• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.1
• /
• pp.22-26
• /
• 2012

An influence of the addition of copper (0.5, 1.0 and 1.5 mass% Cu) on the microstructure and mechanical properties of high purity iron (99.998 mass%) was characterized. The microstructure and microhardness of high-purity iron based samples, which were rolled at room temperature and subsequently annealed, were investigated in this work. The microstructure of the samples has been observed by electron back scattering diffraction (EBSD) and the mechanical properties have been studied by using micro-Vickers hardness test. The results of microstructural observation showed that deformation band was formed in high purity iron by rolling at room temperature, and it was recovered by annealing up to about 900 K. The microhardness results showed that the softening of high-purity iron occurred by annealing up to about 900 K, while the hardness of iron added with about 0.5-1.5 mass% copper was kept over 100 Hv and at the early time of annealing reached a maximum. The hardness of iron added with a small amount of copper may be attributed to precipitation hardening as well as solution hardening. The orientation of crystal in recrystallized grain was almost same as that of deformed grain.

• Transactions of Materials Processing
• /
• v.19 no.5
• /
• pp.311-319
• /
• 2010

Rare earth metal Ce has a relatively low melting point and high specific gravity. Because of its significantly high affinity to oxygen, nitrogen and sulfur, it is highly usable as a steel refining agent. However, because Ce compound has relatively high specific gravity, it is difficult to be separated from molten steel through floatation, and it degrades the purity of molten steel, or may clog the nozzle in continuous casting. Such problem may be solved by using an appropriate deoxidation agent together with Ce and settling molten steel sufficiently after refining. Thus a fundamental study in the formation behavior of non-metallic inclusion in Ce added Hyper Duplex STS melts was investigated. The addition amount of Ce, melt temperature were considered as experimental variables. A main non-metallic inclusion in mother alloy is 51(wt%MnO) - 27.6(wt%SiO$_2$)- 10.9(wt%$Cr_2O_3$). Non-metallic inclusion was dramatically decreased and the particle size was fined as the amount of Ce increased. Moreover (%MnO) and (%SiO$_2$) of non-metallic inclusion were decreased. But (%$Al_2O_3$)were relatively increased. The number of non-metallic inclusion were decreased and the large particle size were increased by increasing the temperature of molten steel.

• Korean Journal of Materials Research
• /
• v.7 no.1
• /
• pp.50-56
• /
• 1997

급냉응고법을 이용하여 고용한도 이상으로 Mn량을 첨가할 때 Mn량에 따른 인장특성의 변화와 시효특성을 조사하였다. 원심분무법으로 AI-4.7%Zn-2.5%Mg-0.2%Zr합금에 Mn량을 각기 달리 첨가한 급냉응고 분말을 제조 하였다. 이 분말을 냉간압축, 진공 탈가스처리를 한 후 15:1로 압출하여 봉상 시편을 만들었다. 분말의 미세조직은 $\alpha$-AI수지상과 수지상간 편석부로 이루어져 있으며 Mn첨가에 따라 조직의 변화는 관찰되지 않았다. 빠른 냉각속도로 인하여 2.0%Mn을 첨가한 경우에도 초정 Mn상을 발견할 수 없었다. 압출재의 미세조직은 아결정립으로 이루어져 있으며 약간의 제2상들이 관찰되었다. 대부분의 Mn 분산상은 압출후 용체화처리 과정에서 형성되었으며 시효경화량은 Mn양에 관계없이 일정하였다. 46$0^{\circ}C$에서 1시간 용체화처리하고 12$0^{\circ}C$에서 24시간 시효처리한 경우 최대의 시효경도값을 나타내었다. 인장강도는 Mn첨가량에 따라 증가 하였는데 이것은 Mn분산상의 밀도증가에 의한 것으로 확인되었다. 2.0%Mn을 첨가한 합금의 시효후 인장강도는 590MPa, 연산율은 4%를 보였다.

• Journal of Powder Materials
• /
• v.19 no.4
• /
• pp.247-252
• /
• 2012

Effect of Cu and $DyF_3$ powder mixing with Cu-free (Nd, Dy)-Fe-B jet-milled powder on the magnetic properties of sintered magnets was investigated. The coercivity of a magnet prepared from the Cu-free (Nd, Dy)-Fe-B powder was about 10 kOe even though the alloy powder already contained some Dy (3.5 wt%). When small copper powder was blended, however, the coercivity of the magnet increased almost 100%, exhibiting about 20 kOe. On the contrary, the coercivity enhancement was moderate, about 4 kOe, when dysprosium content in the sintered magnet was simply increased to 4.9 wt% by the addition of small $DyF_3$3 powder.

• Proceedings of the KIEE Conference
• /
• 2001.04a
• /
• pp.3-5
• /
• 2001

Racetrack coils are used in many areas of superconductivity applications such as generators, motors, maglev, wiggler magnets and so on. The fabrication and characteristics of race-track type High Tc Superconducting (HTS) magnets were carried out. The Magnet is composed of 3 pancake coils wound by 37-filamental Bi-2223/ Ag-alloy tapes. Quench current ($I_q$) of both whole magnet and 3 pancake coils were measured. At 77K under the self-field, $I_q$ of magnet was 12A, while in the case of middle pancake coil, $I_q$ was 15A. The upper pancake coils of racetrack magnet with iron plates, magnet having optimized current distribution and initial magnet are compared with each other through 3D FEA, manufacturing and testing these magnets. The measured performance of the upper pancake coil #3 with iron plates improved by 50% on the basis of initial pancake coil #3. Quench current ($I_q$) of field winding was 12A. In addition, the fabrication processes and the characteristics of HTS magnet are described.

• Nuclear Engineering and Technology
• /
• v.46 no.2
• /
• pp.169-182
• /
• 2014

High-performance research reactors require fuel that operates at high specific power to high fission density, but at relatively low temperatures. Research reactor fuels are designed for efficient heat rejection, and are composed of assemblies of thin-plates clad in aluminum alloy. The development of low-enriched fuels to replace high-enriched fuels for these reactors requires a substantially increased uranium density in the fuel to offset the decrease in enrichment. Very few fuel phases have been identified that have the required combination of very-high uranium density and stable fuel behavior at high burnup. U-Mo alloys represent the best known tradeoff in these properties. Testing of aluminum matrix U-Mo aluminum matrix dispersion fuel revealed a pattern of breakaway swelling behavior at intermediate burnup, related to the formation of a molybdenum stabilized high aluminum intermetallic phase that forms during irradiation. In the case of monolithic fuel, this issue was addressed by eliminating, as much as possible, the interfacial area between U-Mo and aluminum. Based on scoping irradiation test data, a fuel plate system composed of solid U-10Mo fuel meat, a zirconium diffusion barrier, and Al6061 cladding was selected for development. Developmental testing of this fuel system indicates that it meets core criteria for fuel qualification, including stable and predictable swelling behavior, mechanical integrity to high burnup, and geometric stability. In addition, the fuel exhibits robust behavior during power-cooling mismatch events under irradiation at high power.

• Corrosion Science and Technology
• /
• v.15 no.2
• /
• pp.58-68
• /
• 2016

Many industries need the universal standard or technique to obtain the identical CCT regardless of specimen geometries. This study aimed to determine an appropriate applied torque to the cylindrical specimen defining the apparatus and the procedure to measure the temperature of initiating crevice corrosion in tubular shape products such as pipes, tubes and round rods etc; the test method also proved applicable to the plate type specimen. A series of experiments for CCT measurements with the plate type and cylindrical stainless steel specimens of various diameters with different microstructures (austenitic and duplex) and PRENs were conducted to determine the relationship among geometries on CCT. Thus, the apparatus that could measure the CCT of stainless steels with both plate and cylindrical geometries was newly designed. The use of the apparatus facilitated the same CCT value for both geometries only if the specimens were made of the same alloy. The applied torque can be calculated for various diameters of the cylindrical specimens using the following relation; Applied torque, $Nm=-0.0012D^2+0.019D+2.4463$ (D; the diameter of cylindrical specimen, mm). However, upwards of 35 mm diameter cylindrical specimens require 1.58Nm, which is the same torque for the plate type specimen; in addition, this test method cannot be used for cylindrical specimens of less than 15 mm diameter.

• Corrosion Science and Technology
• /
• v.17 no.1
• /
• pp.20-29
• /
• 2018

Ti and its alloys show the excellent corrosion resistance to chloride environments, but they show less corrosion resistance in HCl, $H_2SO_4$, NaOH, $H_3PO_4$, and especially HF environments at high temperature and concentration. In this study, we used the commercially pure titanium and Ti-6Al-4V alloy, and evaluated the effect of the manufacturing process on the electrochemical properties. We used commercial products of rolled and forged materials, and made additive manufactured materials by DMT (Directed Metal Tooling) method. We annealed each specimen at $760^{\circ}C$ for one hour and then air cooled. We performed anodic polarization test, AC impedance measurement, and Mott-Schottky plot to evaluate the electrochemical properties. Despite of the difference of its microstructure of CP-Ti and Ti-6Al-4V alloys by the manufacturing process, the anodic polarization behavior was similar in 20% sulfuric acid. However, the addition of 0.1% hydrofluoric acid degraded the electrochemical properties. Among three kinds of the manufacturing process, the electrochemical properties of additive manufactured CP-Ti, and Ti-6Al-4V alloys were the lowest. It is noted that the test materials showed a Warburg impedance in HF acid environments.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1127-1132
• /
• 1998

The possibilities of producing Al-10%Ti-4%Fe composites through in-situ processing and thus achieving mechanical property improvements over binary Al-10%Ti to a level or higher exhibited by PM SiC/A12124 composites were explored in this study. The microstructure of in-situ processed Al-10%Ti-4%Fe composites was similar to that of Al matrix composites reinforced with discontinuous SiC particulates(SiC/A12124) and significant enhancements in elastic modulus, tensile strength and wear resistance were observed as compared to Al-10%Ti alloy. These results can be attributed to the in-situ formed Al. Fe by third element addition, leading to additional dispersion strengthening effect over $Al_3Ti$ phase reinforcement in Al-Ti system.

• Korean Journal of Materials Research
• /
• v.23 no.2
• /
• pp.135-142
• /
• 2013

The Ti-6Al-4V extra low interstitial (ELI) alloy has been widely used as an orthopedic implant material because of its excellent mechanical properties and biocompatibility. However, it still has many problems, including a high elastic modulus and toxicity of the Al and V elements. Therefore, non-toxic biomaterials with a low elastic modulus need to be developed. A high energy mechanical milling (HEMM) process is introduced to improve the effect of sintering. Rapid sintering of spark plasma sintering (SPS) under pressure was used to make an ultra fine grain of Ti-25 wt.%Nb-7 wt.%Zr-10 wt.%Mo-(10 wt.%CPP) composites with bio-attractive elements for increasing strength. These composites were fabricated by SPS at $1000^{\circ}C$ at 60 MPa using HEMM powders. During the sintering process, $CaTiO_3$, TixOy, and CaO were formed because of the reaction between Ti and CPP. The effects of CPP content on the physical and mechanical properties of the sintered Ti-Nb-Zr-Mo-CPP composites were investigated. The biocompatibility and corrosion resistance of the Ti-Nb-Zr-Mo alloys were improved by the addition of CPP.