• Advances in materials Research
• /
• v.3 no.4
• /
• pp.227-232
• /
• 2014

$Ce^{4+}$, $Eu^{3+}$, $Tb^{3+}$ co-doped $Ca_3Si_3O_8F_2$ phosphor was synthesized via solid state reaction method using $CaF_2$, $CaCO_3$ and $SiO_2$ as raw materials for the host and $Eu_2O_3$, $CeO_2$, and $Tb_4O_7$ as activators. The luminescent properties of the phosphor was analysed by spectrofluorophotometer at room temperature. The effect of excitation wavelengths on the luminescent properties of the phosphor i.e. under near-ultraviolet (nUV) and visible excitations was investigated. The emission peaks of $Ce^{4+}$, $Eu^{3+}$, $Tb^{3+}$ co-doped $Ca_3Si_3O_8F_2$ phosphor lays at 480(blue band), 550(green band) and 611nm (red band) under 380nm excitation wavelength, attributed to the $Ce^{4+}$ ion, $Tb^{3+}$ ion and $Eu^{3+}$ ions respectively. The results reveal that the phosphor emits white light upon nUV (380nm) / visible (465nm) illumination, and a red light upon 395nm / 535nm illumination. RE ions doped $Ca_3Si_3O_8F_2$ is a promising white light phosphor for LEDs. The emission colours can be seen using Commission international de l'eclairage (CIE) co-ordinates. A single host phosphor emitting different colours under different excitations indicates that it is a potential phosphor having applications in many fields.

• Journal of the Korean Applied Science and Technology
• /
• v.29 no.3
• /
• pp.459-465
• /
• 2012

We had synthesized a green dopant material based on the binaphthyl group, 7,7'-(2,2'dimethoxy-1,1'-binaphthyl-3,3'-diyl) bis(4-(thiophen -2-yl) benzo[e][1,2,5] thiadiazole (TBT). We also fabricated the white organic light emitting diode (OLED) with a phosphorescent blue emitter : iridium(III)bis[(4,6-di-fluoropheny)-pyridinato -N,C2]picolinate (FIrpic) doped in N,N'-dicarbazolyl-3,5-benzene (mCP) of hole transport type host material and both TBT and bis(2-phenylquinolinato)- acetylacetonate iridium(III) (Ir(pq)2acac) doped in 1,3,5-tris(N-phenylbenzimidazole -2-yl)benzene (TPBi) of electron transport type host material. As a result, the property of white OLED using TBT, which demonstrated a maximum luminous efficiency and external quantum efficiency of 5.94 cd/A and 3.23 %, respectively. It also showed the pure white emission with Commission Internationale de I'Eclairage (CIE) coordinates of (0.34, 0.36) at 1000 nit.

• The Journal of the Korea Contents Association
• /
• v.2 no.3
• /
• pp.146-151
• /
• 2002

The $Ca_{1-x}$Sr$_{x}$S:CuCl TFEL devices were fabricated by electron-beam deposition system and luminescent characteristics of the TFEL devices were studied. The SrS and CaS powders were mixed to form $Ca_{1-x}$Sr$_{x}$S host materials and 0.2 at% of CuCl was added as the activator. The luminance(lao) and peak emission wavelength of CaS:CuCl TFEL devices were 9.5 cd/m$^2$ and 492 nm, respectively. The luminance(L$_{30}$) and peak emission wavelength of SrS:CuCl TFEL devices were 633 cd/m$^2$ and 500 nm, respectively. It seems that the addition of CaS into the SrS host material generates blue shift of the EL emission characteristics but reduces the luminance and the luminous efficiency of the $Ca_{1-x}$Sr$_{x}$S:CuCl TFEL devices drastically.

• Journal of Radiation Protection and Research
• /
• v.45 no.4
• /
• pp.163-170
• /
• 2020

Background: Gut microflora contributes to the nutritional metabolism of the host and to strengthen its immune system. However, if the intestinal barrier function of the living body is destroyed by radiation exposure, the intestinal bacteria harm the health of the host and cause sepsis. Therefore, this study aims to trace short-term radiation-induced changes in the mouse gut microflora-dominant bacterial genus, and analyze the degree of intestinal epithelial damage. Materials and Methods: Mice were irradiated with 0, 2, 4, 8 Gy X-rays, and the gut microflora and intestinal epithelial changes were analyzed 72 hours later. Five representative genera of Actinobacteria, Firmicutes, and Bacteroidetes were analyzed in fecal samples, and the intestine was pathologically analyzed by Hematoxylin-Eosin and Alcian blue staining. In addition, DNA fragmentation was evaluated by the TdT-mediated dUTP nick-end labeling (TUNEL) assay. Results and Discussion: The small intestine showed shortened villi and reduced number of goblet cells upon 8 Gy irradiation. The large intestine epithelium showed no significant morphological changes, but the number of goblet cells were reduced in a radiation dose-dependent manner. Moreover, the small intestinal epithelium of 8 Gy-irradiated mice showed significant DNA damaged, whereas the large intestine epithelium was damaged in a dose-dependent manner. Overall, the large intestine epithelium showed less recovery potential upon radiation exposure than the small intestinal epithelium. Analysis of the intestinal flora revealed fluctuations in lactic acid bacteria excretion after irradiation regardless of the morphological changes of intestinal epithelium. Altogether, it became clear that radiation exposure could cause an immediate change of their excretion. Conclusion: This study revealed changes in the intestinal epithelium and intestinal microbiota that may pave the way for the identification of novel biomarkers of radiation-induced gastrointestinal disorders and develop new therapeutic strategies to treat patients with acute radiation syndrome.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.2
• /
• pp.90-94
• /
• 2009

Mong Hsu rubies from Myanmar were heat treated in oxidizing(oxygen) atmosphere at $1650^{\circ}C$ for 1 hour. The investigations of the micro-structural defects in the samples before and after heat treatment have been carried out by the variety of analysis techniques of FTIR, UV-VIS-NIR and SEM-EDS. It was found that after heat treatment the dark blue cores region were disappeared and turned to orange red color with the presence of the dense cloudy brownish colored tiny particles in and near former blue zoning. As-received ruby samples only revealed the presence of FTIR absorption peaks of diaspore, boehmite and O-H stretching, at 1986, 2115 and $3078/3319\;cm^{-1}$ respectively. The UV-VIS-NIR absorption of as-received and heat treated ruby samples similarly showed peaks at 405, 554 and 693 nm associated with $Cr^{3+}$, but for the same samples, the absorption peak of heat-treated ruby samples at 693 nm was somewhat stronger than that of the untreated ruby samples. Especially the presence of $Cr^{3+}$ peaks at 659 and 675 nm was found obviously in as-received ruby samples only. The SEM-EDS investigation disclosed the micro-porous defect structures commonly related to the core regions of the untreated ruby samples, which after heat treatment in an oxidizing environment those defect features have been dissolved into the host phase resulting in the lightening or disappearance of the dark coloration of ruby core.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.22 no.2
• /
• pp.179-198
• /
• 2004

Organic electroluminescent devices are light-emitting diodes in which the active materials consist entirely of organic materials. Recently, many fluorescent organic materials have been reported and the study on synthesis and application of new organic light-emitting materials has been demanded. This paper reports the optical and electrical characteristics of OLEDs using novel polymers containing biphenyl structure. First, Optical properties of novel light-emitting biphenyl derivatives doped with poly(9-vinyl carbazole)(PVK) and emitted blue, bluish green color, which is attributed to the overlap area between PL spectrum of host(PVK) and absorption spectra of guests(polymer). This is correspondent with F$\"{o}$rster energy transfer process in the blends. And, OLED devices were fabricated using poly (3,4-ethylenedioxy thiophene) (PEDOT) as a hole injection material and tris-(8-hydroxyquinoline) aluminum ($Alq_3$) as an electron transporting material. EL devices fabricated as ITO/PEDOT/PVK doped with biphenyl derivatives/$Alq_3$/Li:Al and I-V-L chatacteristics and emitting efficiency of EL devices were examined. Finally, the drift mobility of PVK doped with biphenyl derivatives and $Alq_3$ were measured by TOF technique varying applied electric field. EL efficiency was increased as the ratio of hole mobility of PVK doped with biphenyl derivatives and electron mobility of $Alq_3$ was close to one.

• Journal of the Korean Ceramic Society
• /
• v.43 no.3 s.286
• /
• pp.169-172
• /
• 2006

We have synthesized a $Eu^{2+}-activated\;{(Sr,Ba)}_2SiO_4$ yellow phosphor and investigated the development of blue LEDs by combining the phosphor with a InGaN blue LED chip (${\lambda}_{em}$=405 nm). The InGaN-based ${(Sr,Ba)}_2SiO_{4}:Eu$ LED lamp shows two bands at 405 nm and 550 nm. The 405 nm emission band is due to a radiative recombination from a InGaN active layer. This 405 nm emission was used as an optical transition of the ${(Sr,Ba)}_2SiO_{4}:Eu$ phosphor. The 550 nm emission band is ascribed to a radiative recombination of $Eu^{2+}$ impurity ions in the ${(Sr,Ba)}_2SiO_4$ host matrix. In the preparation of UV Yellow LED Lamp with ${(Sr,Ba)}_2SiO_{4}:Eu$ yellow phosphor, the highest luminescence efficiency was obtained at the epoxy-to-yellow phosphor ratio of 1:0.45. At this ratio, the CIE chromaticity was x=0.4097 and y=0.5488.

• Korean Journal of Veterinary Research
• /
• v.33 no.2
• /
• pp.277-283
• /
• 1993

In the present study, observations were made on the life-history of Lymnaea viridis under laboratory conditions, involving incubation period of the eggs and their hatching rate, shell length of the newly hatched snails, sexual maturity, size of the snails when the snail produced the first egg-mass, the number of eggs in each egg-mass, egg-laying, ovipostion, growth rate of the snails, and longevity of the snail. At temperatures between $19.8^{\circ}C$ to $22.5^{\circ}C$, incubation period of the eggs occupied 10~12 days, and after beginning of hatching, all young snails emerged completely from the egg-mass within 5 days. The hatching rate was 88%. The average shell length of the newly hatched snails was about 0.064cm. The rate of growth was extraordinarily rapid under good laboratory conditions. When two snails were reared in one culture vessel($20{\times}15{\times}5cm$) with blue-green algae at about $22^{\circ}C$, snail growth was optimal, taking 37 days to reach 1.2cm in shell length. Sexual maturity reached in about 19 days. The size of the snails at sexual maturity was $0.78{\pm}0.05cm$ in length and $0.47{\pm}0.04cm$ in width. The first egg-masses produced were $0.59{\pm}0.22cm$ in length and $0.34{\pm}0.08cm$ in width, and contained 7~38 eggs. The eggs are usually laid in water. The egg-laying was affected by food and temperature. Snails fed with blue-green algae at about $22^{\circ}C$ produced larger egg-masses than the snails fed with fish food at about $26^{\circ}C$. Under conditions of continuous activity and growth, the maximum expectation of life appears to be 109~350(mean 230) days. And the shell length of snails at death were 1.39~1.64cm.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.39 no.8
• /
• pp.17-23
• /
• 2002

The SrS:CuCl TFEL devices were fabricated by electron-beam deposition and the luminescent characteristics of the fabricated SrS:CuCl TFEL devices were studied. The SrS powder was used as the host materials and 0.05 ~ 0.6 at% of CuCl powder was added as the luminescent center. The deposition conditions of substrate temperature, electron beam current, and deposition rate were 500 $^{\circ}C$ , 20 ~ 40 mA, and 5 ~ 10 /sec, respectively The total thickness of the phosphor layer deposited was 6000 . The blue emission at low CuCl concentrations was observed from the luminescent centers of monomer, dimer, trimer, and tetramer, The bright greenish blue emission at high CuCl concentrations was observed from the dimer and trimer luminescent centers. The maxium luminance was observed from the SrS:CuCl TFEL devices doped with 0.2 at% of CuCl concentration and the threshold voltage, luminance(L$_{40}$ ), efficiency(η$_{20}$) and CIE coordinate obtained were 55 V, 728 cd/$m^2$, 0.49 lm/w, and (0.21, 0.33), respectively..

• Journal of the Institute of Electronics Engineers of Korea TE
• /
• v.39 no.2
• /
• pp.11-16
• /
• 2002

In this paper, single-layer white organic light emitting device was fabricated on ITO glass substrate using PVK as host, Bu-PBD as electron transport layer, Nile Red, Coumarin 6, TPB as red, green, blue color fluorescent dyes. The red, green, blue organic light emitting devices were fabricated respectively. After the characteristic analysis of each color device, the white organic light emitting device was fabricated with optimized condition of each color device by spin coating method. we obtained white emission CIE coordination of (0.32, 0.34) and luminescence of 785cd/$m^2$ at driving voltage of 20V with condition of PVK(70wt%), Bu-PBD(30wt%), Nile Red(0.015mol%), Coumarin 6(0.04mol%), TPB(3mol%).