Effect of Additives on the Stress Corrosion Cracking Behavior of Alloy 600 in High Temperature Caustic Solutions

  • Published : 2004.02.01

Abstract

The effect of inhibitors on the electrochemical behavior and the stress corrosion cracking resistance of Alloy 600(UNS N06600) was evaluated in 10% sodium hydroxide solution at $315^{\circ}C$. The specimens of a C-ring type for stress corrosion cracking test were polarized at 150 mV above the corrosion potential for 120 hours with and without inhibitors such as titanium oxide, titanium boride and cerium boride. The chemical compositions of the films formed on the crack tip in the C-ring specimens were analyzed using a scanning Auger electron spectroscopy. The cerium boride, the most effective, was observed to decrease the crack propagation rate more than a factor of three compared with that obtained in no inhibitor solution. It was found that the changes of the active-passive transition potentials and the film compositions were related to the resistance to stress corrosion cracking in high temperature caustic solution.

Keywords

References

  1. J. Benson, Steam Generator Progress Report, Rev. 14, EPRI Report TE-I 06365-R 14 (Palo Alto, CA, EPRI, 1999)
  2. D.II. Hur, H.S. Chung, U.C. Kim. J Nuclear Materials, 224. 179 (1995) https://doi.org/10.1016/0022-3115(95)00011-9
  3. D. Schneidmiller and D. Stiteler, Steam Generator Chemical Cleaning Process Development, EPRI Report NP-3009 (Palo Alto. CA. EPRI, 1983)
  4. Molar ratio Control Guidelines Committee, PWR Molar Ratio Control Application Guidelines, EPRI Report TR-104811-VI (Palo Alto. CA. EPRI. 1995)
  5. M..J. Partridge. W.S. Zemitis, and J.A. Gorman, Correlation of Secondary-Side IGA/SCC Degradation of Recirculating Steam Generator Tubing With the On-Line Addition of Boric Acid, EPRI Report TR-101010 (Palo Alto, CA, EPRI. 1992)
  6. J.B. Lumsden. S.L. Jeanjaquent, J.P.N. Paine. and A. Mcllree, 'Mechanism and Effectiveness of Inhibitors for SCC in a Caustic Environment'. Proc. 7th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, (Houston, TX. NACE. 1995). p.137
  7. B.P. Miglin, and J.P. Paine, 'Slow Strain Rate Testing to Evaluate Inhibitors for Stress Corrosion Cracking of Alloy 600', Proc. 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power SystemsWater Reactors, (Warrendale, PA. TMS. 1993). p.303
  8. J. Daret, lP.N. Paine. M..J. Partridge. 'Model Boiler Testing to Evaluate Inhibitors for Caustic Induced Stress Corrosion Cracking of Alloy 600 Tubes', Proc. 7th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, (Houston, TX, NACE, 1995), p.177
  9. J. Darer, T. Cassagne, and Y. Lefevre, 'Secondary Degradation of Steam Generator Tubing: Which Inhibitors for Which Causes? A Review of Model Boiler Test Results', Proc. 8th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, (LaGrange Park, IL, ANS, 1997), p.100
  10. J.R. Cels, Corrosion, 34, 198 (1978)
  11. N. Pessall, G.P Airey, and BP. Lingenfelter, Corrosion,35, 100 (1979)
  12. R. Bandy, R. Roberge, and D. van Rooyen, Corrosion,41, 142 (1985)
  13. S.A. Shei and W.J. Yang, 'Stress Corrosion Crack Tip Microstructure in Nickel-Base Alloys', CORROSION/94, Paper No.154 (1994)
  14. P.L. Daniel, and S.L. Harper, Use of Pourbaix Diagrams to Infer Local Pitting Conditions, EPRI Report NP-4831(Palo Alto, CA, EPRI, 1986)
  15. T. Sakai, K. Aoki, T. Shigemitsu, and Y. Kishi, Corrosion, 48, 745 (1992)
  16. R.S. Pathania, J.P.N. Panie, and C.E. Shoemaker, 'Inhibition of Intergranular Attack and Stress Corrosion Cracking With Boric Acid', Proc. Third Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Warrendale, PA, The Metallurgical Socierty, 1987), p.511
  17. T.N.Rhys-Jones, H,J. Grabke, and H. Kudielka, Corrosion Science, 27, 49 (1987)
  18. K.L. Wang, Q.B. Zhang, M.L. Sun, X.G. Wei, and Y.M. Zhu, Corrosion Science, 43, 255 (2001)
  19. P.E. MacDonald, V.N. Shah, L.W. Ward, P.G. Ellison, Steam Generator Tube Failures, NUREG/CR-6365 (U.S. Nuclear Regulatory Commission, 1996), p.105