Aluminum alloys are extensively employed in several industries, such as automobile, aerospace, and architecture, owing to their high specific strength and electrical and thermal conductivities. However, to meet the rising industrial demands, aluminum alloys must be designed with both excellent mechanical and thermal properties. Computer-aided alloy design is emerging as a technique for developing novel alloys to overcome these trade-off properties. Thus, the development of a new experimental method for designing alloys with high-throughput confirmation is gaining focus. A new approach that rapidly manufactures aluminum alloys with different compositions is required in the alloy design process. This study proposes a combined approach to rapidly investigate the relationship between the microstructure and properties of aluminum alloys using a direct energy deposition system with a dual-nozzle metal 3D printing process. Two types of aluminum alloy powders (Al-4.99Si-1.05Cu-0.47Mg and Al-7Mg) are employed for the 3D printing-based combined method. Nine types of Al-Si-Cu-Mg alloys are manufactured using the combined method, and the relationship between their microstructures and properties is examined.

• 한국주조공학회지
• /
• 제17권4호
• /
• pp.379-384
• /
• 1997

Al-15Cu-lMg alloys have been directionally solidified in 3mm diameter alumina tubes under the conditions of $760^{\circ}C$ of furnace temperature and 12 cm/hr of furnace moving velocity(V). By analyzing the evolution of the temperature profiles along the alloy length, the position of the solid/liquid interface, temperature gradient(G) and local growth velocity (R) were determined. These growth characteristics were compared for 6, 10, 14 cm length alloys. Steady state growth region was obtained in 15 cm length alloy, not in 6, 10 cm.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.86-86
• /
• 2002

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.85-85
• /
• 2002

• 한국주조공학회지
• /
• 제42권6호
• /
• pp.337-346
• /
• 2022

본 연구에서는 Al-7Si-(0.3~0.5)Mg-(0~0.5)Cu 합금의 용체화 처리 조건 최적화를 위해 545℃ 온도 조건에서 최대 7시간까지 용체화 처리를 수행한 후 광학현미경 및 FE-SEM을 활용한 미세조직 관찰 및 브리넬 경도 측정을 수행하였다. 합금 내 공정 Si 상은 용체화 처리 초반 3시간 동안 급격한 조대화 현상을 나타내었으며, 이후에는 용체화 처리가 진행되어도 Si 상 크기는 크게 변화하지 않았다. 한편 공정 Si 상의 구상화의 경우, 용체화 처리 시간이 7시간에 도달할 때 까지 지속적으로 진행되었다. Cu가 첨가된 합금의 주방상태에서는 Q-Al₅Cu₂Mg₈Si₆ 상과 θ-Al₂Cu 상이 확인되었으나, 545℃에서 3시간 동안 진행된 용체화 처리 이후에는 모두 분해되었다. 주방상태에서 확인된 π-Al₈FeMg₃Si 상은 5시간의 용체화 처리 이후에 사라지거나(0.3wt%Mg) 혹은 7시간의 용체화 처리 이후에도 존재(0.5wt%Mg)하였다. 초정 α상 내 Mg 및 Cu 함량은 용체화 처리 시간이 5시간에 도달할 때 까지 증가하였으며, 이는 Mg 및 Cu를 함유한 금속간 화합물의 용체화 시간에 따른 분해 거동과 일치하였다. Al-7Si-Mg-Cu 합금의 용체화 처리 과정에서 확인한 미세조직 변화를 종합적으로 고려할 때, 본 연구에서 다룬 합금의 석출강화 효과 극대화를 위해서는 545℃ 조건에서 최소 5시간의 용체화 처리가 필요한 것으로 판단되며, 용체화 처리 조건 별로 측정된 브리넬 경도 데이터로부터 동일한 최적 용체화 처리 조건을 도출할 수 있었다.

• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.86-94
• /
• 2000

This study was performed to investigate types and formation mechanism of cracks in two Al alloy welds, A5083 and A7N01 spot-welded by pulse Nd : YAG laser, using SEM, EPMA and Micro-XRD. In the weld zone, three types of crack were observed : center line crack({TEX}$C_{C}${/TEX}), diagonal crack({TEX}$C_{D}${/TEX}), and U shape crack({TEX}$C_{U}${/TEX}). Also, HAZ crack({TEX}$C_{H}${/TEX}) was observed in the HAZ region, furthermore, mixing crack({TEX}$C_{M}${/TEX}) consisting of diagonal crack and HAZ crack was observed. White film was formed at th hot crack region in the fractured surface after it was immersed to 10% NaOH water. In the case of A5083 alloy, white films in {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack region were composed of low melting phases, {TEX}$Fe_{2}SiAl_{8}${/TEX} and eutectic phases, $Mg_2$Al$_3$ and $Mg_2$Si. Such films observed $CuAl_2$, {TEX}$Mg_{32}(Al,Zn)_{3}${/TEX}, MgZn$_2$, $Al_2$CuMg and $Mg_2$Si were observed in the whitely etched films near {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack regions. The formation of liquid films was due to the segregation of Mg, Si, Fe in the case of A5083 alloy and Zn, Mg, Cu, Sim in the case of A7N01 alloy, respectively. The {TEX}$C_{C}${/TEX} and {TEX}$C_{D}${/TEX} cracks were regarded as a result of the occurrence of tensile strain during the welding process. The formation of {TEX}$C_{M}${/TEX} crack is likely to be due to the presence of liquid film at the grain boundary near the fusion line in the base metal as well as in the weld fusion zone during solidification. The {TEX}$C_{U}${/TEX} crack is considered a result of the collapsed keyhole through incomplete closure during rapid solidification.

• 한국표면공학회지
• /
• 제22권4호
• /
• pp.179-184
• /
• 1989

This study seeks to the morphological changes in the oxide skin of the Al-10wt.%si alloy melts. These changes depend on the oxidation time and the temperature of the molten alloy, as well as the effects of adding Mg, Cu and Ni. Thess affects observed by X-ray diffractometer(XRD) and scanning electron microscope(SEM)' Very litte oxide skins on Al-10wtwt.%Si alloy melts can be detected by XRD because it is less than the measuring capabillity of the XRD, or the formation of noncrystalline oxide skins oxide skins canbe deteced by SEM. The addition of 1%Mg and 1%Cu-1%Mg-2.5%Ni to this base alloy crystallized the structure of the oxide skins and increased the oxidation in proportion to the length of time, but adding 3% had hardiy anyaffect at all on the crystal structure of the oxide skins.

• 대한금속재료학회지
• /
• 제48권5호
• /
• pp.436-444
• /
• 2010

The hot tear susceptibility of Al alloys was investigated by using a constrained-rod mold designed to quantify 8 types of tear tendency. The severity of the crack was scored by 5 grades on a scale of 0 to 4, with 0 being "no crack formed" and 4 being "complete separation by crack". The Hot Tear Susceptibility index (HTS) which consists of crack type scores and position scores, was proposed to compare the hot tear tendency of Al alloys. A356.0 cast alloy and AA6061 wrought Al alloy showed an HTS value of 27.5 and 53 respectively. The effects of Si, Cu, and Mg content on hot tear tendency were also investigated with a constrained-rod mold. The variation of HTS values with alloying elements represents similar behavior in the variation of the solidification range in a pseudo binary phase diagram.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2004년도 추계학술대회 논문집
• /
• pp.355-358
• /
• 2004

In this study, the deformation characteristics of grain-size controlled rheology materials surfaces were investigated as a part of the research on the surface crack prediction in semi-solid formed automobile components. The microstructure of rheology Al-Si alloys consists of primary and eutectic regions. In eutectic regions the crack initiation begins with initial fracture of the eutectic silicon particles and inside other intermetallic phases. Nano-deformation characteristics in the eutectic and primary region of semi-solid aluminum alloys (356 alloy and 319 alloy) were investigated through the nanoindentation/scratch experiments and the AFM observation.

• 대한금속재료학회지
• /
• 제47권4호
• /
• pp.223-227
• /
• 2009

The precipitates, hardness, and tensile properties of Al-6.2Si-2.9Cu AC2B alloy were investigated with respect to solution treatment time at $500^{\circ}C$. $Al(Cu)-Al_2Cu$ eutectic, Si, ${\theta}-(Al_2Cu)$, and $Q-(Al_5Cu_2Mg_8Si_6)$ phases were observed in the as-cast specimen. With increasing the solution treatment time at $500^{\circ}C$, the $Al(Cu)-Al_2Cu$ eutectic and ${\theta}-(Al_2Cu)$ phases were gradually reduced and finally almost disappeared in 5 h. The mechanical properties, such as hardness, tensile strength, and elongation, were improved with solution treatment time until about 5 h due to the dissolution of the $Al_2Cu$ particles. With further holding time, the mechanical properties did not change much. The solution treated specimens for over 5 h at $500^{\circ}C$ exhibit almost the same tensile properties even after aging at $250^{\circ}C$ for 3.5 h. Accordingly, the optimal solution treatment condition of the Al-Si-Cu AC2B alloy is considered to be 5 h at $500^{\circ}C$.