• Macromolecular Research
• /
• v.14 no.2
• /
• pp.194-198
• /
• 2006

Polystyrene, PS, particles of 450 nm diameter and poly(styrene-co-styrene sulfonate), PSS, particles of 140-160 nm diameter were prepared by emulsifier-free emulsion polymerization. The surfaces of the PS and PSS particles were coated with Ag nanoparticles for the application of antimicrobial agents by reduction of Ag ions using ${\gamma}$-irradiation. The Ag-PS and Ag-PSS were characterized by High-Resolution Transmittance Electron Microscopy (HR-TEM), Field-Emission Scanning Electron Microscopy (FE-SEM), and Energy Dispersive X-ray Spectroscopy (EDXS). The HR-TEM and EDXS data showed that the Ag nanoparticles were loaded on the surface of the PS and PSS particles, respectively. The antimicrobial efficiency of the Ag-PS and Ag-PSS particles (0.4 g) with ca. 100 ppm Ag, which was coated onto yam (KS K 0905-1996 rule), was tested against Staphylococcus aureus ATCC 6538 and Klebsiella pneumoniae ATCC 4352 after 100 washing cycles (KS K 0432-1999 rule). The antimicrobial efficiency of the Ag-PS particles against Staphylococcus aureus ATCC 6538 and Klebsiella pneumoniae ATCC 4352 was 99.9% after 100 cycles washing., confirming that the Ag-PS particles can be used as antimicrobial agents.

• Korean Journal of Materials Research
• /
• v.13 no.9
• /
• pp.555-560
• /
• 2003

Ag-coated Cu particles were prepared by dropping method of coating agent and were evaluated by scanning electron microscope and color difference meter. The shape of Cu particles having obvious crystal plan and edge was changed spherically according to the increase of Ag coating amount. When the Ag coating amount was 50 wt% to Cu particles, the whiteness of Ag-coated Cu particles was almost similar to that of pure Ag particles. Adding $NH_4$OH in reductant solution could increase effectively the whiteness of the Ag-coated particles. The Ag-coated particles having the highest whiteness was obtained when the content of hydrazine in reductant solution was 0.48 M.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1220-1223
• /
• 2009

The effect of silver (Ag) nano-particles on OLEDs was investigated by using a finite difference time domain (FDTD) tool. The proposed OLEDs employed Ag nanoparticles thermally deposited in a high vacuum on a cathode. The emission rate of the exciton was improved by 1.8 fold compared to the conventional OLEDs without Ag nano-particles. Less spacing between the dipole source and the Ag nano-particles resulted in a larger emission rate of the exciton in the OLED with nano-particles. The size of the Ag nano-particles was proportional to the emission rate of the exciton in a range of nano-meter scale of nano-particles. The enhancement of the emission rate of the exciton due to Ag nano-particles caused the improvement in the efficiency of the proposed OLED.

• Macromolecular Research
• /
• v.15 no.4
• /
• pp.285-290
• /
• 2007

Ag nanoparticles were distributed onto polystyrene nanoparticle (PS-Ag) beads using two synthetic methodologies. In the first methodology, polystyrene (PS) beads were prepared via emulsion polymerization, with Ag nanoparticles subsequently loaded onto the surface of the PS beads. The polymerization of styrene was radiolytically induced in an ethanol (EtOH)/water medium, generating PS beads. Subsequently, Ag nanoparticles were loaded onto the PS beads via the reduction of Ag ions. The results from the morphological studies, using field emission transmission electron microscopy (FE-TEM), reveal the PS particles were spherical and nanosized, and the average size of the PS spherical particles decreased with increasing volume % of water in the polymerization medium. The size of the PS spherical particles increases with increasing radiation dose for the polymerization. Also, the amount of Ag nanoparticle loading could be increased by increasing the irradiation dose for the reduction of the Ag ions. In the second methodology, the polymerization of styrene and reduction of Ag ions were simultaneously performed by irradiating a solution containing styrene and Ag ions in an EtOH/water medium. Interestingly, the Ag nanoparticles were preferentially homogeneously distributed within the PS particles (not on the surface of the PS particles). Thus, Ag nanoparticles were distributed onto the surface of the PS particles using the first approach, but into the PS clusters of the particles via the second. The antimicrobial efficiency of a cloth coated with the Ag-PS composite nanoparticles was tested against bacteria, such as Staphylococcus aureus and Klebsiella pneumoniase, for 100 water washing cycles.

• Resources Recycling
• /
• v.14 no.1
• /
• pp.26-32
• /
• 2005

A study on the preparation of Ag fine particles was performed through a reduction reaction using ascorbic acids as a reductant, which is one of the indispensable processes for the recycling of silver-bearing wastes. Silver nitrate solution in the range of 10~120 mmole/l was used and Tamol NN8906 or PVP was also used as a dispersant in the preparation of Ag fine particles size analyze, SEM, and TEM to determine the particle size and morphology of them. As a result, the reduction reaction of silver ions with ascorbic acid reached equilibrium within 10 min. It was found that about 60% excess of ascorbic acid was required in order to reduce completely silver ions in the solution. The particle size distribution of Ag particles prepared through the reduction reaction showed typically biomodal or trimodal distribution. Especially, initial Ag concentration in the solution, the type and amount of dispersant added during the reduction reaction played an important role in determining the mean particle size of Ag particles.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.4
• /
• pp.65-71
• /
• 2017

To prepare the Cu-based filler material indicating enhanced oxidation resistance property and Ag content, Ag-coated Cu particles was fabricated by Ag plating of 40 wt % on the spherical Cu particles with an average size of $2{\mu}m$ and their oxidation behavior was also evaluated. In the case that ethylenediaminetetraacetic acid was used alone, the fabricated particles frequently showed broken structures such as delamination at Ag shell/core Cu interface and hollow structure that are induced by excessive galvanic displacement reaction. As a result, fraction of defect particles increased up to 19.88% after the Ag plating of 40 wt.%. However, the fraction in the 40 wt.% Ag-coated Cu particles decreased to 9.01% and relatively smooth surface and dense microstructure in the Ag shell were also observed with additional usage of hydroquinone as a complexing agent. Ag-coated Cu particles having the enhanced microstructure did not show any weight increase by oxidation for exposure to air at $160^{\circ}C$ for 2 h, indicating increased oxidation resistance property.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.3
• /
• pp.51-56
• /
• 2016

To fabricate a copper (Cu)-based fine conductive filler having antioxidation property, submicron silver (Ag)-coated Cu particles were fabricated and their antioxidation property was evaluated. After synthesizing the Cu particles of $0.705{\mu}m$ in average diameter by a wet-reduction process, Ag-coated Cu particles were fabricated by successive Ag plating using ethylene grycol solvent. Main process parameters in the Ag plating were the concentration of reductant (ascorbic acid), the injection rate of Ag precursor solution, and the stirring rate in mixed solution. Thus, Ag plating characteristics and the formation of separate fine pure Ag phase were observed with different combinations of process parameters. As a result, formation of the separate pure Ag phase and aggregation between Ag-coated Cu particles could be suppressed by optimization of the process parameters. The Ag-coated Cu particles which were fabricated using optimal conditions showed slight aggregation, but excellent antioxidation property. For example, the particles indicated the weight gain not exceeding 0.1% until $225^{\circ}C$ when they were heated in air at the rate of $10^{\circ}C/min$ and no weight gain until 75 min when they were heated in air at $150^{\circ}C$.

• Journal of the Korean Chemical Society
• /
• v.43 no.1
• /
• pp.1-7
• /
• 1999

Metal colloidal particles have been prepared by a photo-chemical process in an aqueous solution containing semiconductor nanocrystallites. Metal colloidal particles produced in CdS and AgBr exhibit different absorption spectra. Au particles produced in solution with CdS show typical Au plasmon resonance absorption spectra. On the other hand Ag particles in solution with AgBr shows surface plasmon resonance absorption spectra which are red-shifted, as compared to that of a dispersion of homogeneous Ag colloidal particles in the same host. The extent of red-shift depends on the UV illumination time. This phenomenon is interpreted within the context of effective medium theory for small volume fractions. From the theory, a metal coated particle predicts Ag plasmon resonance, red shifted with respect to 400 nm that would be associated with a silver particle in solution. The absorption peak position is very sensitive to the coating thickness.

• Journal of Powder Materials
• /
• v.17 no.4
• /
• pp.295-301
• /
• 2010

Multi shell graphite coated Ag nano particles with core/shell structure were successfully synthesized by pulsed wire evaporation (PWE) method. Ar and $CH_4$ (10 vol.%) gases were mixed in chamber, which played a role of carrier gas and reaction gas, respectively. Graphite layers on the surface of silver nano particles were coated indiscretely. However, the graphite layers are detached, when the particles are heated up to $250^{\circ}C$ in the air atmosphere. In contrast, the graphite coated layer was stable under Ar and $N_2$ atmosphere, though the core/shell structured particles were heated up to $800^{\circ}C$. The presence of graphite coated layer prevent agglomeration of nanoparticles during heat treatment. The dispersion stability of the carbon coated Ag nanoparticles was higher than those of pure Ag nanoparticles.

• Journal of Magnetics
• /
• v.4 no.3
• /
• pp.92-97
• /
• 1999

A relationship between microstructure and ferromagnetic resonance of Co/Ag multilayers has been studied in as-deposited and annealed multilayers iwth ultrathin (dCo < 1 nm) Co layers. Depending on the nominal thickness of Co Co/Ag multilayers represent a system of fine magnetic particles (dCo < 0.4 nm) or discontionuous layered structure (dCo/0.5 nm). FMR data has been interpreted in the framework of a odel of interacting fine particles exhibiting superparamagnetic behavior. Changes in the FMR spectra upon annealing have been attributed to the growth of the Co particles and to a transition from the fcc to hcp atomic structure of the highly (111) textured Co particles.