• Journal of Powder Materials
• /
• v.7 no.2
• /
• pp.85-92
• /
• 2000

The Cu55Ti45 system was effectively mechanically-alloyed using a pulverizer. Noncrystallinities of the powders were characterized by TEM, X-ray and DSC. The amorphous powders were consolidated without losing their noncrystallinities. The consolidating conditions keeping a non-crystalline were obtained by building a TTT diagram of the amorphous powders. The microhardness of the crystallite and bulk amorphous alloys are also compared.

• Journal of Powder Materials
• /
• v.16 no.5
• /
• pp.316-325
• /
• 2009

Fe based (Fe$_{68.2}$C$_{5.9}$Si$_{3.5}$B$_{6.7}$P$_{9.6}$Cr$_{2.1}$Mo$_{2.0}$Al$_{2.0}$) amorphous powder, which is a composition of iron blast cast slag, were produced by a gas atomization process, and sequently mixed with ductile Cu powder by a mechanical ball milling process. The experiment results show that the as-prepared Fe amorphous powders less than 90 $\mu$m in size has a fully amorphous phase and its weight fraction was about 73.7%. The as-atomized amorphous Fe powders had a complete spherical shape with very clean surface. Differential scanning calorimetric results of the as-atomized Fe powders less than 90 $\mu$m showed that the glass transition, T$_g$, onset crystallization, T$_x$, and super-cooled liquid range $\Delta$T=T$_x$-T$_g$ were 512, 548 and 36$^{\circ}C$, respectively. Fe amorphous powders were mixed and deformed well with 10 wt.% Cu by using AGO-2 high energy ball mill under 500 rpm.

• Journal of Powder Materials
• /
• v.16 no.5
• /
• pp.326-335
• /
• 2009

Fe based (Fe$_{68.2}$C$_{5.9}$Si$_{3.5}$B$_{6.7}$P$_{9.6}$Cr$_{2.1}$Mo$_{2.0}$Al$_{2.0}$) amorphous powder, which is a composition of iron blast cast slag, were produced by a gas atomization process, and sequently mixed with ductile Cu powder by a mechanical ball milling process. The Fe-based amorphous powders and the Fe-Cu composite powders were compacted by a spark plasma sintering (SPS) process. Densification of the Fe amorphous-Cu composited powders by spark plasma sintering of was occurred through a plastic deformation of the each amorphous powder and Cu phase. The SPS samples milled by AGO-2 under 500 rpm had the best homogeneity of Cu phase and showed the smallest Cu pool size. Micro-Vickers hardness of the as-SPSed specimens was changed with the milling processes.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.848-849
• /
• 2006

Bulk metallic glass (BMG) composites combining a $Cu_{54}Ni_6Zr_{22}Ti_{18}$ matrix with brass powders or $Zr_{62}A_{l8}Ni_{13}Cu_{17}$ metallic glass powders were fabricated by spark plasma sintering. The brass powders and Zr-based metallic glass powders added for the enhancement of plasticity are well distributed homogeneously in the Cu-based metallic glass matrix after consolidation. The BMG composites show macroscopic plasticity after yielding, and the plastic strain increased to around 2% without a decrease in strength for the composite material containing 20 vol% Zr-based amorphous powders. The proper combination of strength and plasticity in the BMG composites was obtained by introducing a second phase in the metallic glass matrix.

• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.36-43
• /
• 2010

In present work, amorphous TiCuNi powders were fabricated by mechanical alloying process. Amorphization and crystallization behaviors of the TiCuNi powders during high-energy ball milling and subsequent microstructure changes were studied by X-ray diffraction and transmission electron microscope. TEM samples were prepared by the focused ion beam technique. The morphology of powders prepared with different milling times was observed by field-emission scanning electron microscope and optical microscope. The powders developed a fine, layered, homogeneous structure with milling times. The crystallization behavior showed that glass transition, $T_g$, onset crystallization, $T_x$, and super cooled liquid range ${\Delta}T=T_x-T_g$ were 628, 755 and 127K, respectively. The as-prepared amorphous TiCuNi powders were consolidated by spark plasma sintering process. Full densified TiCuNi samples were successfully produced by the spark plasma sintering process. Crystallization of the MA powders happened during sintering at 733K.

• Journal of the Korean Ceramic Society
• /
• v.28 no.11
• /
• pp.892-896
• /
• 1991

The cyrstallization behavior of lead titanate powders prepared by sol-gel and coprecipitation techniques was investigated. The lead titanate precursors were derived from a mixed solution of lead nitrate and titanium tetrachloride at 4$0^{\circ}C$ to 43$^{\circ}C$ and pH of 9.00 to 9.75. The X-ray diffraction patterns of the dried gel and coprecipitated powders showed it to be amorphous. DTA runs of the powders indicated crystallization to occur at 475~48$0^{\circ}C$. However, the amorphous powders were partially crystallized at 400~45$0^{\circ}C$ with sufficient annealing time. The room temperature Raman spectra from heat-treated powders changed continuously from amorphous to crystalline state with increasing heat-treating temperature. By annealing coprecipitated powders, a dramatic change in the Raman spectra due to the structural relaxation as the annealing temperatures increased, was clearly visible. i.e., coprecipitated, gel, and crystalline structure, in turn.

• Journal of Powder Materials
• /
• v.15 no.4
• /
• pp.285-291
• /
• 2008

Fe based ($Fe_{68.2}C_{5.9}Si_{3.5}B_{6.7}P_{9.6}Cr_{2.1}Mo_{2.0}Al_{2.0}$) amorphous powder were produced by a gas atomization process, and then ductile Cu powder fabricated by the electric explosion of wire(EEW) were mixed in the liquid (methanol) consecutively. The Fe-based amorphous - nanometallic Cu composite powders were compacted by a spark plasma sintering (SPS) processes. The nano-sized Cu powders of ${\sim}\;nm$200 produced by EEW in the methanol were mixed and well coated with the atomized Fe amorphous powders through the simple drying process on the hot plate. The relative density of the compacts obtained by the SPS showed over 98% and its hardness was also found to reach over 1100 Hv.

• Journal of Welding and Joining
• /
• v.17 no.4
• /
• pp.53-59
• /
• 1999

Amorphous alloys have also been called glassy alloys or non-crystalline alloys. They are made by the rapid solidification. The solidification occurs so rapid that the atoms are frozen in their liquid configuration. There are unique magnetic, mechanical, electrical and corrosive behaviors which result form their amorphous structure. In the study. amorphous coatings were manufactured with Ni-Cr-B-Si powders by flame spray. Measurement of hardness, were resistance, corrosion resistance and observation of microstructures and XRD, DSC were performed to investigate characteristics of amorphous coatings. The experimental results obtained as follow: 1) Amorphous powders could not be manufactured with the spraying in the spraying in the liquid nitrogen. But, amorphous coatings could be manufactured with the rotation cooling method by liquid nitrogen. In the fabrication of amorphous coatings, major factor was the rapid cooling by rotation of the substrate. 2) Hardness of coatings was obtained Hv 960 by formation of amorphous phase. But, wear resistance decreased. That was due to porosity in the coatings by the rapid cooling. 3) In the case of corrosion resistance, amorphous coatings were superior to air-cooled coatings. That was due to formation of amorphous phase. 4) After amorphous coatings were heat-treated at 520℃ for 1hr. hardness increased 80% and wear resistance increased 30% comparing with air cooled coatings. These were due to crystallization of amorphous phase and decrease of porosity by heat-treatment.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.625-631
• /
• 2000

In this study, the characteristics and sinterablities of TiO2 powders which were fabricated on sol-gel process and supercritical fluid process were examined. The powders fabricated on sol-gel process were amorphous. The particle size and shape were changed with the amount of water used for hydrolysis of titanium ethoxide. The powders were changed from amorphous to crystalline by heating at 400℃. The crystalline anatase TiO2 powders were directly prepared in ethanol supercritical fluid condition that temperature was 270±3℃ and pressure was 7.3 MPa. It's primary crystalline size was 20 nm and agglomerated as spherical shape whose size was 0.7∼1㎛. The powders prepared on sol-gel process were not sintered densely at 900℃ because of abnormal grain growth. However, the powders which prepared on supercritical fluid process were sintered densely at the comparatively low temperature of 800℃ by ideal growth of grain, which are fired at 900℃.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.936-936
• /
• 2006

Bulk amorphous materials have been intensively studied to apply for various advanced industry fields due to their high mechanical, chemical and electrical properties. These materials have been produced by several techniques such as mechanical alloying, melt spinning and gas atomization, etc. Among them, the atomization is the most potential technique for commercialization due to high cooling rate during solidification of the melt and mass productivity. However, the amorphous powders still have some limitations because of their low ductility and toughness. Therefore, intensive efforts have to be carried out to increase the ductility and toughness. In this study, the Ni-based amorphous powder was produced by the gas atomization process. And in order to increase the ductile toughness, ductile Cu phase was coated on the Ni amorphous powder by spray drying process. The characteristics of the as-synthesis powders have been examined and briefly mentioned. The master alloy with $Ni_{57}Zr_{20}Ti_{16}Si_2Sn_3$ was prepared by vacuum induction melting furnace with graphite crucible and mold. The atomization was conducted at $1450^{\circ}C$ under the vacuum of $10^{-2}$ torr. The gas pressure during atomization was varied from 35 to 50 bars. After making the Ni amorphous powders, the spray drying was processed to produce the Cu -coated Ni amorphous composite powder. The amorphous powder and Cu nitrate solution were mixed together with a small amount of binder and then it was sprayed at temperature of $130^{\circ}C$ and rotating speed of 15,000 R.P.M.