• Proceedings of the KWS Conference
• /
• 1994.05a
• /
• pp.72-74
• /
• 1994

• Journal of Welding and Joining
• /
• v.19 no.4
• /
• pp.379-383
• /
• 2001

Resistance spot welding has been widely used in the sheet metal joining processes because of low cost, high productivity and convenience. Recently, automobile and aerospace industries are trying to replace partly steel sheets with aluminum alloy sheets. But in the case of dissimilar materials, to apply resistance spot welding has been known to be very difficult owing to the effect of melting temperature. On this study, an effort was made to apply spot welding of dissimilar sheet metals, 2024 aluminum alloy and zinc coated steel sheet, evaluate the spot weld quality with tensile-shear strength test and nondestructive evaluation technique, C-scan image methodology. In this study results, as the current below 11 kA, melting of materials is not achieved well. Also as the current exceeds to 13.5 kA, the more spatters happen at welded zone and tensile-shear strength lowered. So, the feasibility of C-scan image technique proposed in the study is found to be suitable evaluation method for resistance spot weldability.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1317-1321
• /
• 2007

Aluminized steel sheet that Al coated on low carbon steel has a excellent heat resistance, thermal reflection and corrosion resistance. It has applied to fuel tank, automotive exhaust systems, etc. Laser weldability of the aluminized steel for the full penetration welding will be described in this paper. We focused on the effect of Al coating conditions on weld strength. For these objectives, aluminized steel sheets that has various thickness and coating weight were prepared for laser welding. And then, tensile-shear and hardness test were carried out. At that same time, Al content mixed in weld after laser welding was evaluated and investigated a correlation between the mixed Al and mechanical properties. Besides, as removing partially coating layer, weldability has been investigated according to position of coating layer. As a result of this study, as increasing Al content in weld, tensile-shear strength was decreased. Also it was identified that Al of coating layer caused grain growth.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.1
• /
• pp.19-28
• /
• 1994

A study on adhesion property of evaporated Al-Cr films was conducted on steel sheet by using two-source evaporator. Adhesion of Al-Cr coated steel was evaluated by tape test after $180^{\circ}$bending. Adhesion was decreased with increasing the Cr content in Al-Cr films. It was thought that the decrease in adhesion with increasing Cr content be related to insufficient wetting and diffusion of Cr atoms in the film. Best adhesion was achieved in the case of pure aluminum film..

• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.2
• /
• pp.89-97
• /
• 1993

An improvement in corrosion resistance of various types of Zn-coated steel sheets is thought to be possible with the addition of fine oxide powder to the coating. In this study the corrosion resistance of the $Al_2O_3$ dispersed Zn-Co-Cr electroplated steel sheet has been investigated and the results were as follows : The corrosion resistance of $Al_2O_3$ dispersed Zn-Co-Cr electroplated steel sheets was improved by increasing the contents of Co and Cr ions, and also $Al_2O_3$ powders in the bath because of the increased amount of Co, Cr and $Al_2O_3$ in deposits. In the $Al_2O_3$ dispersed Zn-Co-Cr electroplated steels sheet, the structure of deposits was changed from fine microstructure as observed in high Co containing deposits to coarse microstructure as in high Cr and $Al_2O_3$ containing deposits. By cold rolling of the $Al_2O_3$ dispersed Zn-Co-Cr electroplated steel sheets to about 2 percent, thr corrosion resistance was improved further.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.4
• /
• pp.183-188
• /
• 2008

Hot press forming allows geometrically complicated parts to be formed from sheet and the rapid cooling hardens them to extremely high strength. The main purpose of this research is to characterize Al coated layer in Al coated boron steel during hot press forming. For the hot press hardening experiment, test specimens were heated up to $810{\sim}930^{\circ}C$ and held for 3, 6 and 9 minutes, respectively. And then, some specimens were press hardened and others were air-cooled without any pressing for the comparison purpose. Al coated layer shows four distinct micro-structural regions of interest; diffusion zone, Al-Fe zone(I) low-Al zone(LAZ) and Al-Fe zone(II). Band-like LAZ is clearly shown at temperature ranges of $810{\sim}870^{\circ}C$ and sparsely dispersed at temperature higher than 900oC. The micro-cracking behavior in the Al coated layer during forming were also analyzed by bending and deep drawing tests. The strain concentration in softer LAZ is found to be closely related with micro-cracking and exfoliation in coated layer during forming.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.5
• /
• pp.454-460
• /
• 2016

Double-layered Al-Mg films have been deposited by using an e-beam deposition method on a cold-rolled steel sheet(CR), which the structure of the film was Al/Mg/CR. The micro-structure, alloy phase, and corrosion resistance of the Al-Mg coated CR were investigated before and after heat treatment at $400^{\circ}C$ for 2, 3, and 10 min in a nitrogen atmosphere. Total thickness of Al-Mg films was fixed at $3{\mu}m$ and the thickness ratio of Al and Mg layers(Al:Mg) has been changed from 5:1 to 1:5. The cross-sectional morphology of the films, which had the thickness ratio of 2:1(Al:Mg), 1:1, and 1:2, was changed after heat treatment from columnar to featureless structure. The x-ray diffraction data for as-deposited films showed only pure Al and Mg peaks. Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ phase appeared after the heat treatment. The Al-Mg coating with the thickness ratio of 1:1(Al:Mg) showed the best corrosion resistance of up to 500 hours by salt spray test.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.533-542
• /
• 2010

The specific motivation for joining an Al alloy and Zn-coated steel arises from the need to save fuel consumption by weight reduction and to enhance the durability of vehicle structures in the automobile industry. In this study, the lap joining A6K31 Al alloy (top) and SGARC340 Zn-coated steel (bottom) sheets with a thickness of 1.0 mm and 0.8 mm, respectively, was carried out using the friction stir weld (FSW) technique. The probe of a tool did not contact the surface of the lower Zn-coated steel sheet. The friction stir welding was carried out at rotation speeds of 1500 rpm and travel speeds of 80~200 mm/min. The effects of tool geometry and welding speed on the mechanical properties and the structure of a joint were investigated. The tensile properties for the joints welded with a larger tool were better than those for the joints done with a smaller tool. A good correlation between the tensile load and area of the welded region were observed. The bond strength using a larger tool (M4 and M3) decreased with an increase in welding speed. Most fractures occurred along the interface between the Zn-coated steel and the Al alloy. However, in certain conditions with a lower welding speed, fractures occurred at the A6K31 Al alloy.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.95-95
• /
• 2013

고온에서의 내열, 내변색 특성이 우수한 용융 Al 도금강판을 제조하기 위하여 소지 강 성분을 조정하여 내변색성, 내산화성 및 밀착성 향상 측면에서 초점을 두고 관찰하였다.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.4
• /
• pp.186-191
• /
• 2014

Double layer films which consisted of aluminum(Al) and magnesium(Mg) have been prepared by e-beam deposition. The structure, alloy phase, and corrosion resistance of the prepared films were investigated before and after heat treatment. The first (bottom) layer fixed with Al, and the thickness ratio between Al and Mg layers has been changed from 1 : 1 to 5 : 1, respectively. Total thickness of Al-Mg film was fixed at $3{\mu}m$. The cold-rolled steel sheet was used as a substrate. Heat treatment was fulfilled in an nitrogen atmosphere at the temperature of $400^{\circ}C$ for 2, 3 and 10 min. Surface morphology of as-deposited Al-Mg film having Mg top layer showed plate-like structure. The morphology was not changed even after heat treatment. However, cross-sectional morphology of Al-Mg films was drastically changed after heat treatment, especially for the samples heat treated for 10 min. The morphology of as-deposited films showed columnar structure, while featureless structure of the films appeared after heat treatment. The x-ray diffraction data for as-deposited Al-Mg films showed only pure Al and Mg peaks. However, Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ appeared after heat treatment of the films. It is believed that the formation of Al-Mg alloy phase affected the structure change of Al-Mg film. It was found that the corrosion resistance of Al-Mg film was increased after heat treatment.