• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.3 s.36
• /
• pp.259-265
• /
• 2005

Characteristics of electroplated Ni films and $Ni-Al_2O_3$ composite films, such as yield strength, fracture elongation, and $Al_2O_3$ content, were evaluated as a function of electroplating current density. $Al_2O_3$ content was $11.48\~11.64\;vol\%$ for $Ni-Al_2O_3$ composite films electroplated at $5\~20\;mA/cm^2$, and decreased to $8.41\;vol\%$ at $30\;mA/cm^2$ $Ni-Al_2O_3$ possessed yield strengths higher than those of Ni films. Especially, $Ni-Al_2O_3$ fabricated at $5\;mA/cm^2$ exhibited $50\%$ improved yield strength. Fracture elongations of Ni and $Ni-Al_2O_3$ decreased with increasing the electroplating current density. $Ni-Al_2O_3$ electroplated at $5\;mA/cm^2$ exhibited more uniform dispersion of $Al_2O_3$ and higher yield strength and larger fracture elongation than the composite films processed at other current densities.

• Journal of Powder Materials
• /
• v.25 no.1
• /
• pp.25-29
• /
• 2018

Porous Cu with a dispersion of nanoscale $Al_2O_3$ particles is fabricated by freeze-drying $CuO-Al_2O_3$/camphene slurry and sintering. Camphene slurries with $CuO-Al_2O_3$ contents of 5 and 10 vol% are unidirectionally frozen at $-30^{\circ}C$, and pores are generated in the frozen specimens by camphene sublimation during air drying. The green bodies are sintered for 1 h at $700^{\circ}C$ and $800^{\circ}C$ in $H_2$ atmosphere. The sintered samples show large pores of $100{\mu}m$ in average size aligned parallel to the camphene growth direction. The internal walls of the large pores feature relatively small pores of ${\sim}10{\mu}m$ in size. The size of the large pores decreases with increasing $CuO-Al_2O_3$ content by the changing degree of powder rearrangement in the slurry. The size of the small pores decreases with increasing sintering temperature. Microstructural analysis reveals that 100-nm $Al_2O_3$ particles are homogeneously dispersed in the Cu matrix. These results suggest that a porous composite body with aligned large pores could be fabricated by a freeze-drying and $H_2$ reducing process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.129-130
• /
• 2009

The P/E characteristics of $HfO_2$ CTF memory capacitor with $SiO_2/HfO_2/Al_2O_3$(OHA) engineered tunnel barrier were investigated. After a growth of thermal oxide with a thickness of 2 nm, 1 nm $HfO_2$ and 3 $Al_2O_3$ layers were deposited by atomic layer deposition (ALD) system. The band offset was calculated by analysis of conduction mechanisms through Fowler-Nordheim (FN) plot and Direct Tunneling (DT) plot. Moreover the PIE characteristics of $HfO_2$ CTF memory capacitor with OHA tunnel barrier was presented.

• Korean Journal of Materials Research
• /
• v.16 no.12
• /
• pp.771-776
• /
• 2006

In this study, we report a method to synthesize the aluminum nitride (AlN) powders from aluminum oxyhydroxide (AlOOH). AlOOH powders were prepared from the aluminum hydroxide ($Al(OH)_3$) by heattreatment at the reaction temperature of $350^{\circ}C$. Simple heat treatment of AlOOH in the flow of $NH_3$ gas leads to the formation of hexagonal AlN powders through intermediate conversion of ${\delta}-,\;{\gamma}-$ and ${\alpha}-Al_2O_3$. The FTIR transmission spectra show a broad peak related to Al-N bonds centered around 690 $cm^{-1}$ confirming the presence of AlN. The major peaks in Raman spectra were observed in 250 $cm^{-1}$ and 659 $cm^{-1}$. From the results, synthesized powders from the AlOOH powders were confirmed AlN powders.

• Journal of the Mineralogical Society of Korea
• /
• v.18 no.1
• /
• pp.11-17
• /
• 2005

Na-A zeolite were synthesized from melting slag of the incinerated ash by the alkaline activation processes. The experiments were performed in stainless steel vessels, with continuous stirring during the reaction periods. The silica-rich solution, a starting material, which was the waste of crystal growth factory, contains 5.7 wt% SiO₂ and 3.2 wt% Na₂O. And NaAlO₂ was made by the reaction of aluminium dross and NaOH solution and its molar ratios were Na₂O/Al₂O₃= 1.2 and H₂O/Na₂O=9. During the residence time of 7∼8 h at 80℃, the mixing of the silica-rich solution, NaAlO₂ and melting slag yields the production of homogeneous Na-A zeolite. The optimal reactant composition in molar ratio of Na₂O:Al₂O₃:SiO₂ was 1.3∼l.4 : 0.8∼0.9 : 2 and mixing ratio of solution and slag was 1/7∼10 (g/cc). Synthesized Na-A zeolite has cubic form uniformly and its size ranges about 1 ㎛. Ca/sup 2+/ ion exchange capacity of the Na-A was about 180∼210 meq/100g, corresponding approximately 80% to the commercial detergent builder.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.149-149
• /
• 2005

• Korean Journal of Materials Research
• /
• v.25 no.7
• /
• pp.330-335
• /
• 2015

A low thermal expansion ceramic, cordierite ($2MgO{\cdot}2Al_2O_3{\cdot}5SiO_2$), was synthesized using pyrophyllite. Pyrophyllite usually consists of $SiO_2$ and $Al_2O_3$, which are the main components of cordierite. $MgCO_3$ and $Al(OH)_3$ were added in various amounts to pyrophyllite and fired for synthesis and sintering. ${\alpha}$-cordierite crystallized from $1000^{\circ}C$ with mixing of 20 wt% $MgCO_3$ and 1.7 wt% $Al(OH)_3$, and un-reacted cristobalite was also detected with the cordierite. As the temperature was increased to $1400^{\circ}C$, the cordierite yield was gradually increased. Powder compacts of the synthesized cordierite were sintered between $1250^{\circ}C{\sim}1400^{\circ}C$; the sintered samples showed a low thermal expansion coefficient of $2.1{\times}10^{-6}/^{\circ}C$ and typical sintering behavior. It is anticipated that it will be possible to synthesize cordierite ceramics on a mass production scale using the mineral pyrophyllite.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.7
• /
• pp.587-593
• /
• 2007

Oil-based nanofluids were prepared by dispersing spherical and fiber shaped $Al_2O_3$ and AlN nanoparticles in transformer oil. Two hydrophobic surface modification processes using oleic acid (OA) and polyoxyethylene alkyl acid ester (PAAE) were compared in this study. The dispersion stability, viscosity and breakdown voltage of the nanofluids were also characterized. $(Al_2O_3+AlN)$ mixed nanofluid was prepared to take an advantage of the excellent thermal conductivity of AlN and a good convective heat transfer property of fiber shaped $Al_2O_3$. For $(Al_2O_3+AlN)$ particles with 1 % volume fraction in oil, the enhancement of thermal conductivity and convective heat transfer coefficient was nearly 11 % and 30 %, respectively, compared to pure transformer oil. The nanofluid, containing $Al_2O_3+AlN$, successfully lowered the temperature of the heating element and oil itself during a natural convection test using a prototype transformer.

• 한국연소학회:학술대회논문집
• /
• 2014.11a
• /
• pp.355-356
• /
• 2014

Catalytic steam reforming of tar produced from biomass gasification was conducted using several Ni-based catalysts. K and Mn were used as a promoter over $Ni/Ru/Al_2O_3$ catalyst. The pellet and monolith type catalysts were prepared and applied to lab and bench-scale biomass gasification system. The $Ni/Ru-K/Al_2O_3$ catalyst shown higher performance than $Ni/Ru-Mn/Al_2O_3$ catalyst at low temperature range.

• Korean Journal of Materials Research
• /
• v.13 no.1
• /
• pp.59-63
• /
• 2003

The microstructural characteristics of $Al_2$$O_3$/Cu composites hot-pressed at different temperatures for atmosphere switching from $H_2$to Ar have been studied. When the composite atmosphere was switched at $1000^{\circ}C$ it led to more homogeneous microstructure than when the atmosphere was switched at $1450^{\circ}C$. The strong sensitivity of Cu to atmosphere, especially the oxygen content in the atmosphere, was found to be responsible for the observed change, based upon the interfacial phenomena related to the formation of $CuAlO_2$. The practical implication of these results is that an optimum processing condition for the design of homogeneous microstructure and stable properties can be established.