• Korean Journal of Materials Research
• /
• v.17 no.8
• /
• pp.447-451
• /
• 2007

We investigated the dependence of the various annealing conditions and thickness ($6\sim45nm$) of the Ti-doped $Al_2O_3$ coating on the electrochemical properties and the capacity fading of Ti-doped $Al_2O_3$ coated $LiCoO_2$ films. The Ti-doped-$Al_2O_3$-coating layer and the cathode films were deposited on $Al_2O_3$ plate substrates by RF-magnetron sputter. Microstructural and electrochemical properties of Ti-doped-$Al_2O_3$-coated $LiCoO_2$ films were investigated by transmission electron microscopy (TEM) and a dc four-point probe method, respectively. The cycling performance of Ti-doped $Al_2O_3$ coated $LiCoO_2$ film was improved at higher cut-off voltage. But it has different electrochemical properties with various annealing conditions. They were related on the microstructure, surface morphology and the interface condition. Suppression of Li-ion migration is dominant at the coating thickness >24.nm during charge/discharge processes. It is due to the electrochemically passive nature of the Ti-doped $Al_2O_3$ films. The sample be made up of Ti-doped $Al_2O_3$ coated on annealed $LiCoO_2$ film with additional annealing at $400^{\circ}C$ had good adhesion between coating layer and cathode films. This sample showed the best capacity retention of $\sim92%$ with a charge cut off of 4.5 V after 50 cycles. The Ti-doped $Al_2O_3$ film was an amorphous phase and it has a higher electrical conductivity than that of the $Al_2O_3$ film. Therefore, the Ti-doped $Al_2O_3$ coated improved the cycle performance and the capacity retention at high voltage (4.5 V) of $LiCoO_2$ films.

• Journal of the Korean Vacuum Society
• /
• v.16 no.4
• /
• pp.267-272
• /
• 2007

Al-doped ZnO (AZO) thin films were grown on glass substrates by radio-frequency magnetron sputtering. The effects of oxygen flow ratio, which was used for a sputtering gas, on the AZO thin films were investigated by using the X-ray diffraction (XRD), atomic force microscopy (AFM), and Hall effects measurement. The AZO thin film, deposited with oxygen flow ratio of 0% at the growth temperature of $400^{\circ}C$, showed a strongly c-axis preferred orientation and the lowest resistivity of $6.9{\times}10^{-4}{\Omega}cm$. The ZnO (002) diffraction peak indicated a tendency to decrease substantially with increasing the oxygen flow ratio. Furthermore, as the oxygen flow ratio was decreased, the carrier concentration and the hall mobility were increased, but the electrical resistivity was decreased.

• Proceedings of the KSME Conference
• /
• 2005.11a
• /
• pp.135.2-135.2
• /
• 2005

• Journal of the Korean Vacuum Society
• /
• v.10 no.3
• /
• pp.335-340
• /
• 2001

$Ga_2O_3$(1 wt%)-doped ZnO(GZO) thin films were grown on ${\alpha}-Al_2O_3$ (0001) by rf magnetron sputtering at $510^{\circ}C$, whose crystal structure was polycrystalline. As-grown GZO thin film shows poor electrical properties and photoluminescence (PL) spectra. To improve these properties, GZO thin films were annealed at 800-$900^{\circ}C$ in $N_2$atmosphere for 3 min. After the rapid thermal annealing(RTA), deep defect-level emission disappears and near-band emission is greatly enhanced. Annealed GZO thin films show very low resisitivity of $2.6\times10^{-4}\Omega$/cm with $3.9\times10^{20}/\textrm{cm}^3$ carrier concentration and exceptionally high mobility of 60 $\textrm{cm}^2$/V.s. These improved physical properties are explained in terms of translation of doped-Ga atoms from interstitial to substitutional site.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.657-659
• /
• 2004

Trivalent cerium ($Ce^{3+}$) activated yttrium aluminum garnet ($Y_3Al_5O_{12}$, YAG) phosphor thin films were deposited on quartz glass substrates by rf magnetron sputtering. The effects of sputtering parameters and annealing condition on the luminescent properties were investigated. The sputtering parameters were $O_2$/Ar gas ratio, rf power, and deposition time. The films were annealed at 1200 $^{\circ}C$ for 5 hours in $N_2+$vacuum atmosphere. Polycrystalline YAG:Ce thin film phosphor could be obtained with a gas ratio of $O_2$/(Ar+$O_2$)=0.5 after post-annealing. PL spectra excited at 450 nm showed a yellow single band at 550 nm.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.252-252
• /
• 2010

AIZTO (Al-In-Sn-ZnO) thin film was deposited on glass substrate at room temperature by facing target sputtering (FTS) system. The FTS system was designed to array two targets facing each other. Two different kinds of targets were installed on FTS system. We used the ITO (In2O3 90wt%, SnO2 10wt%) target and the AZO (ZnO 98wt%, Al2O3 2wt%). AIZTO films were deposited in each of the applied power of the targets. The electrical and structural properties of the as-deposited AIZTO thin films were then examined by hall-effect measurement, and by using atomic force microscope (AFM), X-ray diffractometer (XRD), and energy dispersive x-ray spectroscopy (EDX). The optical property was measured by an UV-VIS spectrometer.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.857-861
• /
• 1996

The influence of rf-plasma operation on the thin film formation containing small particles for Al-Li alloys mainly have been studied as a function of Ar gas pressure and plasma power by means of a 200kV transmission electron microscope (TEM). Under the non-plasma operation, the transition from continuous thin films to clusters of grape-like small particles occurred at Ar gas pressures above 20Pa. Particles were single crystals with clear crystal habit planes. Under the plasma operation, the influence of gas pressures on the film formation at a plasma power of 5W was also examined. Thin films containing particles below 30Pa and the films containing mainly particles above 40Pa were formed. The prominent change of the average particle size was not recognized. The increase of the plasma powers at 20Pa, which formed particles under non-plasma, suppressed growth of particles, and homogeneous films containing very small particles were fabricated. The electric conductivity showed slight decrease with an increase of plasma power.

• Journal of the Korean Applied Science and Technology
• /
• v.16 no.1
• /
• pp.41-44
• /
• 1999

Recently, high luminance and efficiency were realize in organic thin film electroluminescence (EL) cells with multilayer structures including an emitting layer (EML), hole transporting layer (HTL), and an electron transporting layer (ETL). In this study, Bis(10-hydroxybenzo[h]quinolinato)beryllium (Bebq2) was synthesized. PL and EL characteristics of their thin film were investigated by fabricating the devices having a structure of ITO/PVK/Bebq2/Al, ITO/PVK dispersed with TPD/Bebq2/Al. The EL color of these device was greenish and the wavelength of their EL peaks was located, respectly, at 495nm, and 492.5nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.9
• /
• pp.710-712
• /
• 2011

In this study, we fabricate resistive switching random access memory (ReRAM) devices constructed with a Al/$HfO_2$/ITO structure on glass substrates and investigate their memory characteristics. The hafnium oxide thin film used as a resistive switching layer is sputtered at room temperature in a sputtering system with a cooling unit. The Al/$HfO_2$/ITO device exhibits bipolar resistive switching characteristics, and the ratio of the high resistance (HRS) to low resistance states (LRS) is more than 60. In addition, the resistance ratio maintains even after $10^4$ seconds.

• Journal of Sensor Science and Technology
• /
• v.23 no.2
• /
• pp.94-98
• /
• 2014

Aluminum nitride (AlN) thin films with a TiN buffer layer have been fabricated on SUS430 substrate by RF reactive magnetron sputtering at room temperature under 25~75% $N_2$ /Ar. The characterization of film properties were performed using surface profiler, X-ray diffraction, X-ray photoelectron spectroscopy(XPS), and pressure-voltage measurement system. The deposition rates of AlN films were decreased with increasing the $N_2$ concentration owing to lower mass of nitrogen ions than Ar. The as-deposited AlN films showed crystalline phase, and with increasing the $N_2$ concentration, the peak of AlN(100) plane and the crystallinity became weak. Any change in the preferential orientation of the as-deposited AlN films was not observed within our $N_2$ concentration range. But in the case of 50% $N_2$ /Ar condition, the peak of (002) plane, which is determinant in pressure sensing properties, appeared. XPS depth profiling of AlN/TiN/SUS430 revealed Al/N ratio was close to stoichiometric value (45:47) when deposited under 50% $N_2/Ar$ atmosphere at room temperature. The output signal voltage of AlN sensor showed a linear behavior between 26~85 mV, and the pressure-sensing sensitivity was calculated as 7 mV/MPa.