• Journal of Powder Materials
• /
• v.13 no.2 s.55
• /
• pp.119-123
• /
• 2006

The grain growth behavior of $0.95Na_{1/2}Bi_{1/2}TiO_{3}-0.05BaTiO_{3}$ (NBT-5BT) has been investigated with respect to the grain shape. The powder compacts of NBT-5BT were sintered at 1200 for various times. The corresponding equilibrium shape was a round-edged cube with flat {100}-faces. Abnormal grains were not observed in the specimens sintered for 1 to 12 h but abnormal grains appeared when sintered for 24 h. Before the formation of abnormal grains, a valley was observed in the measured grain size distribution of NBT-5BT, showing that the grain size distribution was a combination of two unimodal distributions. The present result suggests that the grain growth in NBT-5BT was governed by the growth of facet planes which would occur via 2-dimansional nucleation and growth.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.3
• /
• pp.127-132
• /
• 2014

$Y_2O_3$-BN ceramic composites were fabricated from the slurries of yttria powder with average particle size of 3~10 ${\mu}m$. The slurry was fabricated by mixing PVA binder, NaOH for Ph control, PEG, BN powder and $Y_2O_3$ powder. The mixed $Y_2O_3$ powders were obtained by spray drying process from the slurry. The $Y_2O_3$-BN composite specimen was shaped in size of ${\O}14mm$ and then sintered at $1550^{\circ}C$ and $1600^{\circ}C$, respectively. The characteristics, microstructure, purities, densities, bulk resistance, thermal expansion, hardness and plasma resistance of the $Y_2O_3$-BN composites were investigated with the function of BN contents and sintering temperature.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.5
• /
• pp.284-289
• /
• 2014

The effects of additives (Nb, Bi and Cr) on the microstructure, varistor properties, and aging behavior of V/Mn/Co/ La/Dy co-doped zinc oxide ceramics were systematically investigated. An analysis of the microstructure showed that all of the ceramics that were modified with various additives were composed of zinc oxide grain as the main phase, and secondary phases such as $Zn_3(VO_4)_2$, $ZnV_2O_4$, and $DyVO_4$. The $Bi_2O_3$-modified samples exhibited the lowest density, the $Nb_2O_5$-modified sample exhibited the largest average grain size, and the $Cr_2O_3$-modified samples exhibited the highest breakdown field. All additives improved the non-ohmic coefficient (${\alpha}$) by either a small or a large margin, and in particular an $Nb_2O_5$ additive noticeably increased the non-ohmic coefficient to be as large as 36. The $Bi_2O_3$-modified samples exhibited the highest stability with variation rates for the breakdown field and for the non-ohmic coefficient (${\alpha}$) of -1.2% and -26.3%, respectively, after application of a DC accelerated aging stress of 0.85 EB/$85^{\circ}C$/24 h.

• Journal of the Korean Ceramic Society
• /
• v.24 no.3
• /
• pp.270-276
• /
• 1987

The microstructure and dielectric properties of a SrTiO3-based GBL (Grain Boundary Layer) capacitor were investigated. The 0.6 mol% Nb2O5 doped SrTiO3 was sintered for 3 hr at 1450$^{\circ}C$ in mixed gas(N2/H2) atmosphere. The Nb2O5 promoted the grain growth of the SrTiO3 ceramics was decreased with the amount of Nb2O5. The oxide mixture(PbO, Bi2O3, B2O3) were painted on the reduced specimen and fired at 1000$^{\circ}C$ to 1100$^{\circ}C$ in air. The penetrated oxide mixture into specimen were located in grain boundaries. A SrTiO3-based GBL capacitor had the apparent permittivity of about 3.0${\times}$104, the dielectric loss of 0.01-0.02, and insulating resistance of 108-109$\Omega$.cm. The capacitor had the stable temperature coefficient of capacitance and exhibited dielectric dispersion over 107 Hz. The capacitance-voltage measurements indicated that the grain boundary was composed of the continuous insulating layers.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.2
• /
• pp.143-150
• /
• 2000

Ferroelectric SrxBi2+yTa2O9+$\alpha$ thin films with various compositions(x=0.7, 0.8, 1, y=0.3, 0.4) were prepared by sol-gel method. The film with moled ratio of 0.8:2.3:2.0 in Sr/Bi/Ta, which was deposited on Pt/SiO2/Si (100), showed better ferroelectric properties than other films. To investigate substrate effects, the same compositions were spin coated on Pt/Ti/SiO2/Si (100) substrates. At an applied voltage of 5V, the dielectric constant($\varepsilon$r), remanent polarization (2Pr) and coercive field (Ec) of the Sr0.8Bi2.3Ta2O9+$\alpha$ thin film prepared on Pt/Ti/SiO2/Si (100) were about 296, 24$\mu$C/$\textrm{cm}^2$ and Ec of 49kV/cm respectively. Both SBT films firred at 80$0^{\circ}C$ revealed no fatigue up to 1010 cycles. Retention characteristics of these capacitors showed no degradation up to 104 sec.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.1
• /
• pp.19-24
• /
• 2007

The effects of $B_2O_3-SiO_2-R(R;CaO,\;BaO,\;ZnO,\;Bi_2O_3)$ borosilicate glass system on the sintering behavior and microwave dielectric properties of ceramic/glass composites were investigated as functions of modifier, glass addition ($30{\sim}50\;vol%$) and sintering temperature ($500{\sim}900^{\circ}C$ for 2 hrs). The addition of 50 and 45 vol% glass ensured successful sintering below $900^{\circ}C$. Sintering characteristics of the composites were well described in terms of modifier. Borosilicate glass enhanced the reaction with $Al_{2}O_{3}$ to form pores, second phases and liquid phases, which was responsible to component of modifier. Dielectric constant (${\varepsilon}_{r},\;Q{\times}f_{o}$) and temperature coefficient of resonant frequency (${\tau}_{f}$) of the composite with 50 and 45 vol% glass contents($B_{2}O_{3}:SiO_{2}:R=25:10:65$) demonstrated A-CaBS(7.8, 2,560 GHz, -81ppm/$^{\circ}C$), A-BaBs(5.8, 3.130 GHz, -64 ppm/$^{\circ}C$), A-ZnBS(5.7, 17,800 GHz, -21 ppm/$^{\circ}C$), A-BiBs(45 vol% glass in total)(8.3, 2,700 GHz, -45 ppm/$^{\circ}C$) which is applicable to substrate requiring an low dielectric properties.

• Journal of the Korean earth science society
• /
• v.22 no.3
• /
• pp.208-222
• /
• 2001

Geochemical investigations on suspended amorphous iron oxide material from the Kwangyang gold mine and its surrounding area, Cheonnam, Korea have been carried out. The sediments samples were collected from 11 location along Kwangyang mine area and were air dried and sieved to -80 mesh. These samples consist mainly of iron, silicon and alumina. The Fe$_2$O$_3$ contents ranges from 17.9 wt.% to 72.3 wt.%. The content of Fe$_2$O$_3$ increase with decreasing Si, Al, Mg, Na, K, Mn, and Ti, whereas the contents of Te, Au, Ga, Bi, Cd, Hg, Sb, and Se increase in the amorphous stream sediments. Amorphous stream sediments have been severely enriched for As (up to 54.9 ppm), Bi (up to 3.77 ppm), Cd (up to 3.65 ppm), Hg (up to 64 ppm), Sb (up to 10.1 ppm), Cu (up to 37.1 ppm), Mo (up to 8.86 ppm), Pb (up to 9.45 ppm) and Zn (up to 29.7 ppm). At the upstream site, the Au content (up to 4.4 ppm) in the amorphous stream sediments are relatively high but those contents decrease with distance of mine location. The content of Ag (up to 0.24 ppm) were low in upstream site but those contents increase significantly in the downstream sites. The X-ray diffraction patterns of the samples have virtually no sharp and discrete peaks, indicating that some samples are amorphous or poorly-ordered. The quartz, goethite, kaolinite and illite were associated in amorphous stream sediments. The infrared spectra for amorphous stream sediments show major absorption bands due to OH stretching, adsorbed molecular water, sulfate and Fe-O stretching, respectively.

• Journal of the Korean Magnetic Resonance Society
• /
• v.17 no.1
• /
• pp.24-29
• /
• 2013

The structural characteristics of 4-coordinate $BO_4$ [B(1)] and 3-coordinate $BO_3$ [B(2)] groups in $BiB_3O_6$ were studied by $^{11}B$ magic angle spinning (MAS) and single-crystal nuclear magnetic resonance (NMR) spectroscopy. The spin-lattice relaxation time in the laboratory frame, $T_1$, for $^{11}B$ decreased slowly with increasing temperature, whereas the spin-lattice relaxation times in the rotating frame, $T_{1{\rho}}$, for B(1) and B(2), which differed from $T_1$, were nearly constant. Further, $T_{1{\rho}}$ for B(1) and B(2) showed very similar trends, although the $T_{1{\rho}}$ value of B(2) was shorter than that of B(1). The 3-coordinate $BO_3$ and 4-coordinate $BO_4$ were distinguished by $^{11}B$ MAS NMR spectrum and $T_{1{\rho}}$.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.689-695
• /
• 2012

We have examined the co-doping effects of 1/2 mol% NiO and 1/4 mol% $Cr_2O_3$ (Ni:Cr = 1:1) on the reaction, microstructure, and electrical properties, such as the bulk defects and the grain boundary properties, of ZnO-$Bi_2O_3-Sb_2O_3$ (ZBS; Sb/Bi = 0.5, 1.0, and 2.0) varistors. The sintering and electrical properties of Ni,Cr-doped ZBS, ZBS(NiCr) varistors were controlled using the Sb/Bi ratio. Pyrochlore ($Zn_2Bi_3Sb_3O_{14}$), ${\alpha}$-spinel ($Zn_7Sb_2O_{12}$), and ${\delta}-Bi_2O_3$ were detected for all of compositions. For the sample with Sb/Bi = 1.0, the Pyrochlore was decomposed and promoted densification at lower temperature by Ni rather than by Cr. A homogeneous microstructure was obtained for all of the samples affected by ${\alpha}$-spinel. The varistor characteristics were not dramatically improved (non-linear coefficient, ${\alpha}$ = 5~24), and seemed to form ${Zn_i}^{{\cdot}{\cdot}}$(0.17 eV) and ${V_o}^{\cdot}$(0.33 eV) as dominant defects. From impedance and modulus spectroscopy, the grain boundaries were found to have been divided into two types, i.e., one is tentatively assigned to ZnO/$Bi_2O_3$ (Ni,Cr)/ZnO (0.98 eV) and the other is assigned to a ZnO/ZnO (~1.5 eV) homojunction.

• Journal of Magnetics
• /
• v.13 no.3
• /
• pp.110-113
• /
• 2008

In this study, heavy rare earth garnet $Tb_2Bi_1Ga_1Fe_4O_{12}$ powders were fabricated by a sol-gel and vacuum annealing process. The crystal structure was found to be single-phase garnet with a space group of Ia3d. The lattice constant $a_0$ was determined to be 12.465 ${\AA}$. From the analysis of the vibrating sample magnetometer (VSM) hysteresis loop at room temperature, the saturation magnetization and coercivity of the sample are 7.64 emu/g and 229 Oe, respectively. The N$\acute{e}$el temperature($T_N$) was determined to be 525 K. The M$\ddot{o}$ssbauer spectrum of $Tb_2Bi_1Ga_1Fe_4O_{12}$ at room temperature consists of 2 sets of 6 Lorentzians, which is the pattern of single-phase garnet. From the results of the M$\ddot{o}$ssbauer spectrum at room temperature, the absorption area ratios of Fe ions on 24d and 16a sites are 74.7% and 25.3%(approximately 3:1), respectively. These results show that all of the non-magnetic Ga atoms occupy the 16a site by a vacuum annealing process. Absorption area ratios of Fe ions are dependent not only on a sintering condition but also on the temperature of the sample. It can then be interpreted that the Ga ion distribution is dependent on the temperature of the sample. The M$\ddot{o}$ssbauer measurement was carried out in order to investigate the atomic migration in $Tb_2Bi_1Ga_1Fe_4O_{12}$.