Several $Al_2O_3$-based polycrystalline which had different dopant ratio in the range of 0.5mol% were prepared by doping pure $Cr_2O_3$, $ZrO_2$, $HfO_3$ Single crystalline which had same composition with above polycrystalline were made by means of floating zone method. This study examined the role of each dopant for enhancing the mefchanical properties of $Al_2O_3$-based Ceramics. Optical micrographs $({\times}200)$ of $Al_2O_3-Cr_2O_3$ single crystal showing not only radial crack (rc) on the specimen surface but median crack (mc) and lateral crack (lc) under surface at the edge of indentation mark. Fracture toughness of $Al_2O_3$-based Ceramics was increased with $ZrO_2$ content. Alloying effect of $Cr_2O_3$ contributed to the hardness of $Al_2O_3$ based ceramics.

• 한국추진공학회지
• /
• 제3권1호
• /
• pp.78-85
• /
• 1999

복기 추진제인 N-5 추진제에 4종의 금속선(Ag, Cu, Al, Ni-Cr선)을 삽입하여 연소 특성을 고찰하여 보았다. 금속선이 삽입된 복기 추진제의 연소속도 증가비($r_w$/$r_sb$)는 Ag선 > Cu선 > Al선 > Ni-Cr선의 순으로서 금속선의 열확산 계수의 크기 순과 일치하였다. 금속선을 삽입한 N-5추진제의 $r_w$/$r_sb$는 단열 불꽃 온도와 구조의 차이에 의하여 혼합형 추진제보다 작게 나타났다. 복기 추진제에 열확산 계수가 비교적 큰 Ag, Cu, Al선을 삽입한 경우, 금속선이 삽입되지 않은 추진제에서 나타난 plateau와 mesa 연소 특성이 사라진 반면 열확산 계수가 작은 Ni-Cr선을 삽입한 경우에서는 plateau와 mesa 연소 특성이 그대로 존재했다.

• 한국표면공학회지
• /
• 제49권6호
• /
• pp.580-586
• /
• 2016

Cr-Si-Al-N coating with different Si content were deposited by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The deposition temperature was $300^{\circ}C$, and the gas ratio of $Ar/N_2$ were 9:1. The CrSi alloy and aluminum targets used for arc ion plating and sputtering process, respectively. Si content of the CrSi alloy targets were varied with 1 at%, 5 at%, and 10 at%. The phase analysis, composition and microstructural analysis performed using x-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) including energy dispersive spectroscopy (EDS), respectively. All of the coatings grown with textured CrN phase (200) plane. The thickness of the Cr-Si-Al-N films were measured about $2{\mu}m$. The friction coefficient and removal rate of films were measured by a ball-on-disk test under 20N load. The friction coefficient of all samples were 0.6 ~ 0.8. Among all of the samples, the removal rate of CrSiAlN (10 at% Si) film shows the lowest values, $4.827{\times}10^{-12}mm^3/Nm$. As increasing of Si contents of the CrSiAlN coatings, the hardness and elastic modulus of CrSiAlN coatings were increased. The morphology and composition of wear track of the films was examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy, respectively. The surface energy of the films were obtained by measuring of contact angle of water drop. Among all of the samples, the CrSiAlN (10 at% Si) films shows the highest value of the surface energy, 41 N/m.

• 한국세라믹학회지
• /
• 제46권4호
• /
• pp.372-378
• /
• 2009

The coloring agents $Cr_2O_3$ and $CrCl_3$ were manipulated in this study to synthesize ZnO-$Al_2O_3-Cr_2O_3$ system pigments by changing their mixing ratio. The addition of varying amounts of mineralizer was also tested to obtain better color development of the pink pigment. In the synthesis of ZnO- $Al(OH)_3-Cr_2O_3-CrCl_3$ pigments, the best composition is $Cr_2O_3$-0.1 mole and $CrCl_3$-0.2 mole when $Cr_2O_3$ is partially substituted with $CrCl_3$ to synthesize them. Among the $ZnAl_{1.6-x}Cr_{0.2+x}O_4$ compositions to which a mineralizer was not added, ZnO-1mole, $Al(OH)_3$-1.7 mole, $Cr_2O_3$-0.075 mole, and $CrCl_3$-0.15 mole showed a desirable pink hue. The measurements of pigments $L^*$, $a^*$ and $b^*$, were $L^*$ 81.81, $a^*$ 16.65 and $b^*$ 0.45, and when the synthesized pigments were applied to a zinc glaze, the measurements were $L^*$ 60.41, $a^*$ 28.39, and $b^*$ 16.97. When adding a mineralizer, a 2 wt% addition resulted in the most favorable pink color. The composition for the most favorable result that included a mineralizer was $Al(OH)_3$-1.8 mole, $Cr_2O_3$-0.05 mole, and $CrCl_3$-0.1 mole, and the calcination temperature was $1250^{\circ}C$. The pigment color analysis showed $L^*$ 82.52, $a^*$17.14 and $b^*$-1.18, and the measurements of $L^*$, $a^*$ and $b^*$ in the glaze were $L^*$ 60.97, $a^*$ 28.77 and $b^*$ 13.72.

• 한국주조공학회지
• /
• 제21권1호
• /
• pp.24-32
• /
• 2001

Recently, iron aluminides based on Fe3Al and FeAl are ordered intermetallic alloys that offer good oxidation resistance, excellent sulfidation resistance, and potentially lower cost than many high-temperature structural materials. They have better strength, elasticity to weight ratio and high temperature strength, therefore, they can be cosidered as candidate heat resistance structural materials for automobiles, ships, airplanes and spaceships applications. The changes in the mechanical properties and fracture behavior were investigated for Fe-30at.%Al-5at.%Cr alloys when Ti, Hf and Zr were added respectively. For mechanical properties such as Rockwell hardness and yield strength at room temperature, those were decreased in the case of Fe-30at.%Al-5at.%Cr alloy then increased in the case of 5at.% and 10at.% addition of Ti alone. However, Rockwell hardness and yield strength decreased again at 15%Ti then increased dramatically due to the precipitation hardening of the second phase on the specimen at 20%Ti. For fracture modes, cleavage fracture showed in the case of Fe-30at.%Al and Fe-30at.%Al-5at.%Cr alloys. As the amount of Ti addition changed cleavage to transgranular fracture and to quasi-cleavage fracture at 20%Ti. When Hf, Zr and Hf+Zr were added respectively, transgranular, cleavage and quasi-cleavage fracture were coexisted.

• 한국분말재료학회지
• /
• 제28권3호
• /
• pp.201-207
• /
• 2021

Ni-Cr-Al metal-foam-supported catalysts for steam methane reforming (SMR) are manufactured by applying a catalytic Ni/Al₂O₃ sol-gel coating to powder alloyed metallic foam. The structure, microstructure, mechanical stability, and hydrogen yield efficiency of the obtained catalysts are evaluated. The structural and microstructural characteristics show that the catalyst is well coated on the open-pore Ni-Cr-Al foam without cracks or spallation. The measured compressive yield strengths are 2-3 MPa at room temperature and 1.5-2.2 MPa at 750℃ regardless of sample size. The specimens exhibit a weight loss of up to 9-10% at elevated temperature owing to the spallation of the Ni/Al₂O₃ catalyst. However, the metal-foam-supported catalyst appears to have higher mechanical stability than ceramic pellet catalysts. In SMR simulations tests, a methane conversion ratio of up to 96% is obtained with a high hydrogen yield efficiency of 82%.

• 자원리싸이클링
• /
• 제25권2호
• /
• pp.10-16
• /
• 2016

본 연구에서는 Inconel 713C 스크랩을 원료로 아르곤-산소 탈탄 공정을 이용하여 니켈계 초내열합금을 재활용 하였다. 아르곤-산소 탈탄 공정에서 아르곤은 1,000 sccm으로 지속적으로 주입되었고 산소는 100, 250, 500 sccm의 유량으로 10, 20, 30 분씩 주입되었다. 산소 주입 초기 단계에서는 산소 양이 증가하면서 Al, Cr, 및 Mo 함량은 증가하였고 탄소 함량은 감소하였다. 그리고 Al 함유량은 탄소의 반응이 끝난 후 Al, Cr 등의 원소와 산화가 일어났기 때문에 첨가원소와 탄소의 반응에 의해 감소하였다. 결과적으로, Al 함유량이 감소하였기 때문에 ${\gamma}^{\prime}$상이 줄어들었으며 이는 Al이 ${\gamma}^{\prime}$을 형성하는 주요 원소이기 때문이다. 또한, 탄소의 양이 줄어들면서 탄화물도 줄어들었으며 산소가 과잉 공급된 시료의 기계적인 물성(강도, 경도 등)은 감소하게 된다.

• 동력기계공학회지
• /
• 제20권4호
• /
• pp.69-74
• /
• 2016

Recently, in order to meet the stricter emission regulations, the proportion of after-treatments for vehicle and vessel is increasing gradually. The purpose of this study is to investigate the de-$CH_4$ characteristics of NGOC in front of proposed combined system according to additive catalyst and support ratio. In the case of Pd addition, the de-$CH_4$ performance of 2Pt-2Pd-3MgO/$Al_2O_3$ NGOC was improved by approximately 10 to 20% for the HC components. The de-$CH_4$ performance of 2Pt-2Pd-3Cr-3MgO/$Al_2O_3$ NGOC was higher compared to five kinds of NGOC catalysts, because Cr particle was smaller and dispersion of Pd was increased. The NGOC(Zeolite:$Al_2O_3$(80%:20%)｝catalyst according to support ratio, was improved performance at low temperature region on CO and NO conversion rate.

• 한국결정학회지
• /
• 제3권2호
• /
• pp.111-119
• /
• 1992

Czochralski법에 의해 alexandrite단길정을 육성 하였다. 결함과 인상속도, 회전속도, Beo의 순도 및 BeO와 Cr3+/Al3+ 치환비의 증발 손실보상 등 결정육성 요소의 관계를 규명하였다. 결과로서 1) 결정육성 원료로서 BeO의 순도는 99.99f) 이상의 고순도이어야 하고, 2) 증발손실 보상은 고품위의 결정을 육성하 기 위한 필수조건으로서 인상속도와 Cr3+/Al3+ 치환 비에 의존되며, 3) 적당한 인상 및 회전속도는 0. 5 ∼1.0mm/hr과 20∼25rpm으로 나타났다. 육성된 결정 은 (001) 방향으로 성장되었으며, 편광현미경으로 여러가지 형태의 결함을 관찰하였고 그 제거 방법을 논의 하였다. 또한 실온에서 흡수 및 형광방출 스펙트럼을 측정·비교하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 센서 박막재료 반도체재료 기술교육
• /
• pp.82-85
• /
• 2002

In recent years, the tantalum nitride(TaN) thin-film has been developed for the electronic resistor and capacitor. In this papers, this study presents the surface profile and sheet-resistance property relationship of reactive-sputtered TaN thin film resistor processed by buffer of Ti and Cr on alumina substrate. The TCR properties of the TaN films were discussed in terms of reactive gas ratio, ratio of nitrogen, crystallization and thin films surface morphology due to annealing temperature. It is clear that the TaN thin-films resistor electrical properties are low TCR related with it's buffer layer condition. Ti buffer layer thin film resistor having a good thermal stability and lower TCR properties then Cr buffer expected for the application to the dielectric material of passive component.