• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.18 no.3
• /
• pp.638-642
• /
• 2014

In this study, we investigate on the crystal microstructure and magneto-resistance (MR) change of Bismuth(Bi) thin films for annealing process, in order to apply Bi thin films to the spin electronic devices. As-prepared Bi thin films show the randomly oriented find grains whose size was measured to about 100 nm and the very low MR (4.7 % at room temperature) while careful annealing results in not only grain growth up to ${\sim}2{\mu}m$ but also drastic MR improvement (404 % at room temperature). The drastic change in the MR after applying the annealing process is attributed to the grain growth decreasing grain boundary scattering of electron. Therefore, in this study, we confirm the annealing effect for the grain boundary formation and MR improvement of Bi thin films, and demonstrate the feasibility of spin electronic devices.

• Journal of Powder Materials
• /
• v.30 no.4
• /
• pp.318-323
• /
• 2023

The thermoelectric effect, which converts waste heat into electricity, holds promise as a renewable energy technology. Recently, bismuth telluride (Bi2Te3)-based alloys are being recognized as important materials for practical applications in the temperature range from room temperature to 500 K. However, conventional sintering processes impose limitations on shape-changeable and tailorable Bi₂Te₃ materials. To overcome these issues, three-dimensional (3D) printing (additive manufacturing) is being adopted. Although some research results have been reported, relatively few studies on 3D printed thermoelectric materials are being carried out. In this study, we utilize extrusion 3D printing to manufacture n-type Bi_1.7Sb_0.3Te₃ (N-BST). The ink is produced without using organic binders, which could negatively influence its thermoelectric properties. Furthermore, we introduce graphene oxide (GO) at the crystal interface to enhance the electrical properties. The formed N-BST composites exhibit significantly improved electrical conductivity and a higher Seebeck coefficient as the GO content increases. Therefore, we propose that the combination of the extrusion 3D printing process (Direct Ink Writing, DIW) and the incorporation of GO into N-BST offers a convenient and effective approach for achieving higher thermoelectric efficiency.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.5
• /
• pp.215-222
• /
• 2006

The passivity behavior of copper anode containing impurities in copper sulfate solution for electrorefining process was studied at several different levels of impurities such as As, Sb, Bi and Pb. The passivity behavior was investigated by electrochemical techniques (galvanostatic, potentiodynamic and cyclic voltammetry tests) and surface analysis (optical microscopy, electron probe microanalysis, scanning electron microscopy). The results were that arsenic, antimony inhibited passivation and bismuth accelerated it and lead containing anode showed different passivity behavior from above anodes. The improved passivity characteristics could be explained by decrease in oxygen content in passivity film which resulted from a reaction among the impurities, oxygen and copper in the anode. The SEM image revealed that arsenic or antimony containing anode exhibited a porous passivity film and bismuth containing anode showed the compact passivity film and lead containing anode had loose passivity film on anode.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.18 no.4
• /
• pp.421-437
• /
• 2020

This study provides an assessment on a proposed method for separation of cesium, strontium, and barium using electrochemical reduction at a liquid bismuth cathode in LiCl-KCl eutectic salt, investigated via cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and scanning electron microscopy with energy dispersive X-ray spectrometry (SEM-EDS). CV studies were performed at temperatures of 723-823 K and concentrations of the target species up to 4.0wt%. Redox reactions occurring during potential sweeps were observed. Concentration of BaCl2 in the salt did not seem to influence the diffusivity in the studied concentration range up to 4.0wt%. The presence of strontium in the system affected the redox reaction of lithium; however, there were no distinguishable redox peaks that could be measured. Impedance spectra obtained from EIS methods were used to calculate the exchange current densities of the electroactive active redox couple at the bismuth cathode. Results show the rate-controlling step in deposition to be the mass transport of Cs+ ions from the bulk salt to the cathode surface layer. Results from SEM-EDS suggest that Cs-Bi and Sr-Bi intermetallics from LiCl-KCl salt are not thermodynamically favorable.

• Journal of Powder Materials
• /
• v.17 no.2
• /
• pp.107-112
• /
• 2010

Carbon-nanotube-embedded bismuth telluride (CNT/$Bi_2Te_3$) matrix composites were fabricated by a powder metallurgy process. Composite powders, whereby 5 vol.% of functionalized CNTs were homogeneously mixed with $Bi_2Te_3$ alloying powders, were successfully synthesized by using high-energy ball milling process. The powders were consolidated into bulk CNT/$Bi_2Te_3$ composites by spark plasma sintering process at $350^{\circ}C$ for 10 min. The fabricated composites showed the uniform mixing and homogeneous dispersion of CNTs in the $Bi_2Te_3$ matrix. Seebeck coefficient of CNT/$Bi_2Te_3$ composites reveals that the composite has n-type semiconducting characteristics with values ranging $-55\;{\mu}V/K$ to $-95\;{\mu}V/K$ with increasing temperature. Furthermore, the significant reduction in thermal conductivity has been clearly observed in the composites. The results showed that CNT addition to thermoelectric materials could be useful method to obtain high thermoelectric performance.

• Journal of Magnetics
• /
• v.12 no.3
• /
• pp.129-132
• /
• 2007

Bismuth-substituted yttrium iron garnet (Bi:YIG, $Bi_{0.5}Y_{2.5}Fe_5O_{12}$) films were deposited with aerosol deposition method and their magnetic and optical properties were investigated as a function of annealing temperature. Since the ceramic films deposited with aerosol deposition method have not a perfect crystal structure due to non-uniform internal stress occurred by mechanical collision during their deposition, the post annealing could be a key process to release its internal stress and to improve its micro structure for optimizing the magnetic and magneto-optic properties of films. The crystallinity of Bi: YIG film was improved with increase of annealing temperature, and the saturation magnetization increased up to 87 emu/cc at $800^{\circ}C$. The Faraday rotation increased up to $1.4deg/{\mu}m$ by annealing at $700^{\circ}C$ around the wavelength of $0.5{\mu}m$. The optical transmittance of the Bi:YIG film was also improved in visible region.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.33.2-33.2
• /
• 2009

Dielectric and piezoelectric properties of Lead-free $(1-x)(Bi_{0.5}K_{0.5})TiO_3-xBiFeO_3$ceramics prepared by a conventional solid state reaction method were investigated in the range of x = 0~10 mol%. Piezoelectric coefficient was increased from 31 pC/N at x = 0 mol% to 64 pC/N at x = 6 mol% then decreased with increasing x. Electromechanical coupling factor ($K_p$) was increased up to 0.18 at x = 10 mol%. On the other hand, mechanical quality factor ($Q_m$) was decreased. Grain size was not much changed with various x and a single perovskite with tetragonal symmetry was maintained at all compositions forming a solid solution between $(Bi_{0.5}K_{0.5})TiO_3$ and $BiFeO_3$. Depolarization temperature ($T_d$) was gradually decreased with increasing x from $302^{\circ}C$ at x = 0 to $245^{\circ}C$ at x = 10 mol%.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.1
• /
• pp.42-47
• /
• 2003

Hot-dip galvanizing process is used widely in industry to achieve corrosion resistant coatings. Poor drainage during this process often leads to problems such as icicle formation and bridging In this work, mild steel specimens were hot-dip galvanized. Influence of the addition of bismuth, aluminum and both (bismuth and aluminum) to the zinc bath on the zinc drainage were determined. Bismuth additions improved the drainage significantly. Zinc bath containing 0.1 wt.% Bi and 0.025∼0.05 wt.% Al showed uniformity of coatings. Industrial trials with this bath composition showed reduction in zinc consumption, reduction of ash and dross, and good luster of workpiece.

• The Korean Journal of Ceramics
• /
• v.1 no.2
• /
• pp.91-95
• /
• 1995

Polycrystalline bismuth- and aluminum- substituted dysporsium and yttrium iron garnet (Bi2R3-xAlyFe5-yO12, R=Dy or Y, $0\leqx\leq3, \; 0\leqy\leq3$) films have been prepared by pyrolysis. The crystallization temperatures, the solubility limit of bismuth ions into the garnet phase, and magnetic and magneto-optic properties of the films have been investigated as a function of bismuth and aluminum concentration. It was found that the crystallization temperatures as a function of bismuth and aluminum concentration. It was found that the crystallization temperatures of these films rapidly decreased as bismuth concentration. It was found that the crystallization temperatures of these films rapidly decreased as bismuth concentration (x) increased up to x=1.5 and then remained temperatures of these films rapidly decreased as bismuth concentration (x) increased up to x=1.5 and then remained unchanged at x>1.5, whereas, showed no changes as aluminum concentration (y) increased up to y=1.0 and then gradually increased at y>1.0. The solubility limit of bismuth ions was x=1.8 when y=0 but increased to x=2.3 when y=1.0. It was demonstrated that the magnetic and magneto-optic properties of the dysprosium iron garnet films could be tailored by bismuth and aluminum substitution suitable for magneto-optic recording as follows. The saturation magnetization and coercivity data obtained for the films indicated that the film composition at which the magnetic compensation temperature became room temperature was y=1.2 when x=1.0. Near this composition the coercivity and the squareness of the magnetic hysteresis loop of the films were several kOe and unit, respectively. The Curie temperatures of the films increased with the increase of x but decreaed with the increase of y, and was 150-$250^{\circ}C$ when x=1.0 and y=0.6-1.4. The Faraday rotation at 633 nm of the films increased as x increased but decreased as y increased, and was 1 deg/$\mu\textrm{m}$ when x=1.0 and y=1.0. Based on the data obtained, the appropriate film composition for magneto-optic recording was estimated as near x=1.0 and y=1.0 or $BiDy_2AlFe_4O_{12}$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.31.1-31.1
• /
• 2009

In an approach to acclimate ourselves torecent ecological consciousness trend, a lead-free piezoelectric material, bismuth sodium titanate (abbreviated as BNT) based bismuth sodium barium titanate (abbreviated as BNT-BT), was considered as an environment-friendly alternative for a lead based piezoelectric system. Ceramic specimens of0.94[(BixNa0.5)TiO3]-0.06[BaTiO3] (x = 0.500~0.515) compositions were prepared by a modified mixed oxide method. To increase the chemical homogeneity andre action activity, high energy mechanical milling machine and pre-milled nanosized powder has been used. In this method (BixNa0.5)TiO3 (x=0.500~0.515) andBaTiO3 were prepared separately from pre-milled constituent materials at low calcination temperature and then separately prepared BNTX (X=1, 2, 3 and 4) and BT were mixed by high energy mechanical milling machine. Without further calcination step the mixed powders were pressed into disk shape and sintered at $1110^{\circ}C$. Microstructures, phase structures and electrical properties of the ceramic specimens were systematically investigated. Highly dense ceramic specimens with homogenous grains were prepared in spite of relatively low sintering temperature. Phase structures were not significantly influenced by the excess amount Bi. Large variation on the piezoelectric and dielectric properties was detected at relative high excess Bi amounts. When $x{\leq}0.505$, the specimens exhibit insignificant variation in piezoelectric and dielectric constant though depolarization temperature is found to be decreased. Considerable amount of decrease in piezoelectric and dielectric properties are observed with higher excess of Bi amounts ($x{\geq}0.505$). This research indicates the advantages of high energy mechanical milling and importance of proper maintenance of Bi stoichiometry.