• Korean Journal of Materials Research
• /
• v.21 no.3
• /
• pp.149-155
• /
• 2011

We investigated tribological characteristics of diamond-like carbon (DLC) in a condition with carbon nanotube (CNT) content of 1wt% in aqueous solution. Si-DLC films were deposited by radio frequency plasma enhanced chemical vapor deposition (RF-PECVD) process on Al6061 aluminum alloy. In this study, the deposition of DLC films was carried out in vacuum with a chamber pressure of 10-5 to 10-3 Torr achieved by mechanical pump followed by turbo molecular pump. The surface adsorbed oxygen on the Aluminum substrates was removed by passing Ar gas for 10 minutes. The RF power was maintained at 500W throughout the experiment. A buffer layer of HMDSO was deposited on the substrate to improve the adhesion of DLC coating. At this point CH4 gas was introduced in the chamber using gas flow controller and DLC coating was deposited on the buffer layer along with HMDSO for 50 min. The thickness of 1 ${\mu}m$ was obtained for DLC films on aluminum substrates The tribological properties of as synthesized DLC films were analyzed by wear test in the presence of dry air, water and lubricant such as CNT ink.

• Tribology and Lubricants
• /
• v.23 no.4
• /
• pp.170-174
• /
• 2007

Wear and scuffing tests were conducted using friction and wear measurement of piston rings and cylinder blocks in low friction diesel engine. The frictional forces, wear amounts and cycles to scuffing in boundary lubricated sliding condition were measured using the reciprocating wear tester. The cylinder blocks were used as reciprocating specimens, and the piston rings with several coatings were used as fixed pin. Several coatings were used such as DLC, TiN, Cr-ceramic and TiAlN in order to improve the tribological characteristics. From the tests wear volume of piston ring surfaces applied various coatings were compared. During the tests coefficients of friction were monitored. Test results showed that DLC coatings showed good tribological properties. TiN and Cr-ceramic coated rings showed good wear resistance properties but produced high friction.

• New & Renewable Energy
• /
• v.1 no.1 s.1
• /
• pp.64-71
• /
• 2005

The stability of alumina-coated NiO cathodes was studied in $Li_{0.62}/K_{0.38}$ molten carbonate electrolyte. Alumina was effectively coated on the porous Ni plate using galvanostatic pulse plating method. The deposition mechanism of alumina was governed by the concentration of hydroixde ions near the working electrode, which was controlled by the temperature of bath solution. Alumina-coated NiO cathodes were formed to $A1_2O_3-NiO$ solid solution by the oxidation process and their Ni solubilities were were than that of NiO up to the immersion time of 100h. However, their Ni solubilities increased and were similar to that of the bare NiO cathode after 100h. It was because aluminum into the solid solution was segregated to $\alpha-LiAlO_2$ on the NiO and its Product did not Play a role of the Physical barrier against NiO dissolution.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.77-78
• /
• 2006

In order to increase the efficiency of LED, transparent electrodes should be also developed. also suitable anti-reflection coating (ARC) is necessary for practical device applications. In our paper, Al-doped ZnO (AZO) films were fabricated by sputtering on GaP substrate(wavelength:620nm). Choosing optimum substrate temperature and sputtering rate, high quality AZO films were formed. We confirmed that the surface and electrical properties, which implemented using the methods of AFM, Hall measurement. The properties of AZO thin films especially depended on the thickness. We presumed that the change of the increase the external quantum efficiency of LED according to the AZO thin film of thickness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.252-255
• /
• 2004

Various Semiconductor/Metal structured nanowires were synthesized from the simple thermal annealing of ball-milled compound powders and the thermal evaporation of metals. Their structural properties were investigated by Scanning Electron Microscopy(SEM) and Transmission Electron Microscopy(TEM), Energy Dispersive X-ray spectroscopy(EDX). Depending on the type of metals and the material of nanowires, uniform somiconductor/metal nanowires(GaN/Al, GaN/Ag) or isolated metal particles on semiconductor nanowires$(SnO_2/Ti,\;Si/Ti)$ were formed on the surface of nanowires.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.152-157
• /
• 2006

New precursor solution with dichloroacetic acid (DCA) was developed for fabricating high $J_c$ REBCO film. DCA based-precursor solution was coated on $LaAlO_3$(001) substrate by dip coating method. Processing parameters such as oxygen partial pressure, water vapor, ramping rate and pyrolysis temperature were controlled in order to obtain a good epitaxial film. The film with thickness of 0.5 micrometer was obtained by single coating and no crack was observed at calcined films. Oxygen partial pressure was controlled in the range of $100{\sim}1,000$ ppm and conversion heat treatment was carried out at the temperature range of $705-765^{\circ}C$. A critical transition temperature ($T_c$) of 90 K and a critical transport current density ($J_c$) of $>0.5\;MA/cm^2$ (77 K and self-field) were obtained for the GdBCO film. It is thought that fluorine-free MOD solution using DCA is promising precursor solution for fabricating high quality REBCO films.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.131-133
• /
• 2012

The photoluminescence (PT) properties of Al-doped ZnO thin films grown by the sol-gel dip-coating method have been investigated. At 12 K, nine distinct PL peaks were observed at 2.037, 2.592, 2.832, 3.027, 3.177, 3.216, 3.260, 3.303, and 3.354 eV. The deep-level emissions (2.037, 2.592, 2.832, and 3.027 eV) were attributed to native defects. The near-band-edge (NBE) emission peaks at 3.354, 3.303, 3.260, 3.216, and 3.177 eV were attributed to the emission of the neutral-donor-bound excitons (D0X), two-electron satellite (TES), free-to-neutral-acceptors (e,A0), donor-acceptor pairs (DAP), and second-order longitudinal optical (2LO) phonon replicas of the TES (TES-2LO), respectively. According to Haynes' empirical rule, we calculated the energy of a free exciton (FX) to be 3.374 eV. The thermal activation energy for D0X in the nanocrystalline ZnO thin film was found to be ~25 meV, corresponding to the thermal dissociation energy required for D0X transitions.

• Carbon letters
• /
• v.6 no.2
• /
• pp.71-78
• /
• 2005

Anti-oxidation coatings are the key technique for carbon/carbon (C/C) composites used as the thermal structural materials. The microstructure and oxidation behavior of several kinds of high-performance ceramic coatings for C/C composites prepared in Northwestern Polytechnical University were introduced in this paper. It showed that the ceramic coatings such as SiC, Si-$MoSi_2$, SiC-$MoSi_2$, $Al_2O_3$-mullite-SiC and SiC/yttrium silicate/glass coatings possessed excellent oxidation resistance at high temperatures, and some of these coatings were characterized with excellent thermal shock resistance. The SiC-$MoSi_2$ coating system has the best oxidation protective property, which can effectively protect C/C composites from oxidation up to 1973 K. In addition, the protection and failure reasons of some coatings at high temperature were also provided.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.111.2-111.2
• /
• 2012

정보 기술 시대에 맞춰 광전소자의 연구가 활발해지면서 투명전극으로 사용될 수 있는 Transparent Conductive Oxide (TCO) 재료에 대한 관심이 높아지고 있다. 하지만 TCO의 대표적인 물질인 Indium Tin Oxide (ITO)의 경우 In의 가격 상승으로 인해 최근에는 낮은 전도도와 높은 투과도를 가질 수 있는 대체 물질에 대한 연구가 활발히 진행되고 있다. 그 중에서 3.2 eV 의 높은 밴드갭을 갖는 ZnO 는 가시광선 영역에서 높은 투과율을 나타낼 뿐만 아니라 Al, Ga을 도핑함으로써 낮은 전도도를 가질 수 있다. 이러한 TCO 재료는 surface texturing을 통하여 optical region 에서 반사를 억제 시킴으로서 빛을 모으는 역할을 하여 태양전지의 효율을 향상 시킬 수 있기 때문에 PV (Photovoltaics) Cell의 anti-reflective coating에 적용 할 수 있다. 본 연구에서는 pulsed DC magnetron sputtering을 이용하여 Ga-doped ZnO (GZO) 박막을 증착하였고, HCl 0.5 wt %로 wet etching을 통하여 surface texturing을 진행하였다. 결정성은 X-ray diffractometer (XRD)로 분석하였으며, 표면 형상은 Scanning Electron Microscope (SEM)을 통해 확인하였다. Van der Pauw 방법을 통해 resistivity, carrier concentration, hall mobility 등의 전기적 특성을 분석하였고 UV-Vis spectrophotometer 를 통해 투과도 및 반사도를 측정하였다.

• Corrosion Science and Technology
• /
• v.10 no.2
• /
• pp.43-46
• /
• 2011

Zinc consumption in a continuous galvanizing line is one of the highest operating cost items in the facility and minimizing zinc waste is a key economic objective for any operation. One of the primary sources of excessive loss of zinc is through the formation of top dross and skimmings in the coating pot. It has been reported that the top skimmings, manually removed from the bath, typically consist of more than 80% metallic zinc with the remainder being entrained dross particles ($Fe_2Al_5$) along with some oxides. Depending on the drossing practices and bath management, the composition of the removed top skimmings may contain up to 2 wt% aluminum and 1 wt% iron. On-going research efforts have been aimed at in-house recovery of the metallic zinc from the discarded top skimmings prior to selling to zinc recycling brokers. However, attempting to recover the zinc entrapped in the skimmings is difficult due to the complex nature of the intermetallic dross particles and the quality and volume of the recycled zinc is highly susceptible to fluctuations in processing parameters. As such, an efficient method to extract metallic zinc from top skimmings has been optimized through the use of a specialized thermo-mechanical process enabling a continuous galvanizing facility to conserve zinc usage on-site. Also, through this work, it has been identified that filtration of discrete dross particles has been proven effective at maintaining the cleanliness of the zinc. Future efforts may progress towards expanded utilization of filters in continuous galvanizing.