• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.51-57
• /
• 2008

we have demonstrated structural evolution and optical properties of Si-nanowires (NWs) synthesized on Si (111) substrates with nanoscale Au-Si islands by rapid thermal chemical vapor deposition (RTCVD). The Au-Si nano-islands (10-50nm in diameter) were employed as a liquid-droplet catalysis to grow Si-NWs via vapor-liquid-solid mechanism. The Si-NWs were grown by a mixture gas of SiH4 and H2 at a pressure of 1.0 Torr and temperatures of $500{\sim}600^{\circ}C$. Scanning electron microscopy measurements showed that the Si-NWs are uniformly sized and vertically well-aligned along <111> direction on Si (111) surfaces. The resulting NWs are ${\sim}60nm$ in average diameter and ${\sim}5um$ in average length. High resolution transmission microscopy measurements indicated that the NWs are single crystals covered with amorphous SiOx layers of ${\sim}3nm$ thickness. In addition, the optical properties of the NWs were investigated by micro-Raman spectroscopy. The downshift and asymmetric broadening of the Si main optical phonon peak were observed in Raman spectra of Si-NWs, which indicates a minute stress effects on Raman spectra due to a slight lattice distortion led by lattice expansion of Si-NW structures.

• Journal of the Korean Vacuum Society
• /
• v.16 no.4
• /
• pp.279-285
• /
• 2007

We have demonstrated structural evolution and optical properties of the Si-NWs on Si (111) substrates with synthesized nanoscale Au-Si islands by rapid thermal chemical vapor deposition(RTCVD). Au nano-islands (10-50nm in diameter) were employed as a liquid-droplet catalysis to grow Si-NWs via vapor-liquid-solid mechanism. Si-NWs were grown by a mixture gas of $SiH_4\;and\;H_2$ at pressures of $0.1{\sim}1.0$Torr and temperatures of $450{\sim}650^{\circ}C$. SEM measurements showed the formation of Si-NWs well-aligned vertically for Si (111) surfaces. The resulting NWs are 30-100nm in diameter and $0.4{\sim}12um$ in length depending on growth conditions. HR-TEM measurements indicated that Si-NWs are single crystals convered with about 3nm thick layers of amorphous oxide. In addition, optical properties of NWs were investigated by micro-Raman spectroscopy. The downshift and asymmetric broadening of the Si optical phonon peak with a shoulder at $480cm^{-1}$ were observed in Raman spectra of Si-NWs.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.11.2-11.2
• /
• 2009

Au-Ag 합금 박막에서 화학적으로 덜 안정한 Ag를 선택적으로 에칭하는 dealloying 기법을 통하여 crack-free 나노기공 gold 박막을 Si 기판에 제조하였다. Au-Ag 합금 박막은 두 가지 방법을 이용하였다: 1) thermal 또는 electron beam 증착법을 이용하여 Au 와 Ag 다층 박막을 Si 기판에 증착시킨 후 열처리를 통한 합금 박막제조; 2) co-thermal 증착법을 이용하여 Au-Ag 합금박막을 Si 기판에 직접 증착. Crack-free 나노기공 gold 박막 제조에 적합한 합금조성을 얻기 위하여 증착 속도, 열처리조건, dealloying 조건등을 조절하였다. Perchloric acid, HClO4 전해질을 이용한 전기화학적 dealloying을 통하여 crack-free 나노기공 gold 박막을 제조하였고, 기공크기를 조절할 수 있었다. 이에 더하여, electrophoretic 방법을 이용하여 나노기공 gold와 semiconductive 양자점 (CdTe 또는 CdSe)의 나노복합박막을 형성시킨 후 특성을 분석하였다.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.2 s.43
• /
• pp.17-21
• /
• 2007

Dense and periodic arrays of holes and Si nano dots were fabricated on silicon substrate. The nanopatterned holes were approximately $15{\sim}40nm$ wide, 40 nm deep and $40{\sim}80\;nm$ apart. To obtain nano-size patterns, self?assembling diblock copolymer were used to produce layer of hexagonaly ordered parallel cylinders of polymethylmethacrylate (PMMA) in polystyrene(PS) matrix. The PMMA cylinders were degraded and removed with acetic acid rinse to produce a PS. $100\;{\AA}-thick$ Au thin film was deposited by using e-beam evaporator. PS template was removed by lift-off process. Arrays of Au nano dots were transferred by using Fluorine-based reactive ion etching(RE). Au nano dots were removed by sulfuric acid. Si nano dots size and height were $30{\sim}70\;nm$ and $10{\sim}20\;nm$ respectively.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.150-150
• /
• 2012

본 연구는 1차원 나노 구조의 합성과 기초적 분석에 관한 연구로써 특히 무기 산화물 나노재료를 그 대상으로 하였다. 내용으로는 첫째, 1차원 코어 나노와이어의 합성을 하였고 Thermal evaporation, substrate의 가열, 그리고 MOCVD 를 사용한 결과들을 나열한다. 둘째, 코어-쉘 나노와이어를 제작하기 위하여 특히 쉘층의 제작방법을 연구하였는데 PECVD, ALD, 그리고 sputtering에 의한 결과들을 나열하고 간단히 설명한다. Thermal evaporation에 의한 1차원 나노와이어 합성의 경우는 MgO의 예를 들었는데 MgO 나노와이어는 Au가 증착된 기판을 열처리하여 Au dot를 형성하고 이의 morphology를 조절하여 최적의 나노와이어 합성조건을 선정하였다. 이로써 기판 morphology가 나노선의 성장및 형상에 영향을 준다는 사실을 알게 되었다. 이 사실은 In2O3기판을 사용하고 이의 표면거칠기를 열처리로 조절하므로써 역시 나노와이어의 성장을 촉진하는 방법을 찾아내었다. 또한 thermal evaporation공법은 source분말의 선택에 따라 다양한 소재를 제작가능하다는 결과를 제시하였다. 예를 들면 SiOx 층이 precoating된 chamber내에서 MgO 나노선을 합성하는 것과 동일한 조건으로 실험을 진행하면 Mg2SiO4 나노와이어가 형성된 것을 확인하였다. 또한 Sn과 MgB2 분말을 함께 적용할 경우 Sn tip을 가진 MgO 나노와이어를 얻을 수 있었다. 이는 Sn이 동시에 촉매의 역할을 하였기 때문일 것으로 추정된다. 한편 Sn과 Bi 혼합분말을 적용한 경우 Bi2Sn2O7 신소재 tip을 포함한 SnO2 나노와이어를 얻을 수 있었다. 이 경우 Bi원자가 적절한 촉매의 역할을 수행한 것으로 사료된다. Substrate의 가열공법에서는 Si wafer상에 각종 금속 즉 Au, Ag, Cu, Co, Mo, W, Pt, Pd등 초박막을 DC sputter 로 형성한후 annealing하는 기술을 사용하였다. 특기할 만한 것은 Co를 사용한 경우 나노와이어의 spring구조를 얻을 수 있었다는 점이다. MOCVD에 의하여는 Ga2O3및 Bi2O3 나노와이어를 비교적 저온에서 합성하였고 In2O3의 경우는 독특한 나노구조를 형성하였고 이의 결정학적 특성에 대하여 조사하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.346-346
• /
• 2011

실리콘 나노와이어는 높은 표면적으로 인해 뛰어난 감지 능력을 가지는 재료 중 하나로 다양한 센서 응용 분야에 사용되고 있다. 이를 제작하는 방법에는 Micro Electro Mechanical Systems (MEMS) 공정을 이용한 Top-down 방식과 Vapor-Liquid-Solid (VLS) 공정을 이용한 Bottom-up 방식이 널리 사용되고 있다. 특히 Plasma-Enhanced Chemical Vapor Deposition(PECVD)와 Au 촉매를 이용한 Bottom-up 방식은 수십 나노미터 이하의 실리콘 나노와이어를 간단한 변수 조절을 통해 성장시킬 수 있다. 또한 Au/Si의 공융점인 363$^{\circ}C$보다 낮은 온도에서 $SiH_4$를 분해시킬 수 있어 열적 효과로 인한 손실을 줄일 수 있는 장점을 지니고 있다. 하지만 PECVD를 이용한 실리콘 나노와이어 성장은 VLS 공정을 통해 표면으로부터 수직으로 성장하게 되는데 이는 센서 응용을 위한 전극 사이의 수평 연결 어려움을 지니고 있다. 따라서 이를 피하기 위한 표면 성장된 실리콘 나노와이어가 요구된다. 본 연구에서는 PECVD VLS 공정을 이용하여 $HAuCl_4$를 촉매로 이용한 표면 성장된 Tree-like 실리콘 나노와이어를 성장시켰다. 공정가스로는 $SiH_4$와 이를 분해시키기 위해 Ar 플라즈마를 사용 하였고 웨이퍼 표면에 HAuCl4를 분사하고 고진공 상태에서 챔버 기판을 370$^{\circ}C$까지 가열한 후 플라즈마 파워(W) 및 공정 압력(mTorr)을 변수로 두어 실험을 진행하였다. 기존의 보고된 연구와 달리 환원된 금 입자 대신 $HAuCl_4$용액을 그대로 사용하였는데 이는 표면 조도(Surface roughness)를 가지는 Au 박막 상태로 존재하게 된다. 이 중 마루(Asperite) 부분에 PECVD로부터 발생된 실리콘 나노 입자가 상대적으로 높은 확률로 흡착하게 되어 실리콘 나노와이어의 표면성장을 유도하게 된다. 성장된 실리콘 나노와이어는 SEM과 EDS를 이용하여 직경, 길이 및 화학적 성분을 측정하였다. 직경은 약 100 nm, 길이는 약 10 ${\mu}m$ 정도로 나타났으며 Tree-like 실리콘 나노와이어가 성장되었다. 향후 전극이 형성된 기판위에 이를 직접 성장시킴으로써 이 물질의 I-V 특성을 파악 할 것이며 이는 센서 응용 분야에 도움이 될 것으로 기대된다.