• 한국재료학회지
• /
• 제12권8호
• /
• pp.669-675
• /
• 2002

CrN film coated by AIP method, improved the mechanical properties (Hardness, Roughness, wear and fatigue) of Ti-6Al-4V alloy. The properties were studied using GXRD, XPS, Hardness, Roughness, wear and fatigue testers. CrN thin film thickness was about 7.5$\mu\textrm{m}$ and grew with (111) orientation. Hardness of CrN thin film was very high (Hv 1390) and roughness of the surface layer was greatly improved (Ra=0.063$\mu\textrm{m}$) compared with matrix alloy (Ra=0.321$\mu\textrm{m}$). Such changes of hardness and roughness could be contributed to improving the wear resistance and fatigue life. Striation like pattern with dimples and voids, a typical fatigue fracture mode, was observed throughout the specimen.

• Journal of Electrical Engineering and Technology
• /
• 제9권2호
• /
• pp.609-614
• /
• 2014

We fabricated amorphous zinc tin oxide (ZTO) transparent thin-film transistors (TTFTs). The effects of Al electrode on the mobility and threshold voltage of the ZTO TTFTs were investigated. It was found that the aluminum (Al)-ZTO contact decreased the mobility and increased the threshold voltage. Traps, originating from $AlO_x$, were assumed to be the cause of degradation. An indium tin oxide film was inserted between Al and ZTO as a buffer layer, forming an ohmic contact, which was revealed to improve the performance of ZTO TTFTs.

• 한국산업융합학회 논문집
• /
• 제26권5호
• /
• pp.743-750
• /
• 2023

Aluminum alloy is a material widely used in the aircraft industry. However, since it has relatively low hardness, strength and tribological properties, it is necessary to improve these properties. In this paper, a TiN thin film was coated on the surface of AL7075-T7351 using DC magnetron sputtering. The coating was performed by setting different deposition pressure, deposition time, and applied power. Then, the tribological properties of the thin film were investigated. As a result of the experiment, the hardness of the thin film was higher than that of the base material, and the specimen with the highest hardness had excellent friction coefficient, wear amount, and adhesive strength characteristics. Through this study, it was confirmed that the tribological characteristics of aluminum alloy can be improved by depositing thin films using DC magnetron sputtering.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 센서 박막재료 반도체재료 기술교육
• /
• pp.82-85
• /
• 2002

In recent years, the tantalum nitride(TaN) thin-film has been developed for the electronic resistor and capacitor. In this papers, this study presents the surface profile and sheet-resistance property relationship of reactive-sputtered TaN thin film resistor processed by buffer of Ti and Cr on alumina substrate. The TCR properties of the TaN films were discussed in terms of reactive gas ratio, ratio of nitrogen, crystallization and thin films surface morphology due to annealing temperature. It is clear that the TaN thin-films resistor electrical properties are low TCR related with it's buffer layer condition. Ti buffer layer thin film resistor having a good thermal stability and lower TCR properties then Cr buffer expected for the application to the dielectric material of passive component.

• 한국재료학회지
• /
• 제24권12호
• /
• pp.645-651
• /
• 2014

GaN is most commonly used to make LED elements. But, due to differences of the thermal expansion coefficient and lattice mismatch with sapphire, dislocations have occurred at about $109{\sim}1010/cm^2$. Generally, a low temperature GaN buffer layer is used between the GaN layer and the sapphire substrate in order to reduce the dislocation density and improve the characteristics of the thin film, and thus to increase the efficiency of the LED. Further, patterned sapphire substrate (PSS) are applied to improve the light extraction efficiency. In this experiment, using an AlN buffer layer on PSS in place of the GaN buffer layer that is used mainly to improve the properties of the GaN film, light extraction efficiency and overall properties of the thin film are improved at the same time. The AlN buffer layer was deposited by using a sputter and the AlN buffer layer thickness was determined to be 25 nm through XRD analysis after growing the GaN film at $1070^{\circ}C$ on the AlN buffer CPSS (C-plane Patterned Sapphire Substrate, AlN buffer 25 nm, 100 nm, 200 nm, 300 nm). The GaN film layer formed by applying a 2 step epitaxial lateral overgrowth (ELOG) process, and by changing temperatures ($1020{\sim}1070^{\circ}C$) and pressures (85~300 Torr). To confirm the surface morphology, we used SEM, AFM, and optical microscopy. To analyze the properties (dislocation density and crystallinity) of a thin film, we used HR-XRD and Cathodoluminescence.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.112-112
• /
• 2009

In this study, the effect of a long post-deposition thermal annealing(600 and 1000 $^{\circ}C$) on the surface acoustic wave (SAW) properties of polycrystalline (poly) aluminum-nitride (AlN) thin films grown on a 3C-SiC buffer layer was investigates. The poly-AlN thin films with a (0002) preferred orientation were deposited on the substrates by using a pulsed reactive magnetron sputtering system. Experimental results show that the texture degree of AlN thin film was reduced along the increase in annealing temperature, which caused the decrease in the electromechanical coupling coefficient ($k^2$). The SAW velocity also was decreased slightly by the increase in root mean square (RMS) roughness over annealing temperature. However, the residual stress in films almost was not affect by thermal annealing process due to small lattice mismatch different and similar coefficient temperature expansion (CTE) between AlN and 3C-SiC. After the AlN film annealed at 1000 $^{\circ}C$, the insertion loss of an $IDT/AlN/3C-SiC/SiO_2/Si$ structure (-16.44 dB) was reduced by 8.79 dB in comparison with that of the as-deposited film (-25.23 dB). The improvement in the insertion loss of the film was fined according to the decrease in the grain size. The characteristics of AlN thin films were also evaluated using Fourier transform-infrared spectroscopy (FT-IR) spectra and X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM) images.

• 한국재료학회지
• /
• 제29권9호
• /
• pp.567-577
• /
• 2019

Aluminum nitride (AlN) has versatile and intriguing properties, such as wide direct bandgap, high thermal conductivity, good thermal and chemical stability, and various functionalities. Due to these properties, AlN thin films have been applied in various fields. However, AlN thin films are usually deposited by high temperature processes like chemical vapor deposition. To further enlarge the application of AlN films, atomic layer deposition (ALD) has been studied as a method of AlN thin film deposition at low temperature. In this mini review paper, we summarize the results of recent studies on AlN film grown by thermal and plasma enhanced ALD in terms of processing temperature, precursor type, reactant gas, and plasma source. Thermal ALD can grow AlN thin films at a wafer temperature of $150{\sim}550^{\circ}C$ with alkyl/amine or chloride precursors. Due to the low reactivity with $NH_3$ reactant gas, relatively high growth temperature and narrow window are reported. On the other hand, PEALD has an advantage of low temperature process, while crystallinity and defect level in the film are dependent on the plasma source. Lastly, we also introduce examples of application of ALD-grown AlN films in electronics.

• 한국전기전자재료학회논문지
• /
• 제25권12호
• /
• pp.969-973
• /
• 2012

AlN thin films were deposited on p-type Si(100) substrates by RF magnetron sputtering method. This study showed the change of the preferential orientation of AlN thin films deposition with the change of the deposition conditions such as sputtering pressure and Ar/N2 gas ratio in chamber. It was identified by X-ray diffraction patterns that AlN thin film deposited at low sputtering pressure has a (002) orientation, however its preferred orientation was changed from the (002) to the (100) orientation with increasing sputtering pressure. Also, it was observed that the properties of AlN thin films such as thickness, grain size and surface roughness were largely dependent on Ar/$N_2$ gas ratio and a high quality thin film could be prepared at lower nitrogen concentration. AlN thin films were investigated relationship between preferential orientation and deposition condition by using XRD, FE-SEM and PFM.

• 한국진공학회지
• /
• 제15권1호
• /
• pp.89-96
• /
• 2006

최근 미세전자 소자에서 초고집적, 적층구조 추세는 선폭이 $0.25{\mu}m$ 이하까지 소형화되고 있는 실정이다. 이러한 미세화는 박막배선에서 높은 전류밀도를 초래하게 된다. 높은 전류밀도 하에서는 엘렉트로마이그레이션에 의한 결함발생이 미세전자 소자에서의 치명적인 문제점의 하나로 대두되고 있다. 본 연구는 Ag, Cu, Au, 그리고 Al 박막 등에서 엘렉트로마이그레이션 특성을 조사함으로써 박막배선 재료를 개선하기 위한 것이다. 고전기전도도를 갖고 있는 Ag, Cu, Au, 그리고 Al 박막배선에서 엘렉트로마이그레이션에 대한 저항 특성을 결함발생 시간 분석으로부터 활성화 에너지를 측정함으로써 조사하였다. 광학현미경 그리고 XPS 분석이 박막에서의 결함분석에 사용되었다. Cu 박막이 엘렉트로마이그레이션에 대해 상대적으로 높은 활성화 에너지를 보였다. 따라서 Cu 박막이 높은 전류빌도 하에서 엘렉트로마이그레이션에 대한 높은 저항성이 요구되는 차세대 미세전자 소자에서 적합한 박막배선 재료로서의 가능성을 갖는 것으로 판단된다. 보호막 처리된 Al 박막은 평균수명 증가, 엘렉트로마이그레이션에 대한 저항 특성 향상을 나타내며 이는 보호막 층과 박막배선 재료 계면에서의 유전 보호막 효과에 기인하는 것으로 사료된다.

• 한국재료학회지
• /
• 제21권3호
• /
• pp.174-179
• /
• 2011

Ultra-thin aluminum (Al) and tin (Sn) films were grown by dc magnetron sputtering on a glass substrate. The electrical resistance R of films was measured in-situ method during the film growth. Also transmission electron microscopy (TEM) study was carried out to observe the microstructure of the films. In the ultra-thin film study, an exact determination of a coalescence thickness and a continuous film thickness is very important. Therefore, we tried to measure the minimum thickness for continuous film (dmin) by means of a graphical method using a number of different y-values as a function of film thickness. The raw date obtained in this study provides a graph of in-situ resistance of metal film as a function of film thickness. For the Al film, there occurs a maximum value in a graph of in-situ electrical resistance versus film thickness. Using the results in this study, we could define clearly the minimum thickness for continuous film where the position of minimum values in the graph when we put the value of Rd3 to y-axis and the film thickness to x-axis. The measured values for the minimum thickness for continuous film are 21 nm and 16 nm for sputtered Al and Sn films, respectively. The new method for defining the minimum thickness for continuous film in this study can be utilized in a basic data when we design an ultra-thin film for the metallization application in nano-scale devices.