• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.305-314
• /
• 1991

This study was conducted to research the formation and the color development of NiO-ZnO-Fe2O3-TiO2-SnO2 system for the purpose of synthesizing the spinel pigments which are stable at high temperature. After preparing ZnO-Fe2O3 as a basic composition, {{{{ chi }}NiO.(l-{{{{ chi }})ZnO.Fe2O3 system, {{{{ chi }}NiO.(l-{{{{ chi }})ZnO.TiO2 system, and {{{{ chi }}NiO.(l-{{{{ chi }})ZnO.SnO2 system were prepared with {{{{ chi }}=0, 0.2, 0.5, 0.7, 1 mole ratio respectively. The manufacturing was carried out at 128$0^{\circ}C$ for 30 minutes. The reflectance measurement and the X-ray analysis of these specimens were carried out and the results were summarized as follows. 1. In the specimens which included NiO, it was difficult for the spinel structure to be formed. 2. As increasing the contents of NiO and Fe2O3, all the groups which were yellow or green colored changed to brown. 3. NiO-ZnO-Fe2O3 system and NiO-ZnO-TiO2 system formed the spinel structure and the illmenite structure appeared in NiO-TiO2 system.

• Journal of Technologic Dentistry
• /
• v.33 no.3
• /
• pp.203-210
• /
• 2011

Purpose: The purpose of this study was to compare color correspondence of different sizes of Vita Mark II$^{(R)}$ and TriLuxe$^{(R)}$ Feldspar blocks. Methods: The three commercially available shades(1M2, 2M2, 3M2) of Mark II & TriLuxe blocks for the CEREC$^{(R)}$ CAD/CAM system were examined. For each of three colors, three different sizes were tested, 5 blocks each. The measurements were made using a spectrophotometer equipped with an integrating sphere using the CIE $L^*$, $a^*$, $b^*$ colorimetric system. Results: The $L^*$, $a^*$, $b^*$ value of Vita Mark II$^{(R)}$ ceramic block showed significantly higher than TriLuxe$^{(R)}$ ceramic block(p<0.05). In comparing the Vita Mark II$^{(R)}$ specimen of the three different shade, color differences between materials(${\Delta}E^*$) showed the lowest value of 2.09, and the highest was 2.24. ${\Delta}E^*$ values of the materials of Vita Mark II$^{(R)}$ were higher than 2. As the size of ceramic block differed, the color correspondence of Vita Mark II$^{(R)}$ showed statistically significant difference but, this result is clinically acceptable. Conclusion: All the different sizes of the different shades of Vita TriLuxe$^{(R)}$ blocks for the CEREC$^{(R)}$ system showed the high degree of color correspondence necessary in industrially prefabricated CAD/CAM blocks. The results of the present study suggested that it would be necessary to establish the reproducible and constant color specification system for an esthetic restoration.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.407-410
• /
• 2012

The properties of Al-doped ZnO (AZO) films were investigated as a function of H2/(Ar + H2) gas ratio using an AZO (2 wt% Al2O3) ceramic target in a radio frequency (RF) magnetron sputtering system. The deposition process was done at 200 ℃ and in 2 × 10-2Torr working pressure and with various ratios of H2/(Ar + H2) gas. During the AZO film deposition process, partial H2 gas affected the AZO film characteristics. The electron resistivity (~ 9.21 × 10-4 Ωcm) was lowest and mobility (~17.8 ㎠/Vs) was highest in AZO films when the H2/(Ar + H2) gas ratio was 2.5%. When the H2/(Ar + H2) gas ratio was increased above 2.5%, the electron resistivity increased and mobility decreased with increasing H2/(Ar + H2) gas ratio in AZO films. The carrier concentration increased with increasing H2/(Ar + H2) gas ratio from 0% to 7.5%. This phenomenon was explained by reaction of hydrogen and oxygen and additional formation of oxygen vacancy. The average optical transmission in the visible light wavelength region over 90% and an orientation of the deposition was [002] orientation for AZO films grown with all H2/(Ar + H2) gas ratios.

• Journal of the Korean Ceramic Society
• /
• v.27 no.4
• /
• pp.548-552
• /
• 1990

Effects of binder addition method during compacting on microstructural change and magnetic characteristics of Sr-ferrite system was investigated. Used binders were PVA and PEG, which were added separately or simultaneously. After compacts were heated at 50$0^{\circ}C$ for 3hr in air for burning out all the binders, they were sintered at 125$0^{\circ}C$ for 2h. Based on results, in the case of using the two binders simultaneously, comparing to single binder system, compacted density was somewhat higher but sintered density was rather lower, and abnormal grain growth was accelerated. According to these sintering characteristics, remanent magnetization and coercive force were also diminished.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.6
• /
• pp.821-828
• /
• 2000

Metal - ceramic restorations have been the standard of fixed oral rehabilitation for over 30 years, and while many advances have been made in materials and research, the esthetic challenges of the light reflective metal substructure will always put clinician in an esthetic dilemma, for only a very talented ceramist / dentist team can create esthetics that rival nature on a repeatable basis. All ceramic restorations have also been a choice in our restorative armamentarium, but in the past, the materials have also had their own limitation, number on being question-able strength to withstand occlusal forces generated during mastication. IPS Empress 2 offers dentistry a metal free alternative to traditional restorative techniques. This clinical report describes the treatment of patients with esthetic problem of anterior dentition using Empress 2 system.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.4
• /
• pp.466-477
• /
• 2005

Statement of problem : Problem of matching the appearance of porcelain restorations with the patient's natural dentition has always been a concern to dental clinicians. Recently, demands for esthetics, even in restorations requiring strength, has brought a revolution to dentistry and increased use of zirconia. Among the various factors, shade and translucency or the core can significantly affect the overall esthetics of the restoration and should be considered when selecting an all-ceramic system. Purpose : The purpose of this study was to spectrophotometrically evaluate the influence of different zirconia systems and core thickness on the final shade of all-ceramic restorations using the CIEL$^*a^*b^*$ system. Material and Methods: Core specimens (n : 20 per group) of In-Ceram Alumina, In-Ceram Zirconia, Digident CAD/CAM Zirconia, Cercon Zirconia were fabricated 20mm in diameter. 10 specimens of each group were fabricated at core thickness of 0.5mm and 0.7mm. These core specimens were veneered with shade Al & A3 porcelain of the recommended manufacturer. CIEL$^*a^*b^*$ coordinates were recorded for each specimen with a spectrophotometer (Model CM-2600d, Minolta, Japan). Color differences were calculated using the equation ${\Delta}E^*=[({\Delta}L^*)^2+({\Delta}a^*)^2+({\Delta}b^*)^2]^{\frac{1}{2}}$. Results : 1. Specimens of core thickness 0.5mm and 0.7mm did not exhibit clinically perceived color difference. 2. Regarding shade reproducibility, In-Ceram Alumina and In-Ceram Zirconia showed significant difference within each group. 3. Cercon Zirconia group showed the highest $L^*$ value and Digident Zirconia group showed lowest $a^*$ & $b^*$ value. 4. Generally the shade difference between materials was higher in the A3 shade group than in the Al shade group. Conclusion: Within the limitations of this study, there was no color difference after increase in core thickness and every all-ceramic system has color characteristics that clinicians have to consider when selecting materials. Also, manufacturers of different porcelain systems must make every effort to achieve color reproducibility.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.6
• /
• pp.522-527
• /
• 2019

In order to fabricate high-quality SiC substrates for power electronic devices, various single crystal growing methods were prepared. These include the physical vapor transport (PVT) and top seeded solution growth (TSSG) methods. All the suggested SiC growth methods generally use induction-heating furnaces. The temperature distribution in this system can be easily adjusted by changing the hot-zone design. Moreover, precise temperature control in the induction-heating furnace is favorably required to grow a high-quality crystal. Therefore, in this study, we analyzed the heat transfer in these furnaces to grow SiC crystals. As the growth temperature of SiC crystals is very high, we evaluated the effect of radiation heat transfer on the temperature distribution in induction-heating furnaces. Based on our simulation results, a heat transfer strategy that controls the radiation heat transfer was suggested to obtain the optimal temperature distribution in the PVT and TSSG methods.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.121-126
• /
• 2000

Metal/Ceramic structures have many attractive properties, with great potential for applications that demand high stiffness, as well as chemical and biological stability, thermal and electrical insulation. They are currently in use for mechanical and thermal protection in cutting tool and engine parts. With all their great advantage, ceramics suffer from one major problem they are brittle, and are especially susceptible to cracking from surface contacts. Delamination at the interfaces with adjacent layers is a particularly disturbing problem, and can cause premature failure of a composite system. so determination of adhesive properties of coating is one of the most important problems for the extension of the use of coated materials. In this work, mechanical characteristics of Interface of ceramic/Metal composites are evaluated by means of hardness test, indentation test apparent interfacial toughness and bonding strength test. The interface indentation test provides a relation between the applied load(P) and the length of the crack(a) created at the interface between the coating and the substrate.

• Journal of Korea Foundry Society
• /
• v.36 no.6
• /
• pp.208-214
• /
• 2016

Casting defects, which are closely related to entrapped air bubbles and metallic oxides, occur very frequently in the casting process. Many researchers have shown that these defects can be reduced by adopting an appropriate gating system design. But, it is difficult for field engineers to identify a specific gating system that is more appropriate for their products. In this study, we tried to draw a comparison of gating system designs with and without ceramic foam filters. A ceramic foam filter was added to the horizontal runner just after the sprue to prevent air bubble generation and to reduce turbulence without change of the gating system design. To verify the effects of initial pouring velocity, the experiment was conducted with four different amounts of water volume in the reservoir. Results of the water modeling experiment applying the filter showed remarkably changed flow characteristics. Although the study confirmed that use of the filter may change the flow characteristics, it needs to be noted that only filter use alone cannot solve all the problems caused by a poorly designed gating system.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.11
• /
• pp.854-858
• /
• 2010

In this study, we have investigated the effects of Cr dopant on the sintering and electrical properties of ZnO-$Sb_2O_3$ (ZS) ceramics for varistor application. Spinel phases including $\alpha-$ and $\beta$-type was formed at ZS system and $\alpha$-spinel was stabilized by Cr doping in ZS system. Densification of ZS and ZSCr system was retarded to $1000^{\circ}C$ by the formation of spinel at $800^{\circ}C$. The morphology and its distribution of spinel phases in ZS system was homogeneous but disturbed by Cr doping. In ZSCr the densification of ZnO compared with ZS system was more retarded by low concentration of Zn interstitial defects induced by Cr doping in addition to the effect of spinel phase formation. The defects in each system were identified as attractive coulombic center (ZS: 0.13 eV, ZSCr: 0.12 eV) and singly charged oxygen vacancy $V_0^{\cdot}$ (ZSCr: 0.33 eV). In all ZS and ZSCr system have week varistor behavior by the formation of double Schottky barrier at grain boundary but its stability of barrier was very sensitive to sintering temperature.