• Journal of Welding and Joining
• /
• 제19권3호
• /
• pp.298-304
• /
• 2001

Turbine blade is subject to force of three types ; the torsional force by torsional mount, the centrifugal force by the rotation of rotor and the cyclic bending force by steam pressure. The cyclic bending force was a main factor on fatigue strength. SEM fractography in root of turbine blade showed micro-clack width was not dependent on stress intensity factor range. Especially, fatigue did not exist on SEM photograph in root of turbine blade. To clear out the fracture mechanism of turbine blade, nanofractography was needed on 3-dimensional crack initiation and crack growth with high magnification. Fatigue striation partially existed on AFM photograph in root of turbine blade. Therefore, to find a fracture mechanism of the torsion-mounted blade in nuclear power plant, the relation between stress intensity factor range and surface roughness measured by AFM was estimated, and then the load amplitude ΔP applied to turbine blade was predicted exactly by root mean square roughness.

• 대한기계학회논문집A
• /
• 제26권9호
• /
• pp.1746-1752
• /
• 2002

Fatigue fracture in machine components is produced by surface micro-crack from stress concentration area such as notch and material defect. It is difficult to predict the remaining fatigue lift of mechanical components because the surface micro-crack on critical area initiates and grows with statistical distribution. Plane bending fatigue tests were carried out on the plain specimen of Al 2024-T3 and the initiation and growth behavior of surface micro cracks were observed. The statistical distribution of surface length of multiple micro cracks and their maximum length were investigated. The maximum surface crack length distributions were analyzed on the basis of the statistics of extremes in order to examine the prediction of remaining life.

• Steel and Composite Structures
• /
• 제49권2호
• /
• pp.181-196
• /
• 2023

Marine structures including offshore wind turbines (OWTs) always work under cyclic loads, which arouses much attention on the fatigue design. The tripod substructure is one of the typical foundation forms for fixed OWTs. The three-planar tubular Y-joint (3Y joint) is one of the important components in fatigue design as it is most likely to have cracks. With the existence of the multiplanar interaction effect, calculating the hot spot stress (HSS) of 3Y joints is complicated. To assist with fatigue design, the distributions of stress concentration factor (SCF) and multiplanar interaction factor (MIF) along weld toe curves induced by the out-of-plane bending moment are explored in this study. An FE analysis method was first developed and verified against experimental results. This method was applied to build a numerical database including 1920 FE models covering common ranges of geometric parameters. A parametric study has been carried out to reveal the distribution patterns of SCF and MIF. After multidimensional nonlinear fittings, SCF and MIF distribution formulas have been proposed. Accuracy and reliability checking prove that the proposed formulas are suitable for calculating the HSS of 3Y joints.

• 한국해양공학회지
• /
• 제36권4호
• /
• pp.232-242
• /
• 2022

This study presents a method for level ice-structure interaction analysis to estimate the fatigue damage of arctic structures by applying plate theory to the behavior of level ice. The boundary element method (BEM), which incurs a lower computational cost than the finite element method (FEM), was introduced to solve the plate bending problem. The BEM formulation was performed by applying the BEM to plate theory. Finally, to check the validity of the proposed method, the BEM results and FEM results obtained using the ABAQUS commercial software were compared. The response results of the BEM analysis agreed well with those of the FEM analysis. Based on the results of the analysis, the BEM approach is considered to be very powerful in level ice-structure interaction analysis for estimating level ice-induced fatigue damage. Further work is being conducted to perform level ice fracture analysis based on the stress field calculated using the boundary element method.

• Nuclear Engineering and Technology
• /
• 제53권11호
• /
• pp.3852-3859
• /
• 2021

This paper presents experimental and numerical analysis results regarding the effects of an incomplete penetration defect on the fatigue lives of socket welded pipes. For the experiment, four-point bending fatigue tests with various defect geometries (defect depth and circumferential length) were performed, and test results are presented in terms of stress-life data. The results showed that for circumferentially short defects, the fatigue life tends to increase with increasing crack depth, but for longer defects, the trend becomes the opposite. Finite element analysis showed that for short defects, the maximum principal stress decreases with increases in crack depth. For a longer defect, the opposite trend was found. Furthermore, the maximum principal stress tends to increase with an increase in defect length regardless of the defect depth.

• Restorative Dentistry and Endodontics
• /
• 제44권2호
• /
• pp.19.1-19.9
• /
• 2019

Objectives: The purpose of this study was to evaluate the cyclic fatigue, bending resistance, and surface roughness of EdgeEvolve (EdgeEndo) and ProTaper Gold (Dentsply Tulsa Dental Specialties) nickel-titanium (NiTi) rotary files. Materials and Methods: The instruments (n = 15/each) were tested for cyclic fatigue in single- ($60^{\circ}$ curvature, 5-mm radius) and double-curved (coronal curvature $60^{\circ}$, 5-mm radius, and apical curvature of $30^{\circ}$ and 2-mm radius) artificial canals. The number of cycles to fracture was calculated. The bending resistance of both files were tested using a universal testing machine where the files were bent until reach $45^{\circ}$. Scanning electron microscopy and x-ray energy-dispersive spectrometric analysis were used for imaging the fractured segments, while the atomic force microscope was used to quantify the surface roughness average (Ra). Results: EdgeEvolve files exhibited higher cyclic fatigue resistance than ProTaper Gold files in single- and double-curved canals (p < 0.05) and both files were more resistant to cyclic fatigue in single-curved canals than double-curved canals (p < 0.05). EdgeEvolve files exhibited significantly more flexibility than did ProTaper Gold files (p < 0.05). Both files had approximately similar Ni and Ti contents (p > 0.05). EdgeEvolve files showed significantly lower Ra values than ProTaper Gold files (p < 0.05). Conclusions: Within the limitation of this study, EdgeEvolve files exhibited significantly higher cyclic fatigue resistance than ProTaper Gold files in both single- and double-curved canals.

• 한국정밀공학회지
• /
• 제25권8호
• /
• pp.96-103
• /
• 2008

In this study, we performed the biomechanical analysis of cervical plate systems by using a computer simulation based on finite element method to derive reliable model by analysis of design variables and fatigue behavior. To simulate the cervical spine movement in-vivo state by surgery, we modeled the cervical plate system which consisted of screws, rings, rivets, and plate and Ultra High Molecular Weight Polyethylene (UHMWPE) Block. The experiment of cervical plate system followed the ASTM F1717 standards that covered the materials and methods for the static and fatigue testing. The result of computer simulation is compared with experimented test. We expected this study is to derive reliable results by analysis of design variables and fatigue behavior for developing a new model.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 1993년도 한국자동제어학술회의논문집(국제학술편); Seoul National University, Seoul; 20-22 Oct. 1993
• /
• pp.307-311
• /
• 1993

Research concerning gears included in rotating machines has been reported using the acoustic emission (AE) method, however, almost no research has been conducted using the AE method in regard to running gears in a bending fatigue processor spur gear teeth. Therefore, in this report, a power circulating-type gear testing machine was used and AE signals and crack length were measured in the bending fatigue process of case-hardened spur gear. Furthermore, the envelope of the AE signal was detected and various analysis were carried out in this data. In the course of the experiments, the following results were observed : the AE signal envelope consists mainly of contact frequency component and twice as many as this;two peaks of AE appear in each tooth contact by the tip corner contact ; as a result of the severe tip corner contact ; as a result of the severe tip corner contact with the sudden increase of crack length, AE signal becomes large.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 춘계학술발표대회 논문집
• /
• pp.241-245
• /
• 2004

An analytical study was conducted to characterize the fatigue crack growth behavior of pre-cracked aluminum plates repaired with asymmetric bonded composite patch. For single-sided repairs, due to the asymmetry and the presence of out-of-plane bending, crack front shape would become skewed curvilinear started from a uniform through-crack profile, as observed from previous studies. In this study, the fatigue analysis of single-sided repairs considering crack front shape development was conducted by implementing three-dimensional successive finite element method coupled with linear elastic fracture mechanics (LEFM) concept, which enables the growing crack front to be directly traced and modeled in a step by step way. Through conducting present analysis technique, crack path of the patched plate as well as the fatigue life was evaluated with sufficient accuracy. The analytical predictions of both the crack front shape evolution and the fatigue life were in good agreement with the experimental observations.

• Journal of Mechanical Science and Technology
• /
• 제16권8호
• /
• pp.1109-1116
• /
• 2002

To investigate the effect of nitriding layer on both fatigue crack initiation and fatigue life, turbine rotor steel ( IC.- 1Mo-0.25V steel) specimens were nitrided by the nitemper method and then put to a rotary bending fatigue test at room and elevated temperatures. In nitriding, temperature and time were controlled to obtain a different nitrided thickness. Microstructure analysis, micro-Victors hardness test, and scanning electron microscope observation were carried out for evaluating experiments. In results, the fatigue cracks of nitrided specimens were initiated at inclusion near the interface between nitrided layer and substrate, which showed fish-eye type appearance in fractograph. The fatigue life of nitrided specimens at every temperature was prolonged compared to that of the non-nitrided. However, there was not observable improvement in fatigue characteristics with the increase of a nitrided thickness.