• 한국주조공학회지
• /
• 제26권3호
• /
• pp.123-128
• /
• 2006

Mechanical and thermal properties of spray-cast hypereutectic Al-20wt.%Si-xwt.%Fe alloys (x=0, 1, 3, 5) were investigated. After the spray-casting, hot extrusion was performed at $400^{\circ}C$. Intermetallic compound (${\beta}-Al_5FeSi$) and primary Si are observed in the spray-cast aluminum alloys. The size of primary Si and intermetallic compound of the spray-aluminum alloys became finer and more uniformly distributed than that of the permanent mold cast ones. Ultimate tensile strength of the spray-cast aluminum alloys increased by increasing Fe contents, but that of the permanent mold cast aluminum alloys decreased by increasing Fe contents possibly due to increased amount of coarse intermatallic compound. The coefficient of thermal expansion (CTEs) of the aluminum alloys became lower with finer primary Si and intermetallic compound, and this is attributed to the increased amount of interfacial area between the aluminum matrix and the phases of finer Si and intermetallic compound.

• 청정기술
• /
• 제18권1호
• /
• pp.63-68
• /
• 2012

본 연구에서는 베이어공정에 의해서 수산화알루미늄($Al(OH)_3$)을 합성하였으며, 고순도 알루미나를 합성하기 위하여 염산 및 초산과 같은 산성용액을 사용하여 $Al(OH)_3$에 함유된 나트륨을 제거하였다. 호주의 퀸즐랜드 주에서 생산된 보크사이트가 베이어공정에 의해 알루미나를 합성하기 위해 사용되었으며, 보크사이트는 attrition mill을 이용하여 10 ${\mu}m$ 이하의 분말로 분쇄하여 사용되었다. 보크사이트에 함유된 알루미나 성분을 용출하기 위하여 분쇄된 보크사이트를 5 N의 NaOH 수용액으로 처리하였으며, 고압반응기 내에서 보크사이트로부터 알루미나의 용출은 $140^{\circ}C$, 3.4 atm에서 수행되었다. 용출 후 고체시료인 레드 머드는 여과에 의해서 액체시료와 분리되었다. 보크사이트와 여과된 레드 머드에 함유된 알루미늄 함량과 구조변화를 XRD와 EDX로 분석하였다. 또한 분리된 용액에 함유된 알루미나는 씨드 물질로 사용된 $Al(OH)_3$의 첨가에 위해서 $Al(OH)_3$로 결정화되었다. 결정화 과정에서 얻어진 $Al(OH)_3$는 증류수에 의해서 수차례 수세과정으로 정제되었다. 또한 산성 용액에 의해서 $Al(OH)_3$에 함유된 나트륨이 제거되는 것을 확인되었다. $Al(OH)_3$ 분말의 순도는 물에 의한 세정으로 99.3%로 생산되었고, 산 처리에 의해서 나트륨의 함량은 약 0.009% 정도로 감소되었다.

• 한국주조공학회지
• /
• 제29권1호
• /
• pp.45-51
• /
• 2009

Conventionally, Al-Sn bearing manufacturing involves casting the Al-Sn alloy and roll-bonding to a steel backing strip. This article will describe the microstructural control of Al-Sn metal bearing alloy following heat treatment. When the pure aluminum rod dipped in the melt of tin maintained below the melting point of aluminum, the melting of aluminum was accelerated with penetration of tin along the grain boundary of aluminum. The length of plate-shaped eutectic tin was decreased with heat treatment time. With even longer heat treatment time over 1 hour the length of eutectic tin didn't decrease any more, while resulting in coarsening of aluminum matrix. Exuded liquid of eutectic tin was formed at the surface of Al-Sn alloy after heat treatment even at below eutectic temperature.

• Corrosion Science and Technology
• /
• 제21권1호
• /
• pp.9-20
• /
• 2022

The aim of this paper is to study corrosion inhibition of Aluminum with Capparis decidua extract. The study was performed in a 1.0 M solution of hydrochloric acid (HCl) and was monitored both by measuring mass loss and by using electrochemical and polarization methods. A scanning electron microscopy (SEM) technique was also applied for surface morphology analysis. The results revealed high inhibition efficiency of Capparis decidua extract. Our data also determined that efficiency is governed by temperature and concentration of extract. Optimum (88.2%) inhibitor efficiency was found with maximum extract concentration at 45 o C. The results also showed a slight diminution of aluminum dissolution when the temperature is low. Based on the Langmuir adsorption model, Capparis decidua adsorption on the aluminum surface shows a high regression coefficient value. From the results, the activation enthalpy (∆H#) and activation entropy (∆S#) were estimated and discussed. In conclusion, the study clearly shows that Capparis decidua extract acted against aluminum corrosion in acidic media by forming a protective film on top of the aluminum surface.

• 한국결정성장학회지
• /
• 제18권1호
• /
• pp.50-55
• /
• 2008

졸-겔 공정을 이용하여 유리기판 위에 Al-doped ZnO(AZO) 박막을 제조하였고, AZO 박막의 특성에 대하여 Al 전구체 종류 및 post-annealing 온도가 미치는 영향에 대하여 고찰하였다. AZO 박막 제조용 졸은 zinc acetate, EtOH, MEA 등을 사용하여 제조하였고, Al doping 을 위한 전구체로는 aluminum nitrate 와 aluminum chloride 를 사용하였다. Sol 내의 Zn 농도는 0.5 mol/l 로 하였고, Al doping 양은 Zn 대비 1 at%로 고정하였다. 유리기판 위에 졸을 spin-coating 한 후 $550^{\circ}C$에서 2 시간 동안 열처리한 후, $N_2$와 $H_2$의 비가 9 : 1인 환원 분위기 내에서 $300^{\circ}C,\;400^{\circ}C,\;500^{\circ}C$인 온도에서 2시간 동안 post-annealing을 진행하였다. 제조된 AZO 박막의 구조적, 전기적, 광학적 특성은 XRD, FE-SEM, AFM, Hall effect measurement system 및 UV-Visible spectroscopy를 이용하여 분석하였다. Al 전구체로서 aluminum nitrate 를 사용한 경우가 aluminum chloride 를 사용하여 제조한 AZO 박막보다 우수한 광학적, 전기적 특성을 나타내었으며, post-annealing 온도가 증가함에 따라 비저항과 투과율은 감소하였다. $500^{\circ}C$에서 post-annealing한 AZO 박막의 전기비저항 값은 $2{\times}10^{-3}{\Omega}{\cdot}cm$이었고, 투과율은 $300^{\circ}C$에서 91%로 가장 높게 나타났다.

• 한국환경생태학회지
• /
• 제6권1호
• /
• pp.9-11
• /
• 1992

목본식물에 대한 Al독성에 관한 기초자료를 얻고자, Al농도별(1.0, 2.5및 5.0mM)수용액과 지하수에 수경삽목한 개나리삽수의 생장관련형질(신초의 생장, 엽수, 엽피해율 및 엽록소함량)을 처리간 비교하였다. 모든 생장관련형질들(신초의 생장, 엽수, 엽피해율 및 엽록소함량)에서 처리간 고도의 통계적 유의차가 인정되었으며. 1.0mM 정도의 Al수용액도 개나리삽수의 생장을 현저히 억제하였다.

• 한국재료학회지
• /
• 제21권2호
• /
• pp.106-110
• /
• 2011

A high thermal conductive AlN composite coating is attractive in thermal management applications. In this study, AlN-YAG composite coatings were manufactured by atmospheric plasma spraying from two different powders: spray-dried and plasma-treated. The mixture of both AlN and YAG was first mechanically alloyed and then spray-dried to obtain an agglomerated powder. The spray-dried powder was primarily spherical in shape and composed of an agglomerate of primary particles. The decomposition of AlN was pronounced at elevated temperatures due to the porous nature of the spray-dried powder, and was completely eliminated in nitrogen environment. A highly spherical, dense AlN-YAG composite powder was synthesized by plasma alloying and spheroidization (PAS) in an inert gas environment. The AlN-YAG coatings consisted of irregular-shaped, crystalline AlN particles embedded in amorphous YAG phase, indicating solid deposition of AlN and liquid deposition of YAG. The PAS-processed powder produced a lower-porosity and higher-hardness AlN-YAG coating due to a greater degree of melting in the plasma jet, compared to that of the spray-dried powder. The amorphization of the YAG matrix was evidence of melting degree of feedstock powder in flight because a fully molten YAG droplet formed an amorphous phase during splat quenching.

• Journal of Welding and Joining
• /
• 제22권5호
• /
• pp.46-52
• /
• 2004

AlSi-Al$_2$O$_3$ composite layer was prepared by plasma spray on steel substrate. The composite powder for plasma spray was prepared by simple mechanical blending. The wear resistance of the composite layers and matrix aluminum alloy were performed in terms of size distribution of ceramic particles. Friction coefficients of AlSi were decreased with incorporation of $Al_2$O$_3$. The tribological properties of coated layers were affected by the size of incorporated $Al_2$O$_3$ particle. The reinforcement of $Al_2$O$_3$ particle into aluminum alloy matrix decreased the friction coefficient as well as wear loss.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1999년도 춘계학술대회논문집
• /
• pp.71-75
• /
• 1999

An approximate similarity theory has been applied to predict the forming load of non-axisymmetric forging of aluminum alloys through model material tests. The approximate similarity theory is applicable when strain rate sensitivity geometrical size and die velocity of model materials are different from those of real materials. Actually the forming load of yoke which is an automobile part made of aluminum alloys(Al-6061) is predicted by using this approximate similarity theory. Firstly upset forging tests are have been carried out to determine the flow curves of three model materials and aluminum alloy(Al-6061) and a suitable model material is selected for model material test of Al-6061 And then and forging tests of aluminum yokes have been performed to verify the forming load predicted from the model material which has been selected from above upset forging tests, The forming loads of aluminum yoke forging predicted by this approximate similarity theory are in good agreement with the experimental results of Al-6061 and the results of finite element analysis using DEFORM-3D.

• 대한기계학회논문집
• /
• 제17권12호
• /
• pp.3083-3093
• /
• 1993

Friction and wear at ceramic coated surfaces of aluminum alloy were experimentally studied using a Ring-on-Block wear test machine. Ceramic materials coated on aluminum alloy surfaces were WC, CrC, $Al_{2}O_{3}$ by a plasma spray; and $Al_{2}O_{3}$,$Al_{2}SiO_{5}$, $Na_{2}B_{4}O_{7}$,$Na_{4}P_{2}O_{7}$, and $Al_{2}O_{3}-ZrO_{2}$ composite coating by an Anodic Spark Depositon. They were tested under the sliding wet contact and compared with aluminum alloys and steels. Test results showed that ceramic coated surfaces, in general, have better anti-wear property than those of aluminum alloys due to increase in the surface hardness ; however, they also showed higher coefficients of friction and changes in wear mechanisms, resulting in brittle fractures.