• Journal of the Korean Ceramic Society
• /
• v.32 no.8
• /
• pp.909-914
• /
• 1995

From alumina powder and TEOS, $\alpha$-Al2O3/SiO2 composite powder for reaction-sintered mullite was synthesized by heterogeneous coagulation and surface coating, and investigated the mullitization reaction and sintering behavor of these powders. In $\alpha$-Al2O3/SiO2 composite powder prepared by heterogeneous coagulation, each alumina particles were surrounded by silica particles of 50~60 nm in size. And the alumina particles in composite powder prepared by surface coating were coated by uniform silica layer with thickness of 50 nm. In both methods, mullitization reaction was completed at 1$650^{\circ}C$ for 3h, and specimen sintered above 145$0^{\circ}C$ was about 95% fo the theoretical relative density. Mullite grains formed from the reaction with composite powders showed spherical shape with a size of 1~2${\mu}{\textrm}{m}$.

• Korean Journal of Materials Research
• /
• v.31 no.6
• /
• pp.331-338
• /
• 2021

Ti-Al-Si target and Cr-Si target are sputtered alternately to develop a multi-layered nitride coating on a steel mold to improve die-casting lifetime. Prior to the multi-layer deposition, a CrN layer is developed as a buffer layer on the mold to suppress the diffusion of reactive elements and enhance the cohesive strength of the multi-layer deposition. Approximately 50 nm CrSiN and TiAlSiN layers are deposited layer by layer, and form about three ㎛-thickness of multi-layered coating. From the observation of the uncoated and coated steel molds after the acceleration experiment of liquid metal injection casting, the uncoated mold is severely eroded by the adhesion of molten metallic glass. On the other hand, the multi-layer coating on the mold prevents element diffusion from the metallic glass and mold erosion during the experiment. The multi-layer structure of the coating transforms the nano-composite structured coating during the acceleration test. Since the nano-composite structure disrupts element diffusion to molten metallic glass, despite microstructure changes, the coating is not eroded by the 1,050 ℃ molten metallic glass.

• Journal of the Korean institute of surface engineering
• /
• v.20 no.2
• /
• pp.49-59
• /
• 1987

The properties of $Cr_2O_3-Al_2O_3-SiO_2$ composite oxide coatings on steel surface were investigated. The results obtained were as follows: The microhardness of oxide coating layer increased with increasing heat-treatment temperature and $Cr_2O_3$ content in coating layer. The hardness showed the highest value (850Hv) treated at 700$^{\circ}C$ for $SiO_2:Al_2O_3:Cr_2O_3$=1:1:4. Increasing heat-treatment temperature, corrosion current density became lower and coating layer became denser. The corrosion current density showed the lowest value $(6.5{\times}10^{-5}\;Acm^2)$ treated at 750$^{\circ}C\;for\;SiO_2:Al_2O_3:Cr_2O_3$=1:1:3. These results were explained by protective layer which was formed during heat-treatment. The bonding between matrix and coating layer is expected to be made mechanically and chemically by the inter diffusion of Ni and Fe. The composite oxide coating was formed by softening of the binder with increasing heat-treatment temperature. The strengthening of coating layer is to be resulted from the dispersion of major oxide particles.

• Journal of Korea Foundry Society
• /
• v.5 no.3
• /
• pp.19-26
• /
• 1985

This study has been carried out to examine into wettability of Cu-5%Sn alloy in $Al_2O_3$, MgO, $SiO_2$ and graphite, respectively and investigated into the change in macrostructure of Cu-5%Sn alloy according to kind and mixing rate of mold-coating. The results obtained from the experiment are summerized as follows; 1. Cu Cu-5%Sn alloy, wettabilities of $Al_2O_3$ and MgO were good, on the other hand, wettabilities of $SiO_2$ and graphite were bad. 2. The fine equiaxed zone was created because of the role of $Al_2O_3$ and MgO as preferential nucleation sites. 3. Notwithstanding change of mixing rate of $SiO_2$ in mold coating the equixed zone was not created. 4. The area of equiaxed zone was varied according to mixing rate in the case of using $Al_2O_3$ and MgO in mold-coating.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.2
• /
• pp.109-115
• /
• 2022

The demand for metal 3D printing technology is increasing in various industries. The materials commonly used for metal 3D printing include aluminum alloys, titanium alloys, and stainless steel. In particular, for applications in the aviation and defense industry, aluminum alloy 3D printing parts are being produced. To improve the corrosion resistance in the 3D printed aluminum alloy outputs, a post-treatment process, such as chromate coating, should be applied. However, powdered materials, such as AlSi7Mg and AlSi10Mg, used for 3D printing, have a high silicon content; therefore, a suitable pretreatment is required for chromate coating. In the desmut step of the pretreatment process, the chromate coating can be formed only when a smut composed of silicon compounds or oxides is effectively removed. In this study, suitable desmut solutions for 3D printed AlSi7Mg and AlSi10Mg materials with high silicon contents were presented, and the chromate coating properties were studied accordingly. The smut removal effect was confirmed using an aqueous desmut solution composed of sulfuric, nitric, and hydrofluoric acids. Thus, a chromate coating was successfully formed. The surfaces of the aluminum alloys after desmut and chromate coating were analyzed using SEM and EDS.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.10
• /
• pp.665-670
• /
• 2016

Prevailing dissemination of machine tools and cutting technology have caused drastic developments of high speed dry machining with work materials of high hardness, and demands on the high-hardness-materials with high efficiency have become increasingly important in terms of productivity, cost reduction, as well as environment-friendly issue. Addition of Si to TiAlN has been known to form nano-composite coating with higher hardness of over 30 GPa and oxidation temperature over $1,000^{\circ}C$. However, it is not easy to add Si to TiAlN by using conventional PVD technologies. Therefore, Ti-Al-Si-N have been prepared by hybrid process of PVD with multiple target sources or PVD combined with PECVD of Si source gas. In this study, a single composite target of Ti-Al-Si was prepared by powder metallurgy of MA (mechanical alloying) and SPS (spark plasma sintering). Properties of he resulting alloying targets were examined. They revealed a microstructure with micro-sized grain of about $1{\sim}5{\mu}m$, and all the elements were distributed homogeneously in the alloying target. Hardness of the Ti-Al-Si-N target was about 1,127 Hv. Thin films of Ti-Al-Si-N were prepared by unbalanced magnetron sputtering method by using the home-made Ti-Al-Si alloying target. Composition of the resulting thin film of Ti-Al-Si-N was almost the same with that of the target. The thin film of Ti-Al-Si-N showed a hardness of 35 GPa and friction coefficient of 0.66.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.128-129
• /
• 2007

Cr-Al-N, Cr-Si-N 그리고 Cr-Al-Si-N 코팅막을 WC-Co 모재위에 AIP법과 DC 마그네트론 스퍼터링 법을 결합한 하이브리드 시스템을 이용하여 합성하였으며, Si함량에 따른 Cr-Al-Si-N 코팅막의 미세구조, 기계적 특성과 마찰 거동에 관해 비교 연구하였다. Cr-Si-N(${\sim}35GPa$)과 Cr-Al-Si-N(${\sim}55GPa$) 코팅막의 경도값은 CrN(${\sim}23GPa$)과 Cr-Al-N(${\sim}25GPa$) 코팅막과 비교하여 각각 증가하였고, CrN(${\sim}0.50$)과 Cr-Al-N(${\sim}0.84$)의 평균 마찰계수는 Si 함량이 9 at.% 일때, Cr-Si-N(${\sim}0.30$)과 Cr-Al-Si-N(${\sim}0.57$)으로 각각 감소하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.255-255
• /
• 2015

나노압침방법을 적용하여 arc ion plating을 통해 제조된 TiAlSiN 코팅층의 질소 함량에 따른 나노 기계적 특성을 평가하였다. 코팅층의 질소 함량은 28~30 [at.%] 이었다. 코팅층에는 AlN, TiSi, $Al_5Ti_3$, $Ti_3AlN$, $Al_5Ti_2$ 상이 형성되었다. 질소 함량이 더 작은 코팅층의 나노경도, 마찰계수, 피로한계의 값이 높아짐을 알 수 있었다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.117-118
• /
• 2012

• Journal of the Korean institute of surface engineering
• /
• v.50 no.5
• /
• pp.339-344
• /
• 2017

Highly corrosion resistance performance of CrAlSiN coatings were obtained by applying ultrathin $Al_2O_3$ thin films using atomic layer deposition (ALD) method. CrAlSiN coatings were prepared on Cr adhesion layer/SUS304 substrates by a hybrid coating system of arc ion plating and high power impulse magnetron sputtering (HiPIMS) method. And, ultrathin $Al_2O_3$ passivation layer was deposited on the CrAlSiN/Cr adhesion layer/SUS304 sample to protect CrAlSiN coatings by encapsulating the whole surface defects of coating using ALD. Here, the high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX) analysis revealed that the ALD $Al_2O_3$ thin films uniformly covered the inner and outer surface of CrAlSiN coatings. Also, the potentiodynamic and potentiostatic polarization test revealed that the corrosion protection properties of CrAlSiN coatings/Cr/SUS304 sample was greatly improved by ALD encapsulation with 50 nm-thick $Al_2O_3$ thin films, which implies that ALD-$Al_2O_3$ passivation layer can be used as an effect barrier layer of corrosion.