• Journal of Powder Materials
• /
• v.28 no.1
• /
• pp.51-58
• /
• 2021

The conversion of carbon preforms to dense SiC by liquid infiltration is a prospectively low-cost and reliable method of forming SiC-Si composites with complex shapes and high densities. Si powder was coated on top of a 2.0wt.% Y2O3-added carbon preform, and reaction bonded silicon carbide (RBSC) was prepared by infiltrating molten Si at 1,450℃ for 1-8 h. Reactive sintering of the Y2O3-free carbon preform caused Si to be pushed to one side, thereby forming cracking defects. However, when prepared from the Y2O3-added carbon preform, a SiC-Si composite in which Si is homogeneously distributed in the SiC matrix without cracking can be produced. Using the Si + C → SiC reaction at 1,450℃, 3C and 6H SiC phases, crystalline Si, and Y2O3 were generated based on XRD analysis, without the appearance of graphite. The RBSC prepared from the Y2O3-added carbon preform was densified by increasing the density and decreasing the porosity as the holding time increased at 1,450℃. Dense RBSC, which was reaction sintered at 1,450℃ for 4 h from the 2.0wt.% Y2O3-added carbon preform, had an apparent porosity of 0.11% and a relative density of 96.8%.

• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.169-174
• /
• 2007

TRISO coated fuel particle is one of the most important materials for hydrogen production using HTGR (high temperature gas cooled reactors). It is composed of three isotropic layers: inner pyrolytic carbon (IPyC), silicon carbide (SiC), outer pyrolytic carbon (OPyC) layers. In this study, TRISO coated fuel particle layers were deposited through CVD process in a horizontal hot wall deposition system. Also the computational simulations of input gas velocity, temperature profile and pressure in the reaction chamber were conducted with varying process variable (i.e temperature and input gas ratios). As deposition temperature increased, microstructure, chemical composition and growth behavior changed and deposition rate increased. The simulation showed that the change of reactant states affected growth rate at each position of the susceptor. The experimental results showed a close correlation with the simulation results.

• Applied Chemistry for Engineering
• /
• v.18 no.3
• /
• pp.227-233
• /
• 2007

Carbon/carbon (C/C) composites as unique materials possess exceptional thermal resistance with light weight, high stiffness, and strength even at high temperature. However, one serious obstacle for application of the C/C composites is their poor oxidation resistance in high temperature oxidizing environments. SiC coating has been employed to protect the composites from oxidation. This study explored combustion characteristics of 4-directional (4D) carbon/carbon composites using liquid fuel rocket engine to investigate ablative motion of the materials. C/C composites were made of coal tar pitch as a matrix precursor, and heat-treated at $2300^{\circ}C$. Throughout repeated densification process, the density of the material reached $1.903g/cm^3$. After machining 4D C/C composites, the nozzle surface was coated by a SiC layer by pack-cementation method to improve oxidation resistance. Erosion characteristics of SiC-coated C/C composites were measured as function of the ratio of oxygen to fuel. The morphological change of the composites after combustion test was investigated using SEM and erosion mechanism also was discussed.

• Journal of Environmental Science International
• /
• v.20 no.2
• /
• pp.223-229
• /
• 2011

Toluene desorption of modified activated carbon for microwave irradiation was evaluated. As a virgin GAC reacted from microwave energy, it created an "arcing" between GAC particles in desorption process. The arcing became more and more vigorous and achieved a red flame of GAC. The silica coated GAC(Si/GAC) was developed to prevent arcing phenomenon and temperature control problem. The result shows virgin GAC with 5wt%, 10wt% and 20wt% silica had no arcing and could control temperature very well. However, the adsorption rate of Si/GAC was decreased by coated silica amount due to decreasing surface area of GAC. The 5wt% Si/GAC adsorption rate was quite similar to virgin GAC adsorption rate. After adsorption, the toluene-loaded GAC and Si/GAC was reactivated by 2450MHz MW irradiation with 300W for 5 min. Quantitative desorption of the toluene was achieved at MW irradiation at 300W with desorption efficiencies as high as 98.59% to 84.65%% after four cycles.

• Korean Chemical Engineering Research
• /
• v.56 no.6
• /
• pp.798-803
• /
• 2018

In order to use Si as an anode material for lithium-ion battery, the particle size was controlled to less than $0.5{\mu}m$ and carbon was coated on the surface with the thickness less than 10 nm. The carbon fiber was grown on the Si surface with 50~150 wt%, and the carbon coating was carried out once again. The Si composite material was mixed with dissimilar metals to increase the conductivity, and graphite was mixed to improve cyclic life characteristics. The physical and electrochemical characteristics of composite materials were measured with XRD, SEM, TEM and coin cell. The discharge capacity of Si/PC/CNF/PC was lower than that of Si/PC (Pyrolytic Carbon)/CNF (Carbon Nano Fiber). However, the cyclic life of Si/PC/CNF/PC was higher. Initial discharge capacity of 1512 mA h g-1 at 0.2 C rate and initial efficiency of 78% were shown. It also showed a capacity retention of 94% in 10 cycles.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.3
• /
• pp.120-125
• /
• 2002

Si-wafers for solar cells were cast in a size of $50{\times}46{\times}0.5{\textrm}{mm}^3$ by vacuum casting method. The graphite mold coated by BN powder, which was to prevent the reaction of carbon with the molten silicon, was used. Without coating, the wetting and reaction of Si melt to graphite mold was very severe. In the case of BN coating, SiC was formed in the shape of tiny islands at the surface of Si wafer by the reaction between Si-melt and carbon of the graphite mold on the high temperature. The grain size was about 1 mm. The efficiency of Si solar cell was lower than that of Si solar cell fabricated on commercial single and poly crystalline Si wafer. The reason of low efficiency was discussed.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2005.02a
• /
• pp.134-134
• /
• 2005

• Tribology and Lubricants
• /
• v.38 no.1
• /
• pp.8-14
• /
• 2022

Amorphous carbon (a-C) has excellent wear resistance and, therefore is used as a coating to protect numerous mechanical components to prolong their lifetimes. Among the a-C coatings, diamond-like carbon (DLC) and DLC-containing silicon (Si-DLC) receive extensive attention owing to their enhanced wear resistance and low frictional characteristics. In this study, the friction and wear characteristics of DLC and Si-DLC coatings are analyzed. For comparative analysis, DLC-coated and Si-DLC-coated vanes are utilized with the counterpart of a roller for the friction tests. Since the lubricated mechanical components are generally vulnerable to wear when a lubricant film does not form properly, friction tests are conducted under boundary lubrication conditions to promote wear. A cylinder-on-cylinder type tribometer is used to perform the friction tests with various normal load conditions. After the friction test, a 3D laser confocal microscope is used for quantifying the wear volume to calculate the wear rate of each specimen. Consequently, the DLC-coated specimen shows a lower coefficient of friction (COF) and wear rate than the specimen without the coating, while the Si-DLC coating shows a higher COF than the bare specimen. The results of this study are expected to contribute to improving the efficiency and reliability of compressors.

• Proceedings of the IEEK Conference
• /
• 1999.06a
• /
• pp.954-957
• /
• 1999

We have synthesized carbon nanotubes by thermal chemical vapor deposition of $C_2$H$_2$ on transition metal-coated silicon substrates. Carbon nanotubes are uniformly synthesized on a large area of the plain Si substrates, different from previously reported porous Si substrates. It is observed that surface modification of transition metals deposited on substrates by either etching with dipping in a HF solution and/or NH$_3$ pretreatment is a crucial step for the nanotube growth prior to the reaction of $C_2$H$_2$gas. We will demonstrate that the diameters of carbon naotubes can be controlled by applying the different transition metals.

• Composites Research
• /
• v.33 no.6
• /
• pp.395-400
• /
• 2020

In this paper, we manufactured silsesquiaznae (SSQZ)-coated carbon nanotube (CNT) surface heating elements, which allowed stable heating at high temperatures. The prepared composite sheet was confirmed by FE-SEM that the SSQZ fully coated the surface of CNT sheet. Furthermore, it was also confirmed that the silicon carbonitride (SiCN) ceramic formed by heat treatment of 800℃ have no defects found and maintain intact structure. The CNT/SiCN composite sheet was able to achieve higher thermal stability than raw CNT sheets in both nitrogen and air atmosphere. Finally, the CNT/SiCN composite sheet was possible to heat up at a temperature of over 700℃ in the atmosphere, and the re-heating was successfully operated after cooling.