as a function of surface energy anisotropy. Depending on the relative values of surface energy for various facet planes, the projected shape of equilibrium sapphire was determined to be rectangle, parallelogram, hexagon or octagon. The results are compared with the experimentally observed shapes of internal cavities of submicron range in sapphire single crystals.

• Journal of the Korean Ceramic Society
• /
• v.27 no.1
• /
• pp.43-47
• /
• 1990

An attempt was made to grow Y-Ba-Cu-O single crystals by skull method(cold crucible process). Grown YBa2Cu3O7-x(YBC) single crystals were obtained from the upper part of the YBC solid mixture. There were plate-like YBC single crystals aligned with solidified flux along the crystal growth direction. Single crystal size was (5$\times$2$\times$0.2㎣) and was grown to a-b plane of YBC crystal structure which can flow super currents. Optical microscope and X-ray diffraction were employed characterize these microstructure and YBC single crystals.

• Journal of the Korean Ceramic Society
• /
• v.28 no.6
• /
• pp.443-450
• /
• 1991

Microstructures of tantalum oxide, anodic-oxidized in oxalic acid, are shown to be related to voltage-time characteristics during formation reaction. It is observed that a crystalline phase transformed from an amorphous phase is recrystallized in the presence of the high electric field within the film, and this recrystallized film has a very porous microstructure. From the results of the XRD, the nonlinearity observed after the first spark voltage is recognized to be due to the local crystallization.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2004.10a
• /
• pp.1057-1058
• /
• 2004

• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.480-488
• /
• 1992

The sintering behaviors of seeded alumina from alkoxide were studied. Room temp. desiccated powder exhibited better sintering behavior due to its packing ability and powder activity. $\alpha$-Al2O3 2wt% seeded compacts sintered with 97.5%TD, 1~3${\mu}{\textrm}{m}$ diameters at 140$0^{\circ}C$, 2hrs. Fe-nitrate doped compacts resulted in enhanced initial sintering behavior due to ionic effects of Fe3+ but failed to refined microstructure.

• Journal of the Microelectronics and Packaging Society
• /
• v.5 no.2
• /
• pp.53-58
• /
• 1998

Sintering and dielectric characteristics of substrates were estimated by mixing rate of alumina and potashborosilicate glass(PBSG) powders. PBSG powders were used 7761(corning code)and alumina powders were used in extra pure rate(99.9%) and had 0.1 ${\mu}$m mean size. After ball milling with organic additives green sheets which were casted by doctor blade machine were sintered at 800$^{\circ}C$ for 1∼3hrs. Microstructure, linear shrinkage and dielectric constant of substrates were surveyed in order to fabricate low-dielectric and low tem-perature sintering substrate.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.34-40
• /
• 1993

ORMOSIL was synthesized with inorganic precursor, TEOS and organic precursor, PDMS, and the variation of composite properties according to the concentration of HCl, solvent content and reaction time were studied. As the concentration of HCl increased, condensation reaction was well proceeded and more regularly distributed network was observed. Increase in reactivity was found with the amount of solvent, and composite had a tendency of forming more porous microstructure as reaction time was increased, which had no influence on the bonding degree.

• Journal of the Korean Ceramic Society
• /
• v.22 no.5
• /
• pp.66-70
• /
• 1985

This study was to investigate physical properties of the system $Ca(Mg_{1-x}Al_x) (Si_{2-x}Al_x)O_6$ by quenching method. This system $\chi$=0.1 to 0.3 had same crystal phase microstructure and similar properties. Bulk density microhardness thermal expansion coefficient and modulus of rupture of these solid solutions were 2.87~2.95g/cm3 850~900kg/$mm^2$, $7.5~7.8{\times}10^{-6}$/$^{\circ}C$ and 1950~1980kg/$cm^2$ respectively.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1238-1239
• /
• 2008

The high Tc supeconductor of ceramic oxides type was studied for finding its application field. The results reportaed in this paper on the stability of the ceramic superconductors and the resistance to ripening in the BCO liquid phase at elevated temperature opens a processing window for engineering the microstructure of large superconductor at the nanoscale level. The results suggest further that the introduction of highly efficient artifical pinning center to bulk ceramics superconductor.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.367-376
• /
• 1992

The powder characteristics of seeded alumina prepared from alkoxide by sol-gel method were studied. When ${\alpha}$-Al2O3 seeded powders used, these ${\alpha}$ phase transformation temperatures decreased than those of unseeded powders by 110$^{\circ}C$ and fine powders under 0.1 $\mu\textrm{m}$ could be obtained. When Fe-nitrate added powders used, fast transformation rate resulted from ionic effects of Fe3+, but hard aggregated morphology exhibited. When ${\alpha}$-Al2O3 and Fe nitrate simultaneously added, these powders represented lower transformation temperature but resulted in microstructure with aggregated particles.