• Tribology and Lubricants
• /
• v.26 no.1
• /
• pp.14-20
• /
• 2010

Tribological properties of nanoporous structured alumina film was investigated. Alumina film (AAO: anodic aluminum oxide) of $60{\mu}m$ thickness having nanopores of 45 nm diameter with 105 nm interpore-diatance was fabricated by mild anodization process. Reciprocating ball-on-flat sliding friction tests using 1 mm diameter steel ball as a counterpart were carried out with wide range of normal load from 1 mN to 1 N in an ambient environment. The morphology of worn surfaces were analyzed using scanning electron microscopy. The friction coefficient was strongly influenced by the applied normal load. Smooth layer patches were formed on the worn surface of both AAO and steel ball at relatively high load (100 mN and 1 N) due to tribochemical reaction and compaction of wear debris. These tribolayers contributed to the lower friction at high loads. Extremely thin layer patches, due to mild plastic deformation of surface layer, were sparsely distributed on the worn surface of AAO at low loads (1 mN and 10 mN) without the evidence of tribochemical reaction. Delaminated wear particles were generated at high loads by fatigue due to repeated loading and sliding.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.6
• /
• pp.394-398
• /
• 2014

We fabricated the electrolyte-dielectric-metal (EDM) sensor on the base of AAO (anodic aluminum oxide) template with variation of the anodizing temperature. When a surface is immersed or created in an aqueous solution, a discontinuity is formed at the interface where such physicochemical variables as electrical potential and electrolyte concentration change significantly from the aqueous phase to another phase. Because of the different chemical potentials between the two phases, charge separation often occurs at the interfacial region [1]. This interfacial region, togeter with the charged surface, is usually known as the electrical double layer (EDL) [2]. The structural and electrochemical properties of AAO sensor were investigated for applications in capacitive pH sensors. To change the thickness of the AAO template, the anodizing temperature was varied from $5^{\circ}C$ to $20^{\circ}C$, the thickness of the AAO template invreased from 300 nm to 477 nm. The pH sensitivity of sensors with the anodizing temperature of $20^{\circ}C$ showed the highest value of 56.4 mV/pH in the pH range of 3 to 11. The EDM sensor with the anodizing temperature of $20^{\circ}C$ exhibited the best long-term stability of 0.037 mV/h.

• Transactions of Materials Processing
• /
• v.29 no.3
• /
• pp.127-134
• /
• 2020

It is known that the difference of texture of the polycrystalline Al sheet is not a critical parameter for the formation of aligned nanopore arrays in anodic aluminum oxide (AAO). This will be related to the polycrystalline grain in the Al sheet. The texture of each grain in the polycrystalline Al sheet is different. The mixed textures of grains have the mixing effects on the nanopore structure of the AAO. Thus, the effect of Al texture on the nanopore structure of the AAO was investigated using three types of Al single crystals with (111), (200) and (220) textures in this paper. These three types of AAO layers were fabricated by the two-step anodizing method at 40 V and temperature of 0-5℃ in oxalic acid solution. In the nanopores formed on the AAO, the average area of one nanopore and the average roundness of one nanopore were measured were measured based on the SEM images. In the hexagon obtained by connecting nanopores on the AAO, the average standard deviation of one angle deviated from 120° was measured. In the AAO nanopores with texture of (111), (200) and (220) single crystal samples, the average area of one nanopore of (200) single crystal sample was the widest, followed by (111), (220) single crystals. The average circularity of one nanopore of (200) single crystal sample was the best, followed by (111), (220) single crystals. The average standard deviation of an angle from 120° of (220) single crystal sample was the largest, followed by (111) and (200) single crystals.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.480-480
• /
• 2011

양극산화(anodization)는 금속을 전기화학적으로 산화시켜 금속산화물로 만드는 기술로서 최근 다양한 크기의 나노 구조를 제조하는 기술로 각광받고 있으며, 이러한 기술에 의하여 얻어지는 anodic aluminum oxide(AAO)는 magnetic data storage, optoelectronic device, sensor에 적용될 수 있는 nano device 뿐만 아니라 nanostructure를 제조하기 위한 template 및 mask로써 최근 광범위 하게 연구되고 있다. 또한, AAO는 Al2O3의 단단한 구조를 가진 무기재료이므로 solid mask로써 다른 porous materials 보다 뛰어난 특성을 갖고 있다. 또한 electron-beam lithography 및 block co-polymer 에 의한 patterning 과 비교하여 매우 경제적이며, 재현성이 우수할 뿐만 아니라 대면적에서 나노 구조의 크기 및 형상제어가 비교적 쉽기 때문에 널리 사용되고 있다. 그러나, AAO 형성 시 생기게 되는 반구형 모양의 barrier layer는 물질(substance)과 기판과의 direct physical and electrical contact을 방해하기 때문에 해결해야 할 가장 큰 문제점 중 하나로 알려져 있다. 따라서 본 연구에서는 실리콘 기판위의 형성된 AAO의 barrier layer를 Cl/BCl3 gas mixture에서 Neutral Beam Etching (NBE)과 Ion Beam Etching (IBE) 로 각각 식각한 후 그 결과와 비교하였다. NBE와 IBE 모두 Cl2/BCl3 gas mixture에서 BCl3 gas의 첨가량이 60% 일 경우 etch rate이 가장 높게 나타났고, optical emission spectroscopy (OES)로 Cl2/BCl3 플라즈마 내의 Cl radical density와 X-ray photoelectron spectroscopy (XPS)로 AAO 표면 위를 관찰한 결과 휘발성 BOxCly의 형성이 AAO 식각에 크게 관여함을 확인 할 수 있었다. 또한, NBE와 IBE 실험한 다양한 Cl2/BCl3 gas mixture ratio 에서 AAO가 식각이 되지만, 이온빔의 경우 나노사이즈의 AAO pore의 charging에 의해 pore 아래쪽의 위치한 barrier layer를 어떤 식각조건에서도 제거하지 못하였다. 하지만, NBE에서는 BCl3-rich Cl2/BCl3 gas mixture인 식각조건에서 AAO pore에 휘발성 BOxCly를 형성하면서 barrier layer를 제거할 수 있었다.

• Korean Chemical Engineering Research
• /
• v.53 no.3
• /
• pp.401-406
• /
• 2015

Getter is a class of materials used in absorbing gases such as hydrogen and moisture in microelectronics or semiconductor devices to operate properly. In this study, we developed a new device structure consisting of porous anodized alumina films on textured silicon wafer, which have cost efficiency in materials and processing aspects. Anodic aluminum oxide (AAO) with controlled pore sizes can be applied to a high-efficiency moisture absorber due to the high surface area and OH- saturated surface property. The moisture sorption capacity was 2.02% (RH=35%), obtained by analyzing isothermal adsorption/desorption curve.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.18 no.9
• /
• pp.2197-2202
• /
• 2014

In this paper, we report on an investigation of highly sensitive sensing performance of a hydrogen sensor composed of palladium (Pd) nanowires. The Pd nanowires have been grown by electrodeposition into nanochannels and liberated from the anodic aluminum oxide (AAO) template by dissolving in an aqueous solution of NaOH. A combination of photo-lithography, electron beam lithography and a lift-off process has been utilized to fabricate the sensor using the Pd nanowire. The hydrogen concentrations for 2% and 0.1% were obtained from the sensitivities (${\Delta}R/R$) for 1.92% and 0.18%, respectively. The resistance of the Pd nanowires depends on absorption and desorption of hydrogen. Therefore, we expect that the Pd nanowires can be applicable for detecting highly sensitive hydrogen gas at room temperature.

• Membrane Journal
• /
• v.22 no.1
• /
• pp.35-45
• /
• 2012

We prepared the highly ordered nano-wires of polypyrrole, polyaniline conductive polymers and polypyrrole/ polyaniline conductive copolymers by templating the anodic aluminum oxide (AAO) porous membrane, in which pore diameter was 20 nm, 100 nm and 200 nm. Those conductive polymers were grown from pore inner surface of AAO membrane forming hollow tubes and then wire structures were formed after 3 hour polymerization. By removing AAO membrane templates using sodium hydroxide solution, the conductive polymer nano-wires were successfully obtained, of which diameter and length were close to the ones of nano-pores in AAO membrane template. Crystallinity and thermal stability of the conductive polymer nano-wires were higher than irregular ones that prepared by solution polymerization. Furthermore, the electrical resistance of conductive polymer nano-wires were reduced by about 4~60% compared with that of the irregular polymers prepared by solution polymerization.

• Journal of the Semiconductor & Display Technology
• /
• v.17 no.4
• /
• pp.11-15
• /
• 2018

The parts of equipment for semiconductor are protected by anodic aluminum oxide film to prevent corrosion. This study investigated contamination particle and cracking behavior of anodic oxidation in sulfuric acid containing cerium salt. The insulating properties of the sample were evaluated by measuring the breakdown voltage. It was confirmed that the breakdown voltage was about 50% higher when the cerium salt was added, and that the breakdown voltage after the heat treatment was 55% and 35% higher at $300^{\circ}C$ and $400^{\circ}C$, respectively. After heating at $300^{\circ}C$ and $400^{\circ}C$, cracks were observed in non cerium and cerium 3mM, and more cracks occur at $400^{\circ}C$ than at $30^{\circ}C$. The amount of contamination particles generated in the plasma is about 45% less than that of non-cerium specimens.

• Applied Chemistry for Engineering
• /
• v.20 no.2
• /
• pp.191-194
• /
• 2009

Porous alumina prepared by anodization has been widely studied since it shows very regular nanostructures at inexpensive prices. In this article, porous alumina is obtained by anodization of aluminum in the oxalic acid. After the first formed oxide is selectively removed from the aluminum substrate, the hexagonal nanostructures on the fresh aluminum are converted to nanodots by the second anodization in boric acid. Nanodots are arrayed in the convex of the hexagonal nanostructures. The optimization condition for the fabrication of nanodots with a height of 20 nm is investigated in detail. Subsequently, a gold film is deposited on the nanodots, resulting in the formation of gold nanodots arrays which are probably interesting substrate for biosensor applications.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.166-167
• /
• 2007

본 연구에서는 Anodic Aluminum Oxide(AAO)-Nano Template 제조 시 알루미늄의 결정방위가 AAO 미세공 형성에 미치는 영향을 연구하였다. 시료는 직경 20mm 두께 2mm의 (200), (220), (111) 세가지 알루미늄 단결정 시편을 사용 하였으며 이는 XRD 장비로 단결정임을 확인 하였다. 양극산화에 앞서 평활한 면을 얻기 위해 다이아몬드 콤파운드($1{\mu}m$)로 미세연마 하였으며 양극산화는 세가지 시편에 대해 모두 동일한 조건에서 2단계 양극산화까지 하였다. 결과는 주사전자현미경(FE-SEM)으로 제조된 AAO 표면의 세공형태와 단면을 모두 관찰 하였으며 그 결과 (200) 결정방위가 (220), (111) 결정 방위보다 세공 형태 균일도 및 단면 정열도와 직진성이 우수함을 관찰 할 수 있었다.