• Corrosion Science and Technology
• /
• v.18 no.6
• /
• pp.285-291
• /
• 2019

In this study, the corrosion characteristics of T22 and T92 steel were investigated in 6O₂ + 16CO₂ + 2SO₂ gas environment at 650 ℃. Corrosion characteristics were characterized by weight gain, oxide layer thickness, scanning electron microscope, optical microscope, energy dispersive X-ray spectroscopy, and X-ray diffraction. T22 and T92 steel tended to stagnate oxide layer growth over time. Oxidation kinetics were analyzed using the data of oxide layer thickness, and a regression model was presented. The regression model was significantly acceptable. The corrosion rate between the two steels through the regression model showed significant difference. The T92 steel was approximately twice as large as the time exponent and showed very good corrosion resistance compared to the T22 steel. In both steels, the oxide layer mainly formed a Fe-rich oxide layer composed of hematite (Fe₂O₃), magnetite (Fe₃O₄), and spinel (FeCr₂O₄). Sulfide segregation occurred in the oxide layer due to SO₂ gas. However, the locations of segregation for the T22 and T92 steel were different.

• Elastomers and Composites
• /
• v.57 no.1
• /
• pp.1-8
• /
• 2022

In this study, the photo-deposition method was used to introduce Ag onto the surface of TiO₂ to synthesize an Ag-TiO₂ composite. The effects of the varying amounts of AgNO₃ precursor and annealing time periods on the Ag content in the composites, as well as their antibacterial characteristics under visible light conditions were studied. SEM analysis revealed the spherical morphology of the Ag-TiO₂ composite. Compared with TiO₂, the Ag particles were too small to be observed. An XPS analysis of the Ag-TiO₂ surface confirmed the Ag content and showed the peak intensities for elements such as Ag, Ti, O, C, and Si. The highest Ag content was observed when 33.3 wt.% of AgNO₃ and an annealing time of 6 h were employed; this was the optimum annealing time for Ti-Ag-O bonding, in that the lowest number of O bonds and the highest number of Ag bonds were confirmed by XPS analysis. Superior antibacterial properties against Bacillus and Escherichia coli, in addition to the widest inhibition zones were exhibited by the Ag-TiO₂ composite with an increased Ag content in a disk diffusion test, the bacterial reduction rate against Staphylococcus aureus and Escherichia coli being 99.9%.

• Journal of Korean Society on Water Environment
• /
• v.35 no.6
• /
• pp.459-469
• /
• 2019

The ozonation of sulfamethoxazole (SMX) was performed at 20℃ using a pilot scale countercurrent bubble column reactor. Ozonation systems were combined with UV irradiation and TiO₂ addition. As the oxidation reaction proceeded in each treatment system, the pH of the sample decreased and in the O₃/UV/TiO₂ system, the pH change was the largest from 4.54 to 2.02. Under these experimental conditions, the scavenger impact of carbonate is negligible. The highest COD and TOC removal rate was observed in the O₃/UV/TiO₂ system due to the UV irradiation and the photocatalytic effect of TiO₂. Also, the highest mineralization ratio(ε) value is 0.2 in the O₃/UV/TiO₂ system, which means theoxidation capacity of the systems. The highest SMX degradation rate constants calculated by COD and TOC values (COD and TOC) were 2.15 × 10^-4 sec^-1 and 1.00 × 10^-4 sec^-1 in the O₃/UV/TiO₂ system, respectively. The activation energy (E_a) of ozone treatment follows the Arrhenius law. It was calculated based on _COD and _TOC. Each activation energy decreased in order of single O₃> O₃/TiO₂> O₃/UV > O₃/UV/TiO₂ system. The result showed that ΔH^≠ is more effective than ΔS^≠ in each SMX ozontaionsystem, that is characteristic of the common oxidation reaction.

• Journal of Conservation Science
• /
• v.36 no.3
• /
• pp.162-177
• /
• 2020

Research was conducted to characterize the copper production and smelting process with 11 copper smelting by-products (copper slag and copper crucible) excavated from the NA and LA areas at the Gwanbuk-ri archeological site in Buyeo. Scanning electron microscopy-energy dispersive spectroscopy, wavelength dispersive X-ray fluorescence, X-ray diffraction, and Raman microspectroscopy were employed in the analysis. The research results reveal that the copper slag from Gwanbuk-ri contained silicate oxide, magnetite, fayalite, and delafossite, which are typical characteristics of crucible slag and refined slag. The outward appearance and microstructure of the slag were grouped as follows: 1. glassy matrix + Cu prill, 2. glassy matrix + Cu prill + magnetite, 3. silicate mineral matrix + Cu prill, 4. crystalline (delafossite and magnetite) + amorphous (Cu prill), 5. magnetite + fayalite, and 6. slag from slag. The copper slags from Guanbuk-ri were found to contain residues of impurities such as SiO₂, Al₂O₃, CaO, SO₄, P₂O₅, Ag₂O, and Sb₂O₃ in their microstructure, and, in some cases, it was confirmed that copper, tin and lead are alloys. These results indicate that refining of intermediate copper(including impurities) and refining of alloys of copper(including impurities) - tin and refining of copper(including impurities) - tin - lead took place during the copper production process at Gwanbuk-ri, Buyeo.

• Journal of the Korean Ceramic Society
• /
• v.49 no.6
• /
• pp.586-591
• /
• 2012

$Zr_2WP_2O_{12}$ powder, which has a negative thermal expansion coefficient, was synthesized by a solid-state reaction with $ZrO_2$, $WO_3$ and $NH_4H_2PO_4$ as the starting materials. The synthesis behavior was dependent on the solvent media used in the wet mixing process. The $Zr_2WP_2O_{12}$ powder prepared with a solvent consisting of D. I. water was fully crystallized at $1200^{\circ}C$, showing a sub-micron particle size. According to the results obtained from a thermal analysis, a $ZrP_2O_7$ was synthesized at a low temperature of $310^{\circ}C$, after which it was reacted with $WO_3$ at $1200^{\circ}C$. A new sintering additive, $Al(OH)_3$, was applied for the densification of the $Zr_2WP_2O_{12}$ powders. The cold isostatically pressed samples were densified with 1 wt% $Al(OH)_3$ additive or more at $1200^{\circ}C$ for 4 h. The main densification mechanism was liquid-phase sintering due to the liquid which resulted from the reaction with amorphous or unstable $Al_2O_3$ and $WO_3$. The densified $Zr_2WP_2O_{12}$ ceramics showed a relative density of 90% and a negative thermal expansion coefficient of $-3.4{\times}10^{-6}/^{\circ}C$. When using ${\alpha}-Al_2O_3$ as the sintering agent, densification was not observed at $1200^{\circ}C$.

• The Plant Pathology Journal
• /
• v.37 no.4
• /
• pp.375-388
• /
• 2021

Rice yellow mottle virus (RYMV) is the most harmful virus that affects irrigated and lowland rice in Africa. The RBe24 isolate of the virus is the most pathogenic strain in Benin. A total of 79 genotypes including susceptible IR64 (Oryza sativa) and the resistant TOG5681 (O. glaberrima) as checks were screened for their reactions to RBe24 isolate of RYMV and the effects of silicon on the response of host plants to the virus investigated. The experiment was a three-factor factorial consisting of genotypes, inoculation level (inoculated vs. non-inoculated), and silicon dose (0, 5, and 10 g/plant) applied as CaSiO₃ with two replications and carried out twice in the screen house. Significant differences were observed among the rice genotypes. Fifteen highly resistant and eight resistant genotypes were identified, and these were mainly O. glaberrima. Silicon application did not affect disease incidence and severity at 21 and 42 days after inoculation (DAI); it, however, significantly increased plant height of inoculated (3.6% for 5 g CaSiO₃/plant and 6.3% for 10 g CaSiO₃/plant) and non-inoculated (1.9% for 5 g CaSiO₃/plant and 4.9% for 10 g CaSiO₃/plant) plants at 42 DAI, with a reduction in the number of tillers (12.3% for both 5 and 10 g CaSiO₃/plant) and leaves (26.8% for 5 g CaSiO₃/plant and 28% for 10 g CaSiO₃/plant) under both inoculation treatments. Our results confirm O. glaberrima germplasm as an important source of resistance to RYMV, and critical in developing a comprehensive strategy for the control of RYMV in West Africa.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.6
• /
• pp.438-441
• /
• 2021

The electrical characteristics of single-crystal composite superconductors produced by a melting process were studied by neutron irradiation. In order to improve the current characteristics of the YBa₂Cu₃O_7-y superconductor, it is necessary to form an effective flux pinning center inside the superconductor. In this study, an increase in flux pinning was attempted through neutron irradiation onto YBa₂Cu₃O_7-y superconductors. The neutron irradiation was performed at 30 MeV for 500 sec, The electrical properties of the superconductors were measured in a magnetic field of 5 Tesla at 50 K using a magnetic properties measurement system (MPMS). After neutron irradiation, the critical current density of the YBa₂Cu₃O_7-y superconductor in a 1 Tesla magnetic field was 1×10⁵ A/cm². Once neutrons were irradiated at 30 MeV and 10 μA for 500 sec, the critical current density was observed to increase significantly. When neutrons are irradiated to a superconductor, micro-defects are created in the superconductor, and they act as flux pinning centers that hold the magnetic field generated when an electric current flows.

• Journal of Wetlands Research
• /
• v.25 no.4
• /
• pp.386-393
• /
• 2023

The domestic marine healing industry is undergoing significant revitalization efforts, with a focus on understanding the efficacy and effectiveness of marine healing resources. This study establishes utilization and management standards through a detailed analysis of the active components within well-recognized marine healing mud materials. Samples of mud materials were collected from domestic tidal flats. These samples exhibited an average composition of 7.87% sand, 74.95% silt, and 17.17% clay, with a combined mud content (silt+clay)(silt+clay) consistently exceeding 90%. Notably, SiO₂ emerged as the most prevalent effective ingredient at 68.4%, followed by Al₂O₃ (13.3%)>Fe₂O₃ (4.0%)>K₂O (2.9%)>Na₂O (2.3%)>MgO (1.6%)>CaO (1.0%)>TiO₂ (0.7%), in terms of average content. Subsequently, through an analysis of effective ingredients, Si, Al, Fe, K, Na, Mg, and Ca were identified as elements demonstrating significant functionality. Among these, key indicator ingredients were selected for quality control, all of which were found to possess efficacious properties. Notably, K, Mg, and Ca exhibited particularly high concentrations. Based on these findings and referencing existing literature, it is recommended that domestic tidal flat mud resources earmarked for utilization as marine healing resources should possess a raw material mud content of no less than 70.0%. Moreover, the cumulative index components K₂O+MgO+CaO should meet or exceed a threshold of 5.0% for optimal effectiveness.

• Journal of the Korean Society of Radiology
• /
• v.9 no.3
• /
• pp.169-174
• /
• 2015

$LiGd_9(SiO_4)_6O_2:Ce^{3+}$ phosphors were synthesized by solid-state reaction method. The structural characteristic was investigated by X-ray powder diffraction analysis. The emission and excitation spectra of the $Ce^{3+}$ ions doped $LiGd_9(SiO_4)_6O_2$ phosphors were obtained under the UV excitation. The emission spectra of $LiGd_9(SiO_4)_6O_2:Ce^{3+}$ shows the band at 410 nm corresponding to the $^2F_{5/2}$ and $^2F_{7/2}$ states of $Ce^{3+}$. The red shift of $Ce^{3+}$ emission is found as the $Ce^{3+}$ concentration increases, which could be explained by the change in crystal-field symmetry and strength with increasing $Ce^{3+}$ concentration. Fluorescence decay time of $Ce^{3+}$ was about 20 ns. When the concentration of $Ce^{3+}$ increases life time was slightly reduced.

• Journal of Surface Science and Engineering
• /
• v.52 no.6
• /
• pp.298-305
• /
• 2019

We investigated a correlation between morphology and photoelectrochemical properties of TiO₂ nanotubes fabricated by well-controlled anodization processes. Anodization in an ethylene-glycol-based electrolyte solution accelerated the rapid grow rate of TiO₂ nanotubes, but also cause problems such as delamination at the interface between TiO₂ nanotubes and a Ti substrate, and debris on the top of the nanotube. The applied voltages for the anodization of TiO₂ were adjusted to avoid the interface delamination. The heat treatment and the anodizing time were also controlled to enhance the crystallinity of the as-prepared TiO₂ nanotubes and to increase the surface area with the varied length of the anodized TiO₂ nanotubes. Additionally, a 2-step anodization process was utilized to remove the debris on the tube top. The photoelectrochemical properties of TiO₂ nanotubes prepared with the carefully tailored conditions were investigated. By removing the debris on TiO₂ nanotubes, applied bias photon-to-current efficiency (ABPE) of TiO₂ nanotubes increased up to 0.33%.