• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.112-113
• /
• 2013

Thin CrAlMgSiN films, whose composition were 30.6Cr-11.1Al-7.3Mg-1.2Si-49.8N (at.%), were deposited on steel substrates in a cathodic arc plasma deposition system. They consisted of alternating crystalline Cr-N and AlMgSiN nanolayers. After oxidation at $800^{\circ}C$ for 200 h in air, a thin oxide layer formed by outward diffusion of Cr, Mg, Al, Fe, and N, and inward diffusion of O ions. Silicon ions were relatively immobile at $800^{\circ}C$. After oxidation at $900^{\circ}C$ for 10 h in air, a thin $Cr_2O_3$ layer containing dissolved ions of Al, Mg, Si, and Fe formed. Silicon ions became mobile at $900^{\circ}C$. After oxidation at $900^{\circ}C$ for 50 h in air, a thin $SiO_2-rich$ layer formed underneath the thin $Cr_2O_3$ layer. The film displayed good oxidation resistance. The main factor that decreased the oxidation resistance of the film was the outward diffusion and subsequent oxidation of Fe at the sample surface, particularly along the coated sample edge.

• Journal of the Semiconductor & Display Technology
• /
• v.20 no.4
• /
• pp.157-160
• /
• 2021

As an insulator for a thin film transistor(TFT) and an encapsulation material of organic light emitting diode(OLED), aluminum oxide (Al₂O₃) has been widely studied using several technologies. Especially, in spite of low deposition rate, atomic layer deposition (ALD) has been used as a process method of Al₂O₃ because of its low process temperature and self-limiting reaction. In the Al₂O₃ deposition by ALD method, Ar Purge had some crucial effects on the film properties. After reaction gas is injected as a formation of pulse, an inert argon(Ar) purge gas is injected for gas desorption. Therefore, the process parameter of Ar purge gas has an influence on the ALD deposited film quality. In this study, Al₂O₃ was deposited on glass substrate at a different Ar purge time and its structural characteristics were investigated and analyzed. From the results, the growth rate of Al₂O₃ was decreased as the Ar purge time increases. The surface roughness was also reduced with increasing Ar purge time. In order to obtain the high quality Al₂O₃ film, it was known that Ar purge times longer than 15 sec was necessary resulting in the self-limiting reaction.

• Current Photovoltaic Research
• /
• v.5 no.4
• /
• pp.135-139
• /
• 2017

We fabricated two different transparent conducting oxide thin films of ZnO doped with Ga ($Ga_2O_3$ 0.9 wt%) as well as Al ($Al_2O_3$ 2.1 wt%) (GAZO) and ZnO doped only with Al ($Al_2O_3$ 3 wt%) (AZO). It was investigated how it affects the moisture resistance of the transparent electrode. In addition, $Cu(In,Ga)Se_2$ thin film solar cells with two transparent oxides as front electrodes were fabricated, and the correlation between humidity resistance of transparent electrodes and device performance of solar cells was examined. When both transparent electrodes were exposed to high temperature distilled water, they showed a rapid increase in sheet resistance and a decrease in the fill factor of the solar cell. However, AZO showed a drastic decrease in efficiency at the beginning of exposure, while GAZO showed that the deterioration of efficiency occurred over a long period of time and that the long term moisture resistance of GAZO was better.

• Journal of the Korean Ceramic Society
• /
• v.51 no.3
• /
• pp.197-200
• /
• 2014

We investigated the influence of blistering on $Al_2O_3$/SiON stacks and $Al_2O_3$/SiNx:H stacks passivation layers. $Al_2O_3$ film provides outstanding Si surface passivation quality. $Al_2O_3$ film as the rear passivation layer of a p-type Si solar cell is usually stacked with a capping layer, such as $SiO_2$, SiNx, and SiON films. These capping layers protect the thin $Al_2O_3$ layer from an Al electrode during the annealing process. We compared $Al_2O_3$/SiON stacks and $Al_2O_3$/SiNx:H stacks through surface morphology and minority carrier lifetime after annealing processes at $450^{\circ}C$ and $850^{\circ}C$. As a result, the $Al_2O_3$/SiON stacks were observed to produce less blister phenomenon than $Al_2O_3$/SiNx:H stacks. This can be explained by the differences in the H species content. In the process of depositing SiNx film, the rich H species in $NH_3$ source are diffused to the $Al_2O_3$ film. On the other hand, less hydrogen diffusion occurs in SiON film as it contains less H species than SiNx film. This blister phenomenon leads to an increase insurface defect density. Consequently, the $Al_2O_3$/SiON stacks had a higher minority carrier lifetime than the $Al_2O_3$/SiNx:H stacks.

• Korean Journal of Materials Research
• /
• v.12 no.8
• /
• pp.676-681
• /
• 2002

Microstructure, mechanical properties, and oxidation resistance of TiAIN thin films deposited on quenched and tempered STD61 tool steel by arc ion plating were studied using XRD, XPS and micro-balance. The TiAIN film was grown with the (200) orientation. The grain size of TiAIN thin film decreased with increasing Al contents, while chemical binding energy increased with Al contents. When hard coating films were oxidized at $850^{\circ}C$ in air, oxidation resistance of both TiN and TiCN films became relatively lower since the surface of films formed non-protective film such as $TiO_2$. However, oxidation resistance of TiAIN film was excellent because its surface formed protective layer such as $_A12$$O_3$ and $_Al2$$Ti_{7}$$O_{15}$, which suppressed oxygen intrusion.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.87-87
• /
• 2010

We report a new patterning technique of inorganic materials by using thin-film transfer printing (TFTP) with atomic layer deposition. This method consists of the atomic layer deposition (ALD) of inorganic thin film and a nanotransfer printing (nTP) that is based on a water-mediated transfer process. In the TFTP method, the Al2O3 ALD growth occurs on FTS-coated PDMS stamp without specific chemical species, such as hydroxyl group. The CF3-terminated alkylsiloxane monolayer, which is coated on PDMS stamp, provides a weak adhesion between the deposited Al2O3 and stamp, and promotes the easy and complete release of Al2O3 film from the stamp. And also, the water layer serves as an adhesion layer to provide good conformal contact and form strong covalent bonding between the Al2O3 layer and Si substrate. Thus, the TFTP technique is potentially useful for making nanochannels of various inorganic materials.

• Journal of Korean Vacuum Science & Technology
• /
• v.5 no.1
• /
• pp.11-18
• /
• 2001

Dielectric passivation effects on the EM(electromigration) have been a great interest with recent ULSI and multilevel structure tends in thin film interconnections of a microelectronic device. SiO$_2$, PSG(phosphosilicate glass), and Si$_3$N$_4$ passivation materials effects on the EM resistance were investigated by utilizing widely used Al-1%Si thin film interconnections. A standard photolithography process was applied for the fabrication of 0.7㎛ thick 3㎛ wide, and 200㎛ ~1600㎛ long Al-1%Si EM test patterns. SiO$_2$, PSG, and Si$_3$N$_4$ dielectric passivation with the thickness of 300 nm were singly deposited onto the Al-1%Si thin film interconnections by using an APCVD(atmospheric pressure chemical vapor deposition) and a PECVD(plasma enhanced chemical vapor deposition) in order to investigate the passivation materials effects on the EM characteristics. EM tests were performed at the direct current densities of 3.2 $\times$ 10$\^$6/∼4.5 $\times$ 10$\^$6/ A/cm$^2$ and at the temperatures of 180 $\^{C}$, 210$\^{C}$, 240$\^{C}$, and 270$\^{C}$ for measuring the activation energies(Q) and for accelerated test conditions. Activation energies were calculated from the measured MTF(mean-time-to-failure) values. The calculated activation energies for the electromigration were 0.44 eV, 0.45 eV, and 0.50 eV, and 0.66 eV for the case of nonpassivated-, Si$_3$N$_4$passivated-, PSG passivated-, and SiO$_2$ passivated Al-1%Si thin film interconnections, respectively. Thus SiO$_2$ passivation showed the best characteristics on the EM resistance followed by the order of PSG, Si$_3$N$_4$ and nonpassivation. It is believed that the passivation sequences as well as the passivation materials also influence on the EM characteristics in multilevel passivation structures.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1123-1132
• /
• 1994

Bi-Sr-Ca-Cu-O superconductor thin films were prepared on MgO and LaAlO3 substrates by MOCVD technique. The films deposited on MgO and LaAlO3 substrates became superconducting at 64 K and 70 K respectively. The measured critical current density of thin film deposited on LaAlO3 substrate was around 104 A/$\textrm{cm}^2$. After annealing at $700^{\circ}C$ for 3 hours, the critical transition temperature(Tc) of films deposited on LaAlO3 was changed from 70 K to 74 K.

• Journal of Sensor Science and Technology
• /
• v.9 no.5
• /
• pp.389-395
• /
• 2000

In this paper, we propose the formation of an $Al_2O_3$ pre-layer using a protective Si-oxide layer and Al layer. Deposition of a thin film layer of aluminum onto a Si surface covered with a thin Si-oxide layer and annealing at $800^{\circ}C$ led to the growth of epitaxial $Al_2O_3$ layer on Si(111). And ${\gamma}-Al_2O_3$ layer was grown on the $Al_2O_3$ per-layer. Etching of the Si substrate by $N_2O$ gas could be avoided in the initial growth stage by the $Al_2O_3$ pre-layer. It was confirmed that the $Al_2O_3$ pre-layer was effective in improving the surface morphology of the very thin ${\gamma}-Al_2O_3$ films.

• Korean Journal of Materials Research
• /
• v.17 no.8
• /
• pp.447-451
• /
• 2007

We investigated the dependence of the various annealing conditions and thickness ($6\sim45nm$) of the Ti-doped $Al_2O_3$ coating on the electrochemical properties and the capacity fading of Ti-doped $Al_2O_3$ coated $LiCoO_2$ films. The Ti-doped-$Al_2O_3$-coating layer and the cathode films were deposited on $Al_2O_3$ plate substrates by RF-magnetron sputter. Microstructural and electrochemical properties of Ti-doped-$Al_2O_3$-coated $LiCoO_2$ films were investigated by transmission electron microscopy (TEM) and a dc four-point probe method, respectively. The cycling performance of Ti-doped $Al_2O_3$ coated $LiCoO_2$ film was improved at higher cut-off voltage. But it has different electrochemical properties with various annealing conditions. They were related on the microstructure, surface morphology and the interface condition. Suppression of Li-ion migration is dominant at the coating thickness >24.nm during charge/discharge processes. It is due to the electrochemically passive nature of the Ti-doped $Al_2O_3$ films. The sample be made up of Ti-doped $Al_2O_3$ coated on annealed $LiCoO_2$ film with additional annealing at $400^{\circ}C$ had good adhesion between coating layer and cathode films. This sample showed the best capacity retention of $\sim92%$ with a charge cut off of 4.5 V after 50 cycles. The Ti-doped $Al_2O_3$ film was an amorphous phase and it has a higher electrical conductivity than that of the $Al_2O_3$ film. Therefore, the Ti-doped $Al_2O_3$ coated improved the cycle performance and the capacity retention at high voltage (4.5 V) of $LiCoO_2$ films.