• Progress in Superconductivity
• /
• v.3 no.2
• /
• pp.247-251
• /
• 2002

In general, the bubbling, generated during the fabrication of the tapes, breaks the superconducting filament, and critical current of the tapes will be decreased. Heat-treatment schemes of Bi-2223/Ag HTS tapes were modified, such as pre-annealing of multi-stacked billet, 2-step main sintering and ramp rate etc. The generation of bubbling was drastically decreased from 20 bubbles/m to 0 ~ 1 bubble/m by the modified heat-treatment. Therefore, the value of critical current of the tapes without bubbling was increased almost twice higher than that of already existing tapes. Critical current up to 42 A in 40 m length Bi-22231Ag tapes have been measured at 77K, self-field, 1$mutextrm{V}$/cm criterion. It could be confirmed that elimination of bubbling is effective to maintain the superconducting property along the tape length.

• Korean Journal of Materials Research
• /
• v.15 no.12
• /
• pp.773-779
• /
• 2005

Properties of Ni-base superalloys of Nimonic 80A alloy system were investigated by the observation of microstructures, precipitates ana hardness as a function of the chemical compositions ana the paths of heat treatment. The higher hardness values showed, the higher Ti/Al ratio among high compositions of Cr and Co element. The lower (Ti+Al) and Fe contents decreased in the same Ti/Al ratio, the higher hardness values showed. This results are considered that coherent deformation was increased with increasing Ti/Al ratio. Hardness showed higher value when Cr contents was $18 wt\%$ less than $21wt\%Cr$. In $3.15 wt\%$Co alloy, $\gamma'$ phase was very fine as around 50nm and, its volume fraction and hardness showed the highest value by 2step-aging treatment.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.193-193
• /
• 2011

To obtain ceramic films, the sol-gel coating technique has been broadly used with heat treatment, but crack formation tend to occur during heat treatment in thick sol-gel films. We prepared PZT thin films by sol-gel method with single-step spin coating process. The PZT solution have been synthesized using lead acetate ($Pb(CH_3COO)_2$), zirconium acetylacetonate ($Zr(OC_3H_7^n)_4$), and titanium diisopropoxide bis(acetylacetonate) 75wt% in isopropanol ($Ti(OC_3H_7^i)_2(OC_3H_7^n)_2$) as starting materials and n-propanol was selected as a solvent. The poly(vynilpyrrolidone) (PVP) was added with 0, 0.25, 0.5, 0.75, and 1 molar ratios to control viscosity of solution. We investigated influence of the viscosity on thickness, microstructure, and electrical properties of final PZT films. Thermo-gravimetric analysis and differential scanning calorimeter (TGA/DSC) was carried out from room temperature to $800^{\circ}C$ in order to measure pyrolysis temperature. Structural characteristics were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Ferroelectric and dielectric properties were measured by RT66A (Radiant) and impedance analyzer (Agilent), respectively. The thicknesses of PZT films depended on incorporation of an excess amount of PVP. Finally, we obtained PZT films of good quality without crack formation via single-step spin coating.

• Journal of Powder Materials
• /
• v.17 no.5
• /
• pp.359-364
• /
• 2010

In an attempt to optimize the magnetic properties of (Nd, Dy)-Fe-B sintered magnets, hydrogenation and post-sintering heat treatment processes were investigated at various hydrogenation temperatures and heat treatment temperatures. The coercivity of (Nd, Dy)-Fe-B sintered magnets hydrogenated at $400^{\circ}C$ increased to about 1.2 kOe without any detrimental effect on the remanence. Moreover, the coercivity of the magnets was enhanced further by a consecutive $2^{nd}$ and $3^{rd}$ step heat treatment. These results eventually leaded to the reduction of the Dy content in a high coercive (> 30 kOe) (Nd, Dy)-Fe-B sintered magnets, as much as 10%.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.2
• /
• pp.16-20
• /
• 2002

Bi-axially textured Ni tapes for YBCO coated conductors were Prepared by cold rolling and heat treatment of Ni Powder compacts. The Ni powder used in this study was 5 urn in particle size and 99.99 % in purity. The process of this study consists of filling of hi powder into a rubber mold, cold-isostatically Pressing and sintering of the powder compacts at 110$0^{\circ}C$ for 6h in 96 % Ar - 4 % H$_2$ atmosphere. The sintered compacts were cold rolled with a 5 % step reduction ratio into a 100 micron-thick tapes and then heat-treated at 100$0^{\circ}C$ for various time periods. The (200) texture of Ni tape was successfully developed through the recrystallization heat treatment of the cold rolled Ni tapes. At 100$0^{\circ}C$, the degree of texture of the heat-treated Ni tapes seems not to be significantly affected by the heat-treatment time. The short heat treatment of S min was sufficient to develop the complete (200) cube texture. The degree of in-Plane and out-of-plane texture of the prepared Ni tapes was 8-10$^{\circ}$. The heat treated Ni tapes consisted of equiaxed grains with a size 50-70 microns. and the AFM sol-face roughness was as smooth as 3 nm.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.2 no.2
• /
• pp.91-94
• /
• 2001

Glass ceramics composed of (5-X)$Li_2O$ㆍ$XAg_2O$ㆍ36CaOㆍ$20TiO_2$.27$P_2O_5$(X=1 to 5) were prepared by melting process and 2 step heat treatment for nucleation at$610^{\circ}C$ and crystallization at $730^{\circ}C$, Fabricated crystal phases were $LiTi_2(PO_4)_3$(LTP),$AgTi_2(PO_4)_3$(AgTP)와 $\beta-Ca_3(PO_4)$. Antibacterial effects and characterizations of the glass ceramics as $Ag_2$O content were investigated. Staphylococcus aureus and Salmonella typhi were used in this study. Staphylococcus aureus and Salmonella typhi bacteria were removed 5 hours added after glass ceramics.

• Journal of the Korean Ceramic Society
• /
• v.29 no.10
• /
• pp.779-784
• /
• 1992

In producing cordierite glass-ceramics by sintering, following experiments were conducted in order to determine the optimum heat-treatment schedule for high-crystallinity and dense sintered body. The glass composition of 11.67MgO-29.46Al2O3-52.88SiO2-5P2O5-1B2O3 (wt%) was selected on the basis of the early experiment. The 3-step heat treatment schedule was determined by the results of DTA, Dilatometric measurement and high-temperature XRD, where the particle-size-controlled glass powder was used. The degree of densification and the crystallinity were evaluated by the measurement of the bulk density and X-ray scattering intensity. The specimen fired with the optimum conditions showed ${\alpha}$-cordierite phase, relative density ∼98%, crystallinity ∼92%, thermal expansion coefficient ∼30${\times}$10-7/$^{\circ}C$, dielectric constant ∼5.5 and resistivity ∼1.0${\times}$1012 {{{{ OMEGA }}cm, respectively.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.22 no.3
• /
• pp.372-379
• /
• 2013

In this study, we investigated the traits of the clad metals used in hot-rolled clad steel plates. We examined the sensitization and mechanical properties of STS 316 steel plate and carbon steel (A516) under the specific circumstances of post heat treatment and whether a weld was multilayered and thick or repeated because of repairs. The test conditions were as follows. The clad steel plates were butt-welded using FCAW/SAW, and the heat treatment was conducted at $625^{\circ}C$, for 80, 160, 320, 640, or 1280 min. The change in the corrosion resistance was evaluated in these specimens. In the case of the carbon steel (A516), as the heat treatment time increased, the annealing effect caused the tensile strength to decrease. The micro- hardness gradually increased and then decreased after 640 min. The elongation and contraction of the area increased gradually. An oxalic acid etch test and EPR test on STS316, a clad metal, showed a STEP structure and no sensitization. From the test results for the multi-layered and repair welds, it could be concluded that there is no effect on the corrosion resistance of clad metals. In summary, the purpose of this study was to suggest some considerations when developing on-site techniques and evaluate the sensitization of stainless steels.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.2
• /
• pp.275-285
• /
• 1996

The effect of heat-treatment on catalytic crystallization in $LI_2O-Al_2O_3-SiO_2$ glass system over its glass transition temperature was investigated. Glass composition $4Li_2O{cdot}22AL_2O_3{cdot}66SiO_2{cdot}2TiO_2{cdot}2.5ZrO_2{cdot}1.5P_2O_5{cdot}1.0Na_2O{cdot}1.0As_2O_3$ (wt%) was selected and heat-treated at different heating conditions to obtain transparent glass-ceramic. Nucleation and crystallization behaviour of this composition were estimated by differential thermal analysis (DTA) and X-ray diffractometer (XRD) and its thermal expansion coefficients were measured by Dilatometer. As a result, glass transition temperature was $730^{\circ}C$ and two maximum nucleation temperatures were estimated at $730^{\circ}C$ and 82$0^{\circ}C$ using JMA(Johson-Mehl-Avrami) equation by DTA. $ZrTiO_4$ $\beta$-Quartz solid solution and $\beta$-Spodumene crystals were identified by XRD. The optimum crystallization temperature was 92$0^{\circ}C$ and three step heating schedule was expected to be useful to obtain transparent glass-ceramic.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.4
• /
• pp.192-197
• /
• 2014

Red-emitting nitride phosphors recently attracted considerable attention because of their high thermal stability and high color rendering index properties. For excellent phosphor of white light-emitting-diode, ternary nitride phosphor of $Sr/SmSi_5N_8:Eu^{2+}$ with different $Eu^{2+}$ ion concentration were synthesized by solid state reaction method. In this work, red-emitting nitride $Sr/SmSi_5N_8:Eu^{2+}$ phosphor was successfully synthesized by using multi-step high frequency induction heat treatment. The effects of molar ratio of component and experimental conditions on luminescence property of prepared phosphors have been investigated. The structure and luminescence properties of prepared $Sr/SmSi_5N_8:Eu^{2+}$ phosphors were investigated by XRD and photoluminescence spectroscopy. The excitation spectra of $Sr/SmSi_5N_8:Eu^{2+}$ phosphors indicated broad excitation wavelength range of 300 - 550 nm, namely from UV to visible area with distinct enhanced emission peaks. With an increase of $Eu^{2+}$ ion concentration, the peak position of emission in spectra was red-shifted from 613 to 671 nm. After via multi-step heat treatment, prepared phosphor showed excellent luminescence properties, such as high emission intensity and low thermal quenching, better than commercial phosphor of $Y_3Al_5O_{12}:Ce^{3+}$. Using $Eu_2O_3$ as a raw material for $Eu^{2+}$ dopant with nitrogen gas flowing instead of using commercial EuN chemical for $Sr/SmSi_5N_8:Eu^{2+}$ synthesis is one of characteristic of this work.