• Corrosion Science and Technology
• /
• 제5권3호
• /
• pp.85-89
• /
• 2006

KAERI(Korea Atomic Energy Research Institute) has developed a repassivation rate test system which can be operated at $300^{\circ}C$. It consists of an autoclave, three electrodes for an electrochemical test and a diamond scratch tip. All the electrodes are electrically insulated from the autoclave by using high temperature fittings. Reproducible repassivation curves of alloy 600 at 300 C were obtained. Repassivation rate of alloy 600 at pH 13 was slower than that of pH 10. Stress corrosion cracking test was carried as a function of the pH at a high temperature. At pH 10, alloy 600 showed a severe stress corrosion cracking(SCC), whereas it did not show a SCC at pH 7. From the viewpoint of a relationship between the current density and the charge density, a big difference was observed in the two solutions; the slope of pH 13 was steeper than that of pH 10. So the stress corrosion susceptibility at pH 13 seems to be higher than that of pH 10. The system would be a good tool to evaluate the SCC susceptibility of alloy 600 at a high temperature.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 광주전남지부
• /
• pp.123-125
• /
• 2006

The $TiO_2$ sol was prepared hydrothermally in an autoclave from aqueous $TiOCl_2$ solutions as a starting precursor. Hollow fibers were obtained when the sol-gel-derived $TiO_2$ sol was treated chemically with a NaOH solution and subsequently heated in the autoclave under various conditions. A systematic analysis of the influence of different NaOH concentrations on the formation of nanotubes was carried out. The details of the nanotubular structure were investigated by using transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray diffraction (XRD). From the TEM images, the outer and the inner diameters of the tubes were measured to be about 8 and 4 nm, respectively, the lengths were measured to be several hundreds of nanometers.

• 분석과학
• /
• 제10권1호
• /
• pp.18-30
• /
• 1997

Si / Al비가 130 정도인 Na, TPA-ZSM-5를 저온 상압법으로 합성하였으며, 이들의 결정화 과정을 XRD, XRF, FT-IR, NMR 및 SEM을 이용하여 고찰하였다. 결정의 형성과정은 autoclave법과는 다소 다르게 나타났으나 최종 생성물의 분광학적 특성은 전형적인 ZSM-5 영역에서 나타났다. 또한 반응 도중 생성된 국부결함은 소성에 의해 제거됨을 알 수 있었으며, 저온상압하에서도 반응시간을 48시간 이내로 단축할 수 있음을 알 수 있었다.

• 공학논문집
• /
• 제4권1호
• /
• pp.87-91
• /
• 2002

본 연구에서는 초임계 건조 및 유체법을 사용하여 얻어진 분말을 열처리하여 나노 크기의 알루미나 분말을 제조하였다. Al-isopropoxide를 출발 물질로 사용하였고, 용매로서는 2가 알코올류인 Ethylene glycol을 사용하였다. 또한 온도 및 압력의 영향을 조사하기 위하여 임계점 이하의 조건에서도 실험도 병행하였다. Autoclave에서 초임계 건조 및 유체법으로 제조된 알루미나는 XRD, SEM 및 TG-DTA 의해 특성을 조사하였고, 열처리 결과 새로운 route로 $\alpha-A12O3$로 전이 되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제25권3호
• /
• pp.37-42
• /
• 1997

This study was carried out to track the heated-air flows within the tree disk through measuring the distribution of wood temperatures during explosing the 7.5mm-thick Japanese cedar disk and to investigate the effects of the time for the first explosion cycle and the number of explosion cycles on the improvement of permeability of tree disk. If the tree disk are explosed when the temperatures of the shell and core of it are not equilibrium yet, all of the inflated airs in the shell after explosion don't flow out toward the autoclave and some of them flow into the core of which the air pressures are lower than those of the shell. It is very effective for the improvement of permeability of tree disk to make the first explosion cycle when the temperatures of the shell and the core equilibrate at the setting temperature of steam in the autoclave. The more tree disks were explosed under the same conditions of first explosion, the more their permeabilities were improved.

• 설비공학논문집
• /
• 제25권8호
• /
• pp.438-442
• /
• 2013

The alternative refrigerant R436B is applied, to assess the application feasibility for a commercial cooling water system. The characteristic stability was verified by Sealed glass tube test and Autoclave test. R436B is chemically stable with the compressor material. The Oil miscibility test shows the usual compressor oil mixed well with R436B. Through the life acceleration test, the cooling performance is maintained. Though slight changes in oil and capillary tube diameter were found, they were within the permitted range. R436B should be applied to commercial cooling water systems as a simple replacement for the usual refrigerant.

• 한국재료학회지
• /
• 제34권3호
• /
• pp.125-137
• /
• 2024

Composite laminates are used in a wide range of applications including defense, automotive, aviation and aerospace, marine, wind energy, and recreational sporting goods. These composite beams still exhibit problems such as buckling, local deformations, and interlaminar delamination. To overcome these drawbacks, a novel viscoelastic autoclave bonding with tapered epoxy reinforcement polyurethane films is proposed. In existing laminates, compression face wrinkling and interlaminar delamination is caused in the sandwich beam. The unique viscoelastic autoclave spunbond interlayer bonding is designed to prevent face wrinkling and absorb and distribute stresses induced by external loads, thereby eliminating interlaminar delamination in the sandwich beam. Also, the existing special reinforcement causes stress concentrations, and the core is not effectively connected, which directly affects the stiffness of the beam. To address this, a novel tapered epoxy polyurethane reinforcement adhesive film is proposed, whose reinforcement thickness gradually tapers as it enters the core material. This minimizes stress concentrations at the interface, preventing excessive adhesive squeeze-out during the bonding process, and improves the stiffness of the beam. Results indicate the proposed model avoids the formation of micro cracks, interlaminar delamination, buckling, and local deformations, and effectively improves the stiffness of the beam.

• 콘크리트학회논문집
• /
• 제15권1호
• /
• pp.117-124
• /
• 2003

최근 강모래의 고갈로 인하여 해사의 사용이 증대되고 있는 실정에 있다. 그러나 해사는 철저하게 제염처리 하여 사용하지 않으면 철근 콘크리트 구조물의 철근에 막대한 영향을 미칠 수 있다. 본 연구에서는 제염처리하지 않은 해사를 시멘트 콘크리트에 직접 사용하여도 철근의 부식을 억제할 수 있는 방청재료를 개발하기 위한 연구의 일환으로서, 기존의 에폭시 철근과 비교하여 경제적이고 방식 성능면에서 우수한 재료로서 폴리머 시멘트 슬러리를 이용하고자 하였다. 각종 폴리머를 사용하고 여러 가지 부식촉진 실험을 통하여 도장하지 않은 철근과 도장한 철근과의 성능을 비교평가하였다. 연구결과, 폴리머 시멘트 슬러리로 도장한 철근은 도장하지 않은 철근에 비해 염화나트륨 수용액에 대한 침지 및 분무시험과 시멘트 콘크리트 속에서의 부식에 관한 실험에 있어서도 매우 우수한 방식성능을 발휘하였다. 다양한 부식촉진 실험결과, 철근의 부식은 염분, 중성화 및 촉진양생에 의해 크게 영향을 받으며, 복합적인 인자가 작용될 때, 더욱더 심한 부식이 발생하였다. 이러한 부식을 폴리머 시멘트 슬러리에 의한 도장으로 억제할 수 있는데, 폴리머 시멘트 슬러리의 매트릭스에 존재하는 폴리머 필림의 연속된 막에 의해 염화물 이온의 침투가 차단되었기 때문이며, 폴리머 시멘트 슬러리의 완벽한 방식효과는 도장두께로 조절할 수 있을 것이다.

• 한국수산과학회지
• /
• 제35권6호
• /
• pp.671-675
• /
• 2002

우렁쉥이 껍질에서 추출한 autoclave 추출구와 neutrase 추출구는 지방흡수력의 경우 대조시료인 chitin과 chitsan에 비해 떨어지는 대략 250$\~$$300\%$ 정도이었으나, 포말성은 각각 0.70과 0.67로, 포말안정성은 0.50과 0.38로 우수하였다 Autoclave 추출구 및 neutrase 추출구의 유화능은 각각 $49.2\%$와 $47.1\%$, 유화안정성의 경우 각각 $48.3\%$와 $44.8\%$ 정도였으며 특히, 색소흡착능은 각각 $85.2\%$와 $85.6\%$로 대조시료에 비해 다소 우수하였다 항혈액응고능은 모든 시료에서 hPn 저 지효과는 나타났으나 PT값은 약 14.5초로 일정하여 혈액응고저지 효과가 거의 없었다. 특히 autoclave 처리구를 DEAE-cellulose ion exchange chromatography하여 얻은 F4 (획분4)는 APTT가 75초로 가장 효과적 이 었으며, Sephadex G-100의 $F_2$가 70초 정도였다. ACE저해능은 모든 시료에서 ACE 저해효과가 있었으며, 채택된 실험방법에 따라 동일시료 경우에 있어서도 저해효과 값이 차이가 났으며, 특히 DEAE-cellulose 이온교환 처리한 $ F_4$ (획분4)가 $35.7\%$로 가장 효과적이었다.

• Composites Research
• /
• 제31권1호
• /
• pp.1-7
• /
• 2018

히트블랑켓을 이용한 통상의 복합재 패치 수리의 경우, 진공백만을 이용하여 접착제에 압력을 가하게 된다. 그러나 본 연구에서는 진공백 위에 다시 공기압을 추가로 가할 수 있는 가압장치를 개발하였다. 개발된 가압장치의 성능을 검증하기 위해 탄소섬유 복합재 적층판을 스카프 패치로 수리하고 인장시험을 수행하여, 결함이 없는 온전한 구조물과의 강도를 비교하였다. 또한 비교를 위해 오토클레이브를 사용하여 패치를 접착한 동일한 형상의 시편에 대한 인장시험도 같이 수행하였다. 시험 결과 외부압력 없이 히트블랑켓과 진공만으로 수리한 시편, 개발된 가압장치로 1 기압을 추가로 가하여 수리한 시편, 그리고 오토클레이브에서 동일한 외부압력을 가하면서 수리한 시편의 인장강도 회복율은 각각 74.9, 81.0, 78.2%로 나타났다. 수분을 포화시킨 시편에 대한 인장강도 시험과 상온건조 인장 피로시험의 결과에서도, 개발된 가압장치를 이용해 1 기압 외부압력으로 제작한 시편은 오토클레이브로 제작한 시편과 동일한 수준 이상의 강도를 보이는 것을 확인하였다.