• 한국재료학회지
• /
• 제30권10호
• /
• pp.542-549
• /
• 2020

Effects of Sc addition on microstructure, electrical conductivity, thermal conductivity and mechanical properties of the as-cast and as-extruded Al-2Zn-1Cu-0.3Mg-xSc (x = 0, 0.25, 0.5 wt%) alloys are investigated. The average grain size of the as-cast Al-2Zn-1Cu-0.3Mg alloy is 2,334 ㎛; however, this value drops to 914 and 529 ㎛ with addition of Sc element at 0.25 wt% and 0.5 wt%, respectively. This grain refinement is due to primary Al₃Sc phase forming during solidification. The as-extruded Al-2Zn-1Cu-0.3Mg alloy has a recrystallization structure consisting of almost equiaxed grains. However, the as-extruded Sc-containing alloys consist of grains that are extremely elongated in the extrusion direction. In addition, it is found that the proportion of low-angle grain boundaries below 15 degree is dominant. This is because the addition of Sc results in the formation of coherent and nano-scale Al₃Sc phases during hot extrusion, inhibiting the process of recrystallization and improving the strength by pinning of dislocations and the formation of subgrain boundaries. The maximum values of the yield and tensile strength are 126 MPa and 215 MPa for the as-extruded Al-2Zn-1Cu-0.3Mg-0.25Sc alloy, respectively. The increase in strength is probably due to the existence of nano-scale Al₃Sc precipitates and dense Al₂Cu phases. Thermal conductivity of the as-cast Al-2Zn-1Cu-0.3Mg-xSc alloy is reduced to 204, 187 and 183 W/MK by additions of elemental Sc of 0, 0.25 and 0.5 wt%, respectively. On the other hand, the thermal conductivity of the as-extruded Al-2Zn-1Cu-0.3Mg-xSc alloy is about 200 W/Mk regardless of the content of Sc. This is because of the formation of coherent Al₃Sc phase, which decreases Sc content and causes extremely high electrical resistivity.

• 한국산학기술학회논문지
• /
• 제17권2호
• /
• pp.58-65
• /
• 2016

본 연구는 조직공학용 지지체로 사용될 막을 개발하기 위한 초도 연구 수행으로, 염화나트륨(NaCl)을 기공형성체로 혼합한 폴리카프로락톤(PCL)용액을 유리 캐스팅판에 분주한 후 필름 어플리케이터를 이용하여 다공성 PCL필름을 성형하였다. 성형된 필름은 건조 후 증류수에 침지시켜 NaCl을 추출하여 최종 멤브레인형 다공성 지지체를 제조하였다. 3차원 다공망을 형성시키기 위하여 NaCl을 기공형성체로 이용하였으며 $4^{\circ}C$, 실온, $40^{\circ}C$의 세 가지 건조조건에 따른 다공망의 형성과 형태를 주사전자현미경(SEM)을 이용하여 관찰 하였으며 기초적인 안전성 확보를 위한 세포독성평가를 시행하였다. 세 가지의 건조조건별 결과에서는 실온 건조조건에서 거대기공과 미세기공이 혼재된 3차원 다공망이 우수하게 형성된 것이 관찰되었으며 세포독성 시험결과 ISO10993-5 규격의 세포독성 판단기준에 따라 grade 2(mildly cytotoxic)로 나타난바 생체용으로 적합하다고 볼 수 있다. 본 연구를 통하여 멤브레인형 다공성 지지체 제조에 건조조건이 3차원 다공망의 형성 및 거대기공과 미세기공이 함께 형성되는 것에도 영향을 미치는 것으로 나타났으며 이 결과는 다공성 멤브레인 지지체의 분해성 조절 및 약물 담지 효과를 개선하기 위한 연구에서 다공도의 조절에 대한 기초적인 공정이 될 수 있다.

• 보존과학회지
• /
• 제33권3호
• /
• pp.155-165
• /
• 2017

공공 예술 조각품과 야외 조형물에 대한 관심과 함께 미술품 보존 관리의 중요성이 높아지고 있다. 야외 조각작품의 경우, 장기간 대기 중에 노출되어 대기오염물과 자연재해 등의 이유로 부식과 열화 등의 손상이 발생하게 되는데, 국립현대미술관 야외조각공원에 전시중인 김찬식의 '정' 역시 부식으로 인해 작품표면의 파티나층이 손상되었다. 따라서 상태조사, 표면연마, 재파티네이션, 왁스코팅 등의 보존처리를 진행하였으며, 그 결과 원형에 가까운 복원을 이룰 수 있었다. 작품의 재질특성에 대한 분석 결과, 구리, 주석, 아연, 납으로 주조된 미술 공예용 청동임을 확인하였다. 작품 표면연마 후 관찰되는 용접, 균열, 밝은 얼룩의 재질 특성 중, 용접부위는 바탕금속보다 구리를 제외한 나머지 주요원소의 함량이 비교적 적은 경향을 보였으며, 밝은 얼룩은 주석과 납의 함량이 13.0 wt%, 10.5 wt%로 바탕금속(주석: 7.0 wt%, 납: 4.4wt%)보다 높게 측정되었다. 또한 미세조직 관찰결과, 작품의 제작은 열처리를 비롯한 인위적인 가공이 가해지지 않은 주조기법이 사용된 것으로 추정되었다.

• 대한기계학회논문집A
• /
• 제36권12호
• /
• pp.1683-1688
• /
• 2012

수직 다관절 로봇의 세 가지 주요 부품인 베이스프레임, 하부프레임, 상부프레임의 경량화를 위하여 위상최적화를 적용하였다. 위상최적화를 위한 설계 영역은 기존 모델을 포함시키는 단순 영역으로 설정하고 이를 삼차원 솔리드 요소로 이산화하였다. 설계 변수들은 SIMP 법을 사용하여 각각의 요소의 물성치를 파라미터화 시켰다. 로봇의 다물체 동역학 해석으로부터 얻어진 하중들을 로봇의 하중조건으로 부여하였으며 최적화의 목적 함수는 구조의 정적, 동적 강성의 조합으로 설정하고 제한조건은 질량제한조건을 부과하였다. 위상최적설계로 얻은 결과는 주조 제조에 용이한 설계로 후처리하였다. 최종 최적화 모델은 기존 모델과 비교하여 비슷하거나 큰 정적, 동적 강성을 가지면서 베이스프레임은 11.0%, 하부프레임은 12.0%, 상부프레임은 10.0% 경량화시킬 수 있었다.

• 공업화학
• /
• 제21권5호
• /
• pp.495-499
• /
• 2010

본 연구에서는 대량 생산 가능한 센서 전극의 생화학 센서 전극 개발을 위하여 탄소나노튜브(carbon nanotube, CNT)를 복합재료화 공정에 의하여 필름과 나노웹 형태의 벌크 재료로 제작한 후, 이들 전극의 넓은 표면적과 뛰어난 화학적 흡착성을 이용하여 화학적 검출 대상에 노출이 되었을 때 이들로 인한 센싱 특성을 연구하였다. CNT 기반 벌크 전극으로 제작하기 위하여 Nafion을 기저재료로 하는 필름과 PAN 기반의 나노 파이버를 전기방사법에 의하여 제작을 한 후 이들 전극의 화학적 영향에 의한 전기적인 특성 변화 실험을 위하여 버퍼 용액의 정전용량에 대한 전기적 임피던스 요소 값인 저항과 정전용량의 변화를 LCR 계측기로 측정하였다. 생화학센서용 전극으로서 CNT벌크전극의 임피던스 변화 형태가 복합소재 전극의 기저재료에 따라 달리 나타났으며 일정량의 버퍼용액 투여 후에는 변화가 없는 포화 상태의 응답을 보였으며 특히, 정전용량이 저항에 비하여 상대적으로 급격하게 큰 변화를 보여 높은 감도 특성을 지니고 있음이 조사되었다. 이들의 전기적인 특성변화는 버퍼 용액의 화학적 성분들이 전극에 흡수 된 후에 CNT에 흡착이 되어 이들의 전기적인 특성을 변화 시키는 것으로 추론된다.

• 한국주조공학회지
• /
• 제11권6호
• /
• pp.475-481
• /
• 1991

In this study the fabrication technology and mechanical properties of AC8A/$Al_2O_3$ Composites by squeeze casting process were investigated to develope for application as the piston materials that require good friction, wear resistance, and thermal stability. AC8A/$Al_2O_3$ composistes without a porosity and the break of preform were fabricated at the melt temperature of $740^{\circ}C$, the preform temperature of $500^{\circ}C$, and mold temperature of $400^{\circ}C$ under the applied pressure of $1200kg/cm^2$ as the results of the observation of microstructures. As the results of this study, the tensile strength of AC8A/$Al_2O_3$ composites was not increased linearly with $Al_2O_3$ volume fraction and so it seemed not to agree with the rule of mixture, which had been used often in metal matrix composite. Also the tensile strength after thermal fatigue test was little different from that before the test. Consequently it was thought that AC8A/$Al_2O_3$ composites fabricated under our experimental conditions had a good thermal stability and subsequently a good interface bonding. Wear rate(i.e., volume loss per unit sliding distance) of AC8A/$Al_2O_3$ composites was decreased with $Al_2O_3$ volume fraction and the sliding speed at both room temperature and $250^{\circ}C$ and so there was a good correlation between wear rate and hardness. Also the wear rate of AC/8A20% $Al_2O_3$ composities was obtained the value of $1.65cm^3/cm$ at sliding speed of 1.14m/sec as compared with about $3.0\;{\times}10^{-8}cm^3/cm$ hyereutectie Al-Si alloy(Al-16%Si-2%Cu-1%Fe-1%Ni), which applied presently for piston materials. The wear behavior of $Al_2O_3$ composites was observed to a type of abrasive wear by the SEM view of wear surface.

• 한국주조공학회지
• /
• 제35권6호
• /
• pp.147-154
• /
• 2015

The effects of Sc and Sr elements on the modification of the eutectic $Mg_2Si$ phase and the castability were investigated in the Al-4wt%Mg-0.9wt%Si-0.3wt%Mn-0.15wt%Fe alloy. Measurements of the cooling curve and microstructure observations were performed to analyze the additional effects of Sc and Sr minor elements during the solidification process. A prominent effect found on the modification of the eutectic $Mg_2Si$ phase with additions of the Sr and Sc elements. Here, a fine eutectic $Mg_2Si$ phase and a decrease in the growth temperature of the eutectic $Mg_2Si$ phase were evident with an addition of Sc element up to 0.2 wt%. The growth temperature of the eutectic $Mg_2Si$ phase decreased and the effect on the modification of the eutectic $Mg_2Si$ phase increased with the addition of Sr element up to 0.02 wt%. The addition of 0.02wt%Sr had the strongest effect on the modification of the eutectic $Mg_2Si$ phase, and the resulting microstructure of the eutectic $Mg_2Si$ phase was found to have a fibrous morphology with a decreased aspect ratio and an increased modification ratio. Fluidity and shrinkage tests were conducted to evaluate the castability of the alloy. The addition of 0.02wt%Sr effectively increased the fluidity of the alloy, while an addition of Sc did not show any effect compared to when nothing was added. The maximum filling length was recorded for 0.01wt%TiB-0.02wt%Sr owing to the effect of the fine ${\alpha}$-Al grains. The macro-shrinkage ratio decreased, while the micro-shrinkage ratio increased with the addition of various eutectic modifiers. The highest ratio of micro-shrinkage was recorded for the 0.02wt%Sr condition. However, the total shrinkage ratio was nearly identical regardless of the amounts added in this study.

• 대한치과기공학회지
• /
• 제37권3호
• /
• pp.131-144
• /
• 2015

Purpose: This study set out to propose plans for more efficient and effective clinical practice by investigating the current state of clinical practice in the field of dental technology and thus provide basic data to develop pre- and post-education programs for clinical practice. Methods: The subjects include dental technicians at dental technical laboratories that were appointed as the place of clinical practice by the Department of Dental Technology of G University. The survey period spanned from December 22, 2014 to January 20, 2015. Total 250 questionnaires were distributed to them, and 190(76.0%) were returned. After excluding 23 whose answers were uncertain or seemed to lack reliability, total 167(66.8%) were used in final analysis. Results: 1. The most frequent practice the student did during clinical practice was articulator attachment, which was followed by pin operation or model making, one's own task and practice, sand and crow sculpturing, burying, casting, and grinding. 2. In case of going through the entire process, porcelain had the most students at 39(23.4%), being followed by crown & bridge at 28(16.8%), clinical model at 23(13.8%), full denture at 17(10.2%), and partial denture at 17(10.2%) in the order. 3. Of the students, 59.8%(30.5% for reinforced basic practice; 29.3% for intensive practice education) said that intensive practice education should be reinforced in school; and 22.3% said that intensive theory and practice education was needed, which indicates that 82.6% voiced their opinion of reinforcing education around practice. 4. The students felt that they lacked diligence, passion, and theoretical knowledge somewhat and were relatively good at clinical adaptation and operational skills. Conclusion: The findings show that the students felt an absolute lack of practice education as the school education was focused on theory and national exams in the field of dental technology, thus raising a need to reinforce practice education. Of all the respondents, 62.9% said there was a need to improve the current education with a focus on jobs. In future, education of dental technology should work to bring up able dental technicians that can perform in clinical dental technology right after graduation by reinforcing job-based practice education.

• 한국세라믹학회지
• /
• 제36권1호
• /
• pp.97-105
• /
• 1999

탄화규소와 카본의 이성분계에서 pH, 계면활성제 및 출발원료의 입도 분포를 이용하여 성형체의 기공크기 및 기공을 제어에 관한 연구를 수행하였다. 성형체는 각각 다른 분산조건을 가지는 슬러리를 이장성형법을 이용하여 제조하였으며, 입자간의 응\ulcorner제어에 따른 상이한 성형미세구조를 가지도록 하였다. 제조된 성형체에 대하여 반응소결 공정은 1$600^{\circ}C$, 진공분위기에서 20분간 응용 실리콘 침윤 공정을 행하였다. 초기 성형 미세구조가 반응소결체의 미세구조에 미치는 영향을 관찰하기 위하여 광학 현미경 및 SEM 분석을 통하여 제조된 소결체의 미세구조를 분석하였으며, 그리고 이에 따른 반응 소결체의 기계적 특성을 평가하였다. 각각의 분산조건에 따라 성형미세구조는 다르게 나타났으며, 미세한 탄화규소를 입자를 사용하였을 경우에 기공크기가 현저하게 작아짐을 확인하였다. 제조된 반응소결체의 미세구조 분석결과 일반적인 반응소결 탄화수소에서 발견되는 bimodal 미세구조는 관찰되지 않았으며, 이는 초기 탄화규소의 카본의 비가 중요항 변수인 것으로 분석하였다. 반응소결 탄화규소의 3-점 곡강도 값은 입자간의 분산이 잘 이루어진 성형체를 사용하였을 경우 310$\pm$40 MPa으로서 응집이 일어난 성형체를 사용한 반응소결체의 260$\pm$50MPa 보다 높았다.

• Korean Chemical Engineering Research
• /
• 제49권4호
• /
• pp.449-455
• /
• 2011

본 연구에서는 폴리비닐알코올(Polyvinyl alcohol : PVA)와 메틸셀룰로오스(Methyl cellulose: MC)를 사용하여 항균성을 갖는 필름을 제조하였다. 메틸셀룰로오스와 폴리비닐알코올 필름에 항균성을 부여하기 위해 ampicillin(0.025~1wt%)과 streptomycin(0.1~1.0 wt%)을 첨가하여 함량에 따른 기계적인 물성과 항균활성을 확인하였다. 중합도와 검화도에 따른 PVA 필름의 기계적인 물성을 보면 중합도와 검화정도에 따라 필름의 인장강도가 20.2~51.5 $N/mm^2$이었고, 메틸셀룰로오스 필름의 경우 점도에 따라 15.44~21.70 $N/mm^2$이었다. 사용한 균주와 항균제의 함량정도에 따라 그 기계적인 물성과 항균활성에 차이를 보였지만 함량이 늘어날수록 전체적으로 기계적인 물성은 약간 저하되는 경향을 보였지만 항균필름의 항균활성은 우수하였다. Ampicillin과 streptomycin을 사용하여 제조한 항균필름의 항균활성은 포도상 구균과 대장균을 disc diffusion test로 확인하였다. 메틸셀룰로오스와 폴리비닐알코올 필름 모두 streptomycin보다 ampicillin을 함유할 때 항균활성이 우수한 경향을 보였다.