• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.661-668
• /
• 2010

Cu(In,Ga)$Se_2$(CIGS) photovoltaic thin films were electrodeposited on Mo/glass substrates with an aqueous solution containing 2 mM $CuCl_2$, 8 mM $InCl_3$, 20 mM $GaCl_3$ and 8mM $H_2SeO_3$ at the electrodeposition potential of -0.6 to -1.0 V(SCE) and pH of 1.8. The best chemical composition of $Cu_{1.05}In_{0.8}Ga_{0.13}Se_2$ was found to be achieved at -0.7 V(SCE). The precursor Cu-In-Ga-Se films were annealed for crystallization to chalcopyrite structure at temperatures of 100-$500^{\circ}C$ under Ar gas atmosphere. The chemical compositions, microstructures, surface morphologies, and crystallographic structures of the annealed films were analyzed by EPMA, FE-SEM, AFM, and XRD, respectively. The precursor Cu-In-Ga-Se grains were grown sparsely on the Mo-back contact and also had very rough surfaces. However, after annealing treatment beginning at $200^{\circ}C$, the empty spaces between grains were removed and the grains showed well developed columnar shapes with smooth surfaces. The precursor Cu-In-Ga-Se films were also annealed at the temperature of $500^{\circ}C$ for 60 min under Se gas atmosphere to suppress the Se volatilization. The Se amount on the CIGS film after selenization annealing increased above the Se amount of the electrodeposited state and the $MoSe_2$ phase occurred, resulting from the diffusion of Se through the CIGS film and interaction with Mo back electrode. However, the selenization-annealed films showed higher crystallinity values than did the films annealed under Ar atmosphere with a chemical composition closer to that of the electrodeposited state.

• Korean Journal of Materials Research
• /
• v.30 no.4
• /
• pp.204-210
• /
• 2020

ZnO thin films are of considerable interest because they can be customized by various coating technologies to have high electrical conductivity and high visible light transmittance. Therefore, ZnO thin films can be applied to various optoelectronic device applications such as transparent conducting thin films, solar cells and displays. In this study, ZnO rod and thin films are fabricated using aqueous chemical bath deposition (CBD), which is a low-cost method at low temperatures, and environmentally friendly. To investigate the structural, electrical and optical properties of ZnO for the presence of citrate ion, which can significantly affect crystal form of ZnO, various amounts of the citrate ion are added to the aqueous CBD ZnO reaction bath. As a result, ZnO crystals show a nanorod form without citrate, but a continuous thin film when citrate is above a certain concentration. In addition, as the citrate concentration increases, the electrical conductivity of the ZnO thin films increases, and is almost unchanged above a certain citrate concentration. Cu(In,Ga)Se₂ (CIGS) solar cell substrates are used to evaluate whether aqueous CBD ZnO thin films can be applicable to real devices. The performance of aqueous CBD ZnO thin films shows performance similar to that of a sputter-deposited ZnO:Al thin film as top transparent electrodes of CIGS solar cells.

• Korean Journal of Materials Research
• /
• v.30 no.10
• /
• pp.566-572
• /
• 2020

In the recent years, thin film solar cells (TFSCs) have emerged as a viable replacement for crystalline silicon solar cells and offer a variety of choices, particularly in terms of synthesis processes and substrates (rigid or flexible, metal or insulator). Among the thin-film absorber materials, SnS has great potential for the manufacturing of low-cost TFSCs due to its suitable optical and electrical properties, non-toxic nature, and earth abundancy. However, the efficiency of SnS-based solar cells is found to be in the range of 1 ~ 4 % and remains far below those of CdTe-, CIGS-, and CZTSSe-based TFSCs. Aside from the improvement in the physical properties of absorber layer, enormous efforts have been focused on the development of suitable buffer layer for SnS-based solar cells. Herein, we investigate the device performance of SnS-based TFSCs by introducing double buffer layers, in which CdS is applied as first buffer layer and ZnMgO films is employed as second buffer layer. The effect of the composition ratio (Mg/(Mg+Zn)) of RF sputtered ZnMgO films on the device performance is studied. The structural and optical properties of ZnMgO films with various Mg/(Mg+Zn) ratios are also analyzed systemically. The fabricated SnS-based TFSCs with device structure of SLG/Mo/SnS/CdS/ZnMgO/AZO/Al exhibit a highest cell efficiency of 1.84 % along with open-circuit voltage of 0.302 V, short-circuit current density of 13.55 mA cm^-2, and fill factor of 0.45 with an optimum Mg/(Mg + Zn) ratio of 0.02.

• Korean Journal of Materials Research
• /
• v.32 no.11
• /
• pp.481-488
• /
• 2022

The Cu₂ZnSn(S_xSe_1-x)₄ (CZTSSe) absorbers are promising thin film solar cells (TFSCs) materials, to replace existing Cu(In,Ga)Se₂ (CIGS) and CdTe photovoltaic technology. However, the best reported efficiency for a CZTSSe device, of 13.6 %, is still too low for commercial use. Recently, partially replacing the Zn²⁺ element with a Cd²⁺element has attracting attention as one of the promising strategies for improving the photovoltaic characteristics of the CZTSSe TFSCs. Cd²⁺ elements are known to improve the grain size of the CZTSSe absorber thin films and improve optoelectronic properties by suppressing potential defects, causing short-circuit current (J_sc) loss. In this study, the structural, compositional, and morphological characteristics of CZTSSe and CZCTSSe thin films were investigated using X-ray diffraction (XRD), X-ray fluorescence spectrometer (XRF), and Field-emission scanning electron microscopy (FE-SEM), respectively. The FE-SEM images revealed that the grain size improved with increasing Cd²⁺ alloying in the CZTSSe thin films. Moreover, there was a slight decrease in small grain distribution as well as voids near the CZTSSe/Mo interface after Cd²⁺ alloying. The solar cells prepared using the most promising CZTSSe absorber thin films with Cd²⁺ alloying (8 min. 30 sec.) exhibited a power conversion efficiency (PCE) of 9.33 %, J_sc of 34.0 mA/cm², and fill factor (FF) of 62.7 %, respectively.