• 열처리공학회지
• /
• 제13권4호
• /
• pp.217-223
• /
• 2000

The boronizing effects of STD 61 steel have been studied on the micro structure and hardness. The STD 61 Steel was soaked in molten salt, consisted of KCl, $BaCl_2$, NaF, $B_2O_3$, FeB, and Ce, at various temperatures and times. The boronizing conditions for the peak hardness were the temperature range of $900^{\circ}C$ to $950^{\circ}C$ for 5 hr and that of $1000^{\circ}C$ for 3 hr, respectively. Four boride layers such as FeB, $Fe_2B$, ${\alpha}$ and matrix layer surface were observed from the microscopic surface examination. The thickness of boride layer was increased by increasing the boronizing time and the temperature. The structure of boride layer was tooth shape.

• 한국표면공학회지
• /
• 제8권3호
• /
• pp.5-11
• /
• 1975

The boronizing method using ferroborn and NaBF4 powder mixture was studied for surface hardening of medium carbon steel. This boride layer was compared with a boride layer that was formed in ferroboron and KBF4 powder mixture. The frequency factor and activation energy were discussed in this paper. The main results obtained can be summerized as follow. 1) The optimum range of NaBF4 content is 10 to 15% of weight to obtain a thick and dense boride layer. 2) The depth of the boride layer was approximately expressed by the following equation : {{{{d=100 exp (-18,000/RT) SQRT { t} }} 3) The oxidating resistance of boronized steel proved to be good at 800$^{\circ}C$ but almost unacceptable near at 900 $^{\circ}C$. 4) The NaBF4 effect was the same as that reported for KBF4.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 1999년도 춘계학술발표회 초록집
• /
• pp.58-59
• /
• 1999

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 1998년도 추계학술발표회 초록집
• /
• pp.60-61
• /
• 1998

• Corrosion Science and Technology
• /
• 제3권1호
• /
• pp.6-13
• /
• 2004

The effect of inhibitors on the electrochemical behavior and the stress corrosion cracking resistance of Alloy 600(UNS N06600) was evaluated in 10% sodium hydroxide solution at $315^{\circ}C$. The specimens of a C-ring type for stress corrosion cracking test were polarized at 150 mV above the corrosion potential for 120 hours with and without inhibitors such as titanium oxide, titanium boride and cerium boride. The chemical compositions of the films formed on the crack tip in the C-ring specimens were analyzed using a scanning Auger electron spectroscopy. The cerium boride, the most effective, was observed to decrease the crack propagation rate more than a factor of three compared with that obtained in no inhibitor solution. It was found that the changes of the active-passive transition potentials and the film compositions were related to the resistance to stress corrosion cracking in high temperature caustic solution.

• 한국분말재료학회지
• /
• 제18권6호
• /
• pp.496-501
• /
• 2011

In this study, the effect of milling time on the microstructure and phase transformation behaviors of Ni-12 wt.%B powders was investigated using vibratory ball milling process. X-ray diffraction patterns showed that the phase transformation of mixed Ni-B elemental powder occurred after 50 hours of milling, with a formation of nickel boride phases. Through the study of microstructures in mechanical alloying process, it was considered that ball milling strongly accelerates solid-state diffusions of the Ni and B atoms during mechanical alloying process. The results of X-ray photoelectron spectroscopy showed that most of B atoms in the powder were linked to Ni with a formation of nickel boride phases after 200 hours of milling. It was finally concluded that mechanical alloying using ball milling process is feasible to synthesize fine and uniform nickel boride powders.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.111-112
• /
• 2006

Injection molding of corrosive super engineering plastics and engineering plastics with various fillers is conducted under severe conditions and causes corrosion and wear problems. We have developed $Mo_2NiB_2$ boride base cermets, which have excellent corrosion-and wear-resistances, and tried to apply them into plastic molding machine parts. In this paper, the effects of V substitution for Cr on the mechanical properties, corrosion resistance and microstructure of Ni-5.0B-51.0Mo-(17.5-X)Cr-XV (mass%) model cermets were investigated. Both transverse rupture strength (TRS) and hardness increased monotonically with increasing V content and reached 2.94GPa and $87.2R_A$ at 10.0%V, respectively. The improvements of TRS and hardness were attributed to microstructural refinement.

• 한국결정성장학회지
• /
• 제15권2호
• /
• pp.75-78
• /
• 2005

본 연구에서는 고온 융점과 높은 Seebeck 계수로 인해 고온 열전 재료로서 매우 우수한 silicon boride ($SiB_6$)의 고밀도 소결체를 방전 플라즈마 소결법(spark plasma sintering, SPS)을 도입하여 제조하였으며, 소결된 시편의 미세구조 및 열전 특성을 평가하였다. $1500^{\circ}C$의 비교적 저온에서 이론 밀도의 약 99%의 소결밀도로 SPS법을 통해 효과적으로 $SiB_6$를 치밀화 할 수 있었으며 이들 시편들의 열전특성 평가로부터, hot-press법으로 제조된 시편과 비교하여 매우 향상된 Seebeck 계수를 얻을 수 있었으며 상대적으로 높은 출력인자 값을 나타냈다.

• 한국표면공학회지
• /
• 제35권6호
• /
• pp.371-376
• /
• 2002

Steam turbine components of power generators are subjected to severe damages from the particle erosion by iron oxides (mainly $Fe_3$$O_4$) which are formed due to the oxidation of boiler tubes, causing high costs for maintaining and repairing. One of the practical ways to minimize the particle erosion is to apply the erosion resistant boride coating on the turbine components which is composed of boride apply. But the evaluation of its performance has not been carried out. A particle erosion tester, which can offer the erosion condition of steam turbine components, was developed to evaluate the performances of the boronized Cr/Mo alloy. The result showed that the boronized Cr/Mo alloy showed superior resistance to particle erosion to the bare Cr/Mo alloy in all test conditions.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.765-766
• /
• 2006

[ $Mo_2FeB_2$ ] boride base cermets produced by a novel sintering technique, called reaction boronizing sintering through a liquid phase, have excellent mechanical properties and wear and corrosion-resistances. Hence, the cermets are applied to the injection molding die-casting machine parts and so on. We investigated that the effect of deoxidization and sintering temperature on mechanical properties and deformation of the MIM processed cermets. As a result, deoxidization temperature of 1323K and sintering temperature of 1518K were suitable. The MIM products of the cermets showed allowable dimensional accuracy and the same mechanical properties as the press-sintered ones.