• Journal of Korean Ophthalmic Optics Society
• /
• v.3 no.1
• /
• pp.21-25
• /
• 1998

We investigated the optical properties of lead zirconate($PbZrO_3$, PZ) thin films. The PZ films for the measurement of optical properties were prepared on ITO glass by sol-gel method. By post annealing, with annealing temperature $T=700^{\circ}C$, the pyrochlore phase of as-deposited specimen was transformed into the perovskite phase. The surface of films were plat, transmittance were from 60 to 80% at 480~2000nm, and refractive index were from 2.1 to 1.9 at 480~1000nm.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.5
• /
• pp.729-736
• /
• 1990

Oxide (RTO), nitrided-oxide(NO), and reoxidized-nitrided-oxide(ONO) films were formed by sequential rapid thermal processing. The film composition was investigated by Auger electron spectroscopy(AES). The Si/SiO2 interface and SiO2 surface are nitrided more preferentially than SiO2 bulk. When the NO is reoxidized, [N](atomic concentration of N) in the NO film decreased` especially, the decrease of [N] at the surface is considerable. The weaker the nitridation condition is, the larger the increase of thickness is as the reoxidation proceeds. The elelctrical characteristics of RTO, NO, and ONO films were evaluated by 1-V, high frequency (1 MHz) C-V, and high frequency C-V after constant current stress. The ONO film-which has 8 nm thick initial oxide, nitrided in NH3 at 950\ulcorner for 60 s, reoxidized in O2 at 1100\ulcorner for 60 s-shows good electrical characteristics such as higher electrical breakdown voltage and less variation of flat band voltage under high electric field than RTO, and NO films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.05a
• /
• pp.133-135
• /
• 2006

SBN60 and SBN60/30 thin films were deposited by ion beam sputtering technique. Using the ceramic target of the same composition and Pt(100)/$TiO_2$/$SiO_2$/Si or Pt(111)/Ti/$SiO_2$/Si substrate, crystallization and orientation behavior as well as electric properties of the films were examined, Thickness was controlled to $3000{\AA}$ and the films were heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation and crystallization behavior were observed which showed the dependence on processing condition($O_2$/Ar ratio, substrate temp, annealing temp...).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.6
• /
• pp.487-490
• /
• 2010

This paper describes the elecrtical and optical characteristics of $N_2$ doped porous 3C-SiC films. Polycrystalline 3C-SiC thin films are anodized by $HF+C_2H_5OH$ solution with UV-LED exposure. The growth of in-situ doped 3C-SiC thin films on p-type Si (100) wafers is carried out by using APCVD (atmospheric pressure chemical vapor deposition) with a single-precursor of HMDS (hexamethyildisilane: $Si_2(CH_3)_6)$. 0 ~ 40 sccm $N_2$ was used for doping. After the growth of doped 3C-SiC, porous 3C-SiC is formed by anodization with $7.1\;mA/cm^2$ current density for anodization time of 60 sec. The average pore diameter is about 30 nm, and etched area is increased with $N_2$ doping rate. These results are attributed to the decrease of crystallinity by $N_2$ doping. Mobility is dramatically decreased in porous 3C-SiC. The band gaps of polycrystalline 3C-SiC films and doped porous 3C-SiC are 2.5 eV and 2.7 eV, respectively.

• Journal of Sensor Science and Technology
• /
• v.9 no.6
• /
• pp.455-460
• /
• 2000

Zinc oxide(ZnO) thin films were cathodically deposited on ITO glass from an aqueous zinc nitrate electrolyte. Three main fabrication parameters were taken into account : deposition potential, solution concentration and growth temperature. Different layers of ZnO thin films grown by varying the three parameters were studied by X-ray diffraction, scanning electron microscope and optical absorption spectroscopy. The prepared ZnO thin films were shown as a hexagonal wurtzite structure on the X-ray diffraction patterns and the good quality of ZnO thin films were obtained by potentiostatic cathodic deposition at -0.7V vs. Ag/AgCl reference electrode onto ITO glass from aqueous 0.1 mol/liter zinc nitrate electrolyte at $60^{\circ}C$.

• Journal of Korean Ophthalmic Optics Society
• /
• v.13 no.3
• /
• pp.73-77
• /
• 2008

Purpose: This research is that prepare amorphous or crystalline ZnO thin films with pure strong UV emission on soda-lime-silica glass (SLSG) substrates by low-temperature annealing. Methods: Growth characteristic and optical properties of the amorphous or nano-crystalline ZnO thin films prepared on soda - lime - silica glass substrates by chemical solution deposition at 100, 150, 200, 250 and $300^{\circ}C$ were investigated using X-ray diffraction analysis, ultraviolet - visible - near infrared spectrophotometer, and photoluminescence. Results: The films exhibited an amorphous pattern even when finally annealed at $100^{\circ}C{\sim}200^{\circ}C$ for 60 min, while crystalline ZnO was obtained by prefiring at 250 and $300^{\circ}C$. The photoluminescence spectrum of amorphous ZnO films shows a strong NBE emission, while the visible emission is nearly quenched. Conclusions: These results indicate it should be possible to cheaply and easily fabricate ZnO-based optoelectronic devices at low temperature, below $200^{\circ}C$, in the future.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.8
• /
• pp.1063-1067
• /
• 1995

The superconducting properties of YBa$_{2}$Cu$_{3}$$O_{7-x}$(YBaCuO) thin films prepared by laser ablation have been investigated. The x-ray diffraction patterns and surface morphology of the films were substantially different from one another. The compositional ratios of YBaCuO films were controlled by the conditions of the target-substrate distance. The YBaCuO films manufactured on MgO(100) substrate were indicated T$_{c}$(zero)=91.2 K, T$_{c}$(onset)=93 K, and J$_{c}$=3.5*10$^{5}$ A/cm$^{2}$(at 77.3K). The optimum conditions were found to be a substrate temperature of 710 .deg. C, a energy density of 2 J/cm$^{2}$, and a target-substrate distance of 60 mm in an oxygen partial pressure of 200 mTorr.0 mTorr.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.3
• /
• pp.129-133
• /
• 2006

Ferroelectric PZT heterolayered thick films were fabricated by the alkoxide-based sol-gel method. PZT(20/80) and PZT(80/20) paste were made and alternately screen-printed on the alumina substrates. The coating and drying procedure was repeated 4 times to form the heterolayered thick films. The thickness of the PZT heterolayered thick films was approximately $60{\mu}m$. All PZT thick films showed the typical XRD patterns of a polycrystalline rhombohedral structure. And in the PZT thick films sintered at $1100^{\circ}C$, the pyrochlore phase was observed due to the evaporation of PbO. The relative dielectric constant and the dielectric loss of the PZT thick films sintered at $1050^{\circ}C$ were 445.2 and 1.90 % at 1 kHz, respectively. The remanent polarization and coercive field of the PZT thick films sintered at $1050^{\circ}C$ were $14.15{\mu}C/cm^2$ and 19.13 kV/cm, respectively.

• Polymer(Korea)
• /
• v.35 no.2
• /
• pp.130-135
• /
• 2011

Along with the fast development of electronics, the demands of portable electronics and wireless sensors are growing rapidly. The need for self-powering materials capable of powering the electrical devices attached to them is increasing, The piezoelectric effect of polyvinylidene fluoride (PVDF) can be used for this purpose. PVDF has a special crystal structure consisting of a ${\beta}$-phase that can produce piezoelectricity. In this paper, multilayer PVDF films were fabricated to increase the ${\beta}$-phase content. A solution of 10% concentration N;N-dimethylacetamide (DMAc) in PVDF (PVDF/DMAc) was used to fabricate the films via spin coating technique with the following optimum process parameters: a spin rate of 850 rpm, spin time of 60 s, drying temperature of $60^{\circ}C$, and drying time of 30 min, Compared with single-layer PVDF films, the multilayer films exhibited higher ${\beta}$-phase content. The ${\beta}$-phase content of the films increased gradually with increasing number of layers until 4, Maximum ratio of ${\beta}$-phase content was 7.72.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.173-176
• /
• 1997

The III-V nitride semiconductor InN thin films which have the direct bandgap in visible light wavelength region have been deposited on Si(100) substrates and AIN/Si(100) substrates by rf reactive sputtering. InN thin films have been investigated on the structural, and electrical properties according to the sputtering parameters such as total pressure, rf power, and substrate temperature. It is found that optimal conditions required for fabricating InN thin films with high crystal Quality, low carrier concentration, high Hall mobility are total pressure 5mTorr, rf power 60W, substrate temperature 6$0^{\circ}C$ . InN thin films deposited on the AIN(60min.)/Si(100) substrates arid AIN(120min.)/Si(100) substrates showed remarkably high crystal quality and electrical properties. It is known that AIN buffer layer is to decrease free energy at interface between InN film and Si substrate, and then promoting lateral growth of InN films.