• 한국주조공학회지
• /
• 제19권1호
• /
• pp.54-65
• /
• 1999

The present work is an attempt to evaluate the relationship between dendrite arm spacing and average cooling rate in gasatomized $Al_{87.3}misch$ $metal_{8.3}Ni_{4.4}$ powder by means of the following methods. One is calculation of heat transfer coefficient and average cooling rate, which are derived from estimated particle velocity during gas-atomization. The other is measurement of secondary dendrite arm spacing, which are observed on the particle surface. Then, we make experimental equation for this relationship in case of permanent mold casting and compare it with similar equation in case of rapidly solidified powder. Both average cooling rates and solidification rates are considered to represent the variance of dendrite arm spacings in two types soidification route. Even though there is a considerable difference in each average cooling rate, the dendrite arm spacing values are similar in two cases; particle diameter, $100\;{\mu}m$, and casting width, 2.05 mm. It is because that each solidification route has similar solidification rate.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.799-800
• /
• 2006

Wrought Si-steels are generally used for electromagnetic valves, which are needed good response. To date, Hitachi Powdered Metals Co., Ltd. have produced Fe-Si base sintered magnetic material, EU-52, which shows a magnetic flux density of more than 1.25T at 2000A/m and a maximum permeability of more than 3500. However these magnetic properties are lower than that of wrought Si-steels. Because EU-52 has a low density of $7.2Mg/m^3$. For improving the magnetic properties, it is necessary to increase the density of sintered cores. To increase density, a new mixing method of coating fine Si powders on atomized iron powders was developed, for avoiding the Kirkendall effect. As the result, developed P/M Fe-Si magnetic cores shows higher density of $7.38Mg/m^3$, higher magnetic flux density of 1.48T at 2000A/m and higher maximum permeability of 6800.

• 대한금속재료학회지
• /
• 제49권11호
• /
• pp.853-859
• /
• 2011

Compressive deformation behavior of Al-10Si-5Fe-1Zr (wt%) alloy preform fabricated by SPS(spark plasma sintering) of gas atomized powder was investigated in the temperature range from 380 to $480^{\circ}C$ and at strain rates from $1.0{\times}10^{-3}$ to $1.0{\times}10^{0}s^{-1}$. Stress-strain curves showed a peak stress (${\sigma}_p$) during initial stage of deformation, followed by a steady state flow at all temperatures and strain rates tested. The (${\sigma}_p$) decreased with both increase in temperature and decrease in strain rate. Nearly full densification was found to occur in the compressively deformed specimens irrespective of test condition. TEM observation revealed a restricted grain growth during steady state flow.

• 한국분말재료학회지
• /
• 제30권1호
• /
• pp.7-12
• /
• 2023

Metal-additive manufacturing techniques, such as selective laser sintering (SLS), are increasingly utilized for new biomaterials, such as cobalt-chrome (Co-Cr). In this study, Co-Cr gas-atomized powders are used as charge materials for the SLS process. The aim is to understand the consolidation of Co-Cr alloy powder and characterization of samples sintered using SLS under various conditions. The results clearly suggest that besides the matrix phase, the second phase, which is attributed to pores and oxidation particles, is observed in the sintered specimens. The as-built samples exhibit completely different microstructural features compared with the casting or wrought products reported in the literature. The microstructure reveals melt pools, which represent the characteristics of the scanning direction, in particular, or of the SLS conditions, in general. It also exposes extremely fine grain sizes inside the melt pools, resulting in an enhancement in the hardness of the as-built products. Thus, the hardness values of the samples prepared by SLS under all parameter conditions used in this study are evidently higher than those of the casting products.

• 한국분말재료학회지
• /
• 제18권2호
• /
• pp.149-158
• /
• 2011

Electro-Discharge Sintering (EDS) employs a high-voltage/high-current-density pulse of electrical energy, discharged from a capacitor bank, to instantaneously consolidate powders. In the present study, a single pulse of 0.57-1.1 kJ/0.45 g-atomized spherical $Ti_{52}Zr_{28}Ni_{20}$ powders in size range of 10~30 and $30\sim50{\mu}m$ consisting of ${\beta}$-(Ti, Zr) and icosahedral phases were applied to examine the structural evolution of icosahedral phase during EDS. Structural investigation reveals that high electrical input energy facilitates complete decomposition of icosahedral phase into C14 laves and ${\beta}$-(Ti, Zr) phases. Moreover, critical input energy inducing decomposition of the icosahedral phase during EDS depends on the size of the powder. Porous Ti and W compacts have been fabricated by EDS using rectangular and spherical powders upon various input energy at a constant capacitance of $450{\mu}F$ in order to verify influence of powder shape on microstructure of porous compacts. Besides, generated heat (${\Delta}H$) during EDS, which is measured by an oscilloscope, is closely correlated with powder size.

• 한국분말재료학회지
• /
• 제22권3호
• /
• pp.197-202
• /
• 2015

In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr- 13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under $45{\mu}m$ and over $180{\mu}m$, and then they were compacted with various pressures and sintered at $1210^{\circ}C$ for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to $79l/min{\cdot}cm^2$. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.

• 한국분말재료학회지
• /
• 제15권2호
• /
• pp.95-100
• /
• 2008

The investigation is to modify the mechanical and chemical properties of Mg alloys using a combination of rapid solidification and surface treatment. As the first approach, $Mg_{95}Zn_{4.3}Y_{0.7}$ was gas atomized and pressure sintered by spark plasma sintering process (SPS), showing much finer microstructure and higher strength than the alloys as cast. Further modification was performed by treating the surface of PM Mg specimen using Plasma electrolytic oxidation (PEO) process. During the PEO processing, MgO layer was initiated to form on the surface of Mg powder compacts, and the thickness and the density of MgO layer were varied with the reaction time. The thickening rate became low with the reaction time due to the limited diffusion rate of Mg ions. The surface morphology, corrosion behavior and wear resistance were also discussed.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.387-390
• /
• 2009

This study was designed to fabricate the micro-electro-mechanical systems (MEMS) parts such as micro spur gears using hot extrusion of gas atomized Al-78Zn powders. For this purpose, it is important to develop new methods to fabricate micro-dies and choose suitable extrusion conditions for a micro-forming. Micro-dies with Ni were fabricated by LIGA technology. LIGA technology was capable to produce micro-extrusion dies with close tolerances, thick bearing length and adequate surface quality. Superplastic Al-78Zn powders have the great advantage in achieving deformation under low stresses and exhibiting good micro formability with average strain rates ranging from $10^{-3}$ to $10^{-2}\;s^{-1}$ and constant temperatures ranging from 503 to 563K. Al-78Zn powders were compacted into a cylindrical shape (${\Phi}3{\times}h10$) under compressive force of 10kN and, subsequently, the compacted powders were extruded at 563k in a hot furnace. Micro-extrusion has succeeded in forming micro-gear shafts.

• 한국군사과학기술학회지
• /
• 제15권3호
• /
• pp.231-240
• /
• 2012

During the past two decades, Metal Injection Molding(MIM) has become a very competitive technology to fabricate small, precise and complex-shaped parts in large quantities. In this research, the applicability of MIM technology in the mass-production of the high precision fuze parts to save manufacturing cost was investigated. The water-atomized 17-4PH stainless steel powder, one of the best corrosion-resistant high strength materials, was injection-molded into real-shape fuze part and flat tensile specimens. The injection-molded parts were thermally debound in hydrogen gas flow without solvent extraction. Sintering of the debound parts was carried out in vacuum at temperatures ranging from $1150^{\circ}C$ to $1370^{\circ}C$. The sintering behavior, mechanical properties, dimensional precision, corrosion resistance of the MIMed 17-4PH stainless parts were investigated. It was found that almost all the properties of the MIMed parts were comparable to those of the mechanically machined parts. Also, actual military field tests using both MIMed and mechanically machined fuze parts were performed as well and were found to be very successful.

• 한국분말재료학회지
• /
• 제11권1호
• /
• pp.34-42
• /
• 2004

The effect of extrusion temperature on the microstructure and mechanical properties were studied in He-gas atomized $Al_{81-(x＋y)}Si_{19}Ni_xCe_y$ alloy powders and their extruded bars using SEM, tensile testing and thermal expansion testing. The extruded bar of $Al_{73}Si_{19}Ni_7Ce_1$ alloy consists of a mixed structure in which fine Si particles with a particle size below 20∼500nm and very fine $Al_3Ni,\;Al_3Ce$ compounds with a particle size below 200nm are homogeneously dispersed in Al martix with a grain size below 500nm. With increasing extrusion temperature, the microstructural scale was decreased. The ultimate tensile strength of the alloy bars has incresed with decreasing extrusion temperature from 500 to 35$0^{\circ}C$ and $Al_{73}Si_{19}Ni_7Ce_1$ alloy extreded at 35$0^{\circ}C$ shows a highest tensile strength of 810 MPa due to the fine namostructure. The addition of Ni and Ce decreased the coefficients of thermal expansion and the effects of extression temperature on the thermal expansion were not significant.