• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1991년도 가을 학술발표회 논문집
• /
• pp.15-20
• /
• 1991

High-strength concrete were produced with super-plasticizer, silica fume, fly ash and blast furnace slag powder. Topics investigated inclued mix proportion, and effects of unit weight of binder, W/C ratio, additive type on the physical properties of high-strength concrete. As the result, at 20% of silica fume, unit weight of binder 700kg/$\textrm{m}^3$ and W/C=0.24, 28days compressive strength of concrete was over 1,000kgf/$\textrm{cm}^2$. And in cases of blending with silica fume 10% and fly ash or slag 10%, it was able to produce economical high-strength concrete with 28 days strength similar to silica fume 20% only, and higher strength after 90days.

• Nuclear Engineering and Technology
• /
• 제52권3호
• /
• pp.568-574
• /
• 2020

The feasibility of the particle-in-cell (PIC) method is assessed to simulate the non-collective phenomena like non-collective Thomson scattering (TS). The non-collective TS in the laser-plasma interaction, which is related to the single-particle behavior, is simulated through a 2D relativistic PIC code (XOOPIC). For this simulation, a non-collective TS is emitted from a 50-50 DT plasma with electron density and temperature of n_e = 3.00 × 10¹³ cm^-3 and T_e = 1000 eV, typical for the edge plasma at ITER measured by ETS system, respectively. The wavelength, intensity, and FWHM of the laser applied in the ETS system are λ_i,0 = 1.064 × 10^-4 cm, I_i = 2.24 × 10¹⁷ erg=s·㎠, and 12.00 ns, respectively. The electron density and temperature predicted by the PIC simulation, obtained from the TS scattered wave, are n_e,TS = 2.91 × 10¹³ cm^-3 and T_e,TS = 1089 eV, respectively, which are in accordance with the input values of the simulated plasma. The obtained results indicate that the ambiguities rising due to the contradiction between the PIC statistical collective mechanism caused by the super-particle concept and the non-collective nature of TS are resolved. The ability and validity to use PIC method to study the non-collective regimes are verified.

• 수산해양기술연구
• /
• 제24권2호
• /
• pp.94-100
• /
• 1988

평면 굽힘부식피로 시험기를 사용하여 선박용 알루미늄합금재의 부식피로파양에 관한 연구를 한 결과 다음과 같은 결론을 얻었다. 1. 비저항이 증가함에 따라서 초기 부식피로균열발생까지의 반복회수는 지연되고, 그 부식감수성은 감소하는 양상을 나타낸다. 2. 비저항이 감소할수록 Paris rule의 실험상수 m 값은 작아지면서 응력강도 계수값에 비해 부식에 의한 영향이 더욱 민감해 진다. 3. 알루미늄 5086 합금의 부식피로균열은 입계균열파양의 양상을 보이고 있다. 4. 응력강도계수값이 증가함에 따라 부식감수성은 감소되어지고 응력강도계수값이 40kg.mm super(-3/2) 이상일 때 부식감수성은 거의 균일하게 된다.

• 한국수산과학회지
• /
• 제20권6호
• /
• pp.484-488
• /
• 1987

단순만곡형과 슈퍼-V형 모형 전개판의 뒷전 쪽에 각각 flap을 부착하고, 회류수조에서 진행각도와 유속에 따른 항력과 전개력을 측정하여 유체역학적인 전개성능을 분석한 결과는 다음과 같다. 1. flap을 부착한 모형 전개판의 전개력계수 $C_L$은 flap각도 $30^{\circ}$와 $50^{\circ}$일 때 단순만곡형은 최대유효진행각도 $\alpha_{max}=25^{\circ}$ 1.75 정도이었고, 슈퍼-V형은 $\alpha_{max}=20^{\circ}$에서 1.80정도로 flap을 부착하지 않은 경우보다 $20\~30\%$ 정도 $C_L$이 증가하였다. 2. 항력계수 $C_D$는 $\alpha_{max}$ 일 때 flap각도에 관계없이 단순만곡형과 슈퍼-V형 모두가 0.5 정도로 거의 차이가 없었고, flap을 부착하지 않은 경우보다는 약간 $C_D$가 증가하였다. 3. 유체효율 $C_L/C_D$는 flap각도 $30^{\circ}$일 경우가 $50^{\circ}$일 경우보다 약간 높았으나, $\alpha_{max}$일 때는 거의 비슷하였으며, flap를 부착하지 않은 경우보다는 악간 높은 경향을 보였다.

• 생물환경조절학회지
• /
• 제30권1호
• /
• pp.37-45
• /
• 2021

본 연구는 식물공장에서 고흡수성 합성고분자(Super absorbent polymer; SAP)를 수경재배에서 배지로서의 활용가능성을 구명하고자 홍화 및 아마란스 새싹의 생육특성과 페놀함량 및 항산화도를 평가하였다. 대조구는 새싹 재배기(19 × 14 × 9cm, W × D × L)에 거즈를 깔고, 처리구에는 거즈 위에 SAP를 추가하여 비교 분석하였다. 홍화 새싹 종자를 30℃의 증류수에 5시간 동안침지한 뒤, 새싹 재배기에 파종 후 식물생장상에서 재배하였다. 식물생장상의 내부 온도는 25 ± 1℃, 습도는 70 ± 4%로 유지되었고 광조건은 35 ± 6μmol·m-2·s-1(광주기 12h)로 설정하였다. 아마란스 새싹은 새싹 재배기에 파종 후 식물생장상 내부 온도 25 ± 2℃, 습도는 70 ± 5%, 광조건은 188 ± 10μmol·m-2·s-1(광주기 16h)로 설정하였다. SAP의 기본적인 특성으로 물리/화학적 분석과 홍화 및 아마란스의 발아율과 생육특성 및 기능성 물질을 분석하였다. 홍화는 발아율, 생육 및 기능성 물질에서 처리구와 대조구간 차이가 없었으나, 아마란스는 생육 측면에서는 대조구와 차이가 없었으나 발아율, 건물중, 페놀함량 및 항산화도에서 처리구가 각각 1.16배, 1.16배, 1.40배, 1.12배의 높은 결과를 보였다. 결과적으로, 이번 연구를 통해 식물공장에서 SAP을 활용한 새싹재배가 가능할 것으로 판단하였으며 추후 SAP가 식물 생리적으로 작용하는 연구가 필요할 것으로 사료된다.

• 한국재료학회지
• /
• 제20권11호
• /
• pp.606-610
• /
• 2010

Films consisting of a silicon quantum dot superlattice were fabricated by alternating deposition of silicon rich silicon nitride and $Si_3N_4$ layers using an rf magnetron co-sputtering system. In order to use the silicon quantum dot super lattice structure for third generation multi junction solar cell applications, it is important to control the dot size. Moreover, silicon quantum dots have to be in a regularly spaced array in the dielectric matrix material for in order to allow for effective carrier transport. In this study, therefore, we fabricated silicon quantum dot superlattice films under various conditions and investigated crystallization behavior of the silicon quantum dot super lattice structure. Fourier transform infrared spectroscopy (FTIR) spectra showed an increased intensity of the $840\;cm^{-1}$ peak with increasing annealing temperature due to the increase in the number of Si-N bonds. A more conspicuous characteristic of this process is the increased intensity of the $1100\;cm^{-1}$ peak. This peak was attributed to annealing induced reordering in the films that led to increased Si-$N_4$ bonding. X-ray photoelectron spectroscopy (XPS) analysis showed that peak position was shifted to higher bonding energy as silicon 2p bonding energy changed. This transition is related to the formation of silicon quantum dots. Transmission electron microscopy (TEM) and electron spin resonance (ESR) analysis also confirmed the formation of silicon quantum dots. This study revealed that post annealing at $1100^{\circ}C$ for at least one hour is necessary to precipitate the silicon quantum dots in the $SiN_x$ matrix.

• Restorative Dentistry and Endodontics
• /
• 제32권6호
• /
• pp.542-549
• /
• 2007

본 연구의 목적은 네 종류의 복합레진의 연마 후의 표면 거칠기에 있어서의 차이와 염색액에 담근 후 색 안정성에 있어서의 차이를 평가하기 위한 것이다. 필러 크기와 함량이 다른(나노입자형, 혼합형, 미세입자형, 흐름성) 네 종류의 광중합 복합레진(색상 A2)을 사용하였다. 산화 알루미늄 마모 디스크(Super-Snap)로 연마하기 전과 후에 평균 표면 거칠기(Ra)를 표면 조도 측정기 (Surftest Formtracer)로 측정하였다. 2% 메틸렌 블루 용액으로 착색하기 전과 후 표본의 색은 SCI geometry를 이용해 spectrophotometer(CM-3700d)로 측정되었다. 표면 거칠기와 색 변화 값은 one-way ANOVA, Scheffe multiple comparison test와 Student t-test로 분석되었다. 연마 후, 표면 거칠기 값은 복합레진의 종류에 관계없이 감소하였다. 연마 후 표면 거칠기와 착색 후 색 안정성에 있어서, 나노입자형 복합레진이 흐름성 레진을 제외한 다른 복합레진들과 유사하였다.

• Restorative Dentistry and Endodontics
• /
• 제35권5호
• /
• pp.313-320
• /
• 2010

연구목적: 본 연구의 목적은 미세 유체 흐름 측정장치를 이용해서 각 상아질 지각과민 처치제의 적용 과정 중 발생하는 상아 세관액 흐름의 유동을 관찰하고, 상아질 지각과민 처치제 간 적용 후 투과도 감소의 차이를 비교하고자 하는 것이다. 연구 재료 및 방법: CEJ 5 mm 하방에서 절단한 소구치를 미세 흐름 측정장치에 연결하여 20 cm $H_2O$의 정수압을 가하였다. 치경부에 상하 3 mm, 근원심 4 mm, 깊이 2 mm의 V자 형태의 5급 와동을 형성하고 smear layer를 제거하기 위해 15초 동안 산 부식한 후 상아질 지각과민 처치제를 적용하였다. 사용된 상아질 지각과민 처치제는 Seal&Protect (SP), SuperSeal (SS), BisBlock (BB), Gluma desensitizer (GL), Bifluoride 12 (BF) 이다. 상아세관액의 흐름은 지각과민 처치제 도포 전부터 도포 후 5분까지 실시간으로 측정되었다. 결과: 실험에 사용한 모든 상아질 지각과민 처치제는 적용 후의 상아세관액 흐름율이 적용 전에 비해 유의하게 감소하였다(p < 0.05). SP는 GL과 BF에 비해 유의하게 투과도 감소가 나타났다 (p < 0.05). SS와 BB는 BF에 비해 유의하게 투과도 감소를 보였다 (p < 0.05). 결론: 지각과민 처치제의 도포 과정 동안 각 처치제의 특징적인 상아세관액의 유동을 미세 유체 흐름 측정장치를 통해 관찰 할 수 있었다.

• 공업화학
• /
• 제32권6호
• /
• pp.640-646
• /
• 2021

본 연구에서는 열분해유 유래 피치 합성 및 합성 피치로부터 이방성 미세구조를 갖는 코크스를 제조하고 그 특성을 평가하였다. 열분해유는 주로 방향족 고리가 2~3개로 구성된 분자로 이루어져 있어, 400 ℃ 이상의 온도에서 흡열반응인 축합중합으로 피치가 제조되었다. 코크스 반응기는 피치를 유동화 시키는 전처리 반응기, 코킹화 열에너지를 가해주는 preheater 및 코크스의 미세구조를 유도하는 코크스 드럼으로 구성되었으며, preheater의 온도를 400~490 ℃로 조절하여 제조된 피치로부터 코크스를 제조하고 편광현미경, XRD 및 Raman spectroscopy로 특성을 평가하였다. Preheater의 온도가 460 ℃에서 제조된 코크스는 이방성 미세조직이 flow 형태로 나타났으며, 높은 결정성으로 전기전도성이 72.0 S/cm이였다. 그리고 전도성 탄소 재료인 Super-P보다 대략 2.2배 높은 전기전도성을 나타냈다.

• 한국주조공학회지
• /
• 제41권6호
• /
• pp.505-515
• /
• 2021

일방향응고로 제조된 니켈기 초내열합금 CM247LC의 다양한 온도 및 응력조건에서 크리프 특성에 대해 고찰하였다. 열처리 후 일부 공정조직이 남아 있었으며 비교적 균일한 육면체의 γ'이 수지상 내부와 수지상간 영역에서 관찰되었다. 상대적 저온인 750℃의 고응력 크리프 영역에서는 1차 크리프 동안 많은 변형이 발생하였으나 고온으로 갈수록 3차 크리프 구간이 크리프 변형시간의 대부분을 차지함을 알 수 있었다. 저온 고응력에서는 부분 전위가 γ'으로 진입하며 적층결함을 γ'내에 생성시켰으며 초기 크리프 변형속도가 증가하는 부분이 있었으나 850℃ 이상의 온도에서는 γ' 내부에서 적층결함이 관찰되지 않았으며 이는 적층결함에너지의 온도의존성 때문인 것으로 판단된다. 고온이어서 확산속도가 빠른 950℃와 1000℃에서는 γ'의 래프팅이 관찰되었다. 온도가 좀 더 낮은 850℃에서는 변형기구가 응력에 따라 다르게 나타나서 상대적으로 크리프 시간이 긴 저응력에서만 래프팅이 관찰되었다.