• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.5
• /
• pp.144-152
• /
• 2007

This study investigated the failure mechanism of RC beams strengthened with AFRP sheets. Total 5 half-scale RC beams were constructed and tested to estimate the effectiveness of various methods to prevent the debonding failure of AFRP sheets. From the experimental results, it was found that increasing bonded length or end U-wrappings does not prevent debonding failure. On the other hand, the beams with center U-wrappings and shear-keys reached the ultimate state with their sufficient performance. The center U-wrappings tended to control debonding of the longitudinal AFRP sheets because the growth of the longitudinal cracks along the edges of the composites was delayed. In case of shear-keys, it was sufficient to eliminate debonding and the beams failed by AFRP sheets rupture due to the sufficient bond mechanism.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.34 no.12
• /
• pp.35-40
• /
• 2018

In this study, experimental research was carried out to evaluate the seismic performance of reinforced concrete exterior beam-column joint regions using hybrid retrofitting with AFRP sheets and embedded CFRP reinforcements in existing reinforced concrete building. Therefore it was constructed and tested three specimens retrofitting the beam-column joint regions using such retrofitting materials. Specimens, designed by retrofitting the beam-column joint regions of existing reinforced concrete structure, were showed the stable failure mode and increase of load-carrying capacity due to the effect of crack control at the times of initial loading and confinement of retrofitting materials during testing. Specimens RBCJ-SRA3 designed by the retrofitting of AFRP sheets and embedded CFRP reinforcements in reinforced exterior beam-column joint regions were increased its maximum load carrying capacity by 1.86 times and its energy dissipation capacity by 1.65 times in comparison with standard specimen RBCJ for a displacement ductility of 5.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.68-71
• /
• 2004

In the shear strengthening with FRP sheets, beams are wrapped around the webs and tension face of critical shear span by fiber sheets. The shear strength of RC beam strengthened with FRP sheets must be calculated based on the effective strain that can be developed in the FRP sheets at ultimate stage because the final failure modes of beams are governed by premature debonding of FRP sheet due to the limitation of bonded length by beam depth. An experimental study is carried out to evaluate the shear strengthening effect of AFRP or GFRP sheets with respect to shear reinforcement ratio of rebar. From the test results, it was found that the additional shear strength provided by GFRP or AFRP can be estimated by $p_w{\cdot}f_w$ based on the maximum effective strain of FRP sheet $4,000m{\mu}$ proposed by ACI 440 committee.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.2
• /
• pp.61-69
• /
• 2011

Fiber Reinforced Plastic (FRP) sheets have been widely used to retrofit and rehabilitate RC structures, while in case of retrofitting steel structures, there are no codes and researches. It stems from configuration of member and characteristics of bonding behavior. This study focused on the static behavior of steel beams reinforcement by AFRP sheets. The main objective of the experimental programme was the evaluation of the force transfer mechanism, the increment of the beam load carrying capacity and the bending stiffness. A bending test was conducted on a H-shaped steel beam, with aramid FRP sheets bonded to its flanges. The mid-span deflection and the strain from three points along AFRP sheets were recorded Test results exhibit that the increment of the load-carrying capacity with reference to a mid-span deflection level of 15 mm(1/125mm of the clear span) was equal to 9.4% and for the two layers case, an elastic stiffness increment is slightly higher than one layer case.

• Journal of Korean Society of Steel Construction
• /
• v.28 no.3
• /
• pp.185-194
• /
• 2016

This paper presents the finite element method results for HSS(Hollow Square Section) steel columns strengthened with Carbon Fiber Reinforced Polymer Plastic(CFRP) sheets. 6 specimens were fabricated and the specimen groups were non-compact short columns, slender short columns, and non-compact long columns. Test parameter was the number of CFRP ply. The finite element analysis was performed by using ANSYS Workbench V.14.0 and the results of FEM were compared with those of Test for failure mode, load-displacement curve, maximum load, and initial stiffness. The comparisons between experimental observations and computed results show that the analyses provided good correlation to actual behavior. Finally, the buckling stress were calculated according to the AISC cold-formed structure provision and the retrofitting effect were verified for each section type.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.84-87
• /
• 2004

Nominal flexural strength of RC members strengthened with FRP sheets is generally based on the tensile strength of composite materials obtained from coupon tests. This method is based on the assumption that bond failure does not occur until the FRP sheet reaches its rupture strength. According to the previous researches, however, bond failure often occurs before the FRP sheet reaches its rupture strength. Some attempts were made to control debonding failure by increasing the bonded length of sheet or wrapping the section around their side of the member(U-wrap). In this study, the flexural failure mechanism of RC beams strengthened with AFRP sheets with different bond lengths is investigated. Their strengthening details to prevent the premature debonding failure are also suggested and its effectiveness is verified.