• Clean Technology
• /
• v.18 no.1
• /
• pp.63-68
• /
• 2012

In this study, aluminum hydroxide ($Al(OH)_3$) was synthesized by Bayer process and sodium contained in $Al(OH)_3$ was removed with the acid solution such as HCl and acetic acid for the synthesis of high purity alumina. The bauxite produced in Queensland of Australia was used for the production of alumina by Bayer, and was crushed to a particle size of below 10 um by attrition mill. The crushed bauxite was treated in sodium hydroxide solution of 5 N for the elution of aluminum component. The elution of aluminum from bauxite was carried out at $140^{\circ}C$ and 3.4 atm in autoclave. The sample solution was separated to the red mud and liquid solution by filter paper. The elution of aluminum from bauxite was confirmed with changing a structure and aluminum content in both bauxite and red mud analyzed by XRD and EDX. Aluminum contained in the separated solution was crystallized to $Al(OH)_3$ with the addition of aluminum hydroxide used as the seed material. $Al(OH)_3$ powder obtained during the crystallization process was purified by several times washing with distillated water. It was also confirmed that the sodium remained in $Al(OH)_3$ powder is removed with acid solution. The purity of $Al(OH)_3$ powder produced in this study was 99.3% and the content of sodium was reduced to approximately 0.009% after the acid treatment.

• Particle and aerosol research
• /
• v.8 no.4
• /
• pp.173-180
• /
• 2012

SiC particles, 8.3 ${\mu}m$ in volume average diameter, were chlorinated in an alumina tubular reactor, 2.4 cm in diameter and 32 cm in length, with reactor temperature varied from 100 to $1200^{\circ}C$. The flow rate of the gas admitted to the reactor was held constant at 300 cc/min, the mole fraction of chlorine in the gas at 0.1 and the reaction time at 4 h. The chlorination was negligibly small up to the temperature of $500^{\circ}C$. Thereafter, the degree of chlorination increased remarkably with increasing temperature until $900^{\circ}C$. As the temperature was increased further from 900 to $1200^{\circ}C$, the increments in chlorination degree were rather small. At $1200^{\circ}C$, the chlorination has nearly been completed. The surface area of the residual carbon varied with chlorination temperature in a manner similar to that with the variation of chlorination degree with temperature. The surface area at $1200^{\circ}C$ was 912 $m^{2}/g$. A simple model was developed to predict the conversion of a SiC under various conditions. A Langmuir-Hinshelwood type rate law with two rate constants was employed in the model. Assuming that the two rate constants, $k_{1}$ and $k_{2}$, can be expressed as $A_{1e}^{-E_{1}/RT}$ and $A_{2e}^{-E_{2}/RT}$, the four parameters, $A_{1}$, $E_{1}$, $A_{2}$, and $E_{2}$ were determined to be 32.0 m/min, 103,071 J/mol, 2.24 $m^{3}/mol$ and 39,526 J/mol, respectively, through regression to best fit experimental data.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.5
• /
• pp.234-239
• /
• 2002

The spinel was calcined at temperatures in the range of $1000^{\circ}C$ to $1300^{\circ}C$ with $100^{\circ}C$ interval to evaluate the effect of calcination temperature on mechanical properties of spinel-glass dental composites. Although the average particle size of spinel calcined at temperatures from $1000^{\circ}C$ to $1200^{\circ}C$ was within 2.8~3.0 $\mu\textrm{m}$, the spinel calcined at $1300^{\circ}C$ was 4.66 $\mu\textrm{m}$ due to abnormal grain growth. Shrinkage and pore size of the spinel preform decreased and increased, respectively, as calcination temperature increased, indicating that the calcination temperature was significant to the powder compaction and the densification of the composites as a result of particle size and distribution. The optimum strength and the fracture toughness of the composite calcined at $1200^{\circ}C$ were 284$\pm$40 MPa, 2.5$\pm$0.1 MPaㆍ$m^{1/2}$ respectively. Optical experimental results showed that transmittance of the spinel-glass composite in the visible region was twice higher than that of the alumina-glass composite, suggesting that the spinel-glass composites possessed better aesthetic properties for all-ceramic dental crown application.

• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.634-641
• /
• 2004

The photocatalytic performance of $TiO_2$ thin films coated on porous alumina balls using various aqueous $TiOCl_2$ solutions as starting precursors, to which 1.0 $mol\%$ transition metal ($Ni^{2+},\;Cr^{3+},\;Fe^{3+},\;Nb^{3+},\;and\;V^{5+}$) chlorides had been already added, has been investigated, together with characterizations for $TiO_2$ sols synthesized simultaneously in the same autoclave through hydrothermal method. The synthesized $TiO_2$ sols were all formed with an anatase phase, and their particle size was between several nm and 30 nm showing ${\zeta}-potential$ of $-25{\sim}-35$ mV, being maintained stable for over 6 months. However, the $TiO_2$ sol added with Cr had a much lower value of -potential and larger particle sizes. The coated $TiO_2$ thin films had almost the same shape and size as those of the sol. The pure $TiO_2$ sol showed the highest optical absorption in the ultraviolet light region, and other $TiO_2$ sols containing $Cr^{3+},\;Fe^{3+}\;and\;Ni^{2+}$ showed higher optical absorption than pure sol in the visible light region. According to the experiments for removal of a gas-phase benzene, the pure $TiO_2$ film showed the highest photo dissociation rate in the ultraviolet light region, but in artificial sunlight the photo dissociation rate of $TiO_2$ coated films containing $Cr^{3+},\;Fe^{3+}\;and\;Ni^{2+}$ was measured higher together with the increase of optical absorption by doping.

• Korean Journal of Materials Research
• /
• v.21 no.4
• /
• pp.220-224
• /
• 2011

Zircon has excellent thermal, chemical, and mechanical properties, but it is hard to make a dense sintered product because of dissociation during the sintering process. This study analyzes how the addition of $SiO_2$ and $Al_2O_3$ affects the mechanical properties of sintered zircon, particularly in regards to reducing the thermal dissociation and improving the mechanical properties of $ZrSiO_4$. Zircon specimens containing different amounts of $SiO_2$ and $Al_2O_3$ were prepared and sintered to observe how the mechanical properties of $ZrSiO_4$ changed according to the differing amount of $SiO_2$ and $Al_2O_3$. The $ZrSiO_4$ that was used for the starting material was ground by ball mill to an average particle size of 3 ${\mu}m$. The $SiO_2$ and $Al_2O_3$ that was used for additives were ground to an average particle size of 3 ${\mu}m$ and 0.5 ${\mu}m$, respectively. Adding $SiO_2$ resulted in transformation in the liquid phase at high temperatures, which had little effect on suppressing the thermal dissociation but enhanced the mechanical properties of $ZrSiO_4$. When $Al_2O_3$ was added, the mechanical properties of $ZrSiO_4$ decreased due to the formation of pores and abnormal grains in the microstructure of the sintered zircon.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.7
• /
• pp.1119-1126
• /
• 2007

Hydrogen gas and carbon nanotubes along with nanocarbon were produced from commercial natural gas using fixed bed catalyst reactor system. The maximum amount of carbon (491 g/g of catalyst) formation was achieved on 25% Ni, 3% Cu supported catalyst without formation of CO/CO2. Pure carbon nanotubes with length of 308 nm having balloon and horn type shapes were also formed at 673 K. Three sets of catalysts were prepared by varying the concentration of Ni in the first set, Cu concentration in the second set and doping with K in the third set to investigate the effect on stabilization of the catalyst and production of carbon nanotubes and hydrogen by copper and potassium doping. Particle size analysis revealed that most of the catalyst particles are in the range of 20-35 nm. All the catalysts were characterized using powder XRD, SEM/EDX, TPR, CHN, BET and CO-chemisorption. These studies indicate that surface geometry is modified electronically with the formation of different Ni, Cu and K phases, consequently, increasing the surface reactivity of the catalyst and in turn the Carbon nanotubes/H2 production. The addition of Cu and K enhances the catalyst dispersion with the increase in Ni loadings and maximum dispersion is achieved on 25% Ni: 3% Cu/Al catalyst. Clearly, the effect of particle size coupled with specific surface geometry on the production of hydrogen gas and carbon nanotubes prevails. Addition of K increases the catalyst stability with decrease in carbon formation, due to its interaction with Cu and Ni, masking Ni and Ni:Cu active sites.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.4
• /
• pp.259-266
• /
• 2016

PURPOSE. The purpose of this study was to assess the effect of surface treatments on shear bond strength of resin composite bonded to thermocycled and non-thermocycled CAD/CAM resin-ceramic hybrid materials. MATERIALS AND METHODS. 120 specimens ($10{\times}10{\times}2mm$) from each material were divided into 12 groups according to different surface treatments in combination with thermal aging procedures. Surface treatment methods were airborne-particle abrasion (abraded with 50 micron alumina particles), dry grinding (grinded with $125{\mu}m$ grain size bur), and hydrofluoric acid (9%) and silane application. According to the thermocycling procedure, the groups were assigned as non-thermocycled, thermocycled after packing composites, and thermocycled before packing composites. The average surface roughness of the non-thermocycled specimens were measured after surface treatments. After packing composites and thermocycling procedures, shear bond strength (SBS) of the specimens were tested. The results of surface roughness were statistically analyzed by 2-way Analysis of Variance (ANOVA), and SBS results were statistically analyzed by 3-way ANOVA. RESULTS. Surface roughness of GC were significantly lower than that of LU and VE (P<.05). The highest surface roughness was observed for dry grinding group, followed by airborne particle abraded group (P<.05). Comparing the materials within the same surface treatment method revealed that untreated surfaces generally showed lower SBS values. The values of untreated LU specimens showed significantly different SBS values compared to those of other surface treatment groups (P<.05). CONCLUSION. SBS was affected by surface treatments. Thermocycling did not have any effect on the SBS of the materials except acid and silane applied GC specimens, which were subjected to thermocycling before packing of the composite resin.

• Korean Journal of Materials Research
• /
• v.17 no.10
• /
• pp.560-566
• /
• 2007

AlN plates were fabricated by hot pressing at $1700-1900^{\circ}C$ using yttria and alumina (3 and $10\;{\mu}m$ particle size) powders as additives and characterized: density, thermal conductivity, transverse rupture strength, and grain size measurement by SEM and EDS. Density values of $3.31-3.34\;g/cm^3$ are largely attributed to hot pressing of powder mixtures in carbon mold under $N_2$ atmosphere which caused effective degree of oxygen removal from yttrium-aluminate phase expected to form at $1100^{\circ}C$. The grain size of hot pressed AlN was almost homogeneous, with size approximately from 3.2 to $4.0\;{\mu}m$ after hot pressing. $Al_2O_3$ powder of $3\;{\mu}m$ particle size resulted in better transverse rupture strength and finer grain size compared to $10\;{\mu}m$ $Al_2O_3$ powder. The thermal conductivity of AlN ranged between $83-92.7\;W/m{\cdot}K$ and decreased with $Al_2O_3$ addition. Fine grain size is preferred for better mechanical properties and thermal conductivity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.117-117
• /
• 2009

Recently, low temperature co-fired ceramic (LTCC) technology has gained a remarkable application potential in sensors, actuators and microsystems fields. In this study, we investigated the effects of annealing treatment on the electrical properties of $Pb(ZrTi)O_3$ (PZT) thin films deposited on LTCC substrate. The LTCC substrates with thickness of 400 ${\mu}m$ were fabricated by laminating 12 green tapes which consist of alumina and glass particle in an organic binder. The PZT thin films were deposited on Au/LTCC substrates by RF magnetron sputtering method. Then, the change of the crystallization of the films was investigated under various annealing temperatures. The results showed that the crystallization of the films were enhanced as increasing annealing temperatures. The film, annealed at $700^{\circ}C$, 3min, was well crystallized in the ferovskite structure. The structural variation of the films were analyzed by using X-Ray diffraction (XRD) and field emmision scanning electron microscopy (FESEM).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.118-118
• /
• 2009

Low temperature co-fired ceramic (LTCC) is one of promising materials for MEMS structures because it has very good electrical and mechanical properties as well as possibility of making various three dimensional (3D) structures. In this work, piezoelectric pressure sensors based on hybrid LTCC technology were presented. The LTCC diaphragms with thickness of 400 um were fabricated by laminating 12 green tapes which consist of alumina and glass particle in an organic binder. The piezoelectric sensing layer consists of $Pb(ZrTi)O_3$ (PZT) thin film deposited by RF magnetron sputtering method on between top and bottom Au electrodes. The results showed that the fabrication method is very suitable for pressure sensor applications. The PZT films deposited on LTCC diaphragms were successfully grown and were analyzed by using X-ray diffraction method (XRD) and field emission scanning electron microscope (FESEM).