ZnO:Al thin film for application to FBAR's bottom electrode using ZnO piezoelectric thin film were prepared by FTS, in order to improve the crystallographic properties of ZnO thin films because the ZnO:Al thin film and ZnO thin films structure is equal each other. So we prepared the ZnO:Al thin film with oxygen gas flow rate. Thickness and c-axis preferred orientation and electric properties of ZnO:Al bottom electrode were evaluated by $\alpha$-step, XRD and 4-point probe..

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.4
• /
• pp.422-425
• /
• 2004

In this study, the AZO thin films were prepared as a function of oxygen gas flow ratio at room temperature by FTS(Facing Targets Sputtering) apparatus using Zn:Al(metal)-Zn:Al(metal) or Zn(metal)-ZnO:Al(ceramic). The film thickness, crystalline and electric properties of AZO thin film was evaluated by $\alpha$-step, XRD and 4-point probe. In the results, the resistivity of AZO thin film was shown the lowest value about 8${\times}$10$^{-2}$ $\Omega$-cm(Zn:Al-Zn:Al), 3${\times}$10$^{-1}$ $\Omega$-cm(Zn-ZnO:Al) at the oxygen gas flow ratio 0.3. And the AZO thin film has good crystalline at oxygen gas flow ration 0.4, using Zn:Al-Zn:Al targets.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1998.09a
• /
• pp.85-90
• /
• 1998

Reactive ion etching (RIE) of Ta-Al alloy thin film and SiO2 thin films was observed during the etching with the CF4 gas and the could be used effectively to etch the Ta-Al alloy thin film. The etching rate of the thin film at a Ta content of 50 mol% was about 67$\AA$/min. No selectivity between the Ta-Al alloy thin film and SiO2 thin films was observed during the etching with the CF4 gas and the etching rate of the SiO2 layer was 12 times faster than that of the Ta-Al alloy thin film. In addition, it was observed that photoresist of AZ5214 was more useful than Shiepley 1400-2 in RIE with the CF4 gas.

• Journal of the Korean Vacuum Society
• /
• v.8 no.1
• /
• pp.31-35
• /
• 1999

In this paper, the lifetime dependence as a function of the line length of Al-1%Si thin film interconnections due to electromigration in semiconductor devices was studied. Al-1%Si thin film interconnections with a pattern of straight type were formed by using a standard photolithography process. The test patterns manufactured have line lengths in the range of 100 to 1600 $mu extrm{m}$. Al-1%Si thin film interconnections with Ti underlayers showed longer lifetime than those without Ti underlayers. Ti underlayers are believed to improve electromigration resistance resulting in a longer lifetime in Al-1%Si thin film interconnections. The dependence of lifetime on the line length in Al-1%Si/Ti thin film interconnections shows a saturation tendency near 800 $\mu\textrm{m}$ line length.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2006.05a
• /
• pp.164-167
• /
• 2006

In this paper, we prepared Al doped ZnO thin films by using facing targets sputtering method. Al doped ZnO thin film was deposited with different working pressure on flexible substrate. We prepared Al doped ZnO thin film at room temperature, because the flexible substrate has weak thermal resistance. From the results, we could obtain thin film with a resistivity of $8.4{\times}10^{-4}{\Omega}cm$, an average transmittance of over 80% and a film thickness of 200nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.235-236
• /
• 2008

Wet etched ZnO:Al films for thin film solar cells were prepared by Facing Target sputtering(FTS) method. Wet etching has been used to produce a rough TCO surface that enables light trapping in the absorber. The ZnO:Al films for thin film solar cells were etched by HCl 0.5%. The etching performance of ZnO:Al films can be tuned by changing etching time. The etched ZnO:Al films compared to a smooth ZnO:Al thin film structure. From the results, the lowest resistivity of deposited films was $5.67\times10^{-4}$ [$\Omega$-cm] and the transmittance of all ZnO:Al thin films were over 80% in visible range.

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.149-154
• /
• 1996

ZnO and Al-doped ZnO thin films were prepared by sol-gel dip-coating method and electrical and optical properties of films were investigated. Using the zinc acetate dihydrate and acetylaceton(AcAc) as a chelating agent stable ZnO sol was synthesized with HCl catalyst. Adding aluminium chloride to the ZnO sol Al-doped ZnO sol could be also synthesized. As Al contents increase the crystallinity of ZnO thin film was retarded by increased compressive stress in the film resulted from the difference of ionic radius between Zn2+ and Al3+ The thickness of ZnO and Al-doped ZnO thin film was in the range of 2100~2350$\AA$. The resistivity of ZnO thin films was measured by Van der Pauw method. ZnO and Al-doped ZnO thin films with annealing temperature and Al content had the resistivity of 0.78~1.65$\Omega$cm and ZnO and Al-doped ZnO thin film post-annealed at 40$0^{\circ}C$ in vacuum(5$\times$10-5 torr) showed the resistivity of 2.28$\times$10-2$\Omega$cm. And the trans-mittance of ZnO and Al-doped ZnO thin film is in the range of 91-97% in visible range.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.246-250
• /
• 2000

Reactive radio frequency (RF)magnetron sputter has been used to deposit AlN thin film on a Si substrate. (002)Preferred orientation of AlN thin film has been obtained at low sputtering pressure and high $\textrm{N}_2$ concentration. Also it has been shown that properties of AlN thin film are affected by presputtering time. As presputtering time increased aluminum and nitride concentration of AlN thin film decreased. But oxygen concentration and grain size increased. The good preferred orientation was shown with the short presputtering time.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.3
• /
• pp.177-181
• /
• 2011

We have studied structural, optical, and electrical properties of the Al-doped ZnO (AZO) thin films being usable in transparent conducting oxides. The AZO thin films were deposited on the corning 1737 glass plate by the RF magnetron sputtering system. To find optimal properties of AZO for transparent conducting oxides, the RF power in sputtering process was varied as 40 W, 60 W, and 80 W, respectively. As RF power increased, the crystallinity of AZO thin film was decreased, the optical bandgap of AZO thin film increased. The transmittance of the film was over 80% in the visible light range regardless of the changes in RF power. The measurement of Hall effect characterizes the whole thin film as n-type, and the electrical property was improved with increasing RF power. The structural, optical, and electrical properties of the AZO thin films were affected by Al dopant content in AZO thin film.

• Journal of Korean Vacuum Science & Technology
• /
• v.7 no.2
• /
• pp.39-44
• /
• 2003

Recent ULSI and multilevel structure trends in microelectronic devices minimize the line width down to a quarter micron and below, which results in the high current densities in thin film interconnections. Under high current densities, an EM(electromigration) induced failure becomes one of the critical problems in a microelectronic device. This study is to improve thin film interconnection materials by investigating the EM characteristics in PSG(phosphosilicate glass)/SiO$_2$ passivated Al-l%Si thin film interconnections. Straight line patterns, wide and narrow link type patterns, and meander type patterns, etc. were fabricated by a standard photholithography process. The main results are as follows. The current crowding effects result in the decrease of the lifetime in thin film interconnections. The electric field effects accelerate the decrease of lifetime in the double-layered thin film interconnections. The lifetime of interconnections also depends upon the current conditions of P.D.C.(pulsed direct current) frequencies applied at the same duty factor.