INFLUENCE OF TOOTH SURFACE ROUGHNESS AND TYPE OF CEMENT ON RETENTION OF COMPLETE CAST CROWNS (치아표면 거칠기와 시멘트 종류가 전부주조관의 유지력에 미치는 영향)

  • Kim, Kil-Su;Song, Chang-Yong;Ahn, Seung-Geun;Park, Charn-Woon
    • The Journal of Korean Academy of Prosthodontics
    • /
    • v.37 no.4
    • /
    • pp.465-473
    • /
    • 1999
  • Bond strength of luting cements to dentin is a critical consideration for success of complete cast crowns. This study was performed to evaluate the relationship between surface characteristics of teeth prepared for complete cast crowns and retention of cemented restorations. Eighty artificial crowns were cast for standardized complete crown tooth preparations accomplished with the use of a special device on recently extracted human teeth. Coarse diamond(#102R, Shofu) and superfine finishing diamond(#SF102R, Shofu) burs of similar shape were used. Crowns in each group were randomly subdivided into few subgroups of 10 for luting cements selected for this study: zinc phosphate cement (FLECK' S), polycarboxylate cement (Poly-F), rein-forced glass ionomer cement (Fuji PLUS). and adhesive resin cement (Panavia 21). Retention was evaluated by measuring the tensile load required to dislodge the artificial crown from tooth preparations with an Instron testing machine, and analysed by one-way ANOVA and Student's t-test. The obtained results were as follows ; 1. When tooth preparation was done with coarse diamond bur, retentive force was diminished in order of Panavia 21 Fuji PLUS, FLECK'S, and Poly-F. Retentive forces showed the significant difference between Fuji PLUS group and FLECK'S group(p<0.001). 2. When tooth preparation was done with superfine diamond bur, retentive force was diminished in order of Fuji PLUS, Panavia 21, FLECK'S, and Poly-F. Retentive forces showed the significant difference between Panavia 21 group and FLECK'S group(p<0.001). 3. Retentive force in coarse tooth surfaces was significantly higher than that in superfine tooth surface with all luting cements(p<0.001), and cement residues were almost retained with-in the cast crown in all groups.

  • PDF

A Study on the Toothbrush-Dentifrice Abrasion of Class V Restroations (치경부 5급 와동 수복의 잇솔질 마모에 관한 연구)

  • Hwang, Su-Jin;Yu, Mi-Kyung;Lee, Kwang-Won
    • Journal of Dental Rehabilitation and Applied Science
    • /
    • v.21 no.1
    • /
    • pp.69-81
    • /
    • 2005
  • The objective of this study was to evaluate the toothbrush abrasion characteristics of class V restorations. Thirty extracted human premolars, which were collected from oral surgery clinics were used. We mounted five teeth in a metal ring mold of 50 mm in diameter and 15 mm in height using chemically cured acrylic resin. Class V cavities were prepared in lingual cervical root surfaces and restored using one of following restorative materials : Dentin Conditioner/Fuji II LC (Group FL), All Bond II/Z-250 (Group ZT), One-up Bond F/Palfigue Estelite (Group PE), F2000 Primer/Adhesive (Group FT), and Prime & Bond 2.1/Dyract AP (Group DR). They were stored under distilled water at $37^{\circ}C$ for seven days. The toothbrush abrasion test was conducted using a wear testing machine of pin-on disk type under a load of 1.5 N for 100,000 cycles. We have examined the bonded interfaces, the changes of surface roughness and color of abraded surfaces. From this experiment, the following results were obtained. 1. The change of surface roughness showed high degree: RMGIC>compomer>composite resin (p<0.05). 2. Because of the protrusion and missing of filler particles, SEM observation of abraded surfaces of RMGIC and compomers revealed the increase of surface roughness due to the selective removal of matrix resin. 3. The color change by toothbrush abrasion was affected in large part by the change of $L^*$ and $b^*$ of resin composites (p<0.05). 4. The color change by toothbrush abrasion was so small to detect by human eyes. 5. SEM observation of abraded surfaces revealed the interface bonding was the best in the FT group.

A SCANNING ELECTRON MICROSCOPIC STUDY ON THE MARGINAL ADAPTIBILITY IN APPLYING THE CAVITY VARNISH AND DENTIN BONDING AGENT IN AMALGAM RESTORATIONS (아말감 수복시(修復時) Cavity varnish와 Bonding agent 도포(塗布)에 따른 접합성(接合性)에 관(關)한 주사전자현미경적(走査電子顯微鏡的) 연구(硏究))

  • Kim, Seok-Hoon;Cho, Young-Gon
    • Restorative Dentistry and Endodontics
    • /
    • v.15 no.1
    • /
    • pp.107-119
    • /
    • 1990
  • The purpose of this study was to evaluate the marginal adaptability of the amalgam restorations in applying the cavity varnish (Copalite$^{(R)}$) and dentin bonding agent (Scotchbond 2$^{(R)}$) under the scanning electron microscope. For this study, eighteen sound extracted human molars were selected. Class I cavities in 12 teeth and class V cavities in 6 teeth were prepared using an air turbine with No. 701 tungsten carbide bur and finished using a low speed handpiece with No. 557 fissure bur. The prepared specimens were then divided into three groups including 4 class I cavities and 2 class V cavities in each group and restored as follows ; Group I. All the prepared cavities were restored with amalgam only (Control). Group II. Two layers of Copalite$^{(R)}$ cavity varnish were applied to the cavities with a gentle stream of air after each application and cavities were restored with amalgam. Group III. The enamel cavity margins were etched with 37% phosphoric acid gel for 60 sec., rinsed for 30 sec. and dried. One layer of visible lightcured Scotchbond Dental Adhesive$^{(R)}$ was applied and immediately cured for 20 seconds with visible light-cure unit and cavities were restored with amalgam. All the specimens were cut at the neck of the teeth and the occlusal halves of specimens were sectioned buccolingually in the longitudinal axis centering the amalgam restorations, using the disk. The cut specimens were ground with sandpapers (400, 600, 800, 1000 grit), and cleaned for 5 minutes in the ultrasonic cleaner (Brason Co. U.S.A.). In the cut surfaces, the amalgam - tooth interfaces were examined under the scanning electron microscope (JSM, 35C type, JEOL). The obtained results were as follows ; 1. The amalgam-tooth interfaces were reduced more significantly in the Copalite$^{(R)}$ and Scotchbond 2$^{(R)}$ application group than in the control group. 2. In the class I cavities, the Scotchbond 2$^{(R)}$ application group showed the findings similar to the Copalite$^{(R)}$ application group in the cavity floor, and the marginal adaptability was better in the side wall than in the cavity floor. 3. In the class I cavities, the Scotchbond 2$^{(R)}$ application group showed better marginal adaptability in the occlusal margin than in the gingival margin. 4. The marginal adaptability was in the order of the Scothbond 2$^{(R)}$ application group, the Copalite$^{(R)}$ application group and the control group.

  • PDF

Influence of Sodium Hypochorite & EDTA on the Microtensile Bond Strength of Ethanol Wet Bonding (Ethanol Wet Bonding에서 NaOCl과 EDTA가 결합강도에 미치는 영향)

  • Kim, Deok-Joong;Song, Yong-Beom;Park, Sang-Hee;Kim, Hyoung-Sun;Lee, Hye-Yoon;Yu, Mi-Kyung;Lee, Kwang-Won
    • Journal of Dental Rehabilitation and Applied Science
    • /
    • v.29 no.1
    • /
    • pp.37-44
    • /
    • 2013
  • Sodium hypochlorite and ethylene diamine tetra acetic acid are substances usually used during endodontic treatment. Several studies found that the bonding was negated with certain irrigants and some of the used irrigants have demineralizing and chealating effects, so it was advocated to omit the etching step in etch and rinse adhesive systems. The purpose of this in vitro study was to evaluate the influence of NaOCl & EDTA on the bonding strength of ethanol wet bonding. Thirty human molars were selected and mesiodistally sectioned into halves, thus providing sixty specimens. The specimens were randomly assigned to 4 groups(n=15) according to the irrigant regimen used : (1) irrigated with distilled water for 10min (control); (2) irrigated with 5.25% NaOCl(10min), flushed with 5.25% NaOCl(1min) (3) irrigated with 5.25% NaOCl, flushed with 17% EDTA (4) irrigated with 5.25% NaOCl, flushed with 17% EDTA. Each group was acid-etched with 37% phosphoric acid(except group 4) and had their dentin surfaces dehydrated with ethanol solutions : 50%, 70%, 80%, 95%, 3x100%, 30s for each application. After dehydration, a primer( 50% all bond 3 resin + 50% ethanol) was used, followed by the adhesive(ALL-BOND 3 RESIN) application. Resin composite build-ups were then prepared using an incremental technique. Specimens were sectioned into beams and submitted to a tensile load using a Micro Tensile Tester(Bisco Inc.). The data were statistically analyzed using one-way ANOVA and Tukey HSD at p<0.5 level. There was no significant difference on G1(control) and G2(irrigated with NaOCl only ). (p>0.05). G3(flushed with EDTA) showed significantly high tensile bonding strength compared to the G2 (p<0.05). G4( treated with EDTA but no acid-etching) was significantly lower value than G3. (p<0.05) Although there was no significant difference, 5.25% NaOCl seemed to have an adverse effect on the bonding strength of ethanol wet bonding. The flushing with EDTA after NaOCl irrigation prevents the decrease of bonding strength. The use of 17% EDTA as a final flush can enhance the bonding strength but EDTA flushing can't substitute for a acid-etching.

A study on the shear bond strengths of veneering ceramics to the colored zirconia core (착색지르코니아 코어와 전장 도재 사이의 전단결합강도에 관한 연구)

  • Kang, Sun-Nyo;Cho, Wook;Jeon, Young-Chan;Jeong, Chang-Mo;Yun, Mi-Jung
    • The Journal of Korean Academy of Prosthodontics
    • /
    • v.47 no.3
    • /
    • pp.312-319
    • /
    • 2009
  • Statement of problem: Delamination of veneering porcelain from underlying ceramic substructures has been reported for zirconia-ceramic restorations. Colored zirconia cores for esthetics have been reported that their bond strength with veneered porcelain is weaker compared to white zirconia cores. Purpose: This study aimed to investigate the shear bond strength by manufacturing the veneering porcelain on the colored zirconia core, using the layering technique and heat-pressing technique, and to evaluate the clinical stability by comparing the result of this with that of conventional metal ceramic system. Material and methods: A Metal ceramic (MC) system was tested as a control group. The tested systems were Katana zirconia with CZR (ZB) and Katana Zirconia with NobelRondo Press (ZP). Thirty specimens, 10 for each system and control, were fabricated. Specimen disks, 3 mm high and 12 mm diameter, were fabricated with the lost-wax technique (MC) and the CAD-CAM (ZB and ZP). MC and ZB specimens were prepared using opaque and dentin veneering ceramics, veneered, 3 mm high and 2.8 mm in diameter, over the cores. ZP specimens were prepared using heat pressing ingots, 3 mm high and 2.8mm in diameter. The shear bond strength test was performed in a Shear bond test machine. Load was applied at a cross-head speed of 0.50 mm/min until failure. Mean shear bond strengths (MPa) were analyzed with the One-way ANOVA. After the shear bond test, fracture surfaces were examined by SEM. Results: The mean shear bond strengths (SD) in MPa were MC control 29.14 (2.26); ZB 29.48 (2.30); and ZP 29.51 (2.32). The shear bond strengths of the tested systems were not significantly different (P > .05). All groups presented cohesive and adhesive failures, and showed predominance of cohesive failures in ceramic veneers. Conclusion: 1. The shear bond strengths of the tested groups were not significantly different from the control group (P >.05). 2. There was no significant different between the layering technique and the heat pressing technique in the veneering methods on the colored zirconia core. 3. All groups presented cohesive and adhesive failures, and showed predominance of cohesive failures in ceramic veneers.

Shear bond strength of the three different kinds of resin cement on CAD/CAM ceramic inlay (CAD/CAM 세라믹 인레이에 대한 3종의 레진 시멘트의 전단결합강도에 관한 연구)

  • Baek, Chul-Woo;Park, Cheol-Woo;Park, Jun-Sub;Ryu, Jae-Jun
    • The Journal of Korean Academy of Prosthodontics
    • /
    • v.51 no.1
    • /
    • pp.20-26
    • /
    • 2013
  • Purpose: The purpose of this study was to evaluate the bond strengths between the latest CAD/CAM ceramic inlay and various resin cements which are used primarily for esthetic restoration. Materials and methods: Cylindrical ceramic blocks(Height: 5 mm, diameter: 3 mm) were fabricated by using Cerec3 and bonded on the dentin of the ninety extracted caries-free molars using three different kinds of resin cement(Unicem$^{(R)}$, Biscem$^{(R)}$, and Variolink II$^{(R)}$) according to the manufacturer's instructions. Ninety specimens were divided into 3 groups according to three different kinds of resin cement. Half of each group were conducted thermocycling under the conditions of the $5-55^{\circ}C$, 5,000 cycle but the other half of them weren't. All specimens were kept in normal saline $37^{\circ}C$, for 24 hours before measuring the bond strength. The shear bond strength was measured by Universal testing machine with a cross head speed of 0.5 mm/min. The results were analyzed statistically by t-test and one-way ANOVA. Results: Unicem$^{(R)}$ group showed the highest shear bond strength despite a slight decline by thermocycling. The shear bond strength of Unicem$^{(R)}$ group and ValiolinkII$^{(R)}$ group were significantly influenced by thermocycling, whereas Biscem$^{(R)}$ group was not influenced (P<.05). There were no significant differences in the bond strength between the three groups without thermocycling, but there was significant differences between Unicem$^{(R)}$ group and Valiolink II$^{(R)}$ group with thermocycling(P<.05). Conclusion: It has been shown to be clinically effective when the self-adhesive resin cements Unicem$^{(R)}$ and Biscem$^{(R)}$ were used instead of the etch-and-rinse resin cement Valiolink II$^{(R)}$ during the bonding of CAD/CAM ceramic inlay restorations with teeth.