• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.351-354
• /
• 2002

In most of electrical applications using Bi-2223/Ag HTS tapes, bending and tension stresses are essentially applied to the tape. Therefore, the critical current of the Bi-2223/Ag tape is degraded by increasing the deformation stress, though brittle superconducting filaments are embedded in the reinforced Ag alloy sheath. It is needed to understand bending and tension properties of HTS tapes at room temperature and cryogen to make superconducting magnet, cable and etc. using Bi-2223/Ag HTS tapes. Actually, bending and tension stress applied to the tapes simultaneously, when winding the tapes on former for applications. In this study, the effect of mechanical deformations, bending and tension, on the critical current of Bi-2223/Ag tape was investigated.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.1
• /
• pp.69-73
• /
• 2001

In this study, we fabricated Bi-2223/Ag high temperature superconducting tapes using PIT(Powder-In-Tube) process to apply the superconducting magnet, cable and etc. It is inevitable to deform the superconducting taps with axial strain for application. Therefore, for the characterization of the strain sensitivity of the superconducting properties, the degradation of Bi-2223/Ag tapes due to axial strain were investigated by measuring the critical current as a function of applied tension strain and external magnetic field. The critical current of Bi-2223/Ag tapes were decreased slightly up to 0.3∼0.4% applied strain but, drastically decreased more than these strains. Superconducting filament cores consisted of brittle ceramic fibers were broken easily by the large strain and current path were decreased simultaneously.

• Transactions of Materials Processing
• /
• v.13 no.1
• /
• pp.78-83
• /
• 2004

High-temperature superconduction materials(Bi2223) possess electrical/electronic and magnetic properties. Because high-temperature superconduction materials is a ceramic powder, that cannot be produced singlehandedly. So Ag sheathed Bi-2223 wire was produced by drawing process using powder-in-tube(PIT) method. This superconductor has many difficulties to produce. The main difficulty is that the mechanical properties of the ceramic powder are very different from those of the Ag sheath. And by these properties, Bi2223 high-temperature superconductor, which has a single filament drawing process and multi-filament drawing process, has a defect like sausaging and bursting at a center. This study analyzed multi-filament drawing process by FEM, and a defect generated during multi-filament drawing was studied by FEH. Specially, in order to prevent a bursting at a center, this study presented a method that inserts a pure Ag at a center of multi-filament wire

• Progress in Superconductivity
• /
• v.6 no.2
• /
• pp.124-128
• /
• 2005

Homogeneous and fine powders for Bi-2223 tape were prepared by ultrasonic spray pyrolysis (SP) method from an aqueous solution of metal nitrates. Bi-2223 precursor powders were synthesized with various solutes concentration and pyrolysis temperature. The synthesized precursor powders had a narrow particle size distribution and an average particle size was $\~{\cal}um$. The reactivity of precursor powder by SP method is very high, attributed to the fine and narrow particle size distribution. Bi-2223/Ag tape was prepared using PIT method and followed by various sintering conditions. The precursor powder by SP method promoted a very quick formation of the Bi-2223 phase for short sintering time while the secondary phase such as large AEC phase and $Ca_2PbO_4$ were minimized for SP tapes.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.45-59
• /
• 2002

Evaluation of the mechanical properties of Bi-2223/Ag HTS tapes was carried out by the tension and bending tests. Most of the Bi-2223/Ag tapes retained critical current up to 10 kgf/mm$_2$ axial tension stress, and 0.2% tension strain at room temperature. Applied tension strain exceeding 0.3% in superconducting tapes at 77 K leaded to rapid degradation of the critical current. It was observed that the more filaments, the better axial tension property at 77 K, self-field The influence of bending strain on critical current degradation was revealed to be less sensitive for Bi-2223/Ag HTS tapes with a more number of filaments and higher silver ratio.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2003.02a
• /
• pp.220-223
• /
• 2003

High-Tc superconducting(HT S) systems are commercialized by many study on high-Tc superconductor. For the successful commercialization of superconducting systems using Bi-2223 wires, the database on the degradation of critical current is essentially needed. In this paper, critical current variation of Bi-2223 wires according to the transport time was investigated. The degradation rate of critical current was also calculated. Solenoid type specimens have the length of 190cm Bi-2223 wire and double-pancake type specimens have the length of l0m wire were tested. Tested Bi-2223 wires are commercialized products of AMSC (American Superconductor) and Innost. When the transportation current was 95% of critical current, the degradation of critical current was appeared after 5 hours of transport time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.810-813
• /
• 2000

In this study, we fabricated Bi-2223/Ag high temperature superconducting tapes using PIT (Powder-In-Tube) process to apply the superconducting magnet, cable and etc. It's inevitable to deform the superconducting tapes with axial strain for application. Therefore, for the characterization of the strain sensitivity of the superconducting properties, the degradation of Bi-2223/Ag tapes due to axial strain were investigated by measuring the critical current as a function of applied tension strain and external magnetic field. The critical current of Bi-2223/Ag tapes were decreased slightly up to 0.3∼0.4% applied strain but, drastically decreased more than these strains. Superconducting filament cores consisted of brittle ceramic fibers were broken easily by the large strain and current path were decreased simultaneously.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.1
• /
• pp.6-11
• /
• 2004

The influences of mixed strain mode of bending-tension on the critical current. Ic in externally reinforced Bi-2223 tapes and their interaction were investigated in this study. A test fixture which providing a mixed deformation mode of bending-tension to HTS tapes has been newly devised. When the total strain induced in the tape in the mixed strain mode was expressed by the superposition of the bending and tensile strains the irreversible strain for the critical current degradation of Bi-2223 tapes increased, as compared with the simple bending mode case. The $I_c$ degradation at the region exceeding the irreversible strain showed a medium between the simple bending case and the simple tension case. As the initial bending strain imparted increased , namely as the diameter of mandrel adopted decreased. the apparent irreversible strain in Bi-2223 tapes increased . but the increment became smaller As a result. it can be found that the tension to be applied to bent Bi-2223 tapes during cabling should be smaller. as the mandrel diameter becomes smaller.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.3
• /
• pp.251-256
• /
• 2001

Bi-2223 tapes have been developed for low-field power applications at liquid nitrogen temperature. When the Bi-2223 tapes are used in an application such as a power transmission cable or a power transformer, they are supplied with an AC transport current simultaneously. AC loss taking into account such real applications is a crucial issue for power applications fo the Bi-2223 tapes to be feasible. In this paper, the transport losses for different AC current levels and arrangements of the neighboring tapes have been measured in a 1./5 m long Bi-2223 tape. The significant increase of the transport losses due to neighboring tape's AC currents is observed. An increase of the transport losses caused by a decrease of the Bi-2223 tape's critical current is a minor effect. The measured trasprot losses could not be explained by a dynamic resistance loss based on DC voltage-current characteristics in combination with the neighboring tape's AC currents.The trasport losses do not depend on the frequency of the neighboring tape's AC currents but is arrangements in the range of small current especially.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.25-28
• /
• 2002

Contact type Ic measurement system is needed to measure Ic continuously for long Bi-2223 tapes. Voltage and current terminals were designed several shapes for 4-probe method Ic measurement. Voltage terminals were made with brass and current terminals were made with Cu. We used 2 kinds of Bi-2223 tapes with different strength. When we measured Ic of Bi-2223 tape with Ag-Mg sheath, The proper weight was 0.3 kg and sharp pin type was better. according to voltage terminal shape and load. In case of Bi-2223 tape with Ag-Mn sheath, the proper terminal weight was 4 kg and sharp pin type was bad. It was possible to make continuous contact type Ic measurement system because We could get proper data - terminal shapes and loads - through these experiments.