• Restorative Dentistry and Endodontics
• /
• v.34 no.4
• /
• pp.371-376
• /
• 2009

We evaluated in vitro microleakage of Mineral Trioxide Aggregate (MTA) powder with 4-methacryloxyethyl trimellitate anhydride (4-META) / methyl methacrylate (MMA) & tri-n-butylborane (TBB) resin as a retrograde filling material by using methylene blue dye method. Fifty-two single rooted, extracted teeth were instrumented and obturated with gutta percha and AH plus sealer. The apical 3mm of each root was resected and 3mm deep ultrasonic root end preparation was done. External surface of roots was coated with nail varnish. Prepared teeth were randomly divided into five groups; Negative control: completely covered with nail varnish; Positive control: coated with nail varnish except for apical foramen; Group 1 (retrofilled with Portland cement); Group 2 (retrofilled with MTA); Group 3 (retrofilled with MTA powder mixed with 4-META/MMA & TBB resin). Immediately after completion of root-end filling, all specimens were submerged in methylene blue dye for 72 hours in $37^{\circ}C$incubator. The roots were longitudinally sectioned and measured for extent of dye penetration by three different examiners under microscope (${\times}$10). The results were statistically analyzed using one way ANOVA and Turkey's HSD test. No leakage was evident in negative control and complete leakage in positive control group. Group 3 showed significantly less leakage than group 1 and 2 (p < 0.01). There was no significant difference between group 1 and 2 (p > 0.01). It was concluded that MTA powder with 4-META/MMA & TBB resin was excellent in reducing initial apical microleakage.

• Journal of Biomedical Engineering Research
• /
• v.16 no.4
• /
• pp.533-542
• /
• 1995

The present study investigated the effectiveness of pretreatment on dentin bonding. The adhesive resin was 5% 4-methacryloyloxyethyl trimellitate anhydride (4-META) in methyl methacrylate (MMA) combined with poly-MMA powder. Polymerization of this resin was initiated by tri-n-butyl borage (TBB). Ground bovine dentin samples were etched with either an aqueous solution of 10% citric (10-0 solution) (Group I) or aqueous solution of 10% citric acid and 3% ferric chloride(10-3 solution) (Group ll ). After etching, the primer (an aqueous solution of 35% hydroxyethyl methacrylate (HEM- A) and 5% glutaraldehyde was applied on the differently etched surfaces (Group III , Group IV). The 10-0 treatment showed the lowest tensile bond strength, followed by the 10-3 treatment, primer application after the 10-0 treatment and primer application after the 10-3 treatment. The relationship among the surface morphology after pretreatment, fractured surface morphology and tensile bond strength was examined. It revealed that the surface morphology change by different pretreatment influenced the bond strength and the resulting fractured surface morphology. The correlation of tensile bond strength with the fracture morphology was explained.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.4
• /
• pp.510-525
• /
• 2000

The effects of pretreatment of Co-Cr alloy, including two adhesive primers that contain either MDP or MAC-10, and silicoating on the bond The result sobtained as follows; o Strength of 4-META/MMA-TBB resin were investigated using FT-IR, SEM, and EDAX. o In the SEM observation of surface morphologies, the sandblasted specimen exibited a very rough surface, whereas the surfaces of the two groups primed with either MDP or MAC-10 were covered with a layer of primer, and the surface morphology of the silicoated specimen remained almost the same after sandblasting. o Before the thermocycling tests, the group treated with MDP demonstrated the highest mean tensile bond strength and the sandblasted group showed the lowest bond strength. o After 20,000 thermocyling, the mean tensile bond strength of the sandblasted group exhibited a 50% reduction in bond strength, while the others showed a $20\sim30%$ reduction. o Observation of the metal-resin interface revealed that in all groups the resin permeated the rough surface formed by sandblasting thereby producing a mechanical bond between the metal and the resin. It was also found that thermocycling resulted in a gap formation at the metal-resin interface of the specimens, and the sandblasted group exhibited a larger gap width than the other groups. o In fracture mode, all specimens indicated a cohesive fracture within the resin before thermocycling. However, thermocyling produced adhesive failure at the edge of the resin-metal interface in most specimens. The sandblasted group, which exhibited the lowest bond strength after thormocycling, also demonstrated the largest area of adhesive failure.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.39 no.4
• /
• pp.222-228
• /
• 2023

Attrition is the loss of tooth hard tissue due to contact between teeth, and in severe cases, dentin is exposed, accompanied by selective corrosion and excessive wear of teeth, which is called cupping. If these lesions are left untreated, the size of the lesion gradually increases, breaking the unsupported enamel, resulting in a decrease in aesthetics and chewing function. In this case report, patients with cupping and enamel fracture due to severe attrition were directly restored using a resin with soft properties containing organic fillers. In the follow-up observation six years later, most of the filling of the occlusal surface was eliminated, but the filling on the buccal surfaces remained relatively intact, and it was confirmed that this type of resin was suitable for the area where the occlusal force was relatively weak rather than the area where the occlusal force was greatly applied.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.4
• /
• pp.417-432
• /
• 2001

The pcf metal primers on the bond strength and durability of 4-META/MMA-TBB resins adhered to an Au-Ag-Pd alloy. For this study, the specimens were divided into 8 groups as follows: Thermocyle 0 : (1) control group : sandblast, (2) Group I : sandblast + Cesead Opaque Primer; (3) Group II : sandblast + Metal Primer; (4) Group III : sandblast + V-Primer; Thermocyle 10,000 (5) control sandblast: (6) Group I : sandblast + Cesead Opaque Primer: (7) Group II : sandblast + Metal Primer; (8) Group III sandblast + V-Primer. The shear bond strength was determined using an Instron were observed with the use of scanning electron microscope. Finally, the strengths of bonded joints were evaluated with regard to their adherence energy using a wedge test. The results obtained were as follows ; (1) The shear bond strength of 4-META/MMA-TBB resin to the Au-Ag-Pd alloy was significantly improved in all the groups treated with the primers (p<0.05). (2) Regardless of the adhesive primers used, a significant difference was observed in the bond strength of the thermocycle 0 groups and 10,000 groups (p<0.05). (3) Both before and after thermocycling, the strongest bond strength between the resin an the alloy was obtained after treatment with a metal primer containing MEPS (p<0.05). (4) In the wedge test, the adherence energies of the control group and Group III decreased more rapidly than those of Group I and II during the 2nd day of storage in water.